CS272467B1

CS272467B1 - Lubricant oil for stomatologic instruments and responsive apparatus

Info

Publication number: CS272467B1
Application number: CS879233A
Authority: CS
Inventors: Pavol Rndr Klucho; Ladislav Ing Szucs; Bohdan Ing Krempasky
Original assignee: Klucho Pavol; Szucs Ladislav; Krempasky Bohdan
Priority date: 1987-12-15
Filing date: 1987-12-15
Publication date: 1991-01-15
Also published as: CS923387A1

Abstract

A lubricating oil for stomatological instruments comprises (a) 70-99.8 wt% of highly refined medicinal vaseline oil with kinematic viscosity 32-65 square mm/sec. at 20 deg.C and solidification point not above -50 deg.C, (b) 0-28% of vegetable or animal oil, and/or (c) 0-10% of esters of monocarboxylic acids and mono-alcohols and/or polyols and/or aliphatic dicarboxylic acids, citric, isocitric, phthalic or terephthalic acid and (un)branched aliphatic mono-alcohols, with mol.wt. 80-800, (d) 0.1-1.5% of polymers with mol.wt. 3,000-120,000, (e) 0.0001-0.1% of a phenolic antioxidant, and (f) 0.0001-0.002% of polysiloxane oils with varying mol.wt., as anti-foam.

Description

Vynález sa týká mazacieho oleja pre stomatologické náradie zostavený na báze ropnéj olejovej zložky zušíachtenej mazivostnými, polymérnymi zahusíujúcimi přísadami, antioxidačnými, antikoróznymi a inými přísadami,BACKGROUND OF THE INVENTION The present invention relates to lubricating oil for dental tools based on an oil-based oil component treated with lubricating, polymeric thickening additives, antioxidant, anticorrosive and other additives,

Doteraz sá na mazanie turbínových násadov stomatologickej vrtačky používá neaditivovaný čistý vazelínový medicinálny olej, ktorý je zmesou tekutých ropných vysokorafinovaných uhíovodíkov, vrůcich nad 360 °C.Until now, it has been using non-additive pure petrolatum medical oil, which is a mixture of liquid petroleum high-refined hydrocarbons boiling above 360 ° C to lubricate the turbine handles of a dental drill.

Funkčná trecie časti, najma guličkove ložiská a hriadele sa poměrně rýchlo 0potrebovávajú, olej oxiduje, stárne a sp8sobuje koróziu kovových častí rozprašovača, zhotoveného z farebných kovov. V dosledku tvorby polymérnych lepivých oxidačných splodín oleja se znižujú funkčné a úžitkové vlastnosti mazacieho oleja na báze neaditívovaného vazelínového medicinálneho oleja.Functional friction parts, especially ball bearings and shafts, are consumed relatively quickly, the oil oxidizes, ages and corrodes the metal parts of the non-ferrous metal sprayer. As a result of the formation of polymeric sticky oxidative fumes of the oil, the functional and performance properties of the lubricating oil based on non-additive petrolatum medical oil are reduced.

Mazací olej podía vynálezu je na báze medicinálneho vazelínového oleja o kineaatickej viskozite 32 až 65 mm^s^-·'' pri 20 °C zušíachteného účinnými mazivostnými přísadami a módifikátormi trenia a opotrebenia ako sú rastlinné oleje: olivový, lanový, palmový, podzemnicový, ricínový, kukuřičný, slnečnicový, sójový, řepkový, hydrcgenačne rafinovaný řepkový olej, fúkaný řepkový olej, fúkaný ricínový olej, destilačné a rafinované frakcie uvedených rostlinných olejov, dimerizované nenasýtené kyseliny z rostlinných olejov alebo ich vzájomné zmesi, Sálej oleje a tuky živočišného p&vodu ako je spermový, rybí, paznechtový lanolínový, kostný olej, loj, bravČová masí a iné,The lubricating oil of the present invention is based on the medicinal vaseline oil on the kineaatickej viscosity of 32-65 mm ^ p ^- · '' at 20 ° C zušíachteného effective lubrication additives, and friction and wear modifiers, such as vegetable oils: olive, linseed, palm, peanut, castor , corn, sunflower, soybean, rapeseed, hydrated refined rapeseed oil, blown rapeseed oil, blown castor oil, distillate and refined fractions of said vegetable oils, dimerized unsaturated acids from vegetable oils or mixtures thereof, , fish, hoof lanolin, bone oil, tallow, pork and others,

Ako Salšie vhodné mazívostné přísady podía tohto vynálezu sa použili zdravotně a hygienicky neškodné a netoxioké estery monokarboxylových a dikarboxylových kyselin s počtom uhlíkov až Ο^θ ako i estery kyseliny citrónovéj a izocitrónovej, ftalovej, tereftalovej a jednomocných alkoholov s počtom uhlíkov až CgQ priamorelazeových alebo rozvětvených alebo ich zmesi, estery monokarboxylových kyselin a polyolov ako sú pentaerytritol, dipentaerytritol, trimetylolpropán, neopentylglykol, glycerín, polymetylolpropán, trimetyloletán, trimetylhexandiol alebo ich vzájomné zmesi.More suitable lubricant additives according to the present invention are the health and hygienically harmless and nontoxic esters of monocarboxylic and dicarboxylic acids with carbon numbers up to Ο θ ako as well as esters of citric and isocitronic, phthalic, terephthalic and monovalent alcohols having carbon numbers up to C 8 or mixtures thereof, monocarboxylic acid esters and polyols such as pentaerythritol, dipentaerythritol, trimethylolpropane, neopentyl glycol, glycerin, polymethylolpropane, trimethylolethane, trimethylhexanediol or mixtures thereof.

Ako účinné polyméme zahusíovače sa v mazacom oleji podía vynálezu používajú polybutény, polyizobutény, polymetakryláty, kopolyméry etylénu a propylénu, styrénu a butadiénu, styrénu a izobutylénu, styrénu a izoprénu o roznej molekulovej hmotnosti a střihových vlastnostiach alebo ich vzájomné zmesi. Použitie vhodných typov zahustovačov - modifikátorov viskozity závisí od požadovaných viskozitnýeh a aerosolových vlastností finálneho oleja.Polybutenes, polyisobutenes, polymethacrylates, copolymers of ethylene and propylene, styrene and butadiene, styrene and isobutylene, styrene and isoprene of different molecular weight and shear properties, or mixtures thereof, are used as effective polymeric thickeners in the lubricating oil of the invention. The use of suitable types of viscosity thickeners depends on the desired viscosity and aerosol properties of the final oil.

Ako antioxidačné přísady sa v mazacom oleji pre zubolekárske nástroje podía vynálezu používajú zdravotně nezávadné, netoxické a vysokorafinované antioxidanty ako sú 2,6-diterč,butyl-4-metylfenol, 2,6-diterč.butylfenol, 2-terc.butyl-4-metoxyfenol, 2-terc.butylhydrochinon, dodecylestery kyseliny galovej, propylester kyseliny galovej, tokoferol alebo ich vzájomné zmesi.The antioxidants used in the lubricating oil for dental instruments according to the invention are non-toxic, non-toxic and highly refined antioxidants such as 2,6-di-tert-butyl-4-methylphenol, 2,6-di-tert-butylphenol, 2-tert-butyl-4- methoxyphenol, 2-tert-butylhydroquinone, gallic acid dodecyl esters, gallic acid propyl ester, tocopherol or mixtures thereof.

Ha zabránenie penenia mazacieho oleja, ktorý sa rozprašuje z rozprašovače pomocou stlačeného vzduchu sa podía vynálezu použily polysiloxanové oleje.According to the invention, polysiloxane oils have been used to prevent foaming of the lubricating oil which is atomized from the atomizer by means of compressed air.

Mazací olej podía vynálezu je určený pre mazanie guličkových ložísk turbínových násadcov a třecích častí stomatologickej vrtačky. Mazací olej sa zo špeciálneho rozCS 272 467 Bl prašovača v podobě olejovej hmly dopravuje stlačeným vzduchom na všetky trecie časti turbínového násadce stomatologickéj vrtačky.The lubricating oil according to the invention is intended for the lubrication of ball bearings of turbine handpieces and friction parts of a dental drill. The lubricating oil is transported from compressed air to all friction parts of the turbine handpiece of the dental drill using a special oil mist powdered powder sprayer.

Keáže je mazací olej pri tomto druhu mazania vystavený oxidačnému účinku vzdušného kyslíka, musí obsahovat vysokoúčinné antioxidanty, ktoré ho chránia proti oxidácii nielen počas prevádzky ale aj skladovania. Okrem toho mazací olej pódia vynálezu vyhovuje ostatným kritériám, ktoré si vyžaduje mazanie olejovou hmlou. Olej má dobré aerosolové charakteristiky, kondenzačně vlastnosti, odlúčivost vzduchu, termic ko-oxidačné vlastnosti, mazacie vlastnosti, antikorozně a protihrdzavostné vlastnosti, nepení a má výhovujúcu životnost.When lubricating oil is exposed to the oxidizing effect of air oxygen in this type of lubrication, it must contain high-performance antioxidants that protect it against oxidation not only during operation but also during storage. In addition, the lubricating oil of the present invention meets other criteria that require oil mist lubrication. The oil has good aerosol characteristics, condensation properties, air separation, thermic co-oxidation properties, lubricating properties, anti-corrosion and anti-corrosion properties, does not foam and has a satisfactory service life.

Mazací olej pódia vynálezu je vhodný na mazanie aj v ostatných mazacích sústavách ako je beztlakové a tlakové olejové mazanie ručně, olejničkou, striekačkou, sprayom, kvapkaním, rozstrekom, hmotovým mazaním atá.The lubricating oil according to the invention is also suitable for lubrication in other lubrication systems such as unpressurized and pressurized oil lubrication by hand, oiler, syringe, spray, drip, spray, mass lubrication etc.

Mazací olej pódia vynálezu určený pre mazanie stomatologického náradia je zostavený na báze základového vazelínového medicinálneho oleja splňujúceho podmienky československého liekopisu ČsL 3 a Salších zušiachtujúcich přísad, ktoré sú netoxické, zdravotně a hygienicky nezávadné a nezapáchájúce.The lubricating oil according to the invention intended for the lubrication of dental tools is composed on the basis of the petroleum jelly base oil meeting the conditions of the Czechoslovak Pharmacopoeia of the Czechoslovak Law No. 3 and other refining additives, which are nontoxic, harmless to health and hygiene and odorless.

Mazací olej podlá vynálezu nekoroduje jemné ložiská a klzné časti turbínového násadca stomatologickéj vrtačky ako i exponované časti špeciélneho rozprašovače zhotoveného z farebných kovov.The lubricating oil according to the invention does not corrode the fine bearings and sliding parts of the turbine handpiece of the dental drill as well as the exposed parts of the special non-ferrous metal sprayer.

Mazací olej pódia vynálezu má oproti doteraz používanému neaditívovánému vazelínovému medicinálnemu olejů lepšie mazacie a protioderové vlastnosti, vyššiu tepelnooxidačnú stabilitu, je nekorozívny na oceli podlá ČSN 41 4220 a médi pódia ČSN 42 3001.The lubricating oil according to the invention has better lubricating and anti-abrasion properties compared to the non-additive petroleum jelly oil used hitherto, higher thermal oxidation stability, it is non-corrosive on steels according to CSN 41 4220 and stage medium CSN 42 3001.

Mazací olej pódia vynálezu možno použit okrem mazania stomatologického náradia aj na mazanie iných jemných prístrojov a mechanizmov.The lubricating oil according to the invention can be used in addition to the lubrication of dental tools also for the lubrication of other fine instruments and mechanisms.

. Základový vazelínový medicinálny olej o kinematickej viskozite 55 mm s pri 20 °C vykázal na štvorguíkovom přístroji záderovú hodnotu 784/882 N a priemernú oderovú stopu pri zatažení 40 kg počas 1 h 0 1,23 mm.. Vaseline medical oil with a kinematic viscosity of 55 mm s at 20 ° C showed a 784/882 N punch value and an average abrasion footprint of 40 kg over 1 h 0 1.23 mm on a four-ball apparatus.

Pre ilustráciu uvádzame příklady, ktorá však neobmedzujú predmet vynálezu.By way of illustration, the following non-limiting examples are provided.

Příklad 1Example 1

Do vazelínové medicinálneho oleja o viskozite 55 mm^s^-^ pri 20 °C sa přidalo 2 % hmotnostně dioktyladipátu, 0,25 % hmotnostných polyizobutylénu s relativnou molekulovou hmctnostou 12 000, 0,0002 % hmotn. 2,6-diterc,butyl-4-metylfenolu a 0,0001 % hmotnostných polysiloxanového oleja. Připravený olej vykázal na štvorguíkovom přístroji záderovú hodnotu 1177/1275 N a priemernú odercvú stopu při zatažení 40 kg počas 1 h 0 1,0 mm. Olej bol nekorozívny na médi a oceli pódia ČSN 42 3C01 resp. 41 4220 a nepenil.To the medicinal vaseline oil with a viscosity of 55 mm ^ ^- ^ at 20 ° C was added 2% by weight of dioctyl adipate, 0.25% by weight of polyisobutylene with a molecular according to weight 12 000, 0.0002% by weight. 2,6-di-tert-butyl-4-methylphenol and 0.0001% by weight of polysiloxane oil. The prepared oil showed a punch value of 1177/1275 N on a four-ball apparatus and an average tear trace of 40 kg over a 1 hour period of 1.0 mm. The oil was non-corrosive on the medium and steel according to ČSN 42 3C01 resp. 41 4220 and did not drank.

CS 272 467 BlCS 272 467 Bl

Příklad 2Example 2

Do vazelínového medicinálneho oleja o kinematickéj viskozitě 65 mm²s při 20 °C sa přidalo 5 % hmotnostných rafinovaného řepkového oleja, 0,25 % hmotnostných polyizobutylénu o relativnéj molekulovej hmotnosti 12 000, 0,0001 % hmotnostných 2,6-diterc. butyl-4-metylfenclu, 0,0001 % hmotnostných polysiloxanového oleja.To the vaseline medical oil with a kinematic viscosity of 65 mm ² s at 20 ° C was added 5% by weight of refined rapeseed oil, 0.25% by weight of polyisobutylene having a relative molecular weight of 12,000, 0.0001% by weight of 2,6-diter. butyl-4-methylphenol, 0.0001% by weight of polysiloxane oil.

Připravený olej vykázal na štvorguíkovom přístroji záderovú hodnotu 1275/1372 Ií a priemernú oderovú stopu pri. zatažení 40 kg počas 1 h 0 0,92 mm. Olej bol nekorozívny na oceli a médi pódia ČSN 41 4220 resp. 42 3001 a nepenil.The prepared oil showed a 1275/1372 µl punch value and an average abrasion footprint at a 4-ball apparatus. load 40 kg in 1 h 0 0,92 mm. The oil was non-corrosive on steel and medium according to ČSN 41 4220 resp. 42 3001 and did not drank.

Příklad 3Example 3

Do vazelínového medicinálneho oleja o viskozitě 60 mm s sa přidalo 8 % hmotnostných rafinovaného řepkového oleja, 0,5 % hmotnostných polymetakrylátu, 0,002 % hmotnostných 2,6-ditere.butyl-4-metylfenolu a 0,0001 % hmotnostných polysiloxanového oleja.To the petrolatum medical oil having a viscosity of 60 mm s, 8% by weight of refined rapeseed oil, 0.5% by weight of polymethacrylate, 0.002% by weight of 2,6-di-butyl-4-methylphenol and 0.0001% by weight of polysiloxane oil were added.

Připravený olej vykázal na štvorguíkovom přístroji záderovd hodnotu 1383/1550 N a priemernú oderovú stopu pri zatažení 40 kg počas 1 h 0 0,49 mm. Olej bol nekorozívny na oceli a médi pódia ČSN 41 4220 resp. 42 3001 a nepenil.The prepared oil showed a 1383/1550 N value and a mean abrasion trace of 40 kg over a 1 hour period of 0.49 mm on a four-pin hitch machine. The oil was non-corrosive on steel and medium according to ČSN 41 4220 resp. 42 3001 and did not drank.

Claims

OBJECT OF THE INVENTION

1. Lubricating oil for dental tools consisting of 70 to 99.0% by weight. a highly refined petrolatum medical oil having a kinematic viscosity of 32 to 65 mm ² s ^-1 at 20 ° C and a freezing point of -5 ° C or less, characterized in that it contains vegetable and / or animal origin oils and / or monocarboxylic acid ester oils and % of monohydric alcohols and / or polyols and / or aliphatic dicarboxylic acids, citric, isocitronic, phthalic or terephthalic acid and monovalent aliphatic straight chain or branched alcohols having an average molecular weight of 80 to 800 or mixtures thereof in an amount of 0.1 to 29.8% by weight. high molecular weight polymers having an average molecular weight of 3000 to 120,000 in an amount of 0.1 to 1.5% by weight; and polysiloxane oils of variously large molecular weights as antifoam agents in an amount of 0.00001 to 1.0C01 wt. and calculated on the resulting oil.

2. Lubricating oil according to Claim 1, characterized in that it may be treated by the addition of essential oils such as menthol