CS271900B1

CS271900B1 - Mixture for production of minigolf balls on plastic base

Info

Publication number: CS271900B1
Application number: CS887618A
Authority: CS
Inventors: Frantisek Ing Kadlec
Original assignee: Frantisek Ing Kadlec
Priority date: 1988-11-21
Filing date: 1988-11-21
Publication date: 1990-12-13
Also published as: CS761888A1

Abstract

The composition of mixtures provide better processing properties, long-term durability and better conditions of the production of mini-golf balls, while it solves their required properties on a large scale, various toughness, cold resistance, hardness, bounce, weight and colour.The mixture for the production of mini-golf balls based on the plastics, of a paste-like to loose- slurry consistence, consists of a paste forming PVC with the combination with that of a non-paste-forming character, further copolymer vinyl chloride/ethylene/ vinyl acetate and softeners dioctyl phthalate, or also dibutyl phthalate, dioctyl adipate and chloroparaffin. The mixture can also further contain polyethylene powder or copolymer vinyl chloride/propylene or even chlorinated polyethylene and also powdery or scale butadiene acrylonitrile and powdery lead oxide (II) or barium sulphate and also other additives.The composition and consistency of these mixtures enable to close the press mould no sooner than after it is filled. By this, the filling of each half of the mould by mixtures of different colours or filling in layers by the mixtures of the different colours (of the same quality) is possible, by which the multicoloured balls and balls being coloured throughout the whole mould are obtained. This also enables the production technology of the balls being mottled in different colours. By addition of lead (II) oxide or, with a smaller effect, of barium sulphate, the weight of the balls can be substantially increased. Additionally, the composition and consistency of these mixtures enable their easier conversion - reprocessing into granulate, from which it is possible to produce mini-golf balls by the technologies of the injection.

Description

Směs pro výrobu minigolfových míčků na bázi plastů, těstovité až sypko-kašovité konzistence, obsahuje pastotvorný polyvinylchlorid v kombinaci s nepastotvorným, dále kopolymer vinylchlorid/ethylén/vinylacetát a změkčovadla dioktylftalát, nebo také dibutylftalát, dioktyladipát a chlorparafín.The mixture for producing mini-golf balls based on plastics, pasty to loose consistency, comprises paste-forming polyvinyl chloride in combination with a non-paste-forming agent, vinyl chloride / ethylene / vinyl acetate copolymer and plasticizers dioctyl phthalate or also dibutyl phthalate, dioctyladipate and chloro paraffin.

Směs může dále obsahovat práškový polyetylén nebo kopolymer vynilchlorid/propylén, nebo i chlorovaný polyethylén a také práškový nebo šupinkový butadiénakrylonitril a práškový oxid olovnatý nebo síran barnatý a i další přísady.The composition may further comprise polyethylene powder or vinyl chloride / propylene copolymer, or even chlorinated polyethylene, as well as butadiene acrylonitrile powder or flakes and lead oxide or barium sulfate powder and other additives.

Skladba a konzistence těchto směsí umožňuje uzavření lisovací formy až po naplnění. Tím je možno plněni každé poloviny formy-směsmi odlišné barvy nebo plnění po vrstvičkách směsmi různých barev (o stejné jakosti),čímž se získají míčky vícebarevné a probar\ené v celé hmotě. Rovněž je tím umožněna technolo gie výroby míčků žíhaných (kropenatých) v různých barvách. Přísadou oxidu olovnatého, nebo s menším účinkem síranu bárnatého je možné výrazně zvyšovat hmotnost míčků. Dále skladba a konzistence těchto směsí umožňuje jejich snadnější převod - přepracování na granulát, ze kterého je pak možné vyrábět minigolfové míčky technologiemi vstřikování.The composition and consistency of these mixtures allows the mold to be closed only after filling. In this way, it is possible to fill each half of the mold with mixtures of different colors or to fill in layers with mixtures of different colors (of the same quality) to give the balls multicolored and colored throughout the mass. It also makes it possible to produce the technology of annealed (speckled) balls in different colors. By adding lead oxide, or with less effect of barium sulfate, it is possible to significantly increase the weight of the balls. Furthermore, the composition and consistency of these blends makes it easier to convert them into granules, from which it is then possible to produce mini golf balls by injection molding technology.

rr

CS 271900 BlCS 271900 Bl

Vynález se týká směsi pro výrobu minigolfových míčků na bázi plastů.BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a composition for the production of plastic-based mini golf balls.

Dosud známá složení směsí pro výrobu minigolfových míčků (dále jen MGM) na bázi plastů jsou jednak ve formě tekuté pasty na bázi pastotvorného polyvinylchloridu (PVC), nebo ve formě granulí či prášků na bázi tavitelných plastů, přičemž způsob výroby MGM spočívá v nalévání či vstřikování tekuté pasty, nebo vstřikování roztavených plastů, otvory do uzavřených forem.The compositions known to date for the manufacture of mini-golf balls (hereinafter referred to as MGM) based on plastics are either in the form of a liquid paste based on pasty-forming polyvinyl chloride (PVC) or in the form of granules or powders based on fusible plastics. liquid paste, or injection of molten plastic, openings into closed molds.

Složeni tekuté pasty sestává z pastotvorného PVC, změkčovedel a dalších přísad. Příklad takové skladby je uveden v tabulce, směs č. B.The liquid paste composition consists of paste-forming PVC, plasticizers and other additives. An example of such a composition is given in the table, Mix No. B.

Nevýhodou pasty je její nezbytná tekutost, přičemž doba její zpracovatelnosti je poměrně krátká, jeden, maximálně 3 týdny. Pasta postupně ryohle houstne a v netekutém stavu není už uvedeným způsobem zpracovatelná. Dále taková pasta neumožňuje výrobu míčků v parametrech širokého sortimentu. Další nevýhodou výroby míčků z pasty PVC nebo z tavitelných plastů je jednobarevné provedení MGM. Tento nedostatek je nahrazován různými povrchovými úpravami, jako nátěry, lakováním apod. Takové povrchové vrstvičky se brzy opotře bí a tím se opět obnaží původní vzhled jednobarevného míčku.The disadvantage of the paste is its necessary flowability, while its pot life is relatively short, one, maximum 3 weeks. The paste gradually thickens rapidly and is not workable in the non-liquid state. Furthermore, such a paste does not allow the production of balls in a wide range of parameters. Another disadvantage of producing balls from PVC paste or fusible plastics is the monochromatic MGM design. This drawback is replaced by various surface treatments, such as paints, varnishes, etc. Such surface layers will soon wear off and thus reveal the original appearance of the monochromatic ball.

Tyto nedostatky odstraňuje směs pro výrobu minigolfových míčků na bázi plastů, podle vynálezu, jehož podstatou je, že tato směs obsahuje 5 až 30 hmotnostníph % pastotvorného polyvinylchloridu v kombinaci s 10 až 60 hmotnostními % nepastotvorného polyvinylchloridu- suspenzního nebo /a emulzního, nebo/a s 2 až 40 hmotnostními % kopolymerů vinylchlorid/etylén/vinylacetátu, dále 15 až 40 hmotnostních % dioktylftalátu nebo/a dibulftalátu, nebo je jich směsi s dioktyladipátem a/nebo s 0,5 až 5 hmotnostními % ohlorparafinu, všechno v souhrnu v různých kombinacích podle požadované houževnatosti, mrazuvzdornosti, tvrdosti a odskoku míčku.These drawbacks are overcome by the composition for the production of plastic-based mini golf balls according to the invention, which comprises 5 to 30% by weight of a paste-forming polyvinyl chloride in combination with 10 to 60% by weight of a non-mono-forming polyvinyl chloride-suspension and / or emulsion; 2 to 40% by weight of vinyl chloride / ethylene / vinyl acetate copolymers, furthermore 15 to 40% by weight of dioctyl phthalate and / or dibulphthalate, or mixtures thereof with dioctyl adipate and / or 0.5 to 5% by weight of paraffin, all combined in various combinations according to required toughness, frost resistance, hardness and ball bounce.

Za účelem úpravy některých dalších vlastností, jako zvýšení tuhosti, odolnosti vůči nárazu, útlumu nebo zvýšení elasticity obsahuje směs 1 až 30 hmotnostních % práškového polyetylénu, nebo kopolymerů vinylchlorid/propylénu, nebo/a 0,5 až 20 hmotnostních % chlorovaného polyetylénu, nebo/a 1 až 25 % práškového nebo šupinkového butadiénakrylonitrilu. Za účelem zvýšení hmotnosti míčků obsahuje dále směs 1 až 60 hmotnostních % oxidů olovnatého, nebo síranu barnatého.In order to modify some other properties, such as increasing stiffness, impact resistance, damping or elasticity, the mixture comprises 1 to 30% by weight of polyethylene powder or vinyl chloride / propylene copolymers, and / or 0.5 to 20% by weight of chlorinated polyethylene, and / or and 1 to 25% butadiene acrylonitrile powder or flakes. In order to increase the weight of the balls, it further comprises a mixture of 1 to 60% by weight of lead oxides or barium sulfate.

Dále směs obsahuje běžné přísady, jako tepelné stabilizátory, pigmenty, plniva a případně i jiné chemikálie.Furthermore, the mixture contains conventional additives such as heat stabilizers, pigments, fillers and possibly other chemicals.

Vyšší účinky vynálezu spočívají jednak v příznivé konzistenci směsi, která umožňuje náhradu tekuté pasty o krátkodobé životnosti, směsí s dlouhodobou zpracovatelskou životností (3 až 12 měsíců), která svou těstovitou až sypkokašovitou·e tím netekutou konzistencí umožňuje uzavření lisovací formy až po samostatném naplnění obou polovin, čímž je umožněno plnění každé poloviny formy směsmi odlišné barvy (stejné jakosti), to znamená výrobu míčků dvoubarevných, nebo plněním po vrstvičkách, výrobu míčků vícebarevných, nebo i žíhaných (kropenatých) v různých barvách. Dále umožňují tyto směsi výrobu míčků o široké škále požadovaných vlastností - o různých tvrdostech, různé houževnatosti, mrazuvzdornosti, o různém odskoku či útlumu (volným pádem z výše 1 m na rovný kamenný podklad), od nulového útlumu až po odskod do výše 50 cm, a také o různé hmotnosti.Higher effects of the invention consist in the favorable consistency of the composition which allows the replacement of the short-life liquid paste, the composition with a long working life (3 to 12 months) which by its pasty to loose consistency and the non-flowable consistency halves, thereby allowing each half of the mold to be filled with mixtures of different colors (of the same quality), i.e., to produce bicolour balls, or to fill them in layers, to produce multicolored balls, or even annealed (speckled) balls in different colors. Furthermore, these blends allow the production of balls with a wide range of required properties - different hardness, different toughness, frost resistance, different rebound or attenuation (free fall from a height of 1 m to a flat stone surface), from zero attenuation to 50 cm and also different weights.

Dále směsi podle vynálezu jsou snáze převoditelné (zpracovatelné) na granulát, který lze pak použít na výrobu minigolfových míčků známými technologiemi vstřikování.Further, the compositions of the invention are more easily convertible into granules which can then be used to produce mini golf balls by known injection molding techniques.

V následující tabulce jsou uvedeny konkrétní příklady skladby směsí v hmotnostních %, včetně základních parametrů finálních minigolfových míčků. - Pro srovnání je zde uvedenaThe following table gives specific examples of the weight composition of the blends, including the basic parameters of the final minigolf balls. - It is given here for comparison

CS 271900 Bl skladba tekuté pasty, směs 6. 8, včetně parametrů finálních míčků.CS 271900 B1 liquid paste composition, mixture 6.8, including final ball parameters.

Směs čísloMixture number

1 1 2 2 3 3 4 4 5 5 6 6 7 7 8 8 Pastotvorný polyvinylchloríd Pasting polyvinyl chloride 20 20 May 15 15 Dec 10 10 10 10 5 5 12 12 5 5 65 65 Nepastotvorný PVC - suspenzní Non-permanent PVC - suspension 55 55 35 35 24 24 22 22nd 22 22nd 10 10 12 12 - - Nepastotvorný PVC - emulzní Non-permanent PVC - emulsion - - 11 11 - - - - - - - - - - - - Kopolymer vinylchlorid/etylén/ Vinyl chloride / ethylene / copolymer vinylacetát vinyl acetate - - - - 22 22nd 18 18 20 20 May 40 40 11 11 - - Práškový polyetylén nebo kopo- Polyethylene or copolymer powder lymer vinylchlorid (propylén) Lymer vinyl chloride (propylene) - - - - - - - - - - 1 1 - - - - Chlorovaný polyetylén Chlorinated polyethylene - - - - - - 6 6 - - - - 0,5 0.5 - - Práškový nebo šupinkový Powdered or flaked butadiénakryloni trii butadiene acrylonitrile trii - - - - - - - - 10 10 - - 1 1 - - Dioktylftalát Dioctyl phthalate 15 15 Dec 20 20 May 12,6 12.6 15 15 Dec 15,6 15.6 10 10 7 7 32 32 Dibutylftalát Dibutyl phthalate 3 3 5 5 14 14 7,6 7.6 15 15 Dec 12 12 7,3 7.3 - - Dioktyladipát Dioctyladipate - - 4 4 8 8 - - 8 8 2 2 - - Chlorparafín Chloroparaffin 2 2 2 2 2,9 2.9 2,9 2.9 2,9 2.9 5 5 0,5 0.5 - - Oxid olovnatý Lead oxide - - - - - - - - - - - - 50 50 - - nebo síran barnatý or barium sulfate Tepelný stabilizátor Thermal stabilizer 0,2 0.2 0,2 0.2 0,2 0.2 0,2 0.2 0,2 0.2 0,2 0.2 0,2 0.2 1 1 Pigmenty (v béčové formě) Pigments (in bean form) 0,2 0.2 0,5 0.5 0,2 0.2 0,3 0.3 1,2 1,2 1,1 1.1 0,5 0.5 1 1 Plniva a jiné přísady Fillers and other additives 4,6 4.6 11,3 11.3 10,1 10.1 10 10 8,1 8.1 0,7 0.7 3 3 1 1 Celkem Total 100 100 ALIGN! 100 100 ALIGN! 100 100 ALIGN! 100 100 ALIGN! 100 100 ALIGN! 100 100 ALIGN! 100 100 ALIGN! 100 100 ALIGN! Základní parametry Basic parameters minigolfových míčků minigolf balls Tvrdost Sh A Sh A hardness 98 98 85 85 75 75 ' 70 '70 65 65 73 73 80 80 77 77 Odskok z výše 1 cm v cm Bounce from above 1 cm in cm 50 50 20 20 May 0 0 5 5 10 10 7 7 0 0 10 10 hmotnost v g weight in g 43 43 47 47 45 45 44 44 44 44 43 43 80 80 43 43

Využití vynálezu je možné především v plastikářském průmyslu, ale i ve výrobních družstvech, či v přidružené výrobě apod., s konečným ptomítnutím využití finálních výrobků - minigolfových míčků - v rekreačních zařízeních, v sportovních areálech, tělovýchovných jednotách apod.Application of the invention is possible mainly in the plastics industry, but also in production cooperatives, or in associated production, etc., with the final question of the use of the final products - minigolf balls - in recreational facilities, sports facilities, sports units etc.

Claims

SUBJECT OF THE INVENTION

A composition for the production of plastic-based mini golf balls, characterized in that it contains 5 to 30% by weight of palatable polyvinyl chloride in combination with 10 to 60% by weight of a non-mono-polyvinyl chloride - euapensive and / or emulsion, and / or β 1 to 40 % of vinyl chloride / ethylene / vinyl acetate copolymers, furthermore 15 to 40% by weight of dioctyl phthalate and / or dibutyl phthalate, or mixtures thereof, and dioctyl adipate and / or with 0.5 and 5% by weight of chloro paraffin.

2. A composition for producing balls according to claim 1, further comprising from 1 to 30% by weight of polyethylene powder or vinyl chloride / propylene copolymers, and / or from 0.5 to 20% by weight of chlorinated polyethylene, and / or from 1 to 25% by weight. of powdered or flaked butadiene acrylonitrile, and / or 1 to 60% by weight of lead oxide and / or barium sulfate.