CS270656B1 - Processing method for obtaining red glazing on products made from glass without blue film - Google Patents
Processing method for obtaining red glazing on products made from glass without blue film Download PDFInfo
- Publication number
- CS270656B1 CS270656B1 CS866352A CS635286A CS270656B1 CS 270656 B1 CS270656 B1 CS 270656B1 CS 866352 A CS866352 A CS 866352A CS 635286 A CS635286 A CS 635286A CS 270656 B1 CS270656 B1 CS 270656B1
- Authority
- CS
- Czechoslovakia
- Prior art keywords
- glass
- firing
- glaze
- blue film
- processing method
- Prior art date
Abstract
Nežádoucímu modrému nádechu červeně lazury, ziekané z lazurovaci eměei na bázi sloučenin mědi, ee zamezi při druhém výpalu v redukčni atmosféře, při kterém se na lazurovaný povrch skláněného předmětu působí plynem, u něhož obsah síry nepřekročí 0,001 % hmotnosti.Unwanted blue tint in red glaze, stained from glaze em based on copper compounds, ee is avoided on the other firing in reducing atmosphere, at which is tilted to the glazed surface the object acts by a gas in which the content sulfur shall not exceed 0,001% by weight.
Description
Vynález se týká způsobu získání červené lazury na povrchu skleněných předmětů bez modrého filmu. Na povrch skleněných předmětů se nanese lazurovaci směs na bázi sloučenin mědi, která se po vysušeni vypálí třemi výpaly, a to nejprve v oxidační atmosféře, po umytí při druhém výpalu v redukční atmosféře a při třetím výpalu v oxidační atmosféře .The invention relates to a method for obtaining a red stain on the surface of glass articles without a blue film. A glazing mixture based on copper compounds is applied to the surface of the glass objects, which, after drying, is fired by three firings, first in an oxidizing atmosphere, after washing in a second firing in a reducing atmosphere and in a third firing in an oxidizing atmosphere.
Lazura je chemické zabarvení povrchových vrstev skla, které je vyvolané difúzí barvicích složek do skla za zvýšené teploty. Barvivo ve směsi s okrem či kaolínem se nanese ve formě vodné nebo terpentinové suspenze na povrch skla. Lazurovaci směs se vysuěí a následují výpaly, jejichž počet a teplotní podmínky závisí na druhu lazurovaci směsi a na požadované barvě konečné lazury.Stain is a chemical coloration of the surface layers of glass, which is caused by the diffusion of coloring components into the glass at elevated temperatures. The dye, mixed with kaolin or kaolin, is applied in the form of an aqueous or turpentine suspension to the glass surface. The staining mixture is dried, followed by firing, the number and temperature conditions of which depend on the type of staining mixture and on the desired color of the final stain.
Lazury jsou stříbrné nebo měděné.The stains are silver or copper.
Stříbrná lazura se získá z lazurovaci směsi na bázi stříbra, např. chloridů, uhličitanů, dusičnanů atříbra, s okrem, kaolinem, jílem, oxidem želazitým smíchaným s vodou, terpentinovým olejem nebo lihem. Stříbrné soli se při výpalu redukuji, vnikají do povrchu skla a zabarvuji jej světle žlutě až žlutohnědě.The silver glaze is obtained from a glazing mixture based on silver, e.g. chlorides, carbonates, nitrates and silver, with the exception of kaolin, clay, iron oxide mixed with water, turpentine oil or alcohol. Silver salts are reduced during firing, penetrate the surface of the glass and turn a light yellow to yellow-brown color.
Sloučeninami mědi se lazuruje žlutozeleně, černě a rubínově červeně. Příprava lazurovaci směsi je shodná jako u lazury stříbrné s tím rozdílem, že ee nahradí sloučeniny stříbra síranem měSnatým. Po vysušení se lazurovaci směs vypaluje dvakrát pro získání lazury černé a třikrát pro získáni lazury červené, která připomíná rubínové sklo barvené zlatém. Při prvním výpalu se lazurovaci směs vypaluje v komorové peci při oxidační atmosféře. Po umytí povrchu skleněného předmětu s lazurovaci směsí a případně přeleštění povrchu se provádí druhý výpal v poklopové peci při redukční atmosféře. Třetí výpal se provádí v pásové peci v oxidační atmosféře. Pro určitý typ skla a složeni lazurovecí směsi se volí doba vypalováni a výška teplot jednotlivých výpalů, aby získaná lazura na konečných výrobcích měla stejné zabarveni při větších sériích výrobků.Copper compounds are used to glaze yellow-green, black and ruby red. The preparation of the glaze mixture is the same as for the silver glaze, except that ee replaces the silver compounds with copper sulphate. After drying, the glaze mixture is fired twice to obtain a black glaze and three times to obtain a red glaze resembling a ruby glass colored gold. During the first firing, the glazing mixture is fired in a chamber furnace under an oxidizing atmosphere. After washing the surface of the glass object with the glazing mixture and possibly polishing the surface, a second firing is carried out in a lid furnace under a reducing atmosphere. The third firing is performed in a belt furnace in an oxidizing atmosphere. For a certain type of glass and the composition of the staining mixture, the firing time and the temperature of the individual firings are chosen so that the stain obtained on the final products has the same color for larger series of products.
Lazurované výrobky se dále zušlechťují např. leptáním, broušením nebo rytím podle žádaných motivů, čímž vznikají výrazné efekty obdobně jako při probrušování vrstveného odlišně zabarveného skla.Glazed products are further refined, for example, by etching, grinding or engraving according to the desired motifs, which creates significant effects similar to the sanding of laminated glass of different colors.
Dodrženi reprodukovatelné barvy a kvality zejména červené lazury js obtížné a vyžaduje přesné dodržováni technologického postupu. Často se při druhém výpalu objevuje nežádoucí modrý film, jehož zabarvení znehodnocuje lazurovaný výrobek. Tento film je nutno z povrchu výrobku odstraňovat, většinou mechanickým leštěním, což Je další technologická operace.Adherence to the reproducible color and quality, especially of the red glaze, is difficult and requires strict adherence to the technological process. Unwanted blue film often appears during the second firing, the color of which degrades the glazed product. This film must be removed from the surface of the product, usually by mechanical polishing, which is another technological operation.
Uvedené nevýhody se odstřeni nebo podstatně omezí řešením podle vynálezu, Jehož podstata spočívá v tom, že na lazurovaný povrch skleněných předmětů se působí při druhém výpalu v redukční atmosféře plynem, u něhož obeah eiry nepřekročí 0,001 % hmotnosti,These disadvantages are eliminated or substantially reduced by the solution according to the invention, the essence of which consists in that the glazed surface of glass objects is treated during the second firing in a reducing atmosphere with a gas in which the weight does not exceed 0.001% by weight.
Tímto způsobem se získá červená lazura bez nežádoucího modrého nádechu, čímž odpadá technologická operace Jejího odstraňováni, a dochází tak k úsporám na výrobních nákladech i zlepšeni pracovního prostředí.In this way, a red glaze is obtained without an undesired blue tinge, which eliminates the technological operation of its removal, and thus saves on production costs and improves the working environment.
Při zkoumáni zamezení modrého filmu na červeně lazurovaných skleněných výrobcích se zjistilo, že modrý film tvoři převážně sulfidy mědi, které vytvářejí na povrchu skleněného předmětu zrcsdlo, podobně antireflexnímu povlaku na čočkách objektivů. Bylo zjištěno, že zvýšený počet modrého zabarveni červené lazury vzniká po druhém, ale i třetím výpalu, kdy skleněné předměty přicházejí do styku s plynem obsahujícím až 0,2 % hmotnosti síry, která se za určitých podmínek slučuje s mědí na sulfidy.When examining the prevention of blue film on red-glazed glass products, it was found that the blue film consists predominantly of copper sulfides, which form a mirror on the surface of the glass object, similar to the anti-reflective coating on objective lenses. It was found that an increased number of blue discoloration of the red glaze occurs after the second but also the third firing, when glass objects come into contact with a gas containing up to 0.2% by weight of sulfur, which under certain conditions combines with copper to sulfides.
Účinky řešení vynálezu Jsou déle objasněny na příkladném provedení.The effects of the present invention are further elucidated by way of example.
Na skleněné užitkové předměty, např. vázy, mísy, dózy, kališkovinu apod., se nanese štětcem nebo střlkaci pistoli stejnoměrná vrstva lazurovaci směsi, připravené smi2On glass utility objects, eg vases, bowls, jars, goblets, etc., apply an even layer of glazing mixture, prepared with a brush, with a brush or spray gun.
CS 270 656 Bl chánlm modré skalice s okrem a vodou na hustou Jemnou kaši. Nanesená lazurovací směs se nechá volně uschnout. Po vyschnuti následuje první výpal lazurovací směsi v komorové peci při oxidační atmosféře. Po vypálení se s povrchu skleněného předmětu smyje lazurovací směs a povrch skla se přeleští. Získaná barva Je slabě žlutozelená. Druhý výpal se provádí v poklopové peci v redukční atmosféře, vytvořené buň dálkovým plynem přečištěným odsiřovacím zařízením tak, aby obsah síry nepřekročil 0,001 % hmotnosti, nebo n čistým propanem, případně butanem. Při druhém redukčním výpalu dochází k redukci difundovaných lontů mědi přes oxid mě3ný na kovovou mě3. Získaná barva povrchu skleněného předmětu ja černá. Třetí výpal se provádí v pásové peci při oxidační atmosféře a získá u se konečná barva lazury rubínově červená.CS 270 656 Bl khanlm blue rock with addition and water to a thick fine slurry. The applied glaze mixture is allowed to dry freely. After drying, the first firing of the glaze mixture follows in a chamber furnace under an oxidizing atmosphere. After firing, the glaze mixture is washed from the surface of the glass object and the glass surface is polished. The color obtained is slightly yellow-green. The second firing is carried out in a lid furnace in a reducing atmosphere formed by the cells with a remote gas-purified desulfurization device so that the sulfur content does not exceed 0.001% by weight, or with pure propane or butane. In the second reduction firing, the diffused copper ions are reduced via copper oxide to metallic copper. The obtained color of the surface of the glass object is black. The third firing is performed in a belt furnace in an oxidizing atmosphere to give in the final color of the ruby red stains.
Popsaného způsobu lze využít i pro zamezeni vzniku modrých filmů na povrchu zrcadlových skel do brýlí, Jež Jsou rovněž tímto filmem znehodnocovány.The described method can also be used to prevent the formation of blue films on the surface of mirror glasses into glasses, which are also degraded by this film.
Claims (1)