CS267751B1

CS267751B1 - Structural plate

Info

Publication number: CS267751B1
Application number: CS857660A
Authority: CS
Inventors: Juraj Ing Dudas; Ladislav Ing Csc Reinprecht; Peter Ing Csc Vercimak; Anton Ing Csc Osvald; Alexander Ing Csc Krakovsky; Juraj Ing Csc Mahut
Original assignee: Dudas Juraj; Ladislav Ing Csc Reinprecht; Peter Ing Csc Vercimak; Osvald Anton; Alexander Ing Csc Krakovsky; Juraj Ing Csc Mahut
Priority date: 1985-10-28
Filing date: 1985-10-28
Publication date: 1990-02-12
Also published as: CS766085A1

Abstract

Riešenie se týká,z loženia konstrukčně; došky, ktorá splňa komplexně požia-. dávky na tepelné a zvukovoizo ta čně vlastnosti, vlhkostnú, požiarnu i biologický odolnost. Konštrukčné doska pozostáva z nosného rámu alebo roštu, opláštovacieho velkoplošného materiálu na báze dřeva, ktorý je retardačně upravený a výplně. Podstatou riešenia je, že,medzi oplášfovacim materiálom je aspoň jedna vrstva výplně z tepelnoizolačněho materiálu na báze fenolplastov s obsahom 1 až 2C " hmot. zmesného esteru kyseliny fosforečnej na báze fenolu a izopropylfenolov s minimálnym obsahom fosforu 7,5 ‘ί. hmot. a 5 až 25 % hmot. práškového oxidu křemičitého, pričom % hmotnostně su vztiahnuté na množstvo sušiny fenol formaIdehydovej živice. Využitie konštrukčnej došky Je možně vo výrobě panelov pre drevostavby, v staveb nictve, prevýrobu obkladov a podhtadov ako aj pri výrobě dveri.The solution relates to the load bearing structure; thatch, which complies with the benefits for thermal and acoustic properties, moisture, fire and biological resistance. The design board consists of supporting frame or grate, sheathing large-scale wood-based material which is retarded and filled. The essence of the solution is that, between the sponge material is at least one a layer of filler from a thermal insulation material based on phenolplasts containing 1 to 2C "by weight mixed ester of the acid Phosphorous based on phenol and isopropylphenols with a minimum phosphorus content 7.5 ‘ί. wt. and 5 to 25 wt. powder % silica, with% by weight are based on the amount of dry matter phenol Formaldehyde resin. exploitation construction dock It is possible in production panels for wooden buildings, in buildings manufacture of tiles and underlays as well as in the manufacture of doors.

Description

Vynález rieši zloženie konštrukčnej došky s výplňou z tepelnoizolačného materiálu na báze f enolpl a s tov .The invention solves the composition of a construction board with a filling made of thermal insulation material based on phenolpl and s tov.

U doteraz známých konštrukčných dosák vyrábáných na báze dřeva a dřevných materiálov oplášrovených velkoplošnými materiální, upevněnými na nosnou ráme clebo rošte, bývá vnútorný priestor vyplněný roznymi materiálmi, ako sů vlnitá lepenka, minerálně vlákna, rošty z dřevovláknitých materiálov, dřevené rošty, celodrevné výplně, polystyrén a pod. Používané výplňové materiály a ich kombinácie nesptňajú komplexné požiadavky na odolnost voč i navlhavosti, horeniu, t epelne j a zvukovej izolácii.In the hitherto known construction boards produced on the basis of wood and wood materials clad with large-area materials, fixed to the supporting frame or grate, the interior is filled with various materials, such as corrugated cardboard, mineral fibers, gratings made of fibrous materials, wooden gratings, all-wood panels etc. The used filling materials and their combinations do not meet the complex requirements for resistance to moisture, moisture, heat and sound insulation.

Uvedené nedostatky sú odstránené konštrukčnou doskou podlá vynálezu, pozostávajúcou Z nosného rámu alebo roštu, opiášlovácitho velkoplošného materiálu, na báze dřeva a vnůtornej výplně, ktorej podstatou je, že nedzi opláštovacím materiálem je aspoň jedna vrstvy výplně z tepelno izotačného materiálu na báze fendplastov s obsahom 1 až 2C Xh.ict. zmesného esteru kyseliny fosforečnej na báze fenolu a izopropylfenolov s minimálnym obsahom fosforu 7,5 Zhmot. a 5 až 25 Zhmot. práškového oxidu křemičitého, p r i č ó a Zhr.ot. sú vztíahnuté na množstvo sušiny feno l formaldehydo vej Živice. Výplň konštrukčnej došky nože byt tvořená aj viacerými vrstvami. Okrem tepelno izolačného materiálu na báze fenolplastov može obsahovat aj 1 až 2 vrstvy minerálnych vlákien.Said drawbacks are eliminated by a construction board according to the invention, consisting of a supporting frame or grate, a opaque large-area material, based on wood and an inner filling, the essence of which is that the lower cladding material is at least one layer of filling of thermal isotonic material based on fendplasts containing 1. to 2C Xh.ict. of a mixed ester of phosphoric acid based on phenol and isopropylphenols with a minimum phosphorus content of 7.5 wt. and 5 to 25 wt. of silica powder, p r i č ó and Zhr.ot. are based on the dry matter content of phenolic formaldehyde resin. The filling of the structural thatched knife flat also consists of several layers. In addition to the thermal insulation material based on phenol plastics, it can also contain 1 to 2 layers of mineral fibers.

Výhody vynálezu spočivajú v tom, že použitý tepelno izolačný materiál na báze fenolplastov ako výplň konštrukčnej došky vykazuje vysoků přilnavost k materiálem na báze dřeva, čim konštrukčná desky dosiahne vysoků pevnost pri relativné nizkej hmotnosti. Úplným vyplněním priestoru v konštrukčnej desk? sa zabráni pohybu vlhkosti v priereze desky, pričom tepelno izotačný materiál je vodovzdorný a má dobré tepelné a izolačné vlastnosti. Použitím modifikovaného tepelno izolačného materiálu na báze fenoplastov a retardačně upraveného velkoplošného materiálu na báze dřeva, sa zlepšujú poži arno-1echnické vlastnosti konštrukčnej desky. Při kombinácií výplně fenolplastu s minerálnym vláknem sa Jo s i ohnu ďalšie požadované vlastnosti konštrukčnej došky, najrnS pružnost jádra voči pláštu došky tam, kde posobia změny v zataženi a kde by tým mohlo doj st k prasknutiu sice pevného, ale křehkého jadra vo vnútri konštrukčnej desky. Fenolplast v kombinácii s minerálnym vláknem zaistuje, že výplň minerátnych vlákien nepadá do spodných části panelov pri přepravě a montáži a tým zaručuje požadovánu tepelnú a zvukovú izoláciu a ďalšie vlastnosti v priereze panelu.The advantages of the invention are that the phenolplast-based thermal insulation material used as a filler for the construction board shows high adhesion to the wood-based material, whereby the construction board achieves high strength at a relatively low weight. Completely filling the space in the construction board? moisture is prevented from moving in the cross section of the board, while the heat-insulating material is waterproof and has good thermal and insulating properties. By using a modified thermal insulation material based on phenoplasts and a retardation-sized large-area wood-based material, the fire-technical properties of the construction board are improved. When combining a phenolic plastic filler with a mineral fiber, other desired properties of the structural sheet are avoided, in particular the resilience of the core to the sheet shell, where it causes changes in tension and where a solid but brittle core inside the structural plate could rupture. Phenolplast in combination with mineral fiber ensures that the mineral fiber filling does not fall into the lower part of the panels during transport and assembly, thus guaranteeing the required thermal and sound insulation and other properties in the cross-section of the panel.

Sposob výroby konštrukčnej došky pozostáva z vytvorenia nosného rámu alebo roštu opiáš(ováného velkoplošným materiálem na báze dřeva a ich modifikácii so zlepšenými ροζ ia rno-techni ckými vlastnostami a vyplněním vnutorného priestoru tepelno izolačným materiálem na báze fenclplastov, pričom vyplnenie vnutorného priestoru konštrukčnej desky je možné realizovat naliatim i nastřeknutin zmesi fenolplastu, ktorý n/v3zne po vypěnění a vytvrdnuti v Jasovou intervale 5 až 15 jinút vytvára vlastnú výplň, alebo vložením hotového tepelno izolaíného materiálu na báze fenolptastov.The method of production of the construction board consists in the creation of a supporting frame or grate of opiates with a large-area wood-based material and their modification with improved technical properties and filling the interior with thermal insulation material based on fenclplasty, while filling the interior of the construction board to be carried out by pouring and spraying a phenolplast mixture, which, after foaming and curing in the brightness interval of 5 to 15, otherwise forms its own filling, or by inserting a finished thermal insulation material based on phenolptasts.

Na přiloženém výkrese je znázorněný prierez dvoch konštrukčných dosák, kde na obr. 1 je vnútorná výplň tvořená len jednou vrstvou a na obr. 2 jednou vrstvou tepelno izolačného materiálu na báze fenclplastov a dvorní vrstvami minerálnych vlákien.The attached drawing shows a cross-section of two construction boards, where in fig. 1 the inner filling is formed by only one layer, and FIG. 2 with one layer of thermal insulation material based on fenclplasty and yard layers of mineral fibers.

Přiklad 1Example 1

Konštrukčná doska bola vytvořená z nosného rámu 2 a opláštovanď retardačně upravenou preglejkou 2- Vnútorná výplň 3 bola vytvořená nastreknutim zmesi fenolplastu zložen i a :The construction board was formed from the supporting frame 2 and the cladding was retarded with plywood 2. The inner filling 3 was formed by spraying a phenol-plastic mixture composed of a:

100 hmot, sušiny fenolplastu použitý 80 X vědný roztok fenolformaldehydovej živice %hmot, nadúvadla NÚ -dinitrozopentametylén tetramin100 wt., Dry phenol plastic used 80 X scientific solution of phenol formaldehyde resin% wt., Blowing agents NÚ - dinitrozopentamethylene tetramine

Xhmot, plnidla oxid křemičitýXmmot, silica fillers

Xhmot. retardéru zmesný ester kyseliny fosforečné} na báze fenolu a izopropylfenolov s minimálnyra obsahom fosforu 7,5 Xhmot.Xhmot. retarder mixed phosphoric acid ester} based on phenol and isopropylphenols with a minimum phosphorus content of 7.5% by weight.

Xhmot. katalyzátora 50 X vodný roztok kyseliny paratoluénsutfónovejXhmot. of catalyst 50 X aqueous solution of paratoluenesulfonic acid

Na tepelno izolačný materiál vyrobený z horeuvedenej zmesi, testovaný podlá ČSN 73 0862 bola zistená priemerná hodnota Q = 120, ktorá zaraduje tento materiál medzi nelahkohortavé - stupen hořlavosti B.For thermal insulation material made from the above mixture, tested according to ČSN 73 0862, an average value of Q = 120 was found, which classifies this material as non-lightly flammable - flammability grade B.

U tepelno izolačného materiálu vyrobeného za rovnakých podmienok ovšem bez přídavku retardére horenia a plnidla, bola priemerná hodnota Q = 315 testovaná podlá ČSN 73 0862, ktorá zaraduje neretardovaný tepelnoizolačný materiál medzi stredne hořlavé materiály - stupen hořlavosti C^.In the case of thermal insulation material produced under the same conditions, but without the addition of flame retardant and filler, the average value Q = 315 was tested according to ČSN 73 0862, which classifies non-retarded thermal insulation material among medium flammable materials - flammability degree C ^.

Přiklad 2Example 2

Konštrukčná doska podlá vynálezu je vytvořená z nosného rámu 1 vnútornej výplně J vytvorenej z jednej vrstvy tvrdej pěny na báze fenoVplastov a dv.och vrstiev minerátnych vlákien. Ovrch konštrukčnej došky je vytvořený z retardačně upravenej preglejky 2. Konštrukčná došky vykazuje dobré tepelno, zvukovoizolačné vlastnosti ako aj proti poži arne vlastnosti.The construction board according to the invention is formed of a support frame 1 of an inner filling J formed of one layer of rigid foam based on phenolic plastics and two layers of mineral fibers. The surface of the construction board is made of retardation-treated plywood 2. The construction board has good thermal, sound-insulating properties as well as fire-retardant properties.

Využitie konítrukčnej došky podlá vynálezu je možné pri výrobě panelov do drevostavby, v stavebnictve pře výrobu obkladov a podkladov, ako aj pri výrobě dveří.The use of the construction board according to the invention is possible in the production of panels for wooden constructions, in the construction industry for the production of tiles and underlays, as well as in the production of doors.

Claims

A construction board consisting of a supporting frame or grate, cladding, a large-area wood-based material which is retarded and an inner filling, characterized in that between the cladding material there is at least one layer of filling of a phenolplastic thermal insulation material with a content of 1 to 20%. . of a mixed ester of phosphoric acid based on phenol and isopropylphenols with a minimum phosphorus content of 7.5% by weight. and 5 to 25 wt. of silica powder, wherein X by weight is based on the dry weight of the phenol-formaldehyde resin.

2. A construction board according to claim 1, characterized in that the filling comprises 1 to 2 layers of mineral fibers.