CS239509B1 - Production method of kitchen utensils - Google Patents
Production method of kitchen utensils Download PDFInfo
- Publication number
- CS239509B1 CS239509B1 CS817572A CS757281A CS239509B1 CS 239509 B1 CS239509 B1 CS 239509B1 CS 817572 A CS817572 A CS 817572A CS 757281 A CS757281 A CS 757281A CS 239509 B1 CS239509 B1 CS 239509B1
- Authority
- CS
- Czechoslovakia
- Prior art keywords
- handle
- unsaturated polyester
- resin
- lignamon
- cured
- Prior art date
Abstract
Vynález se týká způsobu výroby kuchyňského náčiní, zejména nožů spojením upravevené lignamonové rukojeti a kovové části pomocí vytvrzené vrstvy chemicky odolné nenasycené polyesterové pryskyřice. Podstata vynálezu spočívá v tom, že se do lignamonové rukojeti v axiálním směru vydlabe otvor, pak se uvede do styku s roztokem synthetické pryskyřice a takto upravená se po dobu 3 až 60 minut vystaví teplotě 70 až 100 °C. Pak se axiálně vedený otvor naplní chemicky odolnou nenasycenou polyesterovou pryskyřicí s tvarovou stálostí za tepla nejméně 65 °C a se stopkou kovové části opatřené nejméně jedním výřezem a/nebo otvorem se spojí zasunutím. Případný přebytek pryskyřice se setře a spojovací vrstva se vytvrdí vystavením teplotě 70 až 100 °C, načež se lignamonová rukojet po případném přebroušení opatří nátěrem.BACKGROUND OF THE INVENTION The present invention relates to a method of making kitchenware utensils, in particular knives being joined together lignamon handles and metal parts with a cured layer chemically resistant unsaturated polyester resins. The essence of the invention lies in the fact that lignamon handles in the axial direction opening, then contacting the solution synthetic resin and so treated exposed for 3 to 60 minutes temperature of 70 to 100 ° C. Then it is axially guided the hole is filled with chemically resistant unsaturated polyester molded resin at least 65 ° C with a shank metal parts provided with at least one through the slot and / or through the opening by insertion. Any excess resin wipes off and the bonding layer is cured by exposure temperature of 70 to 100 ° C, whereupon lignamonic handle after grinding paint.
Description
(54)(54)
Způsob výroby kuchyňského náčiníMethod of production of kitchen utensils
Vynález se týká způsobu výroby kuchyňského náčiní, zejména nožů spojením upravevené lignamonové rukojeti a kovové části pomocí vytvrzené vrstvy chemicky odolné nenasycené polyesterové pryskyřice.The invention relates to a method for producing kitchen utensils, in particular knives, by joining the treated lignamon handle and the metal part by means of a cured layer of chemically resistant unsaturated polyester resin.
Podstata vynálezu spočívá v tom, že se do lignamonové rukojeti v axiálním směru vydlabe otvor, pak se uvede do styku s roztokem synthetické pryskyřice a takto upravená se po dobu 3 až 60 minut vystaví teplotě 70 až 100 °C. Pak se axiálně vedený otvor naplní chemicky odolnou nenasycenou polyesterovou pryskyřicí s tvarovou stálostí za tepla nejméně 65 °C a se stopkou kovové části opatřené nejméně jedním výřezem a/nebo otvorem se spojí zasunutím. Případný přebytek pryskyřice se setře a spojovací vrstva se vytvrdí vystavením teplotě 70 až 100 °C, načež se lignamonová rukojet po případném přebroušení opatří nátěrem.SUMMARY OF THE INVENTION The invention is based on the fact that an opening is punched into the lignamon handle in the axial direction, then contacted with a synthetic resin solution and subjected to a temperature of 70 to 100 [deg.] C. for 3 to 60 minutes. Then, the axially guided aperture is filled with a chemically resistant unsaturated polyester resin having a thermally stable shape of at least 65 ° C and is inserted into the shank of the metal part provided with at least one cut-out and / or aperture. Any excess resin is wiped off and the bonding layer is cured by exposure to 70-100 ° C, after which the lignamone handle is painted after regrinding.
259 509259 509
- 1“- 1 "
239 509239 509
Vynález popisuje způsob výroby kuchyňského náčiní, zejména nožů spojením upravené lignamonové rukojeti a kovové části pomocí vytvrzené vrstvy chemicky odolné nenasycené polyesterové pryskyřice·The invention discloses a method for producing kitchen utensils, in particular knives, by combining the treated lignamon handle and the metal part with a cured layer of chemically resistant unsaturated polyester resin.
Výroba kuchyňského náčiní, zejména nožů, vidlic apod· patří k nerozsáhlé, ale nepostradatelné strojírenské výrobě· Tyto výrobky jsou někdy celokovové, ale často je rukojeí z estetických, ale i funkčních důvodů vyrobena z jiného vhodného materiálu. V dřívějších dobách bylo pro výrobu rukojetí používáno vhodných dřevin, jako švestky, hrušky, višně, ořechu, buku, dále pak ušlechtilých dřevin jako teaku, palisandru, ebenu apod· Toto střenkování je pracné, proto v současné době je nahrazováno rukojeími z plastických hmot, nejčastěji z polyamidu, acetátů celulosy apod· Přes jednoduchost výroby termoplastických nebo termosetických rukojetí si oblibu u značné části spotřebitelů udržely kuchyňské příbory, nářadí a nože, s dřevěnou rukojetí. Při světovém nedostatku ušlechtilých dřevin a jejich stoupajících cenách bylo značnou úsporou použití tzv· lignamonu, což je v podstatě chemickou cestou ošetřená dřevní hmota, v našem případě pro nožířské zboží buk, lípa, habr. Textura dřeva se značně zvýrazní až ztmavne, tak že lignamon svým vzhledem se podobá těžkým, tvrdým tropickým dřevinám, zejména ebenu, cocobolu, fernambuku a může sloužit jako jejich náhrada. Jakost dřevní suroviny je dána ČSN 49 1511.Production of kitchen utensils, especially knives, forks, etc. · belongs to extensive but indispensable engineering production · These products are sometimes all-metal, but often the handle is made of other suitable material for aesthetic as well as functional reasons. In earlier times, suitable wood species such as plums, pears, sour cherries, walnut, beech, noble wood species such as teak, rosewood, ebony, etc. were used to make the handles. · This grooming is laborious and is currently being replaced by plastic handles, most often made of polyamide, cellulose acetates, etc. · Despite the ease of manufacturing thermoplastic or thermosetting handles, cutlery, utensils and knives, with wooden handles, retained popularity among a large number of consumers. Given the world scarcity of noble trees and their rising prices, the use of so-called lignamone, which is basically chemically treated wood mass, in our case for cutlery, beech, linden, hornbeam, was a considerable saving. The texture of the wood is greatly enhanced to darken, so that lignamone resembles heavy, hard tropical woody species, especially ebony, cocobol, fernambuc, and can serve as a substitute. The quality of wood raw material is given by ČSN 49 1511.
Kovové části např. čepele nožů jsou spojeny s dřevěnou rukojetí pomocí kovových, zpravidla mosazných a hliníkovýchMetal parts such as knife blades are connected to the wooden handle by metal, usually brass and aluminum
239 509 nýtů· U některých typů náčiní sestává rukojeť ze dvou částí a ty se spojují nejčastěji termoplastickými lepidly, u nichž podstatnou část tvoří kalafuna, něho tvrditelná epoxydová pryskyřice. V obou případech se jedná o pevné či silně viskózní látky, které není možno spolehlivě nanést do úzkých otvorů. Navíc termoplastické kompozice postupně vytékají a spoje provedené epoxydovými lepidly nejsou odolné vůči vodě. Všechna tato spojení na počátku pevná se po určité době používání uvolňují. K tomu významně přispívá mytí příborů, nářadí a nožů v horké vodě, zejména s přísadou saponátů. Dřevo nabotná, do mezer mezi kovovou Částí a dřevěnou rukojetí vnikne voda a výrobek postupně ztrácí svou funkční použitelnost. K tomuto procesu jsou zvláště náchylné výrobky, u nichž je použito pro výrobu rukojetí lignamonu. Nyní bylo. nalezeno, že kuchyňské náčiní zejména nože, sestávají z kovové Části, dřevěné rukojeti a spojovacích částí lze vyrábět při dodržování způsobu výroby podle předloženého vynálezu, aniž by docházelo k uváděnému znehodnocování výrobků.239 509 rivets · In some types of utensils, the handle consists of two parts and these are usually joined by thermoplastic adhesives, of which a substantial part consists of rosin, a curable epoxy resin. In both cases, these are solid or strongly viscous substances which cannot be reliably applied to narrow openings. In addition, the thermoplastic compositions flow out gradually and the joints made with epoxy adhesives are not water resistant. All these connections are initially fixed after a period of use. Washing cutlery, tools and knives in hot water, especially with detergent, contributes significantly to this. The wood swells, water enters the gaps between the metal part and the wooden handle and the product gradually loses its functional usability. Particularly susceptible to this process are products in which lignamone handles are used. It was now. It has been found that kitchen utensils, in particular knives, consist of a metal part, a wooden handle and connecting parts which can be produced in accordance with the production method according to the present invention, without detrimenting said products.
Podstata předloženého vynálezu spočívá v tom, že se do lignamonové rukojeti v axiálním směru vydlabe otvor, pak se uvede do styku s roztokem synthetické pryskyřice. Tskto upravené se pak po dobu 3 až 60 minut vystaví teplotě 70 až 100 °C. Potom se axiálně vedený otvor naplní chemicky odolnou nenasycenou polyesterovou pryskyřicí s tvarovou stálostí za tepla nejméně 65 °C a se stopkou kovové části opatřené nejméně jedním výřezem a nebo otvorem se spojí zasunutím. Přebytek pryskyřice se setře a spojovací vrstva se vytvrdí při teplotě 70 až 100 °C. Lignamonová rukojeí se po případném přebroušení opatří nátěrem.The essence of the present invention is that a hole is cut into the lignamon handle in the axial direction, and then contacted with a synthetic resin solution. The treated are then subjected to a temperature of 70 to 100 ° C for 3 to 60 minutes. Thereafter, the axially guided opening is filled with a chemically resistant unsaturated polyester resin having a thermally stable shape of at least 65 ° C and a shank of the metal part provided with at least one cut-out or the opening connected by insertion. The excess resin is wiped off and the bonding layer is cured at 70-100 ° C. The lignamone handle is painted after regrinding.
Uváděný způsob výroby přináší oproti dosud známénu spojo vání pomocí nýtů úsporu nedostatkových kovů - hliníku, mědi a zinku. Odstraňuje rovněž náročnou pracovní operaci - nýtování a zvyšuje produktivitu práce. Kuchyňské náčiní, zejména nože vyrobené podle tohoto vynálezu navíc vykazují řadu výhodThe method of manufacture described above, compared to the previously known rivet jointing, saves scarce metals - aluminum, copper and zinc. It also eliminates demanding work operations - riveting and increases work productivity. Moreover, kitchen utensils, in particular knives made according to the present invention, exhibit a number of advantages
239 509239 509
Majú vysoce estetický vzhled, a jejich funkční vlastnosti, to znamená pevnost spojení kovové části a lignamonové rukojeti, vykazují mnohonásobné vyšší hodnoty než dosud známé spojování nýtováním. Přitom je tato pevnost zachována po celou dobu používání.They have a highly aesthetic appearance, and their functional properties, i.e. the bonding strength of the metal part and the lignamon handle, exhibit many times higher values than the previously known riveting. This strength is maintained throughout the use.
Při výrobě se obvykle postupuje tak, že se do předem vytvarované rukojeti vydlabe otvor. Pak se celá rukojeť napenetruje roztokem uváděných, synthetických pryskyřic nebo se napenetruje jen část - to je axiálně vedený otvor. Takto upravená se po dobu 3 až 60 minut vystaví teplotě 70 až 100 °0. Potom se axiálně vedený otvor naplní chemicky odolnou nenasycenou polyesterovou pryskyřicí s tvarovou stálostí za tepla nejméně 65 °C. Pod tímto vymezením se rozumějí systémy skládající se z výše uváděných pryskyřic, iniciátorů a případně urychlovačů, to je látek umožňujících vytvrzení. Tyto pryskyřice mohou být při ručním způsobu vstřikovány jehlou injekční stříkačky, výhodné je použití automatického dávkovacího zařízení. Do zaplněného otvoru se vsune stopka kovové části· Je výhodné, je-li předehřátá na vyšší teplotu. Přebytek pryskyřice se setře a spojovací vrstva se vytvrdí vystavena teplotě 70 až 100 °C v některém vhodném typu sušárny s dobrým odtahem. To se může dít šaržovitě nebo kontinuálně. Nakonec se rukojeí případně přebrousí a opatří se nátěrem. Nátěr zvyšuje odolnost proti vodě a má i dekorační účel. Součástí této úpravy může být i tisk firemního označení či dekoračních prvků·In the manufacturing process, a hole is usually punched into a preformed handle. Then, the entire handle is primed with a solution of the indicated synthetic resins or only a portion is penetrated - this is an axially guided hole. The treated in this way is exposed to a temperature of 70 to 100 ° C for 3 to 60 minutes. Then, the axially guided aperture is filled with a chemically resistant unsaturated polyester resin having a thermoformability of at least 65 ° C. By this definition are meant systems consisting of the abovementioned resins, initiators and optionally accelerators, i.e. curing agents. These resins may be injected by a syringe needle in a manual method, preferably using an automatic dosing device. The metal shank is inserted into the filled hole. It is advantageous if it is preheated to a higher temperature. The excess resin is wiped off and the bonding layer is cured exposed to a temperature of 70-100 ° C in any suitable type of dryer with good exhaust. This may be batch or continuous. Finally, the handle can be regrinded and painted. The coating increases water resistance and also has a decorative purpose. This may include printing of company labels or decorative elements ·
Pro výrobu kuchyňského náčiní, zejména nožů lze použít jako kovoÝých částí nástrojových ocelí třídy 17 s vhodným ukončením stopky. Jako dřevěné části se používá lignamonu, což je zvláštním chemickým a mechanickým postupem zpracované dřevo, jak je popsáno v úvodní části. Jako synthetických pryskyřic lze použít nenasycených polyesterových pryskyřic, alkydových pryskyřic, dvousložkových epoxydových pryskyřic, epoxyesterů, nitrokombinačních pryskyřic, dvousložkových a jednosložkových polyuretanových pryskyřic apod. Jako chemickyFor the production of kitchen utensils, in particular knives, they can be used as metal parts of tool steels of class 17 with a suitable shank end. Lignamone is used as the wood part, which is a special chemical and mechanical process treated wood as described in the introductory part. As synthetic resins, unsaturated polyester resins, alkyd resins, two-component epoxy resins, epoxy esters, nitrocombine resins, two-component and one-component polyurethane resins, and the like can be used.
239 509 odolné nenasycené polyesterové pryskyřice s tvarovou, stálostí nejméně 65* C lze použít nenasycených polyesterových pryskyřic modifikovaných kyselinou izoftalovou, nebo směsí kyseliny izoftalové a orto-ftalové, případně tereftalová, modifikované 1,3-butandiolem, neepentylglykolem, 1,2-propandiolem a pryskyřic formulovaných na bázi epoxidových pryskyřic, kyseliny akrylové či methakrylevé, fumarové, maleinevé.Unsaturated polyester resins modified with isophthalic acid or a mixture of isophthalic acid and ortho-phthalic or terephthalic, modified with 1,3-butanediol, neepentyl glycol, 1,2-propanediol and resins formulated on the basis of epoxy resins, acrylic acid or methacrylic acid, fumaric acid, maleic acid.
Příkladné převedení vynálezu je schematicky znázorněno na přiloženém výkresu, kde značí ebr.l kuchyňský nůž v nárysu s částečným svislým řezem rukojetí, ebr.2 čepel neže v nárysu a ebr.3 rukojeť v nárysu s částečným svislým řezem.An exemplary embodiment of the invention is shown schematically in the accompanying drawing, where ebr.1 shows a kitchen knife in a front elevation with a partial vertical section of the handle, ebr.2 a blade not in front elevation and ebr.3 a handle in a front elevation with a partial vertical section.
Nejprve se připraví lignamonová rukojeť 6. a do té se vydlabe axiální otvor 5.. De vydlabaného axiálního otvoru 2. se pomocí-injekční stříkačky vstřikne 30 % roztek chemicky odolné nenasycené polyesterové pryskyřice na bázi technického dianbisglycidyléteru a kyseliny methakrylevé ve styrenu, iniciované 3 % hmot.dibenzeylperexidu a katalyzované 2 % hmot.oktoátu kobaltnatého ( obsahuje 2 % hmot.kobaltu jako kovu ). Po 15 minutách se lignamonová rukojeť vloží do sušárny, kde se suší 5 minut při teplotě 70® C. Pak se vyjme, axiální otvor £ se naplní do dvou třetin svého objemu stejnou pryskyřicí jak© bylo použito pro penetraci s tím rozdílem, že její koncentrace ve styrenu je 65 % hmot. Do takto zaplněného axiálního otvoru 2. se stopkou 2 opatřenou výřezem 2. a otvorem £ vsune kovová čepel i· Setře se mírný přetok pryskyřice a kuchyňský nůž se umístí do sušárny, kde se nechá při teplotě 100® C po dobu 10 minut vytvrdit. Tím dojde k vytvrzení spojovací vrstvy která vytvoří pevný a trvalý spoj lignamonová rukojeti 6 a kovwé čepele 1. Lignamonová rukojeť 6 se obrousí a natře dvousložkovým epoxidovým lakem.First, a lignamone handle 6 is prepared and an axial bore 5 is punched out. A 30% dispersion of a chemically resistant unsaturated polyester resin based on technical dianbisglycidyl ether and methacrylic acid in styrene, initiated by 3%, is injected using a syringe. % by weight of dibenzylperexide and catalyzed by 2% by weight of cobalt octoate (containing 2% by weight of cobalt as a metal). After 15 minutes, the lignamone handle is placed in an oven where it is dried at 70 ° C for 5 minutes. Then it is removed, the axial bore se is filled to two thirds of its volume with the same resin as used for penetration, except that its concentration % in styrene is 65 wt. A metal blade 1 is inserted into the filled axial bore 2 with the shank 2 provided with the cutout 2 and the bore 6. A slight overflow of resin is wiped off and the kitchen knife is placed in an oven and allowed to cure at 100 ° C for 10 minutes. This will cure the bonding layer to form a rigid and durable bond between the lignamon handle 6 and the metal blade 1. The lignamon handle 6 is sanded and painted with a two-component epoxy varnish.
239 509239 509
K rytažení kovevé čepele při tlaku kolmo na podélnou esu byle zapetřebí síly 1 500 N a tute vlastnost si nůž uchoval i pe 50 cyklech v automatickém mycím stroji, který pracoval při teplote mycího roztoku 70°C.To engrave the metal blade at a pressure perpendicular to the longitudinal ace, it would require a force of 1,500 N and this property retained the knife for up to 50 cycles in an automatic washing machine operating at a washing solution temperature of 70 ° C.
Pedle jiné výrobní varianty se do lignamenové rukojeti 6. vydlabe axiální otvor 5.. De tohoto axiálního otvoru 5, se na automatickém zařízení vstřikne 30 % roztok alkydové pryskyřice v lakovém benzinu s přídavkem ektoátu kobaltnatého ( 0,05 % hmot. kobaltu jako kovu na sušinu pryskyřice ). Pe hodinách se vystaví v sušárně po dobu 60 minut při 100® C. Pak se vyjme, axiální otvor S. se naplní do tří pětin svého objemu 60% roztokem chemicky odolné nenasycené polyesterové pryskyřice na bázi epoxidu dianového typu, kyseliny methakrylové a fumarové ve styrenu iniciované 2,5 % hmot.dibenzoylperoxidu a katalyzované 1,8 % hmot.resinátu kobaltnatéh©< ( obsahuje 2 % hmot.kobaltu jako kovu ). Do tohoto zaplněného axiálního otvoru 5. se stopkou 2 opatřenou otvorem vsune kovová ěepel 1, Setře se mírný přetek pryskyřice a kuchyňský nůž se umístí do sušárny, kde se nechá při teplotě 95® G po dobu 12 minut vytvrdit. Tím dojde k vytvrzení spojovací vrstvy £, která vytvoří pevný a trvalý spoj lignamenové rukojeti 6 a kovové čepele 1. Lignamonová rukojeí 6 se obrousí a natře epoxyesterovým lakem.Prior to another manufacturing variant, an axial bore 5 is punched out into the lignamen handle 6. From this axial bore 5, a 30% solution of alkyd resin in white spirit with the addition of cobalt ectoate (0.05% by weight of cobalt metal on the resin). It is exposed in an oven for 60 minutes at 100 ° C in the oven. Then removed, the axial bore S. is filled to three fifths of its volume with a 60% solution of chemically resistant unsaturated polyester resin based on dian-type epoxide, methacrylic acid and fumaric acid in styrene. initiated with 2.5% by weight of dibenzoyl peroxide and catalyzed by 1.8% by weight of cobalt (II) resinate (containing 2% by weight of cobalt as metal). A metal blade 1 is inserted into this filled axial bore 5 with the shank 2 provided with the bore. A slight excess of resin is wiped off and the kitchen knife is placed in an oven where it is allowed to cure at 95 ° C for 12 minutes. This will cure the bonding layer 6, which forms a firm and durable bond between the lignamen handle 6 and the metal blade 1. The lignamone handle 6 is abraded and painted with epoxyester lacquer.
K vytažení kovové čepele, při tlaku kolmo na podélnou osu, bylo zapotřebí síly 2 000 N a tute vlastnost si nůž uchoval i po 80 cyklech v automatickém mycím stroji, který pracoval při teplotě mycího rozteku 70® C.A force of 2,000 N was required to pull out the metal blade at a pressure perpendicular to the longitudinal axis, and the blade retained its tute property even after 80 cycles in an automatic washer operating at a 70 ° C washing liquid temperature.
Claims (1)