CS232094B1 - Thermic liquidation method of vaste artifical substances with chlorine compounds content with simultaneous gain of energy - Google Patents
Thermic liquidation method of vaste artifical substances with chlorine compounds content with simultaneous gain of energy Download PDFInfo
- Publication number
- CS232094B1 CS232094B1 CS832341A CS234183A CS232094B1 CS 232094 B1 CS232094 B1 CS 232094B1 CS 832341 A CS832341 A CS 832341A CS 234183 A CS234183 A CS 234183A CS 232094 B1 CS232094 B1 CS 232094B1
- Authority
- CS
- Czechoslovakia
- Prior art keywords
- waste
- energy
- chlorine compounds
- wetted
- weight ratio
- Prior art date
Abstract
Podstata vynálezu spočívá v tom, že se odpadní umělá hmota rozřeže nebo rozdrtí na malé části, její povrch se zaktivizuje tak, aby se po důkladném opláchnutí ve vodě po celé ploše smáčel, načež se takto upravená odpadni umělá hmota smočí vodným roztokem lepidla, po důkladné hmogenizaci se částečně vysuší a v míchačce se smíchá s vápnem nebo s vápencem a popřípadě ještě s odpadními popouštěcími solemi s obsahem dusitanů a dusičnanů a po důkladném promíchání s uhlím se takto upravená směs spaluje ve spalných systémech na pevná paliva.The essence of the invention is that the waste plastic is cut or crushed on small parts, its surface is activated so as to after a thorough rinse in the water he wetted the whole surface, and then he was the thus treated waste plastic is wetted with an aqueous adhesive solution, thorough the hogenization is partially dried and in a mixer is mixed with lime or limestone and optionally with waste tempering agents salts containing nitrites and nitrates a after thorough mixing with the charcoal, this is as follows the treated mixture burns in combustion systems solid fuel.
Description
Vynález se týká ekologicky a energeticky výhodné termické likvidace předem chemicky upravených umělých odpadních hmot s obsahem sloučenin chloru.The invention relates to an environmentally and energy-efficient thermal disposal of pre-treated chlorine-containing synthetic waste materials.
Doposud se odpadní umělé hmoty s obsahem sloučenin chloru typu PVC, umělé kůže a koženky, isolační obaly kabelů a podobné materiály likvidují ukládáním na deponiích, méně často se spalují v různých typech spalovacích zařízení jako jsou roštová ohniště na spalování odpadů, spalovací kotle apod·, kde se obvykle spalují ve směsi s komunálními odpady.Until now, waste plastics containing chlorine compounds of the PVC type, artificial leather and imitation leather, cable insulation and similar materials are disposed of by deposition, less frequently incinerated in different types of incineration plants such as grate fires for combustion, incineration boilers etc., where they are usually incinerated in a mixture with municipal waste.
Nevýhodou těchto způsobů likvidace odpadů umělých hmot je, že v případě zavážení na volné skládky v přírodě je nutno tyto odpady balit /lisovat/, skládky upravovat, chránit je před zneužitím cizími osobami v ohrazeném prostoru a zavážet zeminou, přísně kontrolovat jejich působení na životní prostředí /znečištění povrchových a podzemních vod apod./. Tato opatření představují ve svém souhrnu značné nároky jak na náklady spojené s dopravou odpadů a udržováním skládek, tak i na pracovní síly potřebné k zajištění těchto opatření. V případě likvidace spalováním má tento způsob nevýhodu spočívající hlavně v uvolňování chlorovodíku z odpadu, který reaguje při vysokých teplotách s kovovými částmi spalovacího zařízení a intenzivně je koroduje /tzv. vysokoteplotní koroze/. Kromě toho přechází uvolněný chlorovodík se spalinami do ovzduší a zhoršuje životní prostředí.The disadvantage of these methods of disposal of plastic waste is that in case of landfilling into open landfills in the nature it is necessary to pack / press / treat the landfills, protect them against misuse by third parties in a fenced area and load with soil, strictly control their impact on the environment / pollution of surface and ground water etc.). Taken together, these measures represent considerable demands both on the costs of transporting waste and maintaining landfills, as well as on the labor force needed to ensure these measures. In the case of disposal by incineration, this method has the disadvantage of releasing hydrogen chloride from the waste, which reacts at high temperatures with the metal parts of the combustion plant and intensively corrodes them. high temperature corrosion. In addition, the released flue gas passes into the atmosphere and degrades the environment.
Nevýhody dosavadních způsobů likvidace odpadních umělých hmot s obsahem chlorových sloučenin odstraňuje způsob jejich termické likvidace po předchozí chemické úpravě podle vynálezu, který spočívá v tom, že se odpadní umělá hmota rozřeže nebo rozdrtí na malé části, povrch umělé hmoty se zaktivizuje roztokem manganistanu draselného a kyseliny sírové, aby se po důkladném opláchnutí ve vodě smáčela po celém povrchu, načež se takto upravená odpadní umělá hmota smočí vodným roztokem lepidla, po důkladnéDisadvantages of the prior art methods of disposal of waste plastics containing chlorine compounds are eliminated by the method of their thermal disposal after prior chemical treatment according to the invention, which consists in cutting the waste plastics into small parts, activating the plastic surface with potassium permanganate solution and acid sulfuric so that after thorough rinsing in water it is wetted all over the surface, after which the treated plastic waste is wetted with an aqueous adhesive solution, after
- 2 232 094 homogenizaci se částečně vysuší a v míchačce se smíchá s vápnem popřípadě ještě s odpadními popouštěcími solemi na bázi dusitanů a dusičnanů a po důkladném promíchání s uhlím; takto upravená směs se spaluje ve spalných systémech na pevná paliva.- the 2 232 094 homogenization is partially dried and mixed in the mixer with lime, optionally with waste nitrite and nitrate waste salts, after thorough mixing with coal; the mixture thus treated is combusted in solid fuel combustion systems.
Výhody likvidace odpadních umělých hmot s obsahem chlorovýoh sloučenin spočívají jednak v ozdravění životního prostředí, jednak v energetickém přínosu, poněvadž mají vyšší výhřevnost a podstatně menší obsah popele než méněhodnotné průmyslové uhlí spalované v roštových ohništích průmyslových kotlů, intenzivní hoření odpadů zlepší spalování tohoto uhlí a zvýší účinnost jeho využití. Získává se dvojí energetický efekt: odpadní umělé hmoty se energeticky využijí a méněhodnotné uhlí se spálí dokonaleji s menšími ztrátami· Další výhoda spočívá v tom, že se společně s odpadními umělými hmotami s obsahem chlorových sloučenin mohou termicky zneškodňovat odpadní popouštěcí soli s obsahem dusitanů a dusičnanů, čímž se dosáhne další zlepšení energetické bilance v závodních spalných systémech na pevná paliva. Mimoto se přídavkem vápna, popřípadě vápence k odpadní umělé hmotě váže i síra obsažená v méněhodnotném uhlí, čímž se sníží exhalace silně korozivního oxi- 5 du siřičitého.The benefits of disposing of waste plastics containing chlorine compounds are both environmental recovery and energy benefits, as they have a higher calorific value and considerably less ash content than less valuable industrial coal burned in the grate hearths of industrial boilers, intense combustion of waste will improve combustion of this coal and increase efficiency of its use. There is a double energy effect: waste plastics are used for energy and less valuable coal is burned better with less losses , thereby achieving a further improvement of the energy balance in solid fuel combustion plant systems. In addition, the addition of lime or limestone to the waste plastic also binds the sulfur contained in the low-grade coal, thereby reducing the exhalation of the strongly corrosive sulfur dioxide.
Příklad 1Example 1
Odpadní kusy lepenky potažené vrstvou PVC se roatrhají na malé kousky pilkovým drtičem. Připraví se vodný roztok 4 g.l“1 manganistanu draselného a 5 g.l””' kyseliny sírové /počítána jako 100%ní/ v ocelové uvnitř pogumované vaně. Desintegrované odpady se v děrovaném koši ponoří na několik minut do tohoto roztoku, několikrát se košem zatřese, aby se odpady dokonale smočily. Potom se koš s odpady vynoří a odpady se důkladně opláchnou. Povrch odpadů se musí po celé ploše smáčet. Opláchnuté odpady se nasypou do míchačky a za stálého míchání se přidává ve vodě rozpustné lepidlo na bázi karboxymethylcelulosy a dextrinu /Koramex Spolana/ tak, aby se povrch odpadů smočil· Roztok Koramexu se připraví rozpuštěním 1 dílu v 16 dílech vody. Přípravek se rozpustí během asi 12 hodin. Jako plnivo se používá mletý vápenec, který se přidává k lepidlu v hmotnostním poměru 1:1, přičemž se směs důkladně zhomogenizuje mícháním. Smočená odpadní hmota se nasype na děrovaný plech, síto s většími otvory, aby se zmenšila styčná plocha hmoty se dnem a snížila se tak možnost jejího nalepování k podkladu. Současně odteče přebytečný roztok lepidla do podložené nádoby k dalšímu použití. Hmota se rozprostře vWaste pieces of PVC-coated cardboard are cut into small pieces by a saw mill. An aqueous solution of 4 g / l of potassium permanganate and 5 g / l of sulfuric acid (calculated as 100%) in steel inside the rubberized tub is prepared. The disintegrated waste is immersed in this solution for several minutes in a perforated basket, shaken several times in the basket to completely wet the waste. Then the waste basket emerges and the waste is rinsed thoroughly. The surface of the waste must be wetted over the entire surface. The rinsed wastes are poured into the mixer and water-soluble carboxymethylcellulose-dextrin / Koramex Spolana / glue is added while stirring to wet the surface of the waste. The preparation dissolves within about 12 hours. The filler used is ground limestone, which is added to the adhesive in a 1: 1 weight ratio, the mixture being thoroughly homogenized by stirring. The wetted waste material is poured onto a perforated sheet, a sieve with larger openings, to reduce the contact surface of the material with the bottom and thus reduce the possibility of sticking to the substrate. At the same time, excess adhesive solution flows into the backed container for further use. The mass spreads out in
- 3 232 094 tenké vrstvě na ploše a ponechá se volně zaschnout. Takto upravená hmota se v míchačce smíchá v hmotnostním poměru 1 i 1 s vápnem a směs se přidává v hmotnostním poměru 1s1 ke spalovanému uhlí· Příklad 2,- 3,232,094 a thin layer on the surface and allow to dry freely. The mass treated in this way is mixed in a mixer in a weight ratio of 1 and 1 with lime and the mixture is added in a weight ratio of 1s1 to charcoal.
Odpady z desek z PVC se rozemelou na drí. Její povrch se zaktivizuje jako v předešlém případě. Po opláchnutí ve vodě se drí nasype do míchačky, přidá se za stálého míchání roztok lepidla v takovém množství, aby se povrch odpadu lehce smáčel. Po dokonalém p-rnmíohání se přidává vápno a odpadní popouštěcí soli s obsahem dusitanů a dusičnanů v hmotnostním poměru 1:1:1. Takto upravená směs se spaluje v roštové peci s uhlím v hmotnostním poměru 1:1. Příklad 3=·Waste from PVC boards is pulverized. Its surface is activated as in the previous case. After rinsing in water, it is poured into the mixer, the glue solution is added with stirring so that the surface of the waste is slightly wetted. After complete mixing, lime and waste tempering salts containing nitrites and nitrates in a weight ratio of 1: 1: 1 are added. The mixture thus treated is burnt in a grate furnace with coal in a weight ratio of 1: 1. Example 3 = ·
Odpady z umělé kůže na bázi PVC se desintegrují, jejich povrch se zaktivizuje jako v příkladě 1, smočí se vhodným lepidlem a smíchá se v hmotnostním poměru 1:1 s vápnem. Takto upravené odpady se spalují v rotační peci.PVC-based artificial leather wastes are disintegrated, their surface is activated as in Example 1, wetted with a suitable adhesive and mixed in a 1: 1 weight ratio with lime. The treated waste is burned in a rotary kiln.
Claims (1)