CS230631B1 - Agent for protection of goods suspension during electroplating - Google Patents
Agent for protection of goods suspension during electroplating Download PDFInfo
- Publication number
- CS230631B1 CS230631B1 CS261883A CS261883A CS230631B1 CS 230631 B1 CS230631 B1 CS 230631B1 CS 261883 A CS261883 A CS 261883A CS 261883 A CS261883 A CS 261883A CS 230631 B1 CS230631 B1 CS 230631B1
- Authority
- CS
- Czechoslovakia
- Prior art keywords
- weight
- agent
- protection
- during electroplating
- suspension during
- Prior art date
Description
(54) Prostředek pro ochranu závěsů zboží při galvanickém pokovování(54) Means for protecting hinges of goods during electroplating
Vynález se týká prostředku pro ochranu závěsů zboží při galvanickém pokovování, který poskytuje dokonalou ochranu všem kovovým částem povrchu závěsných zařízení, procházejících sllnš korozivním prostředím pokovovacích lázní.BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a device for protecting hinges of goods during galvanic plating which provides perfect protection to all metal parts of the surface of the hinge devices passing through the corrosively environment of the plating bath.
Dosud se pro ochranu těchto závěsných zařízení používají prostředky na bázi epoxidových pryskyřic, vinylových polymerů a podobně. S použitím těchto prostředků byly často spojeny potíže při nanášení vhodných vrstev. Například ochranné povrchy, tvořené polyetylénem, byly nanášeny obalováním horkého závěsu v práškovém polyetylénu popřípadě stříkáním tohoto prášku na horký povrch závěsu. Navíc povlaky na bázi polyetylénu nemají dlouhou životnost a časem praskají. Povlaky na bázi epoxidových pryskyřic se obtížně nanášejí a dosti rychle stárnou v prostředí lázní, což se projevuje mikrotrhlinami.Heretofore, epoxy resin, vinyl polymer and the like compositions have been used to protect these suspension devices. The use of these compositions has often involved difficulties in applying suitable layers. For example, polyethylene protective surfaces have been applied by wrapping the hot curtain in powdered polyethylene or spraying the powder onto the hot curtain surface. In addition, polyethylene-based coatings do not have a long service life and burst over time. Coatings based on epoxy resins are difficult to apply and age quite quickly in the bath environment, which is manifested by micro-cracks.
Uvedené nedostatky odstraňuje podle vynálezu prostředek pro ochranu závěsů zboží při galvanickém pokovování. Jeho podstata spočívá v tom, že obsahuje 40 až 70 % hmot. pastotvorného polyvinylohloridu, 30 až 60 % hmot. změkčovadla, s výhodou di(2-etylhexyl)ftalátu. Podle dalšího význaku vynálezu obsahuje 1 až 10 % hmot. tepelně stálého pigmentu. Prostředek může podle posledního význaku vynálezu obsahovat jako přísadu pro zvýšení adhese k chráněnému povrchu 0,1 až 10 % hmot. látek na bázi fenolformaldehydových pryskyřic, s výhodou reakční produkt kresolu s formaldehydem a hexametylentetraminem.According to the invention, the above-mentioned drawbacks are eliminated by means for protecting the hinges of goods during electroplating. It consists of 40 to 70 wt. % pasty polyvinyl chloride, 30 to 60 wt. plasticizers, preferably di (2-ethylhexyl) phthalate. According to a further aspect of the invention it comprises 1 to 10 wt. a thermostable pigment. According to the last aspect of the invention, the composition may contain from 0.1 to 10% by weight as an additive for increasing adhesion to the surface to be protected. phenol-formaldehyde resin based substances, preferably the reaction product of cresol with formaldehyde and hexamethylenetetramine.
Základní výhoda prostředku podle vynálezu spočívá v jeho pružnosti, čímž nedochází k jeho snadnému poškozování při manipulaci s háky, má dobré izolační vlastnosti e při delším používání se nevytvoří mikrotrhlinky, jelikož prostředek v podstatě nestárne. Prostředek se snadno nanáší a je tedy nenáročný ne zařízení pro jeho aplikaci.The main advantage of the device according to the invention lies in its flexibility, thus avoiding its easy damage during handling of the hooks, has good insulating properties and does not form micro-cracks during prolonged use, since the device does not substantially age. The composition is easy to apply and is therefore undemanding to the device for its application.
230631 2230631 2
Ochranný prostředek se na závěsná zařízení nanáší následujícím postupem* Závěsy předehřátá na teplotu 100 až 150 °C jsou ponořeny do prostředku podle vynálezu na dobu několika minut. Dobou setrvání v roztoku a teplotou předehřátí závěsu se řídl tloušlka vrstvy povlaku. Po odkapání přebytečného množství prostředku se závěs vyhřívá ne teplotu 170 až 180 °C po dobu 15 až 30 minut. Pro účely ochrany závěsů v galvanotechnice je vhodný poměr hmotností polymeru a změkčovadla přibližně 1:1. Prostředek podle vynálezu může obsahovat pigment vzdorující vysokým teplotám, např. saze, kysličníky kovů (například chrómu, železa) a látky zvyšující adhezi k chráněnému povrchu.The suspensions preheated to a temperature of 100 to 150 ° C are immersed in the composition according to the invention for a few minutes. The thickness of the coating layer was controlled by the residence time in solution and the heater preheating temperature. After the excess composition drips, the hinge is heated to a temperature of 170 to 180 ° C for 15 to 30 minutes. For the purpose of protecting galvanic hinges, a ratio of polymer to plasticizer weight of about 1: 1 is appropriate. The composition of the invention may comprise a high temperature resistant pigment, e.g., carbon black, metal oxides (e.g., chromium, iron), and adhesion enhancers.
Prostředek podle vynálezu je dále blíže popsán na několika příkladech provedení.The composition according to the invention is described in more detail below with reference to several exemplary embodiments.
Příklad 1Example 1
Prostředek složený se 40 až 70 ha. dílů paatotvorného PVC e 30 až 60 hm. dílů di(2-etylhexyDftalitu byl nanesen ha vyhřátý ocelový závěs oěetřený základním vypalovacím lakem, ponořením po dobu 15 min. Povlak byl vypálen po dobu 20 minut při teplotě 170 °C.Compound composed of 40 to 70 ha. e., 30 to 60 wt. parts of di (2-ethylhexylphthalite) was applied to a heated steel hinge treated with a base enamel coating, by immersion for 15 minutes, and the coating was baked for 20 minutes at 170 ° C.
Příklad 2·Example 2 ·
Prostředek složený z 50 ha. dílů paatotvorného PVC, 46 hm. dílů di(2-atylhexyl)ftalátu a 5 ha. dílů sazí byl aplikován natíráním na vyhřátý ocelový závěs ošetřený základním vypalovacím lakem. Výsledný povlak byl vypálen po dobu 15 min. při teplotě 175 °C.The facility consists of 50 ha. parts of palatable PVC, 46 wt. parts of di (2-atylhexyl) phthalate and 5 ha. parts of the carbon black were applied by painting onto a heated steel hinge treated with a base enamel coating. The resulting coating was baked for 15 min. at 175 ° C.
Příklad 3Example 3
Prostředek složený z 50 ha. dílů pastotvorného PVC, 40 ha. dílů di(2-etylhexyl)ftalétu, 5 ha. dílů kysličníku železa a 5 hm. dílů přísady pro zvýšení adheze k povrchu, byl aplikován ponořením po dobu 10 minut závěsu předehřátého na teplotu 160 °C. Po odkapání přebytečného prostředku byl závěs vypalován po dobu 30 min. na teplotu ,80 °C. Vyhřátý závěs byl opět ponořen do prostředku podle vynálezu na dobu 5 min. a vypálen při teplotě 170 °C po dobu lO.ain.The facility consists of 50 ha. parts of paste-forming PVC, 40 ha. parts of di (2-ethylhexyl) phthalate, 5 ha. parts of iron oxide and 5 wt. parts of the additive to increase surface adhesion was applied by immersion for 10 minutes of the hinge preheated to 160 ° C. After the excess agent dripped, the hinge was fired for 30 min. at 80 ° C. The heated hinge was again immersed in the composition of the invention for 5 min. and fired at 170 ° C for 10 min.
Claims (3)