CS226283B1 - Tvrditelné lisovací kompozice - Google Patents
Tvrditelné lisovací kompozice Download PDFInfo
- Publication number
- CS226283B1 CS226283B1 CS430182A CS430182A CS226283B1 CS 226283 B1 CS226283 B1 CS 226283B1 CS 430182 A CS430182 A CS 430182A CS 430182 A CS430182 A CS 430182A CS 226283 B1 CS226283 B1 CS 226283B1
- Authority
- CS
- Czechoslovakia
- Prior art keywords
- viscosity
- koh
- mpa
- unsaturated
- resin
- Prior art date
Description
Předmětem tohoto vynálezu jsou tvrditelné lisovací kompozice, zejména pro výrobu prepregů a vyztužených plastů, obsahující jako pojivá nenasycené polyesterové pryskyřice, dále inhibitory, iniciátory, vláknitá vyztužující plniva, zahušíovadlá, povrchově aktivní látky, nevyztužující plniva, pigmenty, barvivá, separátory, reaktivní a nereaktivní rozpouštědla, dále retardéry hoření, termpblastické polymery, rozlivová činidla, katalyzátory, stabilizátory nebo. jiná aditiva, Podstata vynálezu spočívá v tom, že kompozice obéahují jako pojivo 15 až 60 % hmot® směsi nejméně dvou vlastnostmi rozdílných typů nenasycených polyesterových pryskyřic o molekulové hmotnosti 500 až 5 000 na bázi kondenzačních produktů alkylengLykolů a/nebo polyalkylenglykolů o 2 až 24 atomech uhlíku s o(, fi -nenasycenými alifatickými karboxylovými kyselinami a s ftalovými kyselinami nebo jejich deriváty o 2 až 14 atomech uhlíku· Tvoří 30 áž 75% roztok v nenasycených polymerace schopných monomerech. Jedním z těchto typů je alespoň jedna pryskyřice s číslem kyselosti 15 až 25 mg KOH/g, hydroxýlovým číslem 5 až 30 mg KOH/g, viskozitou při 25 °C 1 000 až 1 500 mPa.s/25 °C a viskozitou po přídavku 0,5 až 3 % hmot· kysličníku hořečnatého a po 14 dnech skladování při 20 °0 1.10^ až 1·10θ mPa.s/25 °C· Druhým typem je alespoň jedná pryákyřice s číslem kyselosti 5 až 30 mg KOH/g, hydroxylovým číslem 10 až 50 mg KOH/g a viskozitou při 25 °C 500 až 1 100 nebo 1 200 až 1 800 mPa.s/25 °C a viskozitou po přídavku uvedeného množství kysličníku hořečnatého a po uvedených podmínkách a době skladování 1.10^ a 1·Τθ^ nebo 1.1Οθ až 1·10® mPa.s/25 °G· Oba typy pryskyřic' jsou ve směsi obsaženy ve hmot. poměru 1 í 6 až 6 s 1. Tvrditelné lisovací kompozice podle tohoto vynálezu mají ve srovnání se známými produkty některé přednosti. Kombinací
dvou i více typů nenasycených polyesterových pryskyřicrůzného chemického složení a reaktivity se získají dlouhodobě skladovatelné hmoty (prepregy) výborných lisotechnických a fyzikálněmechanickýoh vlastností. Polyesterové kompozice vykazují při lisování především velmi.dobré tokové vlastnosti a jsou proto zvláště vhodné pro výrobu složitých a velkých výlisků. Tím se snižuje počet vadných výrobků. Výlisky mají nejen kvalitní povrch a vzhled, nýbrž i zvýšené fyzikální a mechanické vlastnosti. Řízenou volbou složení výchozích druhů polyesterových pryskyřic, jako jsou typy tvrdé, měkké, nehořlavé, chemicky a tepelně odolné, se např. při lisování odstraní vnitřní pnutí a výlisky nepraskají, dále mají sníženou hořlavost, hladký povrch, zvýšenou chemickou oddLnost, zlepšené elektrické vlastnosti a tvarovou stálost i při vyšších teplotách.
Pojivá tvrditelných lisovacích kompozic podle tohoto vynálezu tvoří 15 až 60 % hmot. směsi nejméně dvou nenasycených polyesterových pryskyřic o molekulové hmotnosti 500 až 5 000 na bázi 30 až 75% roztoků nenasycených polyesterů v nenasycených polymerace schopných monomerech. Nenasycené polyestery se připravují známouesterifikací nenasycených a nasycených dikařboxylových kyselin oi jejich derivátů, obsahujících 2 až 14 atomů uhlíku s alkylenglykoly a/nebo polyalkýlenglykoly še 2 až 24 atomy uhlíku, resp. funkčních a substitučních derivátů -těchto výchozích sloučenin. Z nenasycených dikarboxylových kyselin má největší význam kyselina maleinová či její anhydrid, kyselina fumarová, dále itakonová apod. Nasycené dikarboxylové kyseliny jsou zastoupeny především izomery kyseliny ftalové či jejich deriváty, jako je kyselina orthoftalová, izoftalová, tereftalová, tetrachlorftalová, tetrabromftalová, tetrahydroftalová, 4-chlor-1,2,3,6-tetrahydroftalová, 3,6-endome thylent etrahydroftalová, hexachlorendomethylentetrahydroftalová, resp. anhydridy těchto kyse'lin. Z alifatických dikarboxylových kyselin je vhodná hlavně kyselina adipová, sebaková, azelainová a jiné kyseliny s delším řetězcem. Alkylen- a polyalkylenglykoly zahrnu jí především ethylenglykol, diethylenglykol, triethylenglykol a další polyraerhomology, propylenglykolyr butylenglykoly, neopentylglykol, dibromnéopentylglykol a hexandioly. Nenasycené polyestery se rozpouštějí ve vinylických monomerech, jako je styren a jeho deriváty (vinyltoluen, -methylstyren, halogenstyreny), estery kyseliny (meth)akrylové (hlavně methylmethakrylát), vinylestery (vinylaeetát, vinylpřopionát, vinylversatát), divinylbenzen a popř. v allylových sloučeninách (především v diallylorthoftalátu a diallylizoftalátu)« Z velkého počtu známých nenasycených polyesterových pryskyřic j βομ vhodné výhradně směsi obsahující alespoň jednu pryskyřici o čísle kyselosti 15 až 25 mg KOH/g, hydroxylovéra čísle 5 až 30 mg KOH/g, viskozitě při 25 °C 1 000 až 1 500 rnPa.s, která přídavkem 0,5 až 3 % hmot. kysličníku hořečnatého dosáhne při 20 GC během 14 dnů viskozity 1.10^ až 1.10^ mPa.s/25 °C. Druhým typem je alespoň jedna pryskyřice o čísle kyselosti 5 až 30 mg KOH/g, hydroxylovém čísle 10 až 50 mg KOH/g, viskozitě při 25 °C 500 až 1 100 nebo 1 200 až 1 800 rnPa.s, jež se zahustí za stejných o c podmínek jako pryskyřice předchozí na viskozitu 1.10^ až 1.103 nebo 1.10° až 1.10θ mPa.s/25 GC. Hmot. poměr obou pryskyřic se pohybuje v rozmezí 1 : 6 až 6 í 1.
Nenasycené polyesterové pryskyřice se stabilizujíproti samovolné polymeraci přídavkem 0,001 až 0,3 % hmot. inhibitorů polymerace. Mezi nejvíce používané patří sloučeniny fenolické, jako hydrochinon a terč. butylpyrokatechin, chinonové (p-benzochinon, fil- ajj -naftochinon), sloučeniny sirné, jako thiofenoly, dále aminy (anilin* a^-naftylamin), nitro- a nitrozolátky,_ jako nitrobenzen, nitrofenoly, nitrozofenoly apod. Výchozí Nenasycené složky zavádějí do polyesterů polymerace schopné vazby, které pak při vytvrzování reagují s přítomnými nenasycenými monomery. Jejich kopolymerace je iniciována přídavkem 0,1 až 3 % hmot. organických peroxidů, jako je terč. butylperoxybenzoát, terč. butylhydroperoxid, di-terc. butylpaDxid, dikumylperoxid, dibenzoylperoxid, terč. butylperoxyoktoát, 1,1-di-terc.-butylperoxid-3,3,5-trimethylcyklohexan, methylethylketonperoxid, methylizobutylk^tonperoxid a cyklohexanonperoxidy.
Důležitou složkou těchto tvrditelných polyesterových liso„ vacích kompozio jsou vláknitá vyztužujíoí plniva, jejich obsah ' Siní 2O\až 50 % hmot . Nejvýznamnější jsou skelná vlákna obvykle povrchově upravená organokřemičitými sloučeninami, která se používají ve formě prámenců, rohoží, tkanin a sekaných rovingů·
A*
Pro speciální aplikace se používají vlákna celulozová, syntetická, azbestová, uhlíková, grafitová, bórová nebo i kovová.
Kromě vláknitých vyztužujících pojiv obsahují kompozice až 50 % hmot. práškových plniv a pigmentů. Mezi ně patří např. uhličitan a síran vápenatý, hořečnatý a zinečnatý, kysličník křemičitý a hlinitý, kremičitan vápenatý a hlinitý, vápenec, křída, kaolin, kaolinit, bentonit, mastek, živec, křemen, břid- \ lice, sklo, slída, azbest, dále zinková, titanová a antimonová běloba, litopon, chromová žluí a zeleň, železitá červeň a čerň, suřík, rumělka, ultramarín, Saze, sirhík zinečnatý a íSemnatý. Přidávané organická barviva musí ovšem být stálá vůči organickým peroxidům.
Nezbytnou přísadou a součástí lisovacích kompozic jsou zahušlovadla, která zprvu zachovávají nízkou viskozitu pojivá, ale během zrání polyesterové kompozice reagují s nenasycenými polyestery za podstatného zvýšení jejich viskozity a molekulové hmotnosti. Nejvíce se osvědčily sloučeniny kovů 2. periodické skupiny prvků, tj. zejména hořčíku, vápníku, stroncia, baria, berylia, zinku a kadmia. Nejdůležitější je kysličník a hydroxid hořečnatý a vápenatý, příp. kysličník berylnatý a zinečnatý· Přidávají se v množství 0,2 až 5 % hmot., vztaženo na hmotnost nenasycených polyesterových pryskyřic, a to ve formě 10 až 90% past v neionogenních povrchově aktivních látkách (alkylenoxidováných alkylfenolech,mastných alkoholech abkyselinéch, jejich amidech a esterech, hoxSS-ymerech a Mopolymereoh alkylenoxidů a v alifatických aminech) a/nebo ionogenních, hlavně anionaktivních sloučenináchjjako v alkylsulfátech, alkylsulfonátech, alkylfosfátech apod. Pasty mohou být rovněž připraveny ze speciálních nížereaktivníoh polyesterových pryskyřic.
Z dalších aditiv přichází v úvahu t až 3 % hmot. separátorů (kyseliny stearové, steárátuzinečnatého, horečnatého a hlinitého), 1 až 20 % hmot. termpolastických polymerů (homopolymerů a kopolymerů ethylenu, propylenu, styrenu, (meřh)akrylátových sloučenin, vinylacetátu a vinylchloridu, dále polyamidů, polysulfonů/ nasycených polyesterů, derivátů celulózy aj.), dále až 5 % hmot. retardérů hoření (kysličníku antimonitého, hy- . drátovaného kysličníku hlinitého, zásaditých halogenidů hlinitých, bromidu a fosforečnanu amonného apod·), rozlivových činidel (nízkomolekulárních akrylových polymerů, silikonových olejů) a stabilizátorů stárnutí (derivátů 2-hydroxybenzofenonu,
2,6-di-terc.butyl-p-krezolu, organických fosfitů aj»)· Konečně lze do kompozic vnášet plastifikátory (estery kyseliny ftalové, adipové, azelainové a jiných dikarboxylových kyselin s delším alifatickým řetězcem), antistatické prostředky, fungicidní, insektieidní, antikorozivní a jiné sloučeniny;. Před zpracováním je mošno upravovat konzistenci polyesterových lisovacích směsí přídavkem dalších podílů již uvedených reaktivních nenasycených monomerů nebo i nereaktivních organických rozpouštědel, jako např. alkoholů, ketonů a uhlovodíků. i
Tvrditelné lisovací kompozice se podle tohoto vynálezu obvykle připravují následovně. Do mísícího hnetacího zařízení se najednou nebo postupně vloží nejméně dva druhy uvedených nenasycených polyesterových pryskyřic, pasta zahušřovadla v povrchově aktivní látce, inhibitor a iniciátor. Směs se plynule míchá a dále se přidávají další složky, jako plniva, pigmenty, barviva, separátory a jiná aditiva. Suspenzí zahušíovadla v povrchově aktivní látce lze do polyesterové kompozice dávkovat též až těsně před jejím smícháním s vláknitým vyztužujícím plnivem. Získá se tak stabilní polyesterová kompozice, kterou sé na impregnačním zařízení napojí vláknitá výztuž, nej častěji skelná rohož. Impregnovaná výztuž se vloží mezi polyethylenové pásy a navíjí se do rolí. Pak se podrobí zrání při teplotě místnosti po dobu několika dnů až týdnů nebo během několika hodin áž minut při teplotě zvýšené, např. při 60 až 80 °G. Získá se’ tak nelepivý prepreg, který se zpracovává lisováním bučí ihned nebo po době skladování až 6 měsíců. Prepreg se lisuje za zvýšené teploty, např. při 120 až 150 °C a tlaku 2 až 50 MPa po dobu 2 až 10 minut. Výrobky z vytvrzených plastů se používají při náročných'aplikacích v průmyslu elektrotechnickém, strojírenském, leteckém, automobilovém, chemickém, stavebním, dále v raketové technice, při stavbě lodí, výrobě dopravních značek, nábytku a velkorozměrových výlisků (nádrží, cisteren).
Předmět vynálezu je doložen následujícími příklady složení tvrditelných lisovacích kompozic, v nichž uvedená procenta a díly představují jednotky hmotnostní.
' ' ' λ ,
Příklad 1
Nenasycená polyesterová pryskyřice na bázi ftalan- 60,0 hmot. dílů hydridu, maleinanhydridu, ethylenglykolu a propyleriglykolu o čísle kyselosti 20,2 mg KOH/g, hydroxylovém čísle 18,0 mg KOH/g a viskozitě 1 050 mPa.s/25 °C, zahustitelná s 1 % hmot. MgO při 20 °C během 14 dnů na viskozitu 9,7 · W5 mPa.s/25 °C
Nenasycená polyesterová pryskyřice na bázi malein- 241,0 anhydridu, ftalanhydridu, kys. adipové a propylenglykolu o čísle kyselosti 15,0 mg KOH/g, hydroxylovém čísle 27,5 mg KOH/g a viskozitě 880 mPa.s/25 °C, zahustitelná s 1 % hmot.
MgO při 20 °C během 14 dnů na viskozitu 9,5 » v 104 mPa.s/25 °C
1,1-di-terc.butylperoxid-3i3,5-trimethylcyklohexan 4,67 ”
| Kysličník hořečnatý | 4,5 |
| Hydrochinon | 0,, 08 |
| Ethylalkohol | 0,75” |
| Ethoxylovaný nonylfenol | 9,00 ” |
| Vápenec mikromletý | 350,00 |
| Stearát zinečnatý | 10,00 |
| Suspenze titanové běloby v nasyceném polyesteru | 20,00 |
| Skelná výztuž - sekaný roving | 300,00 ” |
Kompozice se lisůje při teplotě 150 °C a tlaku 10 MPa, doba lisování je 40 s/mm tloušťky výlisku.
Mechanické vlastnosti výlisku jsou následující: mez pev2, mez pev900 MPa.
nosti v tahu 115 IvíPa, rázová houževnatost 9,0 J/ci nosti v ohybu 215 MPa a modul pružnosti z ohybu 8 z .
Příklad 2
Nenasycená polyesterová pryskyřice na bázi ftalanhydridu, maleinanhydridu a propylenglykolu o čísle kyselosti 23,5 mg KOH/g, hydroxylovém čísle 15,0 mg KOH/g, viskozitě'7 1 450 itfPa.s/25 °C, zahustitelná s 2 % hmot. MgO při 20 °C během 14 dnů na viskozitu
8.5 . 105 mPa.s/25 °C
Nenasycená polyesterová pryskyřice na bázi hexachlorendomethylentetrahydroftalanhydridu, maleinanhydridu a propylenglykolu o čísle kyselosti 10,0 mg KOH/g, hydroxylovém čísle
34.5 mg-KOH/g, viskozitě 700 mPa.s/25 °C,
241,00 dílů hi
60,00 ” zahustitelná s 2 % hmot. MgO při 20 °C během 14 dnů na viskozitu 2,8 · 10^ mPa.s/25 °C
1,1-di-terc.butylperoxid-3,3,5-trimetylcyklohexan 4,65 ” Kysličník hořečnatý 4,50 n Hydrochinon 0,10 Ethylalkohol - 0,75 ” Ethoxylovaný stearamid „ 9,00 ” Kaolin - 340,00 Kysličník antimonitý 10,00 “ Stearát zinečnatý 10,00 ” Suspenze železité červeni v nasyceném polyesteru 20,00 ” Sekaný skelný roving 300,00 ’’
Kompozice se lisuje za stejných podmínek jako v příkladu 1 s tím rozdíleni, že doba lisování je 45 s/mm tlouštky výlisku.
Mechanické vlastnosti výlisku jsou. následující: mez pevnosti v tahu 112 MPa, rázová houževnatost 9,5 J/ora2, mez pevnosti v ohybu 205 MPa a modul pružnosti z ohybu 8 600 MPa·
Příklad 3
Nenasycená polyesterová pryskyřice na bázi ftalanhy- 150,00 dílů hmot dridu, maleinanhydridu a propylenglykolu o čísle kyselosti 18,8 mg KOH/g, hydroxylovém * čísle 25,1 mg KOH/g a viskozitě 1 180 raPa.s při 25 °C, zahustitelná se 2 % hmot· MgO při 20 °C během 14 dnů na viskozitu 5,5 · 10^ mPa.s/25 °0
Nenasycená polyesterová pryskyřice na bázi fta- 150,00 ” lanhydridu, maleinanhydridu, propylenglykolu a dipropylenglykolir o čísle kyselosti
26,8 mg KOH/g, hydroxylovém čísle 13,5 mg KOH/g a viskozitě 1 800 mPa.s/25 °C, zahustitelná se 2 % hmot. MgO při 20 °0 během 14 dnů na viskozitu 6,5 . 106 mPa.s/25 °C
| Dibenzoylperoxid | 5,67 |
| Hydrochinon | ©,08 |
| Ethylalkohol | 0,75 |
| E,thylenoxidovaný steeraraid | 15,00 |
| Uhličitan hořečnatý. | 290,00 |
| Kysličník hořečnatý | 7,50 |
| Stearát zinečnatý | 10,00 |
| Suspenze zinkové běloby v hasyceném polyesteru | 21,00 |
| Skelná rohož o gramáži 350 g/m2 | 350,00 ” |
Kompozice se lisuje za stejných podmínek jako v příkladu 1. Mechanické vlastnosti výlisku jsou následující: mez pevnosti p
v tahu 125 MPa, rázová houževnatost 11,2 J/cm , mez pevnosti v ohybu 228 NPa a modul pružnosti z ohybů 10 100 MPa, ·\
I το « ..Příklad 4
Nenasycená polyesterová pryskyřice na bázi ma- 100,00 dílů hmot leinanhydridu, ftalanhydridu a propylenglykolu o čísle kyselosti 16,8 mg KOH/g, , hydroxylovém čísle 24,3 mg KOH/g a viskozitě 1 325 mPa.s/25 °C, zahustitelná se 2% hmot.
MgO při 20 °C během 14 dnů na viskozitu
1,8 . 105 mPa.s/25 °C
Nenasycená polyesterová pryskyřice na bázi ma- 300,00 ” leinanhydridu, hexachlorendomethylente- trahydroftalanhydridu a ethylenglykolu o čísle kyselosti 23z, 9 mg KOH/g, hydroxylovém čísle 16,6 mg KOH/g a viskozitě 1 725 raPa.s/25 °C, zahustitelná s 2 % hmot. kysličníku hořečnatého při 20 °C během 14 dnů na viskozitu 7,8 · 10? . mPs^/25 °C
Terc.butylperbenzoát __ 6,62 ” Kysličník vápenatý \ 7,50 Hydrochinon 0,08 ·’ Ethylalkohol - 0,80 Ethoxylovaný nonylfenol 15,00” Kaolin 270,00 ” Stearát vápenatý 10,00 ” Suspenze chromové žluti v nasyceném polyesteru 20,00 Skelná pramencová výztuž 270,00 ”
Kompozice se lisuje za stejných podmínek jako v příkladu 1.
Mechanické vlastnosti výlisku jsou následující: mez pevnosti o v*tahu 80 MPa, rázová houževnatost 7,4 J/cm , mez pevnosti v ohybu'158 MPa a modul pružnosti z ohybu 7 400 MPa.
Claims (1)
- Tvrditelné lisovací kompozice zejména pro výrobu přepřegů a vyztužených plastů, obsahující jako pojivo nenasycené polyesterové pryskyřice, dále inhibitory, iniciátory, vláknitá vyztužující plniva, zahuščovadla, povrchově aktivní látky, nevyztužující plniva, pigmenty, barviva, separátory, reaktivní a nereaktivní rozpouštědla, retardéry hoření, termoplastické polymery, rozlivová činidla, katalyzátory, stabilizátory nebo jiná aditiva, vyznačující se tím, že obsahují jako pojivá 15 až 60 % hmot· směsi nejméně dvou vlastnostmi rozdílných typů nenasycených polyesterových pryskyřic o molekulové hmotnosti 500 až 5 000 na bázi kondenzačních produktů alkylenglykolů a/nebo polýaUylenglykolů o 2 až 24 atomech uhlíku s Κ,β-nenasycenými alifatickými dikarboxylovými kyselinami a s kyselinami fialovými nebo s jejich deriváty o 2 až 14 atomech uhlíkfe, a to ve formě 30 až 75% roztoků v nenasycených polymerace schopných monomerech, kde jedním typem je alespoň jedna pryskyřice s číslem kyselosti 15 až 25 mg KOH/g, hydroxylovým čí šlem 5 až 30 mg KOH/g, viskositou při 25 °C 1 000 až- 1 500 raPa.s a viskozitou po přídavku 0,5 až 3 % hmot· kysličníku horečnatého a po 14 dnech skladování při 20 °C 1 . 10^ až 1 . 108 raPa.s/25 °C a druhým typem je alespoň jedna pryskyřice s číslem kyselosti 5 až 30 mg KOH/g, hydroxylovým číslem 10 až 50 mg KOH/g, viskozitou při 25 °C 500až 1 100 nebo 1 200 až 1 800 mPa.s/25 °0 a viskozitou po přídavku uvedeného množství kysličníku hořečnatého a po uvedených podmínkách a době skladování 1 · 10^ až 1.10^ nebo 1 .108 až 1 « 108 mPa.s/25 °0, přičemž oba typy pryskyřic jsou ve směsi obsaženy ve hmot S poměru 1 i 6 až 6 : 1 ·