CS206193B1 - Thermoplastic mixture on the basis of the copolymere ethylenevinylacetate and asphalt for making the hydroisolating foils - Google Patents

Thermoplastic mixture on the basis of the copolymere ethylenevinylacetate and asphalt for making the hydroisolating foils Download PDF

Info

Publication number
CS206193B1
CS206193B1 CS361579A CS361579A CS206193B1 CS 206193 B1 CS206193 B1 CS 206193B1 CS 361579 A CS361579 A CS 361579A CS 361579 A CS361579 A CS 361579A CS 206193 B1 CS206193 B1 CS 206193B1
Authority
CS
Czechoslovakia
Prior art keywords
asphalt
foils
hydroisolating
ethylenevinylacetate
copolymere
Prior art date
Application number
CS361579A
Other languages
Czech (cs)
Inventor
Vojtech Blaha
Milan Podesva
Original Assignee
Vojtech Blaha
Milan Podesva
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Vojtech Blaha, Milan Podesva filed Critical Vojtech Blaha
Priority to CS361579A priority Critical patent/CS206193B1/en
Publication of CS206193B1 publication Critical patent/CS206193B1/en

Description

Vynález se týká složeni termoplastická směsi na bázi kopolymeru etylen-vinylaoetát asfaltu a ostatních přísad, vhodné pro výrobu hydroizolačních fólií.BACKGROUND OF THE INVENTION The present invention relates to a composition of a thermoplastic composition based on an ethylene-vinyl acetate asphalt copolymer and other additives suitable for the production of waterproofing films.

Materiály používané pro výrobu hydroizolačních pásů a fóliových výrobků lze rozdělit do tři skupin.The materials used for the production of waterproofing membranes and foil products can be divided into three groups.

První a nejrozšířenější skupinu tvoří směs filerizovanýoh asfaltu AOSI používaných k výrobě asfaltovaných pásů typu S (natavitelnýoh). Ve výrobně se nanáší oboustranně na různé druhy nosných vložek, v celkové tloušťoe ooa 4 mm.The first and the most widespread group consists of a mixture of filerized asphalt AOSI used for the production of asphalted strips type S (fusible). In the factory, it is applied on both sides to different types of bearing inserts, with a total thickness of about 4 mm.

Nevýhodou těohto výrobků je malá tažnost, pružnost za nízkých teplot ovzduší, z čehož vy-, plývá i omezená zpracovatelnost do + 5 °C. Rovněž hmotnost povlakové krytiny z těchto výrobků dosahuje dle počtu vrstev 10 až 15 kg/m .The disadvantage of these products is low ductility, flexibility at low air temperatures, which results in limited workability up to + 5 ° C. Also the weight of the covering of these products reaches 10 to 15 kg / m, depending on the number of layers.

V posledních letech se užitné vlastnosti a rozsah zpracovatelnosti zlepšuji modifikací asfaltu termoplastickými kaučuky, ale hmotnost vícevrstvé krytiny se nemení.In recent years, the utility properties and workability range have been improved by modifying asphalt with thermoplastic rubbers, but the weight of the multilayer roofing does not change.

Druhou skupinou jsou kaučuky s vysokým stupněm nasycenosti jako např. EPDM, CR zpracovaných do fóliových bezvložkových materiálů vyznačující se vynikající odolností proti povětrnosti. Nevýhodou těohto materiálů je obtížné zajišťováni spojů lepením lepidly ze syntetických kaučuků. Při vlastní výrobě těohto fólií je pak technicky a časové náročný proces vulkanizaoe, Z hlediska uplatnění Jsou nevýhodné rozměrové změny fólií.The second group are rubbers with a high degree of saturation, such as EPDM, CR processed into foil-free liner materials with excellent weathering resistance. A disadvantage of these materials is the difficulty of securing the joints by gluing with synthetic rubber adhesives. In the actual production of such films, the process of vulcanization is technically and time consuming.

208 193208 193

Třetí skupinou jsou materiály nevyžadující vulkanizaoi jako PVC, EPDM s asfaltem a plnivy, zpracovávané rovněž jako fóliové materiály.A third group are non-vulcanizing materials such as PVC, EPDM with bitumen and fillers, also processed as foil materials.

Složení směsí vhodných pro tyto aplikace je např. uvedeno v patentových spisechThe composition of the compositions suitable for these applications is disclosed, for example, in the patents

US 4 046840, US 1 493951.US 4 046840; US 1 493951.

Uvedená problematika je řešena předmětem tohoto vynálezu, kterým* jeThis is solved by the subject of the present invention, which is

1, Termoplastická směs pro výrobu hydroizolačních fólii na bázi kopolymerů* etylett-vinylacetát a asfaltu vyznačena tím, že sestává z 40 až 80 hmotn. % kopolymerů etyleň-vinyl aoetát s obsahem vinylacetátu od 5 do ÓO $>, 5 až 50 hmotn. asfaltu, 2 30 hmotn. % anorganických plniv a 2 až 25 hmotn. syntetického, nebo přírodního kaučuku.1. A thermoplastic composition for the production of water-proofing films based on ethylene-vinyl acetate and asphalt copolymers, characterized in that it consists of 40 to 80 wt. % of ethylene-vinyl acetate copolymers having a vinyl acetate content of from 5 to 60%, 5 to 50 wt. asphalt, 2 30 wt. % of inorganic fillers and 2 to 25 wt. synthetic or natural rubber.

2, Termoplastická směs pro výrobu hydroizolačních fólií podle bodu 1. vyznačená tlm, že obsahuje 0,1 až 10 hmotn, % změkčovadel nabo maziv.2. A thermoplastic composition for the production of waterproofing membranes according to claim 1, characterized in that it comprises 0.1 to 10% by weight of plasticizers or lubricants.

Směsi lze upravit až do 50 hmotn. % asfaltem, přičemž sé materiály vyznačují ještě velmi dobrými vlastnostmi a jsou ekonomicky výhodné. S výhodou lze použit jako polyměmího změkčovadla přírodní nebo syntetický kaučuk. Zvláště výhodné je použití SBR nebo butyl kaučuku. Pro úpravu zpracovatelných vlastností směsí a z ekonomického hlediska je možno použit anorganická plniva jako např. saze, klozek, změkčovadla a maziva.The mixtures can be treated up to 50 wt. % asphalt, wherein the materials have still very good properties and are economically advantageous. Preferably, natural or synthetic rubber may be used as the polymeric plasticizer. Especially preferred is the use of SBR or butyl rubber. Inorganic fillers such as carbon black, liner, plasticizers and lubricants can be used to adjust the processable properties of the compositions and economically.

Výroba hydroizolačních fólií ze směsi podle vynálezu vyžaduje minimální nároky na výrobní zařízeni, protože odpadá proces vulkanizaoe. Směs je možno např, zpraoovávat na fólie vytlačováním na vytlačovaoioh strojích při teplotách nad 120 °C, odpad Je znovu zpraoovateIný,The production of waterproofing membranes from the composition according to the invention requires minimal production equipment requirements, since the vulcanization process is eliminated. For example, the mixture can be processed into films by extrusion on extruders at temperatures above 120 ° C, the waste being reprocessable.

Předností hydroizolačních fólii je vzhledem ke skladbě směsi snadné 'spojování a vytvářeni detailu svařováním pomooí tepelnýoh zdrojů.The advantage of the waterproofing foils is, due to the composition of the mixture, easy bonding and detailing by welding using heat sources.

Příklad receptury 1Recipe example 1

Jedná se o formulací receptury směsi pro hydroizolační fólie s vysokým obsahem asfaltu.It is a formulation of a mixture for waterproofing foils with a high content of asphalt.

hmotn. % kopolymer etylen-vinylaoetát s obsahem vinylacetátu 50 (ó 40 asfalt 48 butadien-styrenový kaučuk 2 klouzek 10wt. % ethylene-vinyl acetate copolymer with vinyl acetate content 50 (40 40 asphalt 48 butadiene-styrene rubber 2 slip 10

Základní fyzikálně-meohanioké hodnoty směsi Pevnost v tahu 8,9 MPaThe basic physical-meohani properties of the mixture Tensile strength 8.9 MPa

Tažnost Ductility 684 684 % % Tvrdost Hardness 78 78 Sh A Sh A Elastioita Elastioita 29 % 29% Průtažnost Ductility 500 500 % % Mrazuvzdornost NXI ŠP Frost resistance NXI SP -38 -38 °C Noc: 2 ° C Ozonuvzdornos t Ozonuvzdornos t 300 300 pphm pphm 20 % protažení 20% elongation 300 300 h h

bez trhlinwithout cracks

Příklad receptury 2Recipe example 2

Kopolymer etylen-vinylacetát s obsahem vlnylácetátu 8 fi asfalt bUtylkaučuk saze parafinEthylene-vinyl acetate copolymer containing 8-asphalt bilacetate btytyl rubber soot paraffin

206 193 hmotn. fi206 193 wt. fi

Základní fyzikálně-mechanické hodnoty směsiBasic physico-mechanical values of the mixture

Pevnost v tahu Tensile strength 8 8 MPa MPa Tažnost Ductility 730 730 fi fi Tvrdost Hardness 80 80 Sh A Sh A Elasticita Elasticity 20 20 May fi fi Průtažnost Ductility 700 700 fi fi Mrazuvzdornost Nil ŠP Frost resistance of Nile SP -32 -32 °c ° c Oz onuvzdorno s t Oz onuvzdorno s t 300 300 pphm pphm 20 fi protažení 20 fi elongation 300 300 h bez trhlin h without cracks Nasákavost 29 dní/28 °C Absorption 29 days / 28 ° C 0, 0, 3 fi hmotn. 3 fi wt.

Fyzikálně meohanické hodnoty směsi po zkouškách atmosférického stárnutí (v fi).Physical meohanic values of the mixture after atmospheric aging tests (in fi).

Za 1 rok In 1 year Za 5 roku In 5 years Pevnost v tahu Tensile strength - 3,2 - 3,2 - 11,5 - 11,5 - 5,4 - 5,4 Tažnost Ductility - 3,1 - 3,1 - 7,3 - 7,3 - 2,7 - 2,7 Tvrdost Hardness - 0,5 - 0,5 + 3,5 + 3,5 ♦ 3,5 ♦ 3,5

Povrch opatřen reflexním nátěrem RUBOL-RSRUBOL-RS reflective coating

Claims (2)

PŘEDMĚT VYNÁLEZUSUBJECT OF THE INVENTION 1 . Termoplastická směs na bázi kopolymeru etylen-vinylacetát a asfaltu pro výrobu hydroizolačních fólii vyznačená tím, že sestává z 40 až 80 hmotn. fi kopolymeru etylen-vinylacetát s obsahem vinylacetátu od 5 do 60 fi, 5 až 50 hmotn. fi asfaltu, 2 až 30 hmotn. fi anorganických plniv a 2 až 25 hmotn. fi syntetického nebo přírodního kaučuku.1. Thermoplastic mixture based on ethylene-vinyl acetate copolymer and asphalt for the production of waterproofing films characterized in that it consists of 40 to 80 wt. % of ethylene-vinyl acetate copolymer having a vinyl acetate content of from 5 to 60, 5 to 50 wt. % of asphalt, 2 to 30 wt. % of inorganic fillers and 2 to 25 wt. fi synthetic or natural rubber. 2. Termoplastioká směs pro výrobu hydroizolačních fólií podle bodu 1 vyznačená tim, že obsahuje 0,1 až 10 hmotn. fi změkčovadel nebo maziv.2. The thermoplastic composition for the production of waterproofing membranes according to claim 1, characterized in that it comprises 0.1 to 10 wt. fi plasticizers or lubricants.
CS361579A 1979-05-25 1979-05-25 Thermoplastic mixture on the basis of the copolymere ethylenevinylacetate and asphalt for making the hydroisolating foils CS206193B1 (en)