CS201473B1 - Adhesive for sticking textile materials at print and agent for treatment of textile materials before print - Google Patents
Adhesive for sticking textile materials at print and agent for treatment of textile materials before print Download PDFInfo
- Publication number
- CS201473B1 CS201473B1 CS193779A CS193779A CS201473B1 CS 201473 B1 CS201473 B1 CS 201473B1 CS 193779 A CS193779 A CS 193779A CS 193779 A CS193779 A CS 193779A CS 201473 B1 CS201473 B1 CS 201473B1
- Authority
- CS
- Czechoslovakia
- Prior art keywords
- adhesive
- paste
- thermally modified
- textile materials
- Prior art date
Description
(54) Lepidlo pro lepení textilních útvarů při tisku a prostředek pro úpravu textilních útvarů před tis kem(54) Adhesive for gluing textile formations during printing and means for treating textile formations prior to printing
Vynález se týká použití termicky modifi- . kovaného^ oxidovaného škrobu jako lepidla pro lepení textilních útvarů před tiskem.The invention relates to the use of thermally modified materials. forged oxidized starch as an adhesive for bonding textile formations prior to printing.
Dosud známé způsoby používají pro lepení textilních útvarů na tiskací stoly a na textilní tiskové pásy různé druhy polymerních látek, především deriváty celulózy, deriváty škrobu nebo. vybrané druhy přírodních gum a klovatin.The prior art methods use various types of polymeric substances, in particular cellulose derivatives, starch derivatives, or glues, for bonding textile formations to printing tables and textile printing belts. selected types of natural gums and gums.
Nevýhody uvedených způsobů spočívají v nevhodných adhezních a zejména Teologických vlastnostech. Dále jsou uvedené druhy polymerních látek hůře vypratelné běžným způsobem. Speciální deriváty celulózy a škrobu, jakož í přírodní klovatiny a gumy, které splňují technologické požadavky, jsou velmi nákladné a omezeně' dostupné. Dosavadní lepidly jsou tedy vždy jen kompromisem mezi technologickými paramtery a nákladností jednotlivých typů lepidel.The disadvantages of these methods are inadequate adhesion and especially theological properties. Furthermore, these types of polymeric substances are difficult to wash in a conventional manner. Special cellulose and starch derivatives, as well as natural gums and gums that meet the technological requirements are very expensive and limited in availability. Hitherto existing adhesives are always only a compromise between technological parameters and the cost of individual types of adhesives.
Větší část uvedených nedostatků se -odstraní použitím vodné pasty oxidovaného škrobu, termicky modifikovaného v přítomnosti karboxymetylcelulózy jako inhibitoru mazovatění á v přítomnosti anorganických solí, jako lepidla pro lepení textilních útvarů při tisku a jako prostředku proi úpravu textilních útvarů před tiskem. Přítomnost karboxymetylcelulózy při termizačním procesu reguluje rozpad škrobových zrn a reo201473 logické vlastnosti oxidovaného škrobu. Přídavek solí, zejména boraxu, dusičnanu sodného nebo. rhodanidu amonného, reguluje vlastnosti adhezivní, hydratační poměr při termické úpravě a vypírání vodné pasty lepidla z tkaniny. Vločky termicky modifíko- váného škrobu se rozpouštějí ve studené vodě na homogenní pastu bez tvorby shluků. Pasta má zdánlivou viskozitu 10 % vodného roztoku při 25 °C v intervalu 100 až 150 mPa.s.The greater part of these drawbacks, the use of aqueous pastes deprotecting oxidized starch, a thermally modified in the presence of CMC as gelatinization inhibitor and in the presence of inorganic salts, such as adhesives for bonding textile printing units and as a means for treatment and textile formations before printing. The presence of carboxymethylcellulose in the thermization process regulates the decomposition of starch grains and the reo201473 logical properties of oxidized starch. Addition of salts, in particular borax, sodium nitrate or. of ammonium rhodanide, regulates the properties of the adhesive, hydration ratio in the thermal treatment and washing of the aqueous paste of the adhesive from the fabric. The flakes of thermally modified starch dissolve in cold water to form a homogeneous paste without clumping. The paste has an apparent viscosity of a 10% aqueous solution at 25 ° C over a range of 100 to 150 mPa · s.
Vodná pasta se použije k lepení textilních útvarů, především tkanin, na textilní stoly před tiskem. Vodná pasta je rovněž vhodná pro úpravu textilií , na povrchu, pro dosažení' hladkého povrchu textilie, zejména u tkanin s vlasem. Nanášení vodné pasty lepidla ' se. provádí způsobem obvyklým při lepení, jako u dosud používaných lepicích přípravků. Rovněž použití vodné pasty pro úpravu textilních útvarů před tiskem se provádí obvyklým způsobem. Po provedení tisku barvivém je textilie zbavena zbytků vodné pasty lepidla při praní, které se provádí po tisku jako jedna ze závěrečných pracovních operací. Vločky lepidla po termizačním procesu, použité k přípravě vodné pasty lepidla, mají složení 10 až 20 hmotnostních dílů dusičná-, nu sodného' nebo. rhodanidu amonného, 5 až 10 hmotnostních dílů boraxu, 40 až 60 hmotnostních dílů oxidovaného škrobu a 30 až 40 hmotnostních dílů karboxymethylcelulózy.The aqueous paste is used to bond textile formations, especially fabrics, to textile tables prior to printing. The aqueous paste is also suitable for surface treatment of textiles to provide a smooth fabric surface, particularly in pile fabrics. Application of aqueous paste adhesive. It is carried out in the manner usual in gluing, as with the previously used adhesive preparations. Also, the use of an aqueous paste to treat textile structures prior to printing is carried out in a conventional manner. After printing the dye, the fabric is free of aqueous adhesive paste residues during the washing process, which is carried out after printing as one of the final operations. The adhesive flakes after the thermal treatment used to prepare the aqueous adhesive paste have a composition of 10 to 20 parts by weight of sodium nitrate or sodium nitrate. of ammonium rhodanide, 5 to 10 parts by weight of borax, 40 to 60 parts by weight of oxidized starch and 30 to 40 parts by weight of carboxymethylcellulose.
Použití termicky modifikovaného oxidovaného škrobu pro lepení a úpravu přeď tiskem je objasněno ve dvou následujících příkladech.The use of thermally modified oxidized starch for gluing and pre-printing is illustrated in the following two examples.
Příklad 1Example 1
Vodná pasta, pro lepení textilních útvarů, především tkanin, na textilní tiskací stoly před tiskem.Aqueous paste, for bonding textile formations, especially fabrics, to textile printing tables before printing.
400 až 500 g termicky modifikovaného škrobu 600 až 500 g vody 20 °C teplé lOOOg400-500 g thermally modified starch 600-500 g water 20 ° C warm 100 g
Odvážené množství termicky modifikovaného škrobu se rozpustí, nejlépe za stálého míchání, postupným vnášením vloček termicky modifikovaného; škrobu do vody tak, že vznikne homogenní pasta.The weighed amount of thermally modified starch is dissolved, preferably under constant stirring, by successively introducing the thermally modified flakes; starch into water to form a homogeneous paste.
Příklad 2Example 2
Vodná pasta pro úpravu textilií na povr-Aqueous paste for surface treatment of textiles
Claims (1)