CN88105874A - Mulberry silk and cotton-flax blending silk fabric - Google Patents
Mulberry silk and cotton-flax blending silk fabric Download PDFInfo
- Publication number
- CN88105874A CN88105874A CN88105874.2A CN88105874A CN88105874A CN 88105874 A CN88105874 A CN 88105874A CN 88105874 A CN88105874 A CN 88105874A CN 88105874 A CN88105874 A CN 88105874A
- Authority
- CN
- China
- Prior art keywords
- silk
- cotton
- mulberry silk
- fabric
- blending
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
Mulberry silk and cotton-flax blending silk fabric is a kind ofly to weave the high-grade fabric that forms and lining material, underlinen fabric and nightwear lining by a certain percentage with animal fiber mulberry silk and string kenaf-cotton blending yarn.
Description
Mulberry silk and cotton-flax blending silk fabric of the present invention is a kind of textiles that is interwoven by animal fiber and string.
At present, silk ramie silk that silk broadcloth, animal and plant fiber interweave etc. is only arranged on the market, but still do not have the silk of mulberry silk and fiber crops, three kinds of fiber interweavings of cotton blending.The equal complex process of silk broadcloth, silk ramie silk or hemp blended fabric needs air-conditioning, requires constant temperature, and high humidity is knitted and sheltered manyly, and weaving efficiency is low, just can weave after need carrying out sizing or soft treatment through, parallel.These fabrics can not combine the style of mulberry silk, fiber crops, cotton three kinds of natural fabrics together.
Purpose of the present invention just is: provide that a kind of weaving process is simple, cost is low, the weaving efficiency height is knitted and is sheltered fewly, and the advantage that can collect mulberry silk, fiber crops, cotton fiber is the underlinen fabric and the coat of one, material and lining in the high-grade clothing.
The present invention realizes its purpose like this: use the animal fiber mulberry silk, the string kenaf-cotton blending yarn is woven into mulberry silk and cotton-flax blending silk fabric, and the percentage by weight of each fibre fractionation content is in this silk fabric:
Mulberry silk 21-44%
Flax fibre 32-43.5%
Cotton fiber 21-35.5%
The summation of each constituent content is 100%
In the fibre fractionation of the present invention, the animal fiber mulberry silk adopts 2/20/22 dawn or 2/40/44 dawn WHITE STEAM FILATURE YARNS, and numb cotton fiber adopts 21
S-32
SKenaf-cotton blending yarn.
Weaving process of the present invention is: the warp that mulberry silk fiber is formed carries out pre-treatment, turns over, network, warping, weaves then, and the dyeing process with the silk flosssilk wadding combination carries out dyeing and finishing again, promptly singes, practices, floats and put in order.When weaving, make warp, make parallel with kenaf-cotton blending yarn with mulberry silk, through close 50-60 root/centimetre, filling density 24-30 root/centimetre.
Because the present invention contains three kinds of natural fabrics such as above-mentioned mulberry silk, fiber crops, cotton, and weave with weaving process according to the above ratio, make the exquisiteness, smooth, soft of this mulberry silk and cotton-flax blending silk fabric collection mulberry silk, flax fibre well-pressed, tough and tensile, the heat-preservation cold-resistance moisture absorption of cotton fiber is an one, and style separately is melted in the kind, has the good surface appearance effect, can make underlinen fabric and coat, material and lining, nightwear etc. in the high-grade clothing are comfortable and easy to wear attractive in appearance.Technology of the present invention is simple, is difficult for air-conditioning, humidity is little, and parallel does not need pre-treatment, sizing not.Weaving efficiency is than the high 3-4 of same silk broadcloth times, than the also high 2-3 of cotton ramie blended spinning cloth doubly.Cracked ends is few when weaving this mulberry silk and cotton-flax blending silk fabric, not staplings, the latitude that do not contract, knit shelter few.Therefore mulberry silk and cotton-flax blending silk fabric of the present invention is lower than the silk broadcloth cost of same specification, outward appearance and to take effect better than silk broadcloth, but instead of part silk broadcloth are for a new classification has been created in silk textile industry, to play very big reform impetus to this industrial expansion, market will widely be arranged.Because the mulberry silk content of this mulberry silk and cotton-flax blending silk fabric is lower than 50%, can makes textiles and sell (not being only limited to silk outlet), and not be subjected to external quota restrictions again, be a kind of export varieties of earning foreign exchange therefore.
Embodiment:
Embodiment 1, mulberry silk and cotton-flax blending silk fabric optimum formula (by weight percentage)
Mulberry silk 21%
Flax fibre 43.5%
Cotton fiber 35.5%
The summation of each fibre fractionation content is 100%
(1) test method step content:
(1) technological parameter is selected
Graticule is selected: warp adopts mulberry silk, 2/20/22 dawn or 2/40/44 dawn WHITE STEAM FILATURE YARNS, and grade is not less than the 2A level; Parallel adopts 21
SThe 55/45R/C kenaf-cotton blending yarn, outward appearance and inherent quality are not less than first-class, and fiber crops are adopted ramie.
Tissue: plain weave or twill or small jacquard.
Weaving density: through close 50-60 root/centimetre, filling density 24-30 root/centimetre.
Fabric width: outer 115 centimetres, interior 114 centimetres, 45 meters of coupes.
Weave specification: reed: fabric width (centimetre), outer 120.5, interior 119
Reed porter: 24/13,2/4
Warp number:, interior through 5712 outward through 72 * 2
(2) measure powerful and elongation at break of fibrous fracture and elastic restoration ratio under different elongations, mensuration frictional coefficient of fiber etc. are seen the standard that whether reaches.
(3) test weaving observe to detect working order, and cracked ends, staplings, latitude and knit the situation of sheltering, silk fabric face effect etc. contracts.
(4) detect by the check of Sichuan Province's textile fabric; Ultimate strength, washing shrinkage, shrinkage rate of weaving when machine (following shrinkage).
(2) interpretation of result
(1) test weaving is observed: work well, not staplings, the latitude that do not contract, not cracked ends, knit shelter less, silk fabric face effect is good.
(2) Sichuan Province's textile fabric check institute testing result:
Ultimate strength (kilogram): warp-wise 5 * 20(centimetre of sample cloth) 37.5
Broadwise 5 * 20(centimetre of sample cloth) 51.8
Washing shrinkage: 114 centimetre 4.56% of warp-wise fabric width
114 centimetre 1.64% of broadwise fabric width
Shrinkage rate of weaving: 5.43%
As from the foregoing, compare with other silk fabric classes, the ultimate strength of mulberry silk and cotton-flax blending silk fabric reaches national ministry standard, and indivedual indexs surpass GB, dress soft frank, well-pressed, comfortable attractive in appearance, wear-resisting,
Embodiment 2 mulberry silk and cotton-flax blending silk fabric prescriptions (by weight percentage)
Mulberry silk 26%
Flax fibre 38.5%
Cotton fiber 35.5%
The summation of each constituent content is 100%.
(1) test method, step content: with embodiment 1.
(2) interpretation of result
(1) test weaving is observed: work well, staplings, the latitude that do not contract do not have a small amount of cracked ends phenomenon, knit to shelter than embodiment 1 to increase slightly, and silk fabric face effect is good.
(2) Sichuan textile fabric check institute testing result:
Ultimate strength (kilogram): warp-wise 5 * 20(centimetre of sample cloth) 37.8
Broadwise 5 * 20(centimetre of sample cloth) 51.5
Washing shrinkage, shrinkage rate of weaving and other results are to embodiment 1.
Embodiment 3 mulberry silk and cotton-flax blending silk fabric prescriptions (by weight percentage)
Mulberry silk 41%
Flax fibre 32%
Cotton fiber 27%
The summation of each constituent content is 100%
(1) test method, step and content are with embodiment 1.
(2) interpretation of result:
(1) test weaving is observed: with embodiment 1.
(2) Sichuan Province's textile fabric check institute testing result:
5 * 20(centimetre of sample cloth of ultimate strength (kilogram) warp-wise) 38.2
Broadwise 5 * 20(centimetre of sample cloth) 51.2
Washing shrinkage, shrinkage rate of weaving and other results are with embodiment 1.
Embodiment 4 mulberry silk and cotton-flax blending silk fabric prescriptions (by weight percentage)
Mulberry silk 44%
Flax fibre 35%
Cotton fiber 21%
The summation of each constituent content is 100%
(1) test method, step and content: with embodiment 1.
(2) interpretation of result:
(1) test weaving is observed: with embodiment 1.
(2) Sichuan Province's textile fabric check institute testing result:
Ultimate strength (kilogram): warp-wise 5 * 20(centimetre of sample cloth) 38.5
Broadwise 5 * 20(centimetre of sample cloth) 51.3
Washing shrinkage, shrinkage rate of weaving and other results are with embodiment 1.
Claims (3)
1, a kind of textiles mulberry silk and cotton-flax blending silk fabric is made up of animal fiber and string, it is characterized in that: animal fiber is a mulberry silk, and string is a kenaf-cotton blending yarn, and the percentage by weight of each fibre fractionation content is in its mulberry silk and cotton-flax blending silk fabric:
Mulberry silk 21-44%
Flax fibre 32-43.5%
Cotton fiber 21-35.5%
The summation of each constituent content is 100%.
2, mulberry silk and cotton-flax blending silk fabric according to claim 1 is characterized in that: mulberry silk is 2/20/22 dawn or 2/40/44 dawn WHITE STEAM FILATURE YARNS, and string is 21
S-32
SKenaf-cotton blending yarn.
3, the weaving process of the described mulberry silk and cotton-flax blending silk fabric of claim 1 is: after the warp that mulberry silk fiber is formed carries out pre-treatment, turn over, network, arrangement, weave then, adopt the dyeing process of silk flosssilk wadding combination to carry out dyeing and finishing again, promptly singe, practice, float and put in order, it is characterized in that:
(1) make warp with mulberry silk, kenaf-cotton blending yarn is made parallel,
(2) through close 50-60 root/centimetre, filling density 24-30 root/centimetre.