CN86106918A - 水泥复合助磨剂 - Google Patents
水泥复合助磨剂 Download PDFInfo
- Publication number
- CN86106918A CN86106918A CN86106918.8A CN86106918A CN86106918A CN 86106918 A CN86106918 A CN 86106918A CN 86106918 A CN86106918 A CN 86106918A CN 86106918 A CN86106918 A CN 86106918A
- Authority
- CN
- China
- Prior art keywords
- cement
- grinding
- composite grinding
- type composite
- trolamine
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
水泥复合助磨剂,是用于水泥生产过程中的粉磨工序。为提高磨机粉磨效率,降低单位能耗,提高水泥质量所采取的一项有效措施。我们研制出的四个系列水泥复合助磨剂,可根据水泥厂的磨机形式和规格,熟料成分,混合材种类和要求的水泥品种等不同,而分别选用和调整比例。这些水泥复合助磨剂,克服了现用的单成分的三乙醇胺助磨剂价格太贵,质量不稳定,和粉尘飞扬太大的缺点。
Description
本发明属于水泥制造领域,特别是水泥生产工艺中的粉磨工序用的助磨剂。
目前国内外的水泥生产,一般都采用单一成份的助磨剂,不仅价格较贵,而且质量不稳定,助磨效果亦不显著。
我国五十年代末研究过用纸浆废液、煤等作为水泥助磨剂,没有普遍推广使用。七十年代初有抚顺、柳州、大连等十几个水泥厂、及四川水泥研究院、华南工学院等单位亦研究、使用过水泥助磨剂,一般是采用化工厂的付产品或下脚料,主要是三乙醇胺系列产品、如乙二醇、三乙醇胺、多缩乙二醇、二三醇胺等。但由于这些助磨剂价格较贵,每吨需要5000~6000元,而且化工厂的下脚料质量不稳定,助磨效果亦不稳定。因此只有柳州水泥厂在生产出口水泥时使用,其他厂均未采用。
目前国外使用的水泥助磨剂很多。如苏联专利(SU3507247),采用氮基三甲基磷酸和硫酸锌作为水泥助磨剂;苏联化学和化学工艺杂志1979年第22卷第8期报导的水泥助磨剂有丙三醇、三乙醇胺、和丁醇;又据日本专利(JP80/8762),采用木质磺酸钠和二甘醇作水泥助磨剂;另据Inst.Stroit.Mater(Sofia)1976年第6卷第119-373页报导的水泥助磨剂有尿素、三乙醇胺和乙二醇等。这些水泥助磨剂一般都是单一成分,有的助磨剂,如三乙醇胺、丁醇、丙三醇等价格较贵,如采用化工厂的下脚料质量不稳定;有的助磨剂,如木质磺酸钠等,助磨效果不显著;使用尿素作助磨剂时,水泥粉末的细度达不到要求。
本发明的目的、是在水泥粉磨过程中,加入少量对水泥性能无害的助磨剂,来改善粉磨效果,降低水泥生产中粉磨工序的能耗,提高粉磨效率的措施之一。即在水泥细度相同条件下,增加产量;或在水泥产量和磨机功率消耗相同条件下,增加水泥的比表面积,从而提高水泥质量。
通过调查研究,反复试验,研制成功了四个系列十个品种的水泥复合助磨剂,它们是:
1.以尿素为主体的N-系列水泥复合助磨剂,它包括以下三个品种:
(1)N-C型复合助磨剂,复合比例为:尿素60-90%,三乙醇胺中和的低碳酸40-10%。
(2)N-T型复合助磨剂,复合比例为:尿素60-95%,三乙醇胺40-5%。
(3)N-W型复合助磨剂,复合比例为:尿素60-90%二甘醇40-10%。
2.以硫酸钠为主体的S-系列水泥复合助磨剂,它包括以下三个品种:
(1)S-C型复合助磨剂,复合比例为:硫酸钠60-90%,三乙醇胺中和的低碳酸40-10%。
(2)S-T型复合助磨剂,复合比例为:硫酸钠60-95%,三乙醇胺40-5%。
(3)S-W型复合助磨剂、复合比例为:硫酸钠60-90%,二甘醇40-10%。
3.以低聚甘油为主体的L-系列水泥复合助磨剂,它包括以下三个品种:
(1)L-C型复合助磨剂,复合比例为:低聚甘油60-90%,三乙醇胺中和低碳酸40-10%。
(2)L-T型复合助磨剂,复合比例为:低聚甘油60-90%,三乙醇胺40-10%。
(3)L-W型复合助磨剂,复合比例为:低聚甘油60-90%,二甘醇40-10%。
4.53#水泥复合助磨剂,复合比例为:混合乙二醇低聚体50%,低聚甘油40%,混合胺盐10%。
这些水泥复合助磨剂可根据水泥厂的不同磨机型式和磨机规格,熟料成分,混合材种类和要求的水泥品种等不同,而分别选用和调节,一般复合助磨剂的加入量,为水泥的0.05%以下。即可达到提高产量,降低能耗的目的。
这些助磨剂对水泥性能无害,相反还能改善水泥的早期强度,三天抗压强度可提高1-15%,28天抗压强度可提高10%左右。而且抗冻性、抗渗性、蒸养效果及干缩性能均优于目前国内外用的较多的三乙醇胺助磨剂。
本发明的水泥复合助磨剂,与三乙醇胺相比,具有价廉,质量稳定,助磨效果较好,并能改善水泥的性能等优点。
如N-系列水泥复合助磨剂,每吨价约为600-700元,在生产纯硅酸盐水泥时,台时产量提高20-25%,电耗下降20%以上。
又如S系列水泥复合助磨剂,每吨价约400-500元,在生产矿渣水泥时,台时产量提高10%以上,电耗下降10以上。
其余两个系列的水泥复合助磨剂,其效果与N-系列和S-系列的助磨剂基本相同。
在实际的水泥生产中,加入了0.03%的N-T型复合助磨剂,即尿素为90%,三乙醇胺10%,在不降低台时产量的前提下,生产出了625#R硅酸盐水泥,使水泥质量提高了一个标号,每吨水泥能获利33元以上。
Claims (2)
- 一、在水泥生产过程的粉磨工序用的水泥复合助磨剂,其特点是由四个系列十个品种组成:1.以尿素为主体的N-系列水泥复合助磨剂:(1)N-C型复合助磨剂,复合比例为:尿素60~90%,三乙醇胺中和低碳酸40-10%。(2)N-T型复合助磨剂,复合比例为:尿素60-95%,三乙醇胺40-5%。(3)N-W型复合助磨剂,复合比例为:尿素60~90%,二甘醇40-10%。2.以硫酸钠为主体的S-系列水泥复合助磨剂:(1)S-C型复合助磨剂,复合比例为:硫酸钠60-90%,三乙醇胺中和的低碳酸40-10%。(2)S-T型复合助磨剂,复合比例为:硫酸钠60-95%,三乙醇胺40-5%。(3)S-W型复合助磨剂,复合比例为:硫酸钠60-90%,二甘醇醇40-10%。3.以低聚甘油为主体的L-系列水泥复合助磨剂:(1)L-C型复合助磨剂,复合比例为:低聚甘油60-90%,三乙醇胺中和的低碳酸40-10%。(2)L-T型复合助磨剂,复合比例为:低聚甘油60-90%,三乙醇胺40-10%。(3)L-W型复合助磨剂,复合比例为:低聚甘油60-90%,二甘醇40-10%。4.53号水泥复合助磨剂,复合比例为:混合乙二醇低聚体50%,低聚甘油40%,混合胺盐10%。
- 二、如权利要求一的水泥复合助磨剂,其特点是加入量为水泥的0.05%以下。