CN86105187A - A kind of manufacture method of artistic enamelware - Google Patents
A kind of manufacture method of artistic enamelware Download PDFInfo
- Publication number
- CN86105187A CN86105187A CN 86105187 CN86105187A CN86105187A CN 86105187 A CN86105187 A CN 86105187A CN 86105187 CN86105187 CN 86105187 CN 86105187 A CN86105187 A CN 86105187A CN 86105187 A CN86105187 A CN 86105187A
- Authority
- CN
- China
- Prior art keywords
- artistic
- glaze
- enamelware
- manufacture method
- pattern
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of manufacture method of artistic enamelware, it is the enamel base with enamel firing, at first successively sprays colored glaze slip and portray structure on its surface to go out pattern, then the sintering glaze, again will be the pattern that goes out of structure cover with paint, lacquer, colour wash, etc. colored glaze or, burn till after the drying not portraying pattern direct drawing on the agglomerating glaze.Artistic enamelware by the present invention's manufacturing, simple and tasteful, color is mottled, rich and gaudy, the artistic effect that exactly likes an ancient unit of weight kiln " transmutation " and ceramic fancy glaze " transmutation ", give the plastic relief sensation, and this manufacture method is easy, and artistic effect is good, therefore can be applied to widely and make various artistic enamelwares in the porcelain enamel industry.
Description
The present invention is a kind of manufacture method of artistic enamelware.
The manufacture method of existing artistic enamelware, be with at the bottom of the baslled iron enamel firing after the moulding, cover-coat enamel, registering spraying or Freehandhand-drawing go out pattern then, burn till through kiln again.This manufacture method, the flat dullness of pattern lacks the ideal visual sense, and thinks that by the prior art glazed colour layer running porcelain or taking off the porcelain phenomenon very easily appears in thickening.
The purpose of this invention is to provide and a kind ofly can overcome the above-mentioned shortcoming and the manufacture method of expression art enamelled artistic effect preferably, to obtain gratifying enamel artwork.
The present invention be achieved in that with enamel firing spend ground-coat enamel or the end, the enamel base of cover-coat enamel, spray the glaze slip of enameling on its surface with spray gun earlier, colored glaze after the spraying is the dispersed particles shape, dry back carves pattern by the pattern of design with the bamboo pen, or do not portray structure and go out pattern, the stove of putting into temperature then and be 780~900 ℃ is with the colored glaze sintering, again will be after the cooling pattern that goes out of structure cover with paint, lacquer, colour wash, etc. colored glaze slip or directly not portraying pattern on the agglomerating glaze with the colored glaze drawing, put into after drying under 800~900 ℃ of furnace temperature and burn till.
The blast of control spray gun and apart from the height of institute's sprayed surface makes the colored glaze slip after the spraying be the dispersed particles shape, and the blast of general spray gun is 3~4kg/m
3, it is that 350~400mm is advisable from the height of institute's sprayed surface that spray gun is chewed end distance.
The present invention compares with the manufacture method of existing artistic enamelware, the manufacturing process novelty, use the method for spraying colored glaze and the means of portrayal composition, overcome the shortcoming of flat dullness of pattern and visual sense difference preferably, and make colored glaze surface, spraying back form the dispersed particles shape with spraying technology, also preferably resolve the masty race porcelain of prior art or take off the porcelain problem.
So artistic enamelware by the present invention's manufacturing, the large-scale Enamelled Mural made from the present invention particularly, simple and tasteful, color is mottled, rich and gaudy, the artistic effect that exactly likes an ancient unit of weight kiln " transmutation " and ceramic fancy glaze " transmutation " give the sensation of plastic relief, and manufacture method of the present invention is easy, and artistic effect is good, therefore can be applied to widely and make various artistic enamelwares in the porcelain enamel industry.
Below in conjunction with embodiment more specific description is made in invention:
At first with the baslled iron enamel firing ground-coat enamel of moulding or the end, cover-coat enamel.
Then through spraying needed colored glaze slip with spray gun on the enamel base surface of enamel firing, the blast of control spray gun and from the height of institute's sprayed surface makes the colored glaze slip after the spraying be the dispersed particles shape, and the blast of general spray gun is 3~4kg/m
3, it is that 350~400mm is advisable from the height of institute's sprayed surface that spray gun is chewed end distance, the glazed colour layer thickness after the spraying is 1.5~3mm, the material of this colour glaze slip constitutes and ratio: basic glaze frit, 100, enamel pigment, 2.5~10, clay, 4.5~6, water, 45~55, it constitutes the essential substance of colored glaze slip, and basic glaze frit constitutes (Wt%) by following material:
K
2O+Na
2O 16~17、Al
2O
35~6、SiO
246~48、B
2O
311~13、CaF
23.5~4、TiO
25~6、Na
2SiF
67~8.5。
After the colored glaze slip drying of spraying, go out pattern on its surface with bamboo pen portrayal structure, at 780 ℃~900 ℃ sintering temperature, the tarnish of agglomerating glaze has just begun clinkering with glaze during sintering and has been advisable then.
After the agglomerating enamel base cooling, the pattern that goes out of structure is covered with paint, lacquer, colour wash, etc. required colored glaze slip again, puts into after drying is modified under 800~900 ℃ the furnace temperature and burns till.
Claims (4)
1, a kind of manufacture method of artistic enamelware, it is characterized in that: with enamel firing spend ground-coat enamel or the end, the enamel base of cover-coat enamel, earlier spray colored glaze slip on its surface with spray gun, portraying structure then goes out pattern or does not portray structure to go out pattern, put into kiln with the glaze sintering, will portray again pattern that structure goes out cover with paint, lacquer, colour wash, etc. go up colored glaze or not portraying pattern through directly burning till behind the drawing on the agglomerating glaze.
2, according to the manufacture method of right 1 described artistic enamelware, it is characterized in that said spray gun, blast is 3~4kg/m
3, during spraying, it is 350~400mm from the height of institute's sprayed surface that the spray gun rifle is chewed end distance.
3, according to the manufacture method of right 1 described artistic enamelware, it is characterized in that said colored glaze slip with the spray gun spraying, coating thickness is 1.5~3mm, the colored glaze slip surface after the spraying is the dispersed particles shape.
4, according to the manufacture method of right 1 described artistic enamelware, it is characterized in that said sintering, temperature is 780~900 ℃, has just begun clinkering with glaze during sintering and has been advisable, and burns till, temperature is 800~900 ℃.