CN2711177Y - 一种表面抗菌、耐磨的不锈钢制品 - Google Patents

一种表面抗菌、耐磨的不锈钢制品 Download PDF

Info

Publication number
CN2711177Y
CN2711177Y CN 200420045396 CN200420045396U CN2711177Y CN 2711177 Y CN2711177 Y CN 2711177Y CN 200420045396 CN200420045396 CN 200420045396 CN 200420045396 U CN200420045396 U CN 200420045396U CN 2711177 Y CN2711177 Y CN 2711177Y
Authority
CN
China
Prior art keywords
stainless steel
coatings
tiagn
tin
film
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Lifetime
Application number
CN 200420045396
Other languages
English (en)
Inventor
姜培齐
麦桥
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN 200420045396 priority Critical patent/CN2711177Y/zh
Application granted granted Critical
Publication of CN2711177Y publication Critical patent/CN2711177Y/zh
Anticipated expiration legal-status Critical
Expired - Lifetime legal-status Critical Current

Abstract

本实用新型是一种表面抗菌、耐磨的不锈钢制品。本实用新型表面抗菌、耐磨的不锈钢制品包括有不锈钢基材(1)及若干TiAgN镀膜层(2)，TiN和TiAgN镀膜层(2)镀在不锈钢基材(1)的外侧。上述若干TiN和TiAgN镀膜层(2)可为一层或一层以上。上述各TiN和TiAgN镀膜层(2)中所含的银、钛成分呈梯级改变，即内镀膜层含银成分低，含钛成分高，外镀膜层含银成分高，含钛成分低。本实用新型表面抗菌、耐磨的不锈钢制品由于采用在不锈钢基材上镀有若干层TiAgN镀膜层的结构，因此，其不仅具有良好的抗菌性能，而且又具有持久的耐磨性能。本实用新型是一种综合性能较好的表面抗菌、耐磨的不锈钢制品。

Description

一种表面抗菌、耐磨的不锈钢制品
1、技术领域：
本实用新型是一种表面抗菌、耐磨的不锈钢制品，属于不锈钢制品的创新技术。
2、背景技术：
现有的表面抗菌不锈钢制品，主要用于餐具、医疗器械、按钮、拉手、门把等许多制品。目前，国外一些单位研发了掺银不锈钢及其制品，具有良好的抗菌效果，1小时后微生物数量明显减少，24小时可以抑制99％的细菌生长。日本钢管公司利用无机抗菌剂开发了抗菌预涂层钢板，即在预先经过镀锌前涂镀过的钢板上再喷涂上带有无机抗菌剂的聚酯树脂、聚氧乙烯树脂等有机树脂涂层，具有良好的抗菌性能，广泛用于洗衣机缸体、冰箱内层。美国马塞诸塞州维克费尔德市阿金(Agion)公司开发出了一种银沸石涂层不锈钢，已用于医疗设备、食品用具上，具有良好的搞菌性能。上述产品都具有生物抗菌性能，达到了良好的抗菌目的。但因银是贵重金属，掺银的不锈钢产品成本太高，虽然经过磨损之后仍具有抗菌性，由于成本太高限制其使用，且不锈钢产品只是其表面需要抗菌，里层本体抗菌无实际意义，整体均匀掺银的不锈钢产品造成极大浪费。还有其他几种抗菌材料表面都具有良好的抗菌性，但耐磨性差，抗菌效果不能持久。
3、发明内容：
本实用新型的目的在于克服上述缺点而提供一种具有良好抗菌性能，又持久耐磨的表面抗菌、耐磨不锈钢制品。
本实用新型表面抗菌、耐磨不锈钢制品的结构示意图如附图所示，包括有不锈钢基材(1)及若干TiAgN镀膜层(2)，TiN和TiAgN镀膜层(2)镀在不锈钢基材(1)的外侧。
上述若干TiN和TiAgN镀膜层(2)可为一层或一层以上。
上述各TiN和TiAgN镀膜层(2)中所含的银、钛成份呈梯级改变，即内镀膜层含银成份低，含钛成份高，外镀膜层含银成份高，含钛成份低。
上述最内镀膜层的含银成份可为0～0.3％，最外镀膜层的含银成份可为0.3～30％。
上述各TiN和TiAgN镀膜层(2)的厚度从内到外呈梯级改变，即内镀膜层的厚度小，外镀膜层的厚度大。
上述最内镀膜层的厚度可为0.01um～5um，最外镀膜层的厚度可为0.1um～10um。
本实用新型表面抗菌、耐磨的不锈钢制品由于采用在不锈钢基材上镀有若干层TiAgN镀膜层的结构，由于TiN的硬度是不锈钢的3倍以上，具有良好的耐磨性。Ag是具有良好的无机抗菌剂，经溅射后使银纳米化，其抗菌效果增强上百倍，因此，本发明表面抗菌、耐磨不锈钢制品不仅具有良好的抗菌性能，而且又具有持久的耐磨性能。本实用新型是一种综合性能较好的表面抗菌、耐磨不锈钢制品。
4、附图说明：
图1为本实用新型实施例1的结构示意图；
图2为图1中的A-A剖视放大图。
5、具体实施方式：
实施例1：
本实用新型表面抗菌、耐磨不锈钢制品的结构示意图如图1、2所示，包括有不锈钢基材(1)及若干TiAgN镀膜层(2)，TiN和TiAgN镀膜层(2)镀在不锈钢基材(1)的外侧。
上述若干TiN和TiAgN镀膜层(2)可为一层或一层以上。
上述各TiN和TiAgN镀膜层(2)中所含的银、钛成份呈梯级改变，即内镀膜层含银成份低，含钛成份高，外镀膜层含银成份高，含钛成份低。
上述最内镀膜层的含银成份可为0～0.3％，最外镀膜层的含银成份可为0.3～30％。
上述最内镀膜层的含银成份可为0～0.3％，最外镀膜层的含银成份可为0.3～30％。本实施例中，最内镀膜层的含银成份可为0％，最外镀膜层的含银成份可为0.3％。
上述各TiN和TiAgN镀膜层(2)的厚度从内到外呈梯级改变，即内镀膜层的厚度小，外镀膜层的厚度大。
上述最内镀膜层的厚度可为0.01um～5um，最外镀膜层的厚度可为0.1um～10um。本实施例中，最内镀膜层的厚度可为0.01um，最外镀膜层的厚度可为0.1um。
实施例2：
本发明表面抗菌、耐磨不锈钢制品的结构与实施例1相同，不同之处在于TiN和TiAgN镀膜层(2)可为5层。最内镀膜层的含银成份可为0.15％，最外镀膜层的含银成份可为15％。最内镀膜层的厚度可为0.05um，最外镀膜层的厚度可为5um。
实施例3：
本发明表面抗菌、耐磨不锈钢制品的结构与实施例1相同，不同之处在于TiN和TiAgN镀膜层(2)可为6层。最内镀膜层的含银成份可为0.3％，最外镀膜层的含银成份可为30％。最内镀膜层的厚度可为0.1um，最外镀膜层的厚度可为10um。

Claims (6)

1、一种表面抗菌、耐磨不锈钢制品，其特征在于包括有不锈钢基材(1)及若干TiAgN镀膜层(2)，TiN和TiAgN镀膜层(2)镀在不锈钢基材(1)的外侧。
2、根据权利要求1所述的表面抗菌、耐磨不锈钢制品，其特征在于上述若干TiN和TiAgN镀膜层(2)可为一层或一层以上。
3、根据权利要求2所述的表面抗菌、耐磨不锈钢制品，其特征在于上述各TiN和TiAgN镀膜层(2)中所含的银、钛成份呈梯级改变，即内镀膜层含银成份低，含钛成份高，外镀膜层含银成份高，含钛成份低。
4、根据权利要求3所述的表面抗菌、耐磨不锈钢制品，其特征在于上述最内镀膜层的含银成份可为0～0.3％，最外镀膜层的含银成份可为0.3～30％。
5、根据权利要求2所述的表面抗菌、耐磨不锈钢制品，其特征在于上述各TiN和TiAgN镀膜层(2)的厚度从内到外呈梯级改变，即内镀膜层的厚度小，外镀膜层的厚度大。
6、根据权利要求5所述的表面抗菌、耐磨的不锈钢制品，其特征在于上述最内镀膜层的厚度可为0.01um～5um，最外镀膜层的厚度可为0.1um～10um。
CN 200420045396 2004-04-30 2004-04-30 一种表面抗菌、耐磨的不锈钢制品 Expired - Lifetime CN2711177Y (zh)