CN2503149Y - Artificial stone plate - Google Patents
Artificial stone plate Download PDFInfo
- Publication number
- CN2503149Y CN2503149Y CN 01226153 CN01226153U CN2503149Y CN 2503149 Y CN2503149 Y CN 2503149Y CN 01226153 CN01226153 CN 01226153 CN 01226153 U CN01226153 U CN 01226153U CN 2503149 Y CN2503149 Y CN 2503149Y
- Authority
- CN
- China
- Prior art keywords
- resin
- utility
- model
- layer
- stone
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The utility model discloses a man-made stone slab, which is structured as double layers, namely, the mixture of resin, transparent glass particles or transparent fine quartz particles as the upper layer and that of colouring matters, building stone and resin as the lower layer. The product, due to the reflection and refraction principle of beam, has the advantages of high lustrousness, stand wear and tear and profoundness; seen from the transparent layer to the lower layer, the marble or granite appear extremely remarkable and gorgeous. The utility model, by sufficiently utilizing the leftover from the natural stone material industry and other industries, realizes the fully automatic production, which is able to form industrialized mass production with high efficiency.
Description
The utility model relates to a kind of novel decorative constructional materials, especially a kind of artificial slabstone.
The development of man-made stone, having experienced with cement is adhesive, again to being adhesive with the macromolecule resin.Because from taking all factors into consideration of each side such as mechanical performance of products, rupture strength, manufacturing cost, the world today uses unsaturated polyester resin as adhesive more.The mode of moulding is formed through the section polishing by in the past balk moulding again, develops into the pressing plate moulding of today.The balk moulding is then wasted bigger when section, and production efficiency is low.Existing artificial slabstone is to be adhesive by resin, is bone essence with stone flour, rock ballast, stone grain, and repressed, polishing forms, and it mainly exists surface gloss relatively poor, the problem that abrasion resistance is relatively poor.
The purpose of this utility model just provides a kind of have high gloss, anti abrasive artificial slabstone.
The utility model can be realized by following mode: be matrix with building stones, building stones are made up of stone grain, rock ballast and stone flour, and there is hyaline layer on the surface of matrix, and hyaline layer is quartzy particulate layer, also can be the glass granulosas.
The artificial slabstone that the utility model is made adopts double-decker, and the upper strata is the mixture of resin and clear glass grain or suprasil particulate, and lower floor is the mixture of colorant, building stones and resin.Because the reflection and the refraction principle of light make this product have high gloss, wear-resistant and deep sense, naked eyes are penetrated into lower floor from hyaline layer, and marble or granitic tone sense are very obvious, feel magnificent unusually.The utility model makes full use of lithotome industry and other industrial leftover bits and pieces, has realized full-automatic production, can form large-scale industrialization production, the production efficiency height.
Below in conjunction with accompanying drawing, the utility model will be further described.
Fig. 1 is a structural representation of the present utility model.
Please read Fig. 1, artificial slabstone is matrix 1 with building stones, on the surface of matrix 1 hyaline layer 2 is arranged, and hyaline layer 2 is quartzy particulate layers, or the glass granulosa.
Embodiment one (artificial slabstone with manufacturing 600mm * 600mm * 12mm is an example)
1, the mixing of resin and building stones is stirred
Color according to manufactured goods is earlier painted on resin, get 0.85 kilogram of resin, add small number of curing agents (peroxidating first and second caves) and accelerator (cobalt iso-octoate), drop into diameter and be 5 millimeters 5.1 kilograms of stone grains, 1.7 kilograms of 80 order rock ballasts, 1.7 kilograms of 180 order stone flours stirred 5 minutes, and it is mixed.
2, the high-pressure molding of heating
Raw material through mixing and stirring are delivered to forming machine by conveyer belt, one mold is installed in the forming machine (emptyly in the mould is 605mm * 605mm * 12mm), be divided into upper die and lower die, on, ultimate range was 0.5 meter when counterdie was opened, on, thermocouple and electrothermal tube are housed in the bed die, 130 ℃ of patrix temperature, 100 ℃ of counterdie temperature, earlier patrix is opened to highest point, material feeder is evenly broadcast mixed raw material in counterdie automatically then, back and forth raw material is wipeed off, return the original place, then slowly to moving down, forming machine produces high pressure with the upper and lower mould matched moulds to patrix, and this moment, pressure was 12.5MPa, after high pressure was heated 5 minutes, open patrix, at this moment, the raw material in the mould are curing molding.Three automatic square thimbles eject the goods of forming, put into drying room and carry out heating cure in 24 hours and handle, temperature be 100 ℃ or with goods flat stack to put carried out in 7 days from solidifying then, as setting out, with from being cured as then with energy conservation.
3, corase grind fixed thick and positive corase grind in the back side is fixed thick
The goods back side is ground off surperficial glue-line with diamond disk, and the assurance back side is smooth, and raising and cement bonded sand, slurry adherence force, treat back side grinding and polishing to go out smooth and coarse surface occurs, and when exposing chicken girt fully, grind off 1.5mm thickness approximately, promptly the goods back side is upwards transferred to facing up and carry out the front corase grind by automatic panel-turnover, grind off 1.5mm thickness approximately, make the thickness of entire plate.
4, the oven dry that dewaters
Adopt the hot-air seasoning goods, temperature is 250 ℃.
5, frictioning upper surface covering layer
Automatically spreading machine is 1.96 kilograms of 20 order glass grains or suprasil grains, 0.35 kilogram of resin, and the mixture that curing compound and accelerator are an amount of is evenly coated in the surface course of goods, and its thickness is 3 millimeters.
6, hot-air seasoning solidifies surface course
Mode with hot blast drying makes surface course solidify 240 ℃ of hot blast temperatures fast.
7, floated thin throwing
The polishing abrading block divides 60 successively
#, 120
#, 240
#, 320
#, 400
#, 600
#, 800
#, 1200
#Polish, transparent layer surface is ground to smooth and glossy degree.
8, water under high pressure cuts in length and breadth
Water under high pressure cutting machine in length and breadth is slit into 600mm * 600mm * 12mm automatically, and cut smooth, do not collapse and lose.
9, destatic processing
A Destaticizing device is installed in upper end at conveyer belt, makes every product all through destaticing processing.This artificial slabstone static electrification not has without dust characteristics like this, is convenient to keep clean.
10, waxing
Waxing makes the surperficial pore of product with sealing with wax, and product in use is difficult for immersing spot.After classification and Detection and packing can dispatch from the factory.
If when the stone grain used marmorean stone grain, the sheet material of manufacturing was artificial marble; If when the stone grain used granitic stone grain, the sheet material of manufacturing was the stonite.
The physical and chemical index of product: glossiness 〉=80 gloss unit, hardness Barcol 〉=50, rupture strength 〉=8.5MPa, density 〉=2.3 gram/cm
3
Claims (3)
1, a kind of artificial slabstone is matrix (1) with building stones, it is characterized in that there is hyaline layer (2) on the surface of matrix (1).
2,, it is characterized in that hyaline layer (2) is quartzy particulate layer according to the described artificial slabstone of claim 1.
3,, it is characterized in that hyaline layer (2) is the glass granulosa according to the described artificial slabstone of claim 1.