CN219137080U

CN219137080U - Washable quick-drying fabric

Info

Publication number: CN219137080U
Application number: CN202223496888.1U
Authority: CN
Inventors: 郭亮; 彭海琼; 唐水玉
Original assignee: Foshan Aoxuan Technology Co ltd
Current assignee: Foshan Aoxuan Technology Co ltd
Priority date: 2022-12-27
Filing date: 2022-12-27
Publication date: 2023-06-06
Anticipated expiration: 2032-12-27

Abstract

The utility model relates to the technical field of warp knitting, in particular to a washable quick-drying fabric; the novel warp knitting machine is formed by weaving a guide bar GB1 and a guide bar GB2, wherein the organization structure of the guide bar GB1 is 1-0/4-5// full penetration, the organization structure of the guide bar GB2 is 1-2/1-0// full penetration, yarns adopted by the guide bar GB1 are core-spun yarns, and yarns adopted by the guide bar GB2 are blended yarns; the guide bar GB1 and the guide bar GB2 form a knitting structure with saw-tooth-shaped grooves on the surface, and the saw-tooth-shaped grooves greatly enlarge the contact area with air when clothes are dried, so that the quick-drying characteristic is improved; the guide bar GB1 occupying a larger area of the fabric is woven by adopting the core spun yarn, and the yarns made of other short fibers are wrapped outside the core spun yarn, so that the advantages of high stiffness, folding resistance, easy washing and quick drying of the yarn core can be fully exerted.

Description

Washable quick-drying fabric

Technical Field

The utility model relates to the technical field of warp knitting, in particular to a washable quick-drying fabric.

Background

In daily life, it is desirable to have a fabric that can be repeatedly washed and quickly dried to make garments for labor and sports. The fabric for quick-drying clothing at present is mainly composite fabric. The composite fabric combines a plurality of fabrics with different structures and different functions in a hot melting/hot pressing/sewing mode, and has multiple functions, for example, the water-resistant pure cotton fabric and the quick-drying nylon fabric are compounded, so that the composite fabric has certain functions in the aspects of water resistance and quick-drying. In addition, many quick-drying fabrics adopt surface groove designs and hollow fibers to improve the water guiding and quick-drying effects. For example, a moisture-absorbing and quick-drying fabric disclosed in chinese patent, patent No. 201822250484.1, in which: including inlayer, intermediate level and skin, the inlayer is elasticity moisture absorption layer, elasticity moisture absorption layer is mixed with silk fibre by special-shaped fiber and is woven, the intermediate level is quick wet-guiding layer, quick wet-guiding layer is mixed by hollow fiber and combed cotton yarn and is woven, the skin is hydrophilic quick-drying layer, hydrophilic quick-drying layer is mixed by hydrophilic yarn and superfine anti-pilling acrylic fiber and is woven, evenly distributed such as surface on hydrophilic quick-drying layer has a plurality of slots. The inner layer of the utility model utilizes the micro grooves formed on the surfaces of the special-shaped fibers and the silk fibers to quickly absorb moisture and sweat on the surface layer of the skin, so that the inner layer is more comfortable when contacting with a human body, the capillary core structure of the inner layer is utilized to improve the air permeability and water and sweat transmission performance of the fabric, and the outer layer adopts a hydrophilic quick-drying layer with grooves. Also for example, the moisture-absorbing and quick-drying fabric disclosed in Chinese patent publication No. 201520197171.8, wherein: including inlayer, intermediate level and the skin that sets gradually, the inlayer is elasticity moisture absorption layer, and it is woven by special-shaped fiber and forms, the internal surface of elasticity moisture absorption layer has a plurality of recesses, the intermediate level is quick moisture-conducting layer, and it is mixed by hollow fiber and combed cotton yarn and weave and form, the skin is hydrophilic quick-drying layer, hydrophilic quick-drying layer is woven by hydrophilic yarn and forms, the surface of hydrophilic quick-drying layer is the curved surface, its inlayer adopts special-shaped fiber to weave, utilize the fine groove that special-shaped fiber surface formed, reach and absorb skin top layer moisture and sweat rapidly, the intermediate level adopts hollow fiber, utilize its capillary core structure to improve the gas permeability of fabric and water delivery sweat guiding performance, the outer hydrophilic quick-drying layer that has the curved surface that adopts improves its moisture removal area, improve evaporation efficiency in addition.

However, the prior art has two major disadvantages: 1. the multi-layer fabric is required to be combined, the thickness of the multi-layer fabric is inevitably increased after the multi-layer fabric is combined, the heat dissipation function is inevitably reduced due to the increase of the thickness, the weight of the garment is increased with high probability, and the multi-layer fabric is not suitable for being used as the fabric of labor and sportswear; 2. although the above technical solutions all describe that the outer surface of the fabric with the quick-drying function is uniformly provided with a plurality of grooves (hydrophilic quick-drying layers with curved surfaces), the above technical solutions do not disclose why the structure is a textile structure.

Disclosure of Invention

Aiming at the defects of the prior art, the utility model provides a washable quick-drying fabric.

The technical scheme of the utility model is as follows:

the quick-drying fabric resistant to washing is formed by weaving guide bars GB1 and guide bars GB2, the organization structure of the guide bars GB1 is 1-0/4-5// full penetration, the organization structure of the guide bars GB2 is 1-2/1-0// full penetration, yarns adopted by the guide bars GB1 are core-spun yarns, and yarns adopted by the guide bars GB2 are blended yarns.

In one embodiment, the blended yarn is a cotton fiber/tencel fiber blended yarn, the cotton fiber/tencel fiber blended yarn comprises a wire core and a wrapping layer wound around the wire core, the wire core is made of cotton fibers with single fiber fineness of 1.7dtex and tencel fibers with single fiber fineness of 0.7dtex, and the wrapping layer is made of tencel fibers with single fiber fineness of 0.7 dtex. The GB2 guide bar weaving part has the effects of moisture guiding and skin non-sticking.

In one embodiment, the core spun yarn is a spandex core spun yarn. Has low cost, water washing resistance and easy airing.

In one embodiment, the core spun yarn is a core spun yarn of short fiber-covered microporous alkali-soluble polyester filaments, which is characterized by water-resistance and quick-drying properties.

The beneficial effects of the utility model are as follows: the guide bar GB1 and the guide bar GB2 form a knitting structure with saw-tooth-shaped grooves on the surface, and the saw-tooth-shaped grooves greatly enlarge the contact area with air when clothes are dried, so that the quick-drying characteristic is improved; the guide bar GB1 occupying a larger area of the fabric is woven by adopting the core spun yarn, and the yarns made of other short fibers are wrapped outside the core spun yarn, so that the advantages of high stiffness, folding resistance, easy washing and quick drying of the yarn core can be fully exerted.

Drawings

FIG. 1 is a diagram of the yarn laying movement of the utility model GB 1;

FIG. 2 is a diagram of the yarn laying movement of the utility model GB 2;

fig. 3 is a physical micrograph of one embodiment.

Detailed Description

The following is a further description of embodiments of the utility model, taken in conjunction with the accompanying drawings:

example 1

As shown in figures 1 and 2, the washable quick-drying fabric is formed by weaving a guide bar GB1 and a guide bar GB2, wherein the structure of the guide bar GB1 is 1-0/4-5// full, the structure of the guide bar GB2 is 1-2/1-0// full, yarns adopted by the guide bar GB1 are core-spun yarns, and yarns adopted by the guide bar GB2 are blended yarns.

The blended yarn is made of cotton fiber/tencel fiber blended yarn, the cotton fiber/tencel fiber blended yarn comprises a wire core and a wrapping layer wrapping the wire core, the wire core is made of cotton fiber with single fiber fineness of 1.7dtex and tencel fiber with single fiber fineness of 0.7dtex, and the wrapping layer is made of tencel fiber with single fiber fineness of 0.7 dtex.

The core spun yarn adopts spandex core spun yarn.

This example uses an HKS2 warp knitting machine.

As shown in fig. 3, the guide bar GB1 (front guide bar) and the guide bar GB2 (rear guide bar) of the present embodiment are combined, and the woven fabric structure forms an obvious zigzag groove (black line in the figure) on one side thereof, so that the quick-drying property during airing can be effectively improved. In addition, the figure shows that the fabric has only one layer, and the thickness is thinner after the fabric is made into clothing, so that the heat dissipation property and the portability can be ensured.

Example 2

The core spun yarn adopts the core spun yarn of short fiber coated microporous alkali soluble polyester filament, and is characterized by water resistance and quick drying property. Other structures of this embodiment are the same as those of embodiment 1.

The foregoing embodiments and description have been provided merely to illustrate the principles and best modes of carrying out the utility model, and various changes and modifications can be made therein without departing from the spirit and scope of the utility model as defined in the appended claims.

Claims

1. The utility model provides a washing-resistant quick-drying surface fabric which characterized in that: the novel warp knitting machine is formed by weaving a guide bar GB1 and a guide bar GB2, wherein the organization structure of the guide bar GB1 is 1-0/4-5// full penetration, the organization structure of the guide bar GB2 is 1-2/1-0// full penetration, yarns adopted by the guide bar GB1 are core spun yarns, and yarns adopted by the guide bar GB2 are blended yarns.

2. The washable quick-drying fabric of claim 1, wherein: the blended yarn is made of cotton fiber/tencel fiber blended yarn, the cotton fiber/tencel fiber blended yarn comprises a wire core and a wrapping layer wrapping the wire core, the wire core is made of cotton fiber with single fiber fineness of 1.7dtex and tencel fiber with single fiber fineness of 0.7dtex, and the wrapping layer is made of tencel fiber with single fiber fineness of 0.7 dtex.

3. The washable quick-drying fabric of claim 2, wherein: the core spun yarn adopts spandex core spun yarn.

4. A water-fast-drying fabric according to claim 3, characterized in that: the core spun yarn adopts core spun yarn of short fiber covered microporous alkali soluble polyester filament.