CN217869327U

CN217869327U - Antibacterial water absorption towel for human body

Info

Publication number: CN217869327U
Application number: CN202221669758.0U
Authority: CN
Inventors: 谢文
Original assignee: Individual
Current assignee: Individual
Priority date: 2022-06-29
Filing date: 2022-06-29
Publication date: 2022-11-22
Anticipated expiration: 2032-06-29

Abstract

The utility model discloses an antibacterial water absorption towel for human body, which comprises a base cloth made of polyester-nylon composite superfine fiber, wherein a silver ion antibacterial layer is arranged outside the polyester-nylon composite superfine fiber, the front side of the base cloth is set as a short hair suede, and the back side of the base cloth is set as a long hair suede; the utility model arranges the opened short pile face and the long pile face on the front and back of the base cloth respectively, the short pile rows are arranged in parallel, and the long pile rows are arranged in a staggered way; the long pile velvet surface is fluffy and soft when in use, the short pile surface is fresh and cool, and the water absorption performance of the towel is enhanced; the silver ion antibacterial layer on the outer side of the polyester-nylon composite superfine fiber has a good antibacterial effect, and the towel is prevented from being mildewed in the using process; this application still is provided with and sews up limit and the area of drying in the air of hanging, strengthens holistic practicality and aesthetic property.

Description

Antibacterial water absorption towel for human body

Technical Field

The utility model relates to a towel, in particular to an antibacterial water absorption towel for human body.

Background

The existing water absorption towels are mostly used for cleaning and wiping, and due to the problems of raw materials or manufacturing processes, the problems of hardness, stickiness, dryness, messy hair, mildew, reduced water absorption and the like can occur after a period of time, so that the comfort level during use is reduced, certain damage is caused to the skin, and particularly the delicate skin of infants is damaged; in addition, in general, a common towel on the market has a structure in which at least one surface of the towel is formed into a plurality of loops, so that the number of production processes is reduced, and a refreshing touch feeling is brought about even when the towel is in contact with the skin.

Disclosure of Invention

In order to overcome the defects of the prior art, the utility model provides an antibacterial water absorption towel for human body.

The utility model provides a technical scheme that its technical problem adopted is:

the antibacterial water absorption towel comprises a base cloth made of polyester-nylon composite superfine fibers, wherein a silver ion antibacterial layer is arranged on the outer side of the polyester-nylon composite superfine fibers, the front side of the base cloth is set to be a short hair suede surface, and the back side of the base cloth is set to be a long hair suede surface.

The edge of the base fabric is provided with a sewing edge, the front side of the sewing edge is not provided with a short pile face, and the back side of the sewing edge is not provided with a long pile face.

And the sewing edge is fixed on the base cloth in a sewing mode after being folded towards the short wool pile surface.

At least one hanging and airing belt parallel to the sewing edge is sewn and fixed on the short plush surface.

The short pile suede is vertically provided with a plurality of short pile bundles with the length of 0.1-0.2mm, and the long pile suede is vertically provided with a plurality of long pile bundles with the length of 0.3-0.5mm.

The short pile bundles and the long pile bundles respectively form a plurality of short pile rows and long pile rows which are closely arranged, the short pile rows are arranged in parallel, and the long pile rows are arranged in a staggered manner.

The utility model has the advantages that: the utility model arranges the opened short pile surface and the long pile surface on the front and the back of the base cloth respectively, the short pile rows are arranged in parallel, and the long pile rows are arranged in a staggered way; the long pile face is fluffy and soft in touch during use, the short pile face is fresh and cool in touch, and the water absorption performance of the towel is enhanced; the silver ion antibacterial layer on the outer side of the polyester-nylon composite superfine fiber has a good antibacterial effect, and the towel is prevented from being mildewed in the use process; this application still is provided with and sews up the limit and hang the area that dries in the air, strengthens holistic practicality and aesthetic property.

Drawings

The present invention will be further explained with reference to the drawings and examples.

Fig. 1 is a schematic structural diagram of the present invention;

FIG. 2 is a schematic structural view before sewing;

FIG. 3 is a schematic view of the structure of a partial cross section of the utility model before sewing;

fig. 4 is a schematic view of the structure of the present invention with a partial cross section.

Detailed Description

Referring to fig. 1 to 4, the antibacterial water absorption towel for a human body comprises a base cloth 2 made of polyester-nylon composite superfine fibers, wherein a silver ion antibacterial layer is arranged on the outer side of the polyester-nylon composite superfine fibers, the front surface of the base cloth 2 is provided with a short pile suede 1, and the back surface of the base cloth is provided with a long pile suede 3; preferably, the length of the pile on the short pile face 1 is 0.1-0.2mm, and the length of the pile on the long pile face 3 is 0.3-0.5mm.

Different from a common towel loop structure in the market, the short pile suede 1 is provided with a plurality of short pile bundles, the long pile suede 3 is provided with a plurality of long pile bundles, in order to enhance the use comfort of the short pile surface 1 and the long pile surface 3 with different pile lengths, the short pile bundles and the long pile bundles respectively form a plurality of short pile rows and long pile rows which are closely arranged, the short pile rows are arranged in parallel, and the long pile rows are arranged in a staggered manner; the touch of the short pile fabric surface 1 is cool and fluffy.

The edge of the base fabric 2 is provided with a sewing edge 4, the front side of the sewing edge 4 is not provided with a short pile suede 1, and the back side of the sewing edge 4 is not provided with a long pile suede 3; the sewing edge 4 is folded towards the short pile suede 1 and fixed on the base cloth 2 in a sewing mode; the sewing edge 4 is the edge of the base cloth 2, and the sewing edge 4 and the base cloth 2 are integrally arranged and are not easy to loosen and fall off; the sewing edge 4 needs to be folded and fixed on the base cloth 2, if the front and back sides of the sewing edge 4 are respectively provided with the short pile face 1 and the high pile face 3, the edge of the towel is too thick, and the finished product is not beautiful and is not easy to dry; the product structure that this application designed makes towel sewing trace unobvious, and the whole is more pleasing to the eye.

At least one hanging and airing belt 5 parallel to the sewing edge 4 is sewn on the short wool suede 1, and when the towel is hung and aired, the hanging and airing belt 5 can be hung on a clothes rack or a hook, so that the towel is not easy to drop in the hanging and airing process, and the practicability is enhanced.

Preferably, the polyester-nylon composite superfine fiber adopted by the base fabric 2 is prepared from the following raw materials in parts by weight: 75 parts of terylene and 25 parts of chinlon, wherein the terylene has the characteristic of generating flat, stiff and fluffy shapes after being shaped, so that the terylene is not easy to deform after being washed for many times, and the prepared towel still has neat hair surface after being washed and dried for many times without generating disorder hair; the nylon has the characteristics of wear resistance, high strength, easy dyeing and moisture absorption, so that the finished towel product has soft and plump touch feeling, and also has high water absorption and air permeability.

A method for preparing the antibacterial water absorption towel comprises the following steps:

(1) Preparing the warped polyester-nylon composite superfine fiber into grey cloth by using a warp knitting towel machine, and performing pre-setting treatment on the grey cloth at the temperature of 180 ℃; the front and back sides of the grey cloth prepared in the step are provided with the looped piles with different lengths, and the looped piles on the front and back sides of the grey cloth are flat and stiff through the presetting treatment, so that the looped piles in the next step can be conveniently cut.

(2) Carrying out double-sided ironing treatment on the grey cloth subjected to the pre-setting treatment in the step (1) at the temperature of 180 ℃ by using a double-roller ironing machine, and then carrying out double-sided shearing on the grey cloth by using a shearing machine; the double-side polishing treatment enables the terry to be brighter and upright, and is easy to cut, and the shearing machine is used for shearing the coils on the front side and the back side of the grey cloth, so that the fiber opening in the next step is facilitated.

(3) And (3) splitting the grey cloth subjected to double-sided shearing in the step (2): according to the following steps: the bath ratio of 10, the grey cloth is put into a solution, and the solution contains water, 5g/L alkali beads and 1g/L degreasing agent; heating the solution to 130 ℃ at the heating rate of 2 ℃/min, and then preserving heat for 45min to obtain split grey cloth; because the polyester-nylon composite superfine fiber with high proportion prepared from 75 parts of polyester and 25 parts of nylon is adopted, the fiber can be fully opened in the step, and compared with sanding treatment, the formed wool bundles are more fluffy and softer; in addition, as the terry is cut off in the previous step, the polyester-nylon composite superfine fiber can be completely unfolded after opening, so that the front and back sides of the towel are softer and more comfortable.

(4) And (4) putting the split grey cloth prepared in the step (3) and an antistatic agent into a double overflow high-temperature high-speed dyeing machine for dyeing, drying the grey cloth at the temperature of 180 ℃ after dyeing is finished to obtain the dyed grey cloth, wherein the static electricity of the split grey cloth is larger due to the fact that the split treatment is carried out on the polyester-nylon composite superfine fibers in the previous step, and therefore the antistatic agent needs to be added to eliminate the static electricity in the step.

(5) Carrying out double-sided shearing on the dyed gray fabric prepared in the step (4) by using a shearing machine, then carrying out setting treatment on the dyed gray fabric subjected to secondary shearing and an antibacterial agent at the temperature of 160 ℃ to obtain a set gray fabric, and carrying out double-sided shearing on the previous step again so as to cut off missed-sheared terry in the step (2) and hair balls generated by friction in the step (4); the towel is shaped again, so that the hair surface is neat after the towel is washed and dried for many times, and the condition of disordered hair is avoided; because the antibacterial agent is added for shaping treatment, the antibacterial performance can still be kept after multiple times of washing.

(6) Performing sewing treatment on the edge of the shaped gray fabric prepared in the step (5) to obtain a finished towel product, and performing ozone sterilization and packaging treatment on the finished towel product in sequence to obtain the antibacterial water-absorbing towel, wherein specifically, the sewing treatment is to perform sewing after the edge of the gray fabric is folded towards the short plush surface 1; in the step, the finished towel is subjected to ozone sterilization treatment, so that double sterilization is guaranteed.

In the present application, the portions not particularly emphasized with respect to the temperature and the pressure are both normal temperature and normal pressure; preferably, the type of the warp knitting towel machine adopted in the step (1) is YJHKS4M-CF-EL-218; the model of the double-roller natural luster finishing machine adopted in the step (2) is SME47CC; the type of the shearing machine adopted in the step (2) and the step (5) is ME533C; the alkali beads in the step (3) are sodium hydroxide; the antibacterial agent in the step (4) is a silver ion textile antibacterial agent of Silvadur brand of Dupont Xian Shield, and the drying step is carried out by using a tension-free high-efficiency fluffy drying machine with the model of HJ-30; and (3) the shaping step in the step (1) and the step (5) is processed by a Yonglutong shaping machine with the model number of YLMD 908.

The performance detection of the antibacterial water absorption towel prepared by the preparation method comprises the following detection steps:

testing the water absorption performance: firstly weighing a dry towel, then soaking the dry towel in a water container for one minute, wherein the water container has enough space and enough water, naturally airing the towel for one minute after soaking the towel for one minute to obtain the towel after water absorption, then weighing the towel after water absorption, and bringing the weight of the towel before and after soaking water into the following water absorption formula: water absorption (%) =100% × (weight after water absorption-dry weight)/dry weight.

The weight of the dry towel is 200g, the weight after water absorption is 1600g, and the weight is substituted into the formula of 100% × (1600-200)/200 =700%; according to the water absorption performance detection, the antibacterial water absorption towel prepared by the method has good water absorption performance.

And (3) testing antibacterial performance: the test method comprises the following steps: evaluation method of AATCC 100-2012 antibacterial textile

Test sample 1: towel prepared according to the above method

Test sample 2: towel blank samples prepared according to the above method after 50 washes mimicking the home wash mode: towel without addition of antibacterial agent and ozone sterilization treatment

And (3) testing results: compared with the blank sample, the numbers of the bacteria of the test sample 1 and the test sample 2 to staphylococcus aureus and klebsiella pneumoniae can be reduced by more than 99%.

It can be seen that the fresh towel prepared according to the above method or the towel used for a certain period of time has good antibacterial property.

To sum up, this application makes fluffy softness of hair matte 1 and plush face 3 through step (3) splitting, makes through step (5) wash the fixed antibiotic layer of silver ion that is provided with in the bright and beautiful compound microfiber outside, this application the towel has good water absorption performance and antibacterial performance, can be used to the human skin of direct contact, when guaranteeing use comfort, strengthens the security performance of using.

The above embodiments are not intended to limit the scope of the present invention, and those skilled in the art will not depart from the present invention as it relates to the whole concept of the present invention, and the equal modification and change will still belong to the scope of the present invention.

Claims

1. The antibacterial water absorption towel for the human body is characterized by comprising a base cloth (2) made of polyester-nylon composite superfine fibers, wherein a silver ion antibacterial layer is arranged on the outer side of the polyester-nylon composite superfine fibers, the front side of the base cloth (2) is set to be a short-hair suede (1), and the back side of the base cloth is set to be a long-hair suede (3).

2. The antibacterial and water-absorbing towel as claimed in claim 1, characterized in that the edges of the base fabric (2) are provided with a sewing edge (4), the front surface of the sewing edge (4) is not provided with the short pile fabric (1), and the back surface is not provided with the long pile fabric (3).

3. The antibacterial water-absorbing towel according to claim 2, characterized in that the sewing edge (4) is fixed on the base fabric (2) by sewing after being folded towards the short pile face (1).

4. The antibacterial water absorption towel according to claim 3, characterized in that at least one hanging and airing belt (5) parallel to the sewing edge (4) is sewn and fixed on the short pile suede (1).

5. The antibacterial water absorption towel according to claim 1, characterized in that a plurality of short pile bundles with the length of 0.1-0.2mm are vertically arranged on the short pile face (1), and a plurality of long pile bundles with the length of 0.3-0.5mm are vertically arranged on the long pile face (3).

6. The antibacterial and water-absorbent towel according to claim 5, wherein the short pile bundles and the long pile bundles are respectively formed into a plurality of short pile rows and long pile rows which are closely arranged, the short pile rows are arranged in parallel, and the long pile rows are arranged in a staggered manner.