CN215850110U - Easily-repaired and easily-glued thermoplastic composite board - Google Patents
Easily-repaired and easily-glued thermoplastic composite board Download PDFInfo
- Publication number
- CN215850110U CN215850110U CN202023352124.6U CN202023352124U CN215850110U CN 215850110 U CN215850110 U CN 215850110U CN 202023352124 U CN202023352124 U CN 202023352124U CN 215850110 U CN215850110 U CN 215850110U
- Authority
- CN
- China
- Prior art keywords
- layer
- thermoplastic composite
- hot melt
- melt adhesive
- pet film
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The utility model belongs to the field of thermoplastic composite materials, and particularly relates to a thermoplastic composite material plate easy to repair and glue. The composite material plate consists of a PET film, a hot melt adhesive layer, a buffer layer, an enhancement layer and a dielectric layer. The easily repaired and adhered thermoplastic composite board provided by the utility model can be directly foamed or adhered, can form a carriage board with a sandwich structure with a thermal insulation material, a honeycomb core or a foam board and the like, has excellent mechanical property, ageing resistance and antibacterial property, has an attractive and elegant surface, is easy to adhere, and can be sealed and adhered by adopting conventional glue for repairing.
Description
Technical Field
The utility model belongs to the technical field of thermoplastic composite materials. And more particularly to a repairable and glueable thermoplastic composite sheet.
Background
At present, due to the characteristics of light weight, high rigidity, high toughness, recoverability and the like, the fiber reinforced thermoplastic composite material serving as an inner lining plate material is widely applied to the field of light weight of commercial vehicles such as refrigerated vehicles, refrigerated containers or van trucks, but is only limited to be used as the inner lining plate, the situation of external application is less, the main reason is that the maintenance performance of accident car repair and daily scraping maintenance is stricter than that of inner plates because the outer-applied van plate has higher requirements on the mechanical property, ageing resistance, corrosion resistance, heat insulation and other service performances of the material, and the processing treatment such as adhesive sealing, paint spraying, printing and the like is also needed. However, the existing thermoplastic composite material plate has the problems of uneven surface, difficulty in adhesion, difficulty in repair after sealing and accidents and the like, and the trend of greatly limiting the lightweight application market and high-speed growth is high, so that the development of a thermoplastic composite material plate suitable for external use is urgently needed.
Patent CN 107571577A discloses a combined material board, still include respectively with combined material layer upper and lower surface bonding rubberizing adhesive linkage and lower adhesive linkage as an organic whole, and with the functional surface course as an organic whole of rubberizing adhesive linkage upper surface bonding, and with the protection film that strippable of functional surface course upper surface bonding as an organic whole, this combined material board has excellent shock resistance and high mechanical strength, ageing resistance and advantage such as resistant scraping, can do the interior welt of special transportation facilities such as cold-storage container, refrigerator car, freight train, car as a house, replace traditional steel sheet or thermosetting combined material product, it is big to have solved traditional material proportion, shock resistance subalternation problem.
Patent CN 208069046U discloses a continuous glass fiber reinforced polypropylene composite side fascia for car as a house, by outer and interior BOPET thin layer, hot melt adhesive film adhesive linkage, continuous glass fiber reinforced PP composite base plate layer, polyester non-woven fabrics layer of being equipped with in proper order, have advantages such as high glossiness, appearance quality voucher, impact strength height, environmental protection branch of academic or vocational study are retrieved, do not have VOC, lightweight. The method solves the problem of influence on the environment in the production process of the traditional thermosetting material, has no volatilization of any organic solvent, high production efficiency and no need of a curing process.
The easily repaired and glued thermoplastic composite material is a multifunctional material plate compounded by a fiber reinforced thermoplastic composite material and a polyester film, can replace the traditional carriage plate material, and solves the use problems of uneven surface, difficult bonding, difficult repair and the like of the existing thermoplastic composite material.
Disclosure of Invention
The utility model aims to solve the technical problems of overcoming the defects and the defects that the existing thermoplastic composite material plate is difficult to bond/seal and repair, and providing a novel functional surface layer, and the thermoplastic composite material plate which is processed by the novel functional surface layer, is suitable for external use, is easy to repair and glue, can be directly foamed or glued, and forms a carriage plate with a sandwich structure together with a heat insulation material, a honeycomb core or a foam plate and the like.
The utility model aims to provide a thermoplastic composite plate easy to repair and glue. The purpose is to provide a lining plate for the thermoplastic composite material, which can solve the problems of appearance, difficulty in adhesion and difficulty in repair of the thermoplastic composite material in a breakthrough manner and is externally used.
The above purpose of the utility model is realized by the following technical scheme:
the composite material plate consists of a PET film, a hot melt adhesive layer, a buffer layer, a reinforcing layer and a dielectric layer, wherein the buffer layer is respectively embedded into the hot melt adhesive layer and the reinforcing layer, and the dielectric layer is partially embedded into the reinforcing layer; the lower surface of the PET film is attached to the upper surface of the hot melt adhesive layer, and a strippable interface is formed; the lower surface of the hot melt adhesive layer and the upper surface of the enhancement layer have no obvious interface and can not be peeled.
Preferably, the thickness of the PET film is 0.1 mm-1 mm. When hot-pressed at high temperature, the composite material is not easy to shrink and wrinkle, and is suitable for hot-press molding with a plurality of layers of composite materials.
The PET film comprises 80-90% of PET resin, 1-10% of polyester resin, 0.5-10% of an auxiliary agent, 0.5-10% of a filler and the like. The polyester resin is one or a combination of more of PEN, PTT, PETG and other high molecular resin materials compatible with PET, and can improve the water-gas barrier property of the PET film, enhance the barrier property and heat resistance or tearing property of ultraviolet rays and the like; the auxiliary agent comprises one or more of primary antioxidant (such as phenolic antioxidant), secondary antioxidant (such as phosphite ester and thioether antioxidant), light stabilizer (such as benzotriazole ultraviolet absorber, oxalic acid amide light stabilizer, triazine light stabilizer and hindered amine light stabilizer), antibacterial and antifungal agent (such as inorganic antibacterial agent of metal ions and photocatalysis), lubricant (such as zinc stearate, calcium stearate, fatty amide, polyethylene wax, silicone plastic auxiliary agent and the like), antistatic agent and the like; the filler comprises one or more of nanometer titanium dioxide, zinc sulfide, zinc oxide, talcum powder and the like. The modified PET film has polar groups on the surface, is suitable for gluing and sealing most of polyurethane glue, is easy to repair, has excellent performances of yellowing resistance, ageing resistance, moisture barrier and high temperature resistance, has permanent antibacterial and mildewproof properties, meets the food safety requirements, is not limited by external environment, and can be used for both inside and outside.
Preferably, the hot melt adhesive layer is a modified PES (polyether sulfone) adhesive film/net, and the surface density is 40-120 gsm. The PET film can be directly hot-melted and bonded, has high peel strength, and does not need to be subjected to corona treatment; the environment is protected, and toxic and harmful components are not contained; TVOC is low, odor grade 3 or less.
Preferably, the buffer layer is a porous and loose non-woven fabric material, and the material forming the non-woven fabric is polyester fiber with the length of 10-65 mm (ensuring the uniformity and strength of the non-woven fabric) or fiber formed by mixing one or more of polyester fiber and regenerated natural fiber such as viscose fiber and bamboo fiber. The consolidation mode of the non-woven fabric is spunlace and hot rolling, the spunlace non-woven fabric is preferably selected, and the surface is flat and uniform. The surface density of the non-woven fabric is 5-50 gsm, when the content of the resin matrix of the buffer layer is more than or equal to 50%, the melt flow rate is more than or equal to 30g/10min, the density range of the surface of the buffer layer is 30-50 gsm, when the content of the resin matrix of the buffer layer is less than 50%, the melt flow rate is less than 30g/10min, and the density range of the surface of the buffer layer is 5-30 gsm. The higher the content of the resin matrix is, the higher the melt flow rate is, the higher the corresponding buffer layer density is, and if the selected non-woven fabric surface density is too low, the buffer effect is poor; the surface density is too high, and delamination damage is easy to occur in the non-woven fabric.
The buffer layer with proper surface density can be used as an adhesive medium between the hot melt adhesive layer and the reinforcing layer, so that the peeling strength of the PET film is improved; the surface shrinkage cavity of the thermoplastic composite material reinforcing layer can be filled to obtain the appearance of a product with a smooth surface; the problem of scrap pollution caused by exposed fibers in the reinforcing layer after the PET film is scratched can be avoided, and the scratch resistance of the product is improved.
Preferably, the reinforcement layer consists of a plurality of layers of continuous fiber reinforced thermoplastic composite prepreg sheets.
Preferably, the ply structure of the reinforced layer belongs to a symmetrical ply, including but not limited to the following ply mode, and the preferred ply structure is [0/90/0 ]]ns，[0/90/90/0]ns，[90/0/0/90]ns，[0/90/90/0/90/0]ns，[90/0/90/0/0/90]ns，[0/90/90/0/0/90/90/0]ns，[0/90/0/90/90/0/90/0]nsAnd [90/0/90/0/0/90/0/90]nsWherein n is the number of unit cycles, n is an integer greater than or equal to 1, and the size of n depends on the thickness and performance requirements of the product. The number of layers is more than or equal to 4, and the thickness is more than or equal to 1.2 mm. The continuous fiber reinforced thermoplastic composite material prepreg sheet is formed by fully impregnating and processing the reinforced fibers with molten matrix resin. The reinforcing fiber is glass fiber, carbon fiber, basalt fiber, aramid fiber and the like, the linear density is 1200tex, 2400tex and 4800tex, and the content is 40-70%. The matrix resin comprises main resin, modification auxiliary agent and the like. Wherein the main resin is polyolefin resin; the modified auxiliary agent comprises one or more of fiber reinforced master batch, calcium carbonate master batch, silicone master batch, compatilizer, antioxidant, lubricant, ultraviolet-resistant stabilizer, zinc oxide and other functional additives.
Preferably, the medium layer is a non-woven fabric material with a special structure, the non-woven fabric is composed of one or more than one of chemical fibers or regenerated natural fibers with the length of 10-70 mm and the melting point higher than 220 ℃, the chemical fibers comprise one or more than one of polyester fibers, viscose fibers and bamboo fibers, and the non-woven fabric can be obtained by adopting a carding net or an air-laid net and a hot rolling or spunlace reinforcing mode, and is blended by multiple materials and multiple dimensions of fibers, loose in surface structure, compact in internal structure, short in surface fiber and long in internal fiber. After the dielectric layer and other enhancement layers are subjected to hot-pressing compounding, 30% -70% of the dielectric layer is embedded into the matrix resin of the enhancement layers, and the other non-embedded part provides the function of an adhesive medium or an enhancement medium, is not limited by the influence of glue components and an adhesive mechanism, and can realize the adhesion with various materials. The adhesive bonding of physical bonding or chemical reaction is beneficial to rapid permeation, air exhaust, bonding, consolidation and the like of glue, and provides higher stripping force. When the penetration depth of glue and the like is shallow and the gluing amount is small, large-area peeling is not easy to occur, the air exhaust is facilitated, and the problems of bulging and the like are not easy to occur.
The medium layer is preferably hot-rolled non-woven fabric or spunlace non-woven fabric with the surface density of 60-150 gsm. The shape of the rolling point of the hot-rolled non-woven fabric is diamond, square or oval, the preferred area proportion range of the rolling is 25-50%, the shortest distance between adjacent rolling is 1.5-3.0 mm, and the rolling point depth is less than or equal to 1/3 thickness of the non-woven fabric. This range can provide a higher peel strength in both directions of the final article. The spunlace non-woven fabric is preferably a two-way cross non-woven fabric, the difference between the radial and latitudinal mechanical strength, the shrinkage rate and the like is small, and the prepared composite material plate is flat and is not easy to warp.
The utility model has the following beneficial effects:
1) the easily repaired and adhered thermoplastic composite plate provided by the utility model has a polar surface, can be adhered and easily repaired, and has the advantages of appearance, ageing resistance, antibiosis, easiness in cleaning, scraping resistance and the like of a glass fiber reinforced plastic FRP plate product.
2) The easily repaired and easily glued thermoplastic composite board provided by the utility model has excellent printing performance and coating performance, the surface can be subjected to various printing or spraying without any special corona treatment, and the adhesion performance with a surface coating is good.
3) The easily repaired and glued thermoplastic composite material plate provided by the utility model has excellent bonding performance and is suitable for bonding various structural adhesives, sealants and the like.
4) The easily repaired and easily glued thermoplastic composite board provided by the utility model has excellent low temperature resistance, can be normally used at the temperature of-30 ℃, has the lowest temperature resistance even reaching-60 ℃, is very suitable for some alpine regions, and has other characteristics which are also kept outstanding at low temperature.
Drawings
Fig. 1 is a schematic structural diagram of an easily repairable and easily adhesive thermoplastic composite sheet according to the present invention.
The PET film comprises a 1-PET film, a 2-hot melt adhesive layer, a 3-enhancement layer, a 4-buffer layer, a 5 and a dielectric layer.
Detailed Description
The present invention is further illustrated by the following specific examples, which are not intended to limit the utility model in any way. Reagents, methods and apparatus used in the present invention are conventional in the art unless otherwise indicated.
Unless otherwise indicated, reagents and materials used in the following examples are commercially available.
Example 1
The composite material plate consists of a PET film, a hot melt adhesive layer, a buffer layer, a composite material layer and an adhesive medium layer, wherein the buffer layer is respectively embedded into the hot melt adhesive layer and the enhancement layer, and the medium layer is partially embedded into the enhancement layer; the lower surface of the PET film is attached to the upper surface of the hot melt adhesive layer, and a strippable interface is formed; the lower surface of the hot melt adhesive layer and the upper surface of the enhancement layer have no obvious interface and can not be peeled.
The PET film comprises 80 wt% of PET resin and 6 wt% of PEN resin; 0.2 wt% of phenolic antioxidant, 0.2 wt% of phosphite ester, 0.2 wt% of benzotriazole ultraviolet absorbent, 0.2 wt% of zinc stearate, 0.5 wt% of Ag2O, 0.2 wt% alkanolamide; 10 wt% of nano titanium dioxide and 2.5 wt% of zinc oxide. The thickness of the modified PET film is 0.5 mm.
The hot melt adhesive layer is a modified PES adhesive film, and the surface density is 100 gsm.
The buffer layer is made of porous loose non-woven fabric materials, and the non-woven fabric is made of polybutylene terephthalate fibers with the length of 38 mm. The non-woven spunlace non-woven fabric is flat and uniform in surface. The areal density of the nonwoven was 35 gsm.
The reinforcement layer is composed of a plurality of layers of continuous fiber reinforced thermoplastic composite prepreg sheets.
The reinforced layer paving structure belongs to a symmetrical paving layer, and the paving layer structure is [0/90/90/0/0/90/90/0 ]]nsThe number of layers was 8, and the thickness was 1.6 mm. The continuous fiber reinforced thermoplastic composite material prepreg sheet is formed by fully impregnating and processing the reinforced fibers with molten matrix resin. The reinforced fiber is glass fiber, the linear density is 4800tex, and the content is 55%. The matrix resin consists of main resin and a modification auxiliary agent. Wherein the main resin is polypropylene accounting for 95 wt%; the modified auxiliary agent consists of 1 wt% of calcium carbonate master batch, 1 wt% of LDPE-g-MAH 1 wt%, 6181 wt% of calcium stearate, 1 wt% of UV3280.5wt% of zinc oxide and 0.5 wt% of functional additive.
The medium layer is a non-woven fabric material with a special structure, the non-woven fabric is formed by carding polybutylene terephthalate fibers with the length of 40mm into a net and reinforcing the net in a hot rolling mode, and the non-woven fabric which is formed by blending multiple materials and multiple-scale fibers, is loose in surface structure, compact in internal structure, short in surface fiber and long in internal fiber can be obtained. After the dielectric layer and other reinforcing layers are subjected to hot-pressing compounding, 50% of the dielectric layer is embedded into the matrix resin of the reinforcing layers, and the other non-embedded part provides the function of an adhesive medium or a reinforcing medium, is not limited by the influence of glue components and an adhesive mechanism, and can realize the adhesion with various materials.
The media layer density was 100gsm hot-rolled nonwoven. The shape of the rolling point of the hot-rolled non-woven fabric is diamond, the proportion range of the area of the rolling is 40%, the shortest distance between adjacent rolling is 2.5mm, and the depth of the rolling point is less than or equal to 1/3 thickness of the non-woven fabric.
The above embodiments are preferred embodiments of the present invention, but the present invention is not limited to the above embodiments, and any other changes, modifications, substitutions, combinations, and simplifications which do not depart from the spirit and principle of the present invention should be construed as equivalents thereof, and all such changes, modifications, substitutions, combinations, and simplifications are intended to be included in the scope of the present invention.
Claims (5)
1. The utility model provides an easy sticky thermoplasticity composite board of easy restoration which characterized in that: the composite material plate consists of a PET film, a hot melt adhesive layer, a buffer layer, an enhancement layer and a dielectric layer, wherein the buffer layer is respectively embedded into the hot melt adhesive layer and the enhancement layer, and the dielectric layer is partially embedded into the enhancement layer; the lower surface of the PET film is attached to the upper surface of the hot melt adhesive layer, and a strippable interface is formed; the lower surface of the hot melt adhesive layer and the upper surface of the enhancement layer have no obvious interface and can not be peeled.
2. A repairable and easily adherable thermoplastic composite sheet according to claim 1, wherein: the thickness of the PET film is 0.1 mm-1 mm.
3. A repairable and easily adherable thermoplastic composite sheet according to claim 1, wherein: the hot melt adhesive layer is a modified PES adhesive film/net, and the surface density is 40-120 gsm.
4. A repairable and easily adherable thermoplastic composite sheet according to claim 1, wherein: the reinforcement layer is composed of a plurality of layers of continuous fiber reinforced thermoplastic composite prepreg sheets.
5. A repairable and easily adherable thermoplastic composite sheet according to claim 4, wherein: the layer structure of the reinforced layer belongs to a symmetrical layer, and the layer structure is [0/90/0 ]]ns，[0/90/90/0]ns，[90/0/0/90]ns，[0/90/90/0/90/0]ns，[90/0/90/0/0/90]ns，[0/90/90/0/0/90/90/0]ns，[0/90/0/90/90/0/90/0]nsAnd [90/0/90/0/0/90/0/90]nsWherein n is the number of unit cycles, and n is an integer not less than 1.