CN215210180U - Infrared stealth cloth for military combat uniform - Google Patents
Infrared stealth cloth for military combat uniform Download PDFInfo
- Publication number
- CN215210180U CN215210180U CN202022050824.3U CN202022050824U CN215210180U CN 215210180 U CN215210180 U CN 215210180U CN 202022050824 U CN202022050824 U CN 202022050824U CN 215210180 U CN215210180 U CN 215210180U
- Authority
- CN
- China
- Prior art keywords
- layer
- coating
- flame
- base cloth
- retardant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The utility model relates to an infrared invisible cloth for military combat uniform, which comprises a base cloth layer and a coating layer; the waterproof units are arranged in the base cloth layer and are uniformly distributed in the base cloth layer by being soaked in a waterproof solvent; the front side of the base cloth layer is provided with a printing layer, the back side of the base cloth layer is provided with a coating layer, and the coating layer comprises a flame-retardant coating, a breathable coating, a far infrared hidden layer and an anti-aging PU coating; the flame-retardant coating comprises a first flame-retardant coating and a second flame-retardant coating, the first flame-retardant coating is arranged on the reverse side of the base cloth layer, and the second flame-retardant coating is arranged on the lower surface of the first flame-retardant coating far away from the base cloth layer; the breathable coating is arranged on the lower surface of the second flame-retardant coating far away from the base cloth layer; the far infrared hidden layer is arranged on the lower surface of the breathable coating layer far away from the base cloth layer; the anti-aging PU coating is arranged on the lower surface of the far infrared invisible layer far away from the base cloth layer; the utility model discloses absorb the infrared ray that soldier self produced effectively, strengthened stealthy performance.
Description
Technical Field
The utility model relates to an infrared stealthy cloth for military combat uniform belongs to base cloth processing technology field.
Background
The invisible material technology refers to a technology and a method for manufacturing weapons by using invisible materials or applying the invisible materials on the surfaces of the weapons to absorb radar waves so as to inhibit the electromagnetic signal characteristics of targets of other parties, so that the targets are prevented from being discovered by an electronic reconnaissance system of the other party as much as possible.
At present, the general military combat uniform has poor performance in the aspect of stealth, and modern soldiers are equipped with a lot of high-tech equipment, so that the requirement on the infrared performance of the military combat uniform is higher and higher in order to deal with more and more infrared detection technologies.
SUMMERY OF THE UTILITY MODEL
The utility model aims at overcoming the not enough of prior art and providing an infrared stealthy cloth for military combat uniform, have waterproof, pass through wet, fire-retardant, infrared stealthy characteristic.
In order to achieve the above purpose, the utility model adopts the technical scheme that: the waterproof cloth comprises a base cloth layer and a coating layer, wherein a waterproof unit is arranged in the base cloth layer, and the waterproof unit is soaked in a waterproof solvent and is uniformly distributed in the base cloth layer; the front side of the base cloth layer is provided with a printing layer, and the back side of the base cloth layer is provided with a coating layer; the coating layer comprises a flame-retardant coating, a breathable coating, a far infrared hidden layer and an anti-aging PU coating; the flame-retardant coating comprises a first flame-retardant coating and a second flame-retardant coating, the first flame-retardant coating is arranged on the reverse side of the base cloth layer, and the second flame-retardant coating is arranged on the lower surface of the first flame-retardant coating far away from the base cloth layer; the breathable coating is arranged on the lower surface of the second flame-retardant coating far away from the base cloth layer; the far infrared hidden layer is arranged on the lower surface of the breathable coating layer far away from the base cloth layer; the anti-aging PU coating is arranged on the lower surface of the far infrared invisible layer far away from the direction of the base cloth layer.
Preferably, the base cloth layer is plain cloth or twill cloth formed by interweaving modified nylon high-strength yarns with flame retardant property serving as raw materials.
Preferably, the titer of the modified nylon high-strength yarn is 600D-650D, and the density of the base cloth layer is between 10 x 10 and 20 x 20 per centimeter.
Preferably, the flame-retardant glue of the first flame-retardant coating layerThe sizing amount is 45-55 g/m2。
Preferably, the gluing amount of the flame-retardant glue of the second flame-retardant coating is 25-30 g/m2。
Preferably, the gluing amount of the air-permeable glue of the air-permeable coating is 25-35 g/m2。
Preferably, the gluing amount of the infrared-proof invisible glue of the far infrared invisible layer is 15-25 g/m2。
Preferably, the gluing amount of the anti-aging PU glue of the anti-aging PU coating is 10-15g/m2。
Preferably, the weight of the finished product processed by the infrared stealth fabric is controlled to be 270-300 g/m2And (4) the following steps.
Because of above-mentioned technical scheme's application, compared with the prior art, the utility model have the following advantage:
the infrared stealth cloth for military combat uniform of the utility model can effectively absorb the infrared ray generated by soldiers, greatly enhances stealth performance, and is flame-retardant, waterproof and self-extinguishing when leaving fire; the modified nylon high-strength yarn is adopted, the toughness is high, the wear resistance is good, the breathable layer is additionally arranged, the wearing is more comfortable, the safety and the reliability are realized, the product performance is good, the service life is long, and the market prospect is good.
Drawings
The technical scheme of the utility model is further explained by combining the attached drawings as follows:
FIG. 1 is a cross-sectional view of an infrared stealth fabric for military combat uniform according to the present invention;
wherein: 1. a base cloth layer; 2. printing layer; 3. a first flame retardant coating; 4. a second flame retardant coating; 5. a breathable coating; 6. a far infrared hidden layer; 7. an anti-aging PU coating; 8. a flame retardant coating; 9. and (5) coating the layer.
Detailed Description
The present invention will be described in further detail with reference to the accompanying drawings and specific embodiments.
Referring to fig. 1, the first embodiment:
the utility model discloses a be used for army of schemeThe infrared stealthy cloth used as a combat uniform comprises a base cloth layer 1 and a coating layer 9; the base cloth layer 1 is plain cloth formed by interweaving 650D modified nylon high-strength yarns serving as raw materials, and the density of the base cloth layer 1 is 14 multiplied by 17 per centimeter; waterproof units are arranged in the base cloth layer 1 and are uniformly distributed in the base cloth layer 1 through being soaked in a waterproof solvent; the front side of the base cloth layer 1 is provided with a printing layer 2, the back side of the base cloth layer 1 is provided with a coating layer 9, and the coating layer 9 comprises a flame-retardant coating 8, a breathable coating 5, a far infrared hidden layer 6 and an anti-aging PU coating 7; the flame-retardant coating 8 comprises a first flame-retardant coating 3 and a second flame-retardant coating 4, the first flame-retardant coating 3 is arranged on the reverse side of the base fabric layer 1, and the gluing amount of the flame-retardant glue of the first flame-retardant coating 3 is 45g/m2(ii) a The second flame-retardant coating 4 is arranged on the lower surface of the first flame-retardant coating 3 far away from the base cloth layer 1, and the gluing amount of the flame-retardant glue of the second flame-retardant coating 4 is 28g/m2(ii) a The breathable coating 5 is arranged on the lower surface of the second flame-retardant coating 4 far away from the base cloth layer 1, and the gluing amount of the breathable glue of the breathable coating 5 is 25g/m2(ii) a The far infrared hidden layer 6 is arranged on the lower surface of the breathable coating 5 far away from the base cloth layer 1, and the gluing amount of the infrared-proof hidden glue of the far infrared hidden layer 6 is 25g/m2(ii) a The anti-aging PU coating 7 is arranged on the lower surface of the far infrared hidden layer 6 far away from the direction of the base cloth layer 1, and the gluing amount of the anti-aging PU glue of the anti-aging PU coating 7 is 10-15g/m2。
Please refer to fig. 1, embodiment two:
the utility model relates to an infrared invisible cloth used for military combat uniform, which comprises a base cloth layer 1 and a coating layer 9; the base cloth layer 1 is plain cloth formed by interweaving 600D modified nylon high-strength yarns serving as raw materials, and the density of the base cloth layer 1 is 17 multiplied by 19 per centimeter; waterproof units are arranged in the base cloth layer 1 and are uniformly distributed in the base cloth layer 1 through being soaked in a waterproof solvent; the front side of the base cloth layer 1 is provided with a printing layer 2, the back side of the base cloth layer 1 is provided with a coating layer 9, and the coating layer 9 comprises a flame-retardant coating 8, a breathable coating 5, a far infrared hidden layer 6 and an anti-aging PU coating 7; the flame retardant coating 8 comprises a first barrierA flame-retardant coating layer 3 and a second flame-retardant coating layer 4, wherein the first flame-retardant coating layer 3 is arranged on the reverse side of the base fabric layer 1, and the gluing amount of the flame-retardant glue of the first flame-retardant coating layer 3 is 40g/m2(ii) a The second flame-retardant coating 4 is arranged on the lower surface of the first flame-retardant coating 3 far away from the base cloth layer 1, and the gluing amount of the flame-retardant glue of the second flame-retardant coating 4 is 35g/m2(ii) a The breathable coating 5 is arranged on the lower surface of the second flame-retardant coating 4 far away from the base cloth layer 1, and the gluing amount of the breathable glue of the breathable coating 5 is 15g/m2(ii) a The far infrared hidden layer 6 is arranged on the lower surface of the breathable coating 5 far away from the base cloth layer 1, and the gluing amount of the infrared-proof hidden glue of the far infrared hidden layer 6 is 25g/m2(ii) a Ageing resistance PU coating 7 sets up on the lower surface of keeping away from 1 direction on the base cloth layer is kept away from to the stealthy layer 6 of far infrared, ageing resistance PU coating 7's ageing resistance PU glues rubberizing volume is 10g/m2。
Please refer to fig. 1, embodiment three:
the utility model relates to an infrared invisible cloth used for military combat uniform, which comprises a base cloth layer 1 and a coating layer 9; the base cloth layer 1 is plain cloth formed by interweaving 620D modified nylon high-strength yarns serving as raw materials, and the density of the base cloth layer 1 is 14 multiplied by 19 per centimeter; waterproof units are arranged in the base cloth layer 1 and are uniformly distributed in the base cloth layer 1 through being soaked in a waterproof solvent; the front side of the base cloth layer 1 is provided with a printing layer 2, the back side of the base cloth layer 1 is provided with a coating layer 9, and the coating layer 9 comprises a flame-retardant coating 8, a breathable coating 5, a far infrared hidden layer 6 and an anti-aging PU coating 7; the flame-retardant coating 8 comprises a first flame-retardant coating 3 and a second flame-retardant coating 4, the first flame-retardant coating 3 is arranged on the reverse side of the base fabric layer 1, and the gluing amount of the flame-retardant glue of the first flame-retardant coating 3 is 50g/m2(ii) a The second flame-retardant coating 4 is arranged on the lower surface of the first flame-retardant coating 3 far away from the base cloth layer 1, and the gluing amount of the flame-retardant glue of the second flame-retardant coating 4 is 25g/m2(ii) a The breathable coating 5 is arranged on the lower surface of the second flame-retardant coating 4 far away from the base cloth layer 1, and the gluing amount of the breathable glue of the breathable coating 5 is 22g/m2(ii) a The far infrared hidden layer 6 is arranged in the direction of the breathable coating 5 far away from the base cloth layer 1The gluing amount of the infrared-proof invisible glue of the far infrared invisible layer 6 on the lower surface is 20g/m2(ii) a Ageing resistance PU coating 7 sets up on the lower surface of keeping away from 1 direction on the base cloth layer is kept away from to the stealthy layer 6 of far infrared, ageing resistance PU coating 7's ageing resistance PU glues rubberizing volume is 8g/m2。
The above is only a specific application example of the present invention, and does not constitute any limitation to the protection scope of the present invention. All the technical solutions formed by equivalent transformation or equivalent replacement fall within the protection scope of the present invention.
Claims (9)
1. The utility model provides an infrared stealthy cloth for military combat uniform which characterized in that: comprises a coating layer (9) and a base cloth layer (1) with waterproof performance; the front side of the base cloth layer (1) is provided with a printing layer (2), the back side of the base cloth layer (1) is provided with a coating layer (9), and the coating layer (9) comprises a flame-retardant coating layer (8), a breathable coating layer (5), a far infrared hidden layer (6) and an anti-aging PU coating layer (7); the flame-retardant coating (8) comprises a first flame-retardant coating (3) and a second flame-retardant coating (4), the first flame-retardant coating (3) is arranged on the reverse side of the base fabric layer (1), and the second flame-retardant coating (4) is arranged on the lower surface of the first flame-retardant coating (3) far away from the base fabric layer (1); the breathable coating (5) is arranged on the lower surface of the second flame-retardant coating (4) far away from the base cloth layer (1); the far infrared hidden layer (6) is arranged on the lower surface of the breathable coating (5) far away from the base cloth layer (1); the anti-aging PU coating (7) is arranged on the lower surface of the far infrared hidden layer (6) far away from the direction of the base cloth layer (1).
2. The infrared stealth fabric for military combat uniforms of claim 1, wherein: the base cloth layer (1) is plain cloth or twill cloth formed by interweaving modified nylon high-strength yarns with flame retardant property serving as raw materials.
3. The infrared stealth fabric for military combat uniforms of claim 2, wherein: the titer of the modified nylon high-strength yarn is 600D-650D, and the density of the base cloth layer (1) is between 10 multiplied by 10 and 20 multiplied by 20 per centimeter.
4. The infrared stealth fabric for military combat uniforms of claim 1, wherein: the gluing amount of the flame-retardant glue of the first flame-retardant coating (3) is 45-55 g/m2。
5. The infrared stealth fabric for military combat uniforms of claim 1, wherein: the gluing amount of the flame-retardant glue of the second flame-retardant coating (4) is 25-30 g/m2。
6. The infrared stealth fabric for military combat uniforms of claim 1, wherein: the gluing amount of the infrared-proof invisible glue of the far infrared invisible layer (6) is 15-25 g/m2。
7. The infrared stealth fabric for military combat uniforms of claim 1, wherein: the gluing amount of the air-permeable glue of the air-permeable coating (5) is 25-35 g/m2。
8. The infrared stealth fabric for military combat uniforms of claim 1, wherein: the gluing amount of the anti-aging PU glue of the anti-aging PU coating (7) is 10-15g/m2。
9. The infrared stealth fabric for military combat uniforms of claim 1, wherein: the weight of a finished product processed by the infrared stealth fabric is controlled within 270-300 g/m 2.