CN212357129U

CN212357129U - Outdoor air brushing reflection of light sign

Info

Publication number: CN212357129U
Application number: CN202020414908.8U
Authority: CN
Inventors: 程健; 王洪峰; 褚亚华
Original assignee: Sichuan Jiangyou Yushu Yeshili Reflective Material Co ltd
Current assignee: Sichuan Jiangyou Yushu Yeshili Reflective Material Co ltd
Priority date: 2020-03-27
Filing date: 2020-03-27
Publication date: 2021-01-15
Anticipated expiration: 2030-03-27

Abstract

The utility model discloses an outdoor air brushing reflection of light sign belongs to reflection of light sign technical field, has solved the reflection of light sign among the prior art and has leaded to the problem that the function received more restriction with the mode preparation of manual work inlaying, the utility model discloses a substrate layer, the surface of substrate layer is by supreme white printing ink layer, colored printing ink layer, clear glue film and the glass pearl layer of having set gradually down, and the bottom surface of substrate layer has connected gradually pressure sensitive adhesive layer from top to bottom and has left the type rete. The utility model discloses it is efficient, with low costs, the product has price competition advantage, and the color of air brushing is abundant, and the complete intensity of structure is high.

Description

Outdoor air brushing reflection of light sign

Technical Field

The utility model belongs to the technical field of the reflection of light sign, concretely relates to outdoor air brushing reflection of light sign.

Background

With the development of national economy, traffic roads develop very rapidly, the highway mileage of China increases rapidly, and the high-speed and informatization of highway traffic engineering becomes the development direction. Along with the construction and development of urbanization in China, urban environment and beautification become elements, more and more urban roads are available in all-around and full interchange, simultaneously, the quantity of various vehicles is larger and larger, and the traffic prosperity degree is increased day by day. Along with this, traffic management and traffic safety are put forward to a very important position, so that the enhancement of traffic management and the guarantee of traffic safety to ensure the development of national economy and the guarantee of life and property safety of people are common knowledge of people, and the increase of traffic signs, road traffic safety facilities, vehicle marks and indication signs is a very important part of traffic safety management.

The reflective mark is a road traffic sign made of reflective materials. When the vehicle is driven at night, under the irradiation of the street lamp or the vehicle headlamp, the graph or the character of the mark can be displayed, thereby being convenient for identification and safe driving. The reflecting material includes reflecting paint (mixed with fine glass beads in the paint, painted on the mark or marked line), reflecting film (patch made of fine glass beads, stuck on the mark) and reflecting button (made of glass or plastics, embedded in metal container, used as raised road sign).

The existing commonly used method for manufacturing the reflective marker is manual embedding, however, the method for manually embedding the reflective marker has low working efficiency, cannot produce the marker with gradient color, has more limitations on the types of the markers which can be manufactured, cannot meet the requirements of various functions, and has fewer applicable scenes.

SUMMERY OF THE UTILITY MODEL

The utility model aims to provide a:

for solving the problem that the function is more restricted due to the fact that the reflection sign in the prior art is manufactured in a manual embedding mode, the outdoor painting reflection sign is provided.

The utility model adopts the technical scheme as follows:

the utility model provides an outdoor air brushing reflection of light sign, its characterized in that, the surface of substrate layer is by supreme white printing ink layer, colored printing ink layer, clear adhesive layer and the glass pearl layer of having set gradually down, and the bottom surface of substrate layer has connected gradually pressure sensitive adhesive layer from top to bottom and has left the type rete.

Further, the substrate layer is composed of canvas.

Further, the substrate layer is composed of a rubber and plastic sheet, and the thickness of the rubber and plastic sheet is less than or equal to 2 mm.

Further, the release film layer is one of a single-silicon release film or release paper.

Further, the glass bead layer is composed of glass beads of a rainy night type.

The utility model discloses a reflection of light sign includes following step when the preparation:

a. preparing a base material layer: carrying out heat treatment on a base material forming the base material layer, wherein the base material uses canvas or a rubber plastic sheet with the thickness less than or equal to 2 mm;

b. spray painting an ink layer: sequentially spraying white UV ink and colored UV ink on the heat-treated substrate;

c. coating a surface glue layer: coating colorless and transparent wear-resistant surface cleaning glue on the ink layer;

d. polishing glass beads: throwing rain night glass beads on the clear adhesive layer;

e. drying: drying the surface polished with the glass beads;

f. covering a pressure-sensitive adhesive layer and a release film layer at the bottom of the base material in sequence;

g. trimming edges: and trimming the edges of the layers, and removing burrs to form a flat edge.

Further, the retroreflective luminance coefficient of the glass beads of the rainy night type is more than 150 mcd/(lx.m2).

Further, the 180 DEG peel strength of the pressure sensitive adhesive to the stainless steel plate is greater than 90N/IN.

To sum up, owing to adopted above-mentioned technical scheme, the beneficial effects of the utility model are that:

the utility model discloses a method that reflection of light sign was makeed through the air brushing has overcome the manual various restrictions that receive when inlaying the preparation, and the sign has the gradual change, and the color is abundant, more convenient discernment, and the substrate is through heat treatment, can reduce the size shrink in follow-up process and the use, and the intensity of structure is higher, and the integrality is stronger, and the efficiency of air brushing preparation is obviously higher than the efficiency of manual preparation of inlaying simultaneously, and the cost is lower, and product competition advantage is bigger.

Drawings

Fig. 1 is a structural diagram of the reflective sign of the present invention.

The labels in the figure are: 1-substrate layer, 2-white ink layer, 3-colored ink layer, 4-clear adhesive layer, 5-glass bead layer, 6-pressure sensitive adhesive layer and 7-release film layer.

Detailed Description

In order to make the objects, technical solutions and advantages of the present invention more clearly understood, the present invention is further described in detail below with reference to the accompanying drawings and embodiments. It should be understood that the specific embodiments described herein are for purposes of illustration only and are not intended to limit the invention.

The utility model provides an outdoor air brushing reflection of light sign, the surface of substrate layer 1 is by supreme white printing ink layer 2, colored printing ink layer 3, clear adhesive layer 4 and the glass pearl layer 5 of having set gradually down, and the bottom surface of substrate layer 1 has connected gradually pressure sensitive adhesive layer 6 from top to bottom and has left type rete 7.

Preferably, the substrate layer 1 consists of canvas.

Preferably, the base material layer 1 is composed of a rubber and plastic sheet, and the thickness of the rubber and plastic sheet is less than or equal to 2 mm.

Preferably, the release film layer 7 is one of a single silicon release film or release paper.

Preferably, the glass bead layer 5 is composed of glass beads of the rainy night type.

Example 1

The utility model discloses a preparation of reflection of light sign includes following step:

a. preparing a base material layer 1: carrying out heat treatment on the base material layer 1, wherein the base material layer is canvas or a rubber and plastic sheet with the thickness of 2 mm;

b. spray painting an ink layer: sequentially spraying white UV ink and colored UV ink on the heat-treated substrate, wherein the ink with good weather resistance and good substrate adhesion is used;

c. coating a surface glue layer 4: the printing ink layer is coated with colorless and transparent wear-resistant surface cleaning glue, and the surface cleaning glue has good low-temperature toughness, sun resistance, stain resistance and water resistance;

d. polishing glass beads: throwing rain night glass beads on the clear adhesive layer 4;

e. drying: drying the surface polished with the glass beads;

f. coating a pressure sensitive adhesive: the pressure-sensitive adhesive layer 6 and the release film layer 7 are sequentially covered at the bottom of the base material;

Preferably, the raindrop-type glass beads provide a white logo with a retroreflective luminance coefficient of 180mcd/(lx.m2) during continuous rainfall.

Preferably, the pressure sensitive adhesive has a 180 peel strength to stainless steel plate of 110N/IN.

Example 2

The preparation method comprises the following steps:

a. preparing a base material layer 1: carrying out heat treatment on the base material layer 1, wherein the base material layer is made of canvas or a rubber and plastic sheet with the thickness of 1.5 mm;

e. drying: drying the surface polished with the glass beads;

Preferably, the raindrop-type glass beads provide a white logo with a retroreflective luminance coefficient of 160mcd/(lx.m2) during continuous rainfall.

Preferably, the pressure sensitive adhesive has a 180 peel strength to stainless steel plate of 100N/IN.

The above description is only exemplary of the present invention and should not be taken as limiting the scope of the present invention, as any modifications, equivalents, improvements and the like made within the spirit and principles of the present invention are intended to be included within the scope of the present invention.

Claims

1. The utility model provides an outdoor air brushing reflection of light sign, its characterized in that, includes substrate layer (1), the surface of substrate layer (1) is by supreme white printing ink layer (2), colored printing ink layer (3), clear glue film (4) and glass pearl layer (5) of having set gradually down, and the bottom surface of substrate layer (1) has connected gradually pressure sensitive adhesive layer (6) from top to bottom and has left type rete (7).

2. The outdoor painted reflective sign according to claim 1, wherein the substrate layer (1) is composed of canvas.

3. The outdoor painted reflective sign according to claim 1, wherein the substrate layer (1) is made of a rubber-plastic sheet, and the thickness of the rubber-plastic sheet is less than or equal to 2 mm.

4. The outdoor inkjet-printed reflective mark according to claim 1, wherein the release film layer (7) is one of a single-silicon release film or release paper.

5. The outdoor painted reflective sign according to claim 1, wherein the glass bead layer (5) is made of glass beads of a rainy night type.