CN111269669A - Outdoor spray-painted reflective mark and manufacturing method thereof - Google Patents
Outdoor spray-painted reflective mark and manufacturing method thereof Download PDFInfo
- Publication number
- CN111269669A CN111269669A CN202010227913.2A CN202010227913A CN111269669A CN 111269669 A CN111269669 A CN 111269669A CN 202010227913 A CN202010227913 A CN 202010227913A CN 111269669 A CN111269669 A CN 111269669A
- Authority
- CN
- China
- Prior art keywords
- layer
- outdoor
- glass beads
- sensitive adhesive
- reflective
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an outdoor spray-painted reflective mark and a manufacturing method thereof, belongs to the technical field of reflective marks, and solves the problem that functions of the reflective mark in the prior art are more limited due to the fact that the reflective mark is manufactured in a manual embedding mode. The method for manufacturing the reflective mark comprises the steps of preparing a substrate layer, spraying and painting an ink layer, coating a surface adhesive layer, polishing glass beads, drying, coating a pressure sensitive adhesive and trimming edges. The invention has the advantages of high efficiency, low cost, competitive price of products, rich colors of spray painting and high structural integrity and strength.
Description
Technical Field
The invention belongs to the technical field of reflective marks, and particularly relates to an outdoor spray-painted reflective mark and a manufacturing method thereof.
Background
With the development of national economy, traffic roads develop very rapidly, the highway mileage of China increases rapidly, and the high-speed and informatization of highway traffic engineering becomes the development direction. Along with the construction and development of urbanization in China, urban environment and beautification become elements, more and more urban roads are available in all-around and full interchange, simultaneously, the quantity of various vehicles is larger and larger, and the traffic prosperity degree is increased day by day. Along with this, traffic management and traffic safety are put forward to a very important position, so that the enhancement of traffic management and the guarantee of traffic safety to ensure the development of national economy and the guarantee of life and property safety of people are common knowledge of people, and the increase of traffic signs, road traffic safety facilities, vehicle marks and indication signs is a very important part of traffic safety management.
The reflective mark is a road traffic sign made of reflective materials. When the vehicle is driven at night, under the irradiation of the street lamp or the vehicle headlamp, the graph or the character of the mark can be displayed, thereby being convenient for identification and safe driving. The reflecting material includes reflecting paint (mixed with fine glass beads in the paint, painted on the mark or marked line), reflecting film (patch made of fine glass beads, stuck on the mark) and reflecting button (made of glass or plastics, embedded in metal container, used as raised road sign).
The existing commonly used method for manufacturing the reflective marker is manual embedding, however, the method for manually embedding the reflective marker has low working efficiency, cannot produce the marker with gradient color, has more limitations on the types of the markers which can be manufactured, cannot meet the requirements of various functions, and has fewer applicable scenes.
Disclosure of Invention
The invention aims to:
in order to solve the problem that functions of a reflective mark are limited due to the fact that the reflective mark is manufactured in a manual embedding mode in the prior art, an outdoor spray-painting reflective mark and a manufacturing method thereof are provided.
The technical scheme adopted by the invention is as follows:
the utility model provides an outdoor air brushing reflection of light sign, its characterized in that, the surface of substrate layer is by supreme white printing ink layer, colored printing ink layer, clear adhesive layer and the glass pearl layer of having set gradually down, and the bottom surface of substrate layer has connected gradually pressure sensitive adhesive layer from top to bottom and has left the type rete.
Further, the substrate layer is composed of canvas.
Further, the substrate layer is composed of a rubber and plastic sheet, and the thickness of the rubber and plastic sheet is less than or equal to 2 mm.
Further, the release film layer is one of a single-silicon release film or release paper.
Further, the glass bead layer is composed of glass beads of a rainy night type.
A method for manufacturing an outdoor painting reflective mark is characterized by comprising the following steps:
a. preparing a base material layer: carrying out heat treatment on a base material forming the base material layer, wherein the base material uses canvas or a rubber plastic sheet with the thickness less than or equal to 2 mm;
b. spray painting an ink layer: sequentially spraying white UV ink and colored UV ink on the heat-treated substrate;
c. coating a surface glue layer: coating colorless and transparent wear-resistant surface cleaning glue on the ink layer;
d. polishing glass beads: throwing rain night glass beads on the clear adhesive layer;
e. drying: drying the surface polished with the glass beads;
f. coating a pressure sensitive adhesive: covering a pressure sensitive adhesive layer on the dried glass beads;
g. trimming edges: and trimming the edges of the layers, and removing burrs to form a flat edge.
Further, the retroreflection luminance coefficient of the glass bead is more than 150 mcd/(lx.m2).
Further, the 180 DEG peel strength of the pressure-sensitive adhesive to a stainless steel plate is more than 90N/IN.
In summary, due to the adoption of the technical scheme, the invention has the beneficial effects that:
the reflective mark is manufactured by a spray painting method, various limitations on manual embedding manufacture are overcome, the mark has gradient color, is rich in color and convenient to identify, the base material can reduce the size shrinkage in subsequent processes and use after being subjected to heat treatment, the structural strength is higher, the integrity is stronger, meanwhile, the spray painting manufacture efficiency is obviously higher than that of the manual embedding manufacture, the cost is lower, and the product competition advantage is larger.
Drawings
FIG. 1 is a block diagram of a retroreflective sign of the present invention;
FIG. 2 is a flow chart of a method for making the reflective marker of the present invention;
the labels in the figure are: 1-substrate layer, 2-white ink layer, 3-colored ink layer, 4-clear adhesive layer, 5-glass bead layer, 6-pressure sensitive adhesive layer and 7-release film layer.
Detailed Description
In order to make the objects, technical solutions and advantages of the present invention more apparent, the present invention is described in further detail below with reference to the accompanying drawings and embodiments. It should be understood that the specific embodiments described herein are merely illustrative of the invention and are not intended to limit the invention.
The utility model provides an outdoor air brushing reflection of light sign, the surface of substrate layer 1 is by supreme white printing ink layer 2, colored printing ink layer 3, clear adhesive layer 4 and the glass pearl layer 5 of having set gradually down, and the bottom surface of substrate layer 1 has connected gradually pressure sensitive adhesive layer 6 from top to bottom and has left type rete 7.
Preferably, the substrate layer 1 consists of canvas.
Preferably, the base material layer 1 is composed of a rubber and plastic sheet, and the thickness of the rubber and plastic sheet is less than or equal to 2 mm.
Preferably, the release film layer 7 is one of a single silicon release film or release paper.
Preferably, the glass bead layer 5 is composed of glass beads of the rainy night type.
Example 1
A method for manufacturing an outdoor painting reflective mark comprises the following steps:
a. preparing a base material layer 1: carrying out heat treatment on the base material layer 1, wherein the base material layer is canvas or a rubber and plastic sheet with the thickness of 2 mm;
b. spray painting an ink layer: sequentially spraying white UV ink and colored UV ink on the heat-treated substrate, wherein the ink with good weather resistance and good substrate adhesion is used;
c. coating a surface glue layer 4: the printing ink layer is coated with colorless and transparent wear-resistant surface cleaning glue, and the surface cleaning glue has good low-temperature toughness, sun resistance, stain resistance and water resistance;
d. polishing glass beads: throwing rain night glass beads on the clear adhesive layer 4;
e. drying: drying the surface polished with the glass beads;
f. coating a pressure sensitive adhesive: covering the dried glass beads with a pressure sensitive adhesive layer 6;
g. trimming edges: and trimming the edges of the layers, and removing burrs to form a flat edge.
Preferably, the raindrop-type glass beads provide a white logo with a retroreflective luminance coefficient of 180mcd/(lx.m2) during continuous rainfall.
Preferably, the pressure sensitive adhesive has a 180 peel strength to stainless steel plate of 110N/IN.
Example 2
A method for manufacturing an outdoor painting reflective mark comprises the following steps:
a. preparing a base material layer 1: carrying out heat treatment on the base material layer 1, wherein the base material layer is made of canvas or a rubber and plastic sheet with the thickness of 1.5 mm;
b. spray painting an ink layer: sequentially spraying white UV ink and colored UV ink on the heat-treated substrate, wherein the ink with good weather resistance and good substrate adhesion is used;
c. coating a surface glue layer 4: the printing ink layer is coated with colorless and transparent wear-resistant surface cleaning glue, and the surface cleaning glue has good low-temperature toughness, sun resistance, stain resistance and water resistance;
d. polishing glass beads: throwing rain night glass beads on the clear adhesive layer 4;
e. drying: drying the surface polished with the glass beads;
f. coating a pressure sensitive adhesive: covering the dried glass beads with a pressure sensitive adhesive layer 6;
g. trimming edges: and trimming the edges of the layers, and removing burrs to form a flat edge.
Preferably, the raindrop-type glass beads provide a white logo with a retroreflective luminance coefficient of 160mcd/(lx.m2) during continuous rainfall.
Preferably, the pressure sensitive adhesive has a 180 peel strength to stainless steel plate of 100N/IN.
The above description is only for the purpose of illustrating the preferred embodiments of the present invention and is not to be construed as limiting the invention, and any modifications, equivalents and improvements made within the spirit and principle of the present invention are intended to be included within the scope of the present invention.
Claims (8)
1. The utility model provides an outdoor air brushing reflection of light sign, its characterized in that, includes substrate layer (1), the surface of substrate layer (1) is by supreme white printing ink layer (2), colored printing ink layer (3), clear glue film (4) and glass pearl layer (5) of having set gradually down, and the bottom surface of substrate layer (1) has connected gradually pressure sensitive adhesive layer (6) from top to bottom and has left type rete (7).
2. The outdoor painted reflective sign according to claim 1, wherein the substrate layer (1) is composed of canvas.
3. The outdoor painted reflective sign according to claim 1, wherein the substrate layer (1) is made of a rubber-plastic sheet, and the thickness of the rubber-plastic sheet is less than or equal to 2 mm.
4. The outdoor inkjet-printed reflective mark according to claim 1, wherein the release film layer (7) is one of a single-silicon release film or release paper.
5. The outdoor painted reflective sign according to claim 1, wherein the glass bead layer (5) is made of glass beads of a rainy night type.
6. A method for manufacturing an outdoor painting reflective mark is characterized by comprising the following steps:
a. preparing a base material layer (1): carrying out heat treatment on the base material forming the base material layer (1), wherein canvas or a rubber plastic sheet with the thickness less than or equal to 2mm is used as the base material;
b. spray painting an ink layer: sequentially spraying white UV ink and colored UV ink on the heat-treated substrate;
c. coating a surface glue layer (4): coating colorless and transparent wear-resistant surface cleaning glue on the ink layer;
d. polishing glass beads: throwing rain night glass beads on the clear adhesive layer (4);
e. drying: drying the surface polished with the glass beads;
f. coating a pressure sensitive adhesive: covering a pressure sensitive adhesive layer (6) on the dried glass beads;
g. trimming edges: and trimming the edges of the layers, and removing burrs to form a flat edge.
7. The method for making the outdoor painted reflective sign according to claim 6, wherein the retroreflective brightness coefficient of the glass beads at rainy night is greater than 150mcd/lx/m 2.
8. The method for making the outdoor painted reflective sign according to claim 6, wherein the 180-degree peel strength of the pressure-sensitive adhesive to the stainless steel plate is greater than 90N/IN.