CN211759160U - Explosion welding construction structure of base-composite equal-thickness metal composite material - Google Patents
Explosion welding construction structure of base-composite equal-thickness metal composite material Download PDFInfo
- Publication number
- CN211759160U CN211759160U CN201922268967.9U CN201922268967U CN211759160U CN 211759160 U CN211759160 U CN 211759160U CN 201922268967 U CN201922268967 U CN 201922268967U CN 211759160 U CN211759160 U CN 211759160U
- Authority
- CN
- China
- Prior art keywords
- metal sheet
- explosive
- base
- composite
- medicine box
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The utility model provides a base-compound isopachous metal composite's explosive welding construction structures, includes the ground, the level has been placed basic unit's metal sheet on the ground, with the compound layer metal sheet of basic unit's metal sheet isopachous, be located the clearance support column between basic unit's metal sheet and the compound layer metal sheet, set up at the medicine box at compound layer metal sheet top and lay the explosive in the medicine box, wherein, basic unit's metal sheet bottom is provided with rather than the supplementary welt of equidimension, basic unit's metal sheet spot welding is on the surface of supplementary welt, just supplementary welt thickness is 2 times of basic unit's metal sheet thickness at least. The utility model discloses a method of supplementary welt, one of them metal sheet of formally thickening is as the base plate board, makes its base complex thickness proportion with the compound plywood of uniform thickness reach the required 3 of explosive welding theory: 1, so that the purpose of explosion welding of the base composite equal-thickness composite plate by using the conventional explosion welding process can be realized.
Description
Technical Field
The utility model relates to an explosive welding technical field specifically is a base-compound isopachous metal composite's explosive welding construction structures.
Background
The production process of explosion-welded composite board is characterized by that the composite board is placed on the base board, on the composite board the explosive is spread, after the explosive is detonated, the composite board can be impacted on the base board at high speed, and the high-temp. and high-pressure produced between two boards can make the interface of two materials implement solid-phase metallurgical combination so as to attain the goal of welding. Theory and practice of explosion welding has shown that, in order to obtain a high-quality welding interface, the thickness ratio of the base plate to the clad plate should be greater than 3:1, and the ratio of the thickness of the base material to the thickness of the clad material is usually not less than 3, as also specified in the standards NB/T47002.1 for explosion-welded clad plates for pressure vessels. For base composite equal-thickness metal composite materials required in the market, such as composite materials for small naval vessels, copper-aluminum composite conductive bars and the like, the conventional explosive welding process and welding construction structure are difficult to realize.
SUMMERY OF THE UTILITY MODEL
The difficult problem to the compound isopachous composite sheet of explosive welding base that can not directly be applied to current explosive welding construction structures, the utility model discloses a method of supplementary welt thickens one of them metal sheet as the base plate in the form, makes its compound thickness proportion of base with the compound plywood of isopachous reach the required 3 of explosive welding theory: 1, so that the purpose of explosion welding of the base composite equal-thickness composite plate by using the conventional explosion welding process can be realized.
The utility model discloses a solve the technical scheme who takes of above-mentioned problem and do: the utility model provides a base-compound isopachous metal composite's explosive welding construction structures, includes the ground, the level has been placed basic unit's metal sheet on the ground, with the compound layer metal sheet of basic unit's metal sheet isopachous, be located the clearance support column between basic unit's metal sheet and the compound layer metal sheet, set up at the medicine box at compound layer metal sheet top and lay the explosive in the medicine box, wherein, basic unit's metal sheet bottom is provided with rather than the supplementary welt of equidimension, basic unit's metal sheet spot welding is on the surface of supplementary welt, just supplementary welt thickness is 2 times of basic unit's metal sheet thickness at least.
Preferably, the auxiliary lining plate is a Q235B steel plate.
Preferably, the height of the gap support column is 10 mm.
Preferably, the spacing between any two adjacent interstitial support posts is 200 and 280 mm.
Preferably, the gap supporting columns are arranged on the surface of the base metal plate in a rhombic shape.
Preferably, the medicine box is a paper medicine box with the area matched with the multi-layer metal plate, the height of the medicine box is 45mm, and the medicine box is adhered to the multi-layer metal plate through an adhesive tape.
Preferably, the explosive is expanded ammonium nitrate explosive, the height of the explosive is flush with that of the explosive box, and an electric detonator for detonation is arranged in the explosive.
Preferably, the electric cap is provided at a position in the middle of the longer side of the medicine cartridge.
Preferably, the foundation is a flat foundation of a sandy soil structure.
Compared with the prior art, the utility model discloses following beneficial effect has:
the utility model discloses utilize ripe explosive welding technology, improve the construction mounting structure of traditional current explosive welding's base and compound board, at not increasing the process step, under the condition of raw and other materials cost, the technological problem that traditional explosive welding technology and construction structure can not explosive welding isopachous metal clad plate has been broken through, thereby the complicated process methods such as casting copper steel that production isopachous metal clad plate adopted before having changed, rolling aluminium copper, etc. have opened up a new, efficient process method for realizing that scale industrial production isopachous metal clad plate.
The utility model discloses a method of supplementary welt is one of them metal sheet through supplementary welt thickening in the form to together regard supplementary welt and basic unit's metal sheet as the base plate, make its base compound thickness proportion with the compound plywood of this basic unit's metal sheet isopachous reach the required 3 of explosive welding theory: 1, so that the purpose of explosion welding of the base composite equal-thickness composite plate by using the conventional explosion welding process can be realized.
Drawings
Fig. 1 is a schematic view of the construction installation structure of the present invention.
Detailed Description
The present invention will be described in detail with reference to the following embodiments, which are based on the technical solution of the present invention and provide detailed embodiments and specific operation processes.
As shown in the figure, the utility model relates to a base-compound isopachous metal combined material's explosive welding construction structures, including ground 8, base metal sheet 6, with base metal sheet 6 isopachous multiple metal sheet 3, be located base metal sheet 6 and multiple metal sheet 3 between clearance support column 5, the setting at the medicine box 2 at multiple metal sheet 3 top and lay the explosive 4 in medicine box 2 of multiple metal sheet 3 are placed to the level on ground 8, wherein, base metal sheet 6 bottom is provided with rather than the supplementary welt 7 of equidimension, base metal sheet 6 spot welding is on the surface of supplementary welt 7, just the thickness of supplementary welt 7 is 2 times of base metal sheet 6 thickness at least.
The foregoing is a basic embodiment of the invention, and further modifications, optimizations, or limitations may be made on the foregoing.
Further, the auxiliary liner plate 7 is a Q235B steel plate.
Further, the height of the gap supporting column 5 is 10 mm.
Further, the distance between any two adjacent gap support pillars 5 is 200 and 280 mm.
Furthermore, the gap supporting columns 5 are arranged on the surface of the base metal plate in a rhombic shape.
Further, the medicine box 2 is a paper medicine box with the area matched with the multiple-layer metal plate 3, the height of the medicine box 2 is 45mm, and the medicine box is bonded on the multiple-layer metal plate 3 through an adhesive tape.
Further, the explosive 4 is expanded ammonium nitrate explosive, the height of the explosive 4 is flush with that of the explosive box 2, and an electric detonator 1 for detonation is arranged in the explosive 4.
Further, the electric cap 1 is disposed at a central position of a longer side of the medicine cartridge 2.
Further, the foundation 8 is a flat foundation with a sandy soil structure.
The utility model discloses utilize ripe explosive welding technology, improve the construction mounting structure of traditional current explosive welding's base and compound board, at not increasing the process step, under the condition of raw and other materials cost, the technological problem that traditional explosive welding technology and construction structure can not explosive welding isopachous metal clad plate has been broken through, thereby the complicated process methods such as casting copper steel that production isopachous metal clad plate adopted before having changed, rolling aluminium copper, etc. have opened up a new, efficient process method for realizing that scale industrial production isopachous metal clad plate.
The above description is only a preferred embodiment of the present invention, and the present invention is not limited to the above description, and although the present invention has been described with reference to the preferred embodiment, it is not limited to the present invention, and any skilled person in the art can make equivalent modifications or changes within the technical scope of the present invention, and any simple modifications, equivalent changes and modifications made by the technical spirit of the present invention to the above embodiments are within the technical scope of the present invention.
Claims (9)
1. The utility model provides a base-compound isopachous metal composite's explosive welding construction structures, includes ground (8), its characterized in that: base metal sheet (6), with compound layer metal sheet (3) of base metal sheet (6) isopachous, be located clearance support column (5) between base metal sheet (6) and compound layer metal sheet (3), set up at medicine box (2) at compound layer metal sheet (3) top and lay explosive (4) in medicine box (2), wherein, base metal sheet (6) bottom is provided with rather than the supplementary welt (7) of equidimension, base metal sheet (6) spot welding is on the surface of supplementary welt (7), just the thickness of supplementary welt (7) is 2 times of base metal sheet (6) thickness at least.
2. The explosive welding construction structure of a matrix-composite equal thickness metal composite material as claimed in claim 1, wherein: the auxiliary lining plate (7) is a Q235B steel plate.
3. The explosive welding construction structure of a matrix-composite equal thickness metal composite material as claimed in claim 1, wherein: the height of the gap supporting column (5) is 10 mm.
4. The explosive welding construction structure of a matrix-composite equal thickness metal composite material as claimed in claim 1, wherein: the distance between any two adjacent gap support columns (5) is 200 mm and 280 mm.
5. The explosive welding construction structure of a matrix-composite equal thickness metal composite material as claimed in claim 1, wherein: the gap supporting columns (5) are arranged on the surface of the base metal plate in a rhombic shape.
6. The explosive welding construction structure of a matrix-composite equal thickness metal composite material as claimed in claim 1, wherein: the medicine box (2) is a paper medicine box with the area matched with the multi-layer metal plate (3), the height of the medicine box (2) is 45mm, and the medicine box is adhered to the multi-layer metal plate (3) through an adhesive tape.
7. The explosive welding construction structure of a matrix-composite equal thickness metal composite material as claimed in claim 1, wherein: the explosive (4) is expanded ammonium nitrate explosive, the height of the explosive (4) is parallel and level with the explosive box (2), and an electric detonator (1) for detonation is arranged in the explosive (4).
8. The explosive welding construction structure of a matrix-composite equal thickness metal composite material according to claim 7, wherein: the electric detonator (1) is arranged in the middle of the longer side of the medicine box (2).
9. The explosive welding construction structure of a matrix-composite equal thickness metal composite material as claimed in claim 1, wherein: the foundation (8) is a flat foundation with a sandy soil structure.