CN211734618U

CN211734618U - Multi-component color-imitating strip grid fabric

Info

Publication number: CN211734618U
Application number: CN201921963949.6U
Authority: CN
Inventors: 钟婧; 陈红霞; 沈玲; 袁洪胜
Original assignee: Jiangsu Goldsun Textile Science and Technology Co Ltd
Current assignee: Jiangsu Goldsun Textile Science and Technology Co Ltd
Priority date: 2019-11-14
Filing date: 2019-11-14
Publication date: 2020-10-23
Anticipated expiration: 2029-11-14

Abstract

The utility model discloses a multi-component imitated yarn dyed strip lattice fabric, which is formed by interweaving warps and wefts, wherein the warps adopt three kinds of yarns, the first warps are formed by blending acrylic fibers, regenerated cellulose fibers and cotton fibers in a spinning mode of combing compact spinning, the second warps are monochromatic double-component AB yarns formed by blending the acrylic fibers and the regenerated cellulose fibers in a spinning mode of combing compact siro spinning, and the third warps are acrylic fibers; the weft yarn is one or more of the three warp yarns. The utility model discloses a surface fabric has the characteristics of the high-grade, the style classic of outward appearance, use close skin comfortable, be suitable for multiple life scene next to the shin, and production simple process, flow are short, with low costs, efficient moreover.

Description

Multi-component color-imitating strip grid fabric

Technical Field

The utility model belongs to the technical field of domestic fabrics, concretely relates to imitative look of multicomponent knitwear check surface fabric.

Background

The yarn-dyed strip-lattice fabric has rich color combinations, clear textures and decorative effects, has a classical style and a popular color system, and is popular with consumers in the fields of high-grade shirts, coats, home wear, bedding and the like. Along with the development of the coloring spinning process in recent years, the product combining the coloring spun yarn and the yarn-dyed process better meets the current simple consumption demand. However, the production period of the colored spun yarn is about 25 to 50 days generally and is longer than that of dyed yarn, so that the large-scale production is difficult and the cost is high.

At present, some fabrics adopt yarns with different dyeing properties, and form a color-imitating weaving effect after blending or interweaving. The imitative look that patent CN 208685146U disclosed weaves cotton and washes fashion surface fabric, washes the different characteristics of coloring according to the cotton, through effective collocation, forms the surface fabric of the little check shape of other utensil style through the dyeing and finishing, nevertheless because the surface fabric adopts 2 upper and lower two-sided twill organizations, therefore the third dimension is not strong, and the color level is not abundant enough, does not reach the effect of high-grade look weaving surface fabric.

The patent CN 110284241A discloses a design method and a production process of a color-imitating textile fabric, wherein purple/white nylon filaments are selected and processed into non-twisted double-color covered filaments by utilizing the principle of air covered filaments, and the color-imitating textile fabric can reduce the production cost, but the defect is similar to the existing color-weaving process, each batch needs to be dyed and then woven, and the requirements of multiple varieties, large batch and short cross period cannot be simultaneously realized.

Disclosure of Invention

The utility model aims at the not enough of above-mentioned prior art, the utility model aims at providing a multi-component imitative look knitstrip check surface fabric has the characteristics that the outward appearance is high-grade, the style is classic, use close skin comfortable next to the shin, be suitable for multiple life scene, and production simple process, flow are short moreover, with low costs, efficient.

In order to achieve the above purpose, the utility model adopts the following technical scheme:

a multi-component yarn-imitated strip-grid fabric is formed by interweaving warp yarns and weft yarns;

the warp yarns adopt three yarns, wherein:

the first warp is formed by blending acrylic fibers, regenerated cellulose fibers and cotton fibers in a spinning mode of combing compact spinning, the blending proportion of the acrylic fibers is 10-20%, the acrylic fibers are fine denier anti-pilling acrylic fibers, and the regenerated cellulose fibers are viscose, modal or tencel fibers;

the second warp is a single-color bicomponent AB yarn formed by blending acrylic fibers and regenerated cellulose fibers in a spinning mode of combing compact siro spinning, the blending proportion of the acrylic fibers is 50%, and the acrylic fibers are fine-denier anti-pilling acrylic fibers;

the third warp is acrylic fiber and is spun by a spinning mode of combing compact spinning;

the weft yarn is one or more of the three warp yarns.

Furthermore, the fabric adopts a small jacquard composite weave, the first warp and weft adopt a 4-over-1-under satin weave, the second warp and weft adopt a 4-over-1-under twill weave, and the third warp and weft adopt a 4-over-1-under weave.

Further, the yarn proportion in a single circulation of the fabric is as follows: the width of the stripe formed by the first warp yarn is 2cm-10cm, the width of the stripe formed by the second warp yarn is 0.1cm-0.3cm, and 1 warp yarn is used as the third warp yarn.

After the obtained fabric is subjected to processes of singeing, cold batch desizing, sanding (whether sanding is determined according to needs), cationic dyeing, washing, tentering and setting and the like, the dyed colors have obvious difference due to different proportions of acrylic fibers in three warp yarns and weft yarns, and the effect of yarn-dyed stripes or lattices with strong stereoscopic impression is formed.

Has the advantages that:

1. the utility model discloses a strip check surface fabric is knitted to multi-component imitative look adopts warp and woof that three kinds of different constitution, different spinning modes obtained, and the dyeing is again interweaved according to a certain proportion, and first warp forms the wide stripe of light color textile texture shading, and the second warp forms the narrow stripe of similar colored AB yarn, and the third warp forms dark suture effect, and the stripe that three kinds of warp formed has obvious difference in the aspect of colour, texture, style, and the level is clear and have the third dimension. When the weft direction adopts single yarn, the fabric is in a color woven stripe style, and when the weft direction adopts two to three kinds of yarns which are the same as those in the warp yarns, the fabric is in a color woven lattice style.

2. The fabric contains three different components of acrylic fibers, cotton and regenerated cellulose fibers, and after the fabric is dyed by adopting cationic dye, the effects of different depths are formed due to different proportions of the acrylic fibers in the three groups of yarns, and the color styles are completely differentiated due to the difference of the structures and the fabric tissues of the yarns.

3. The production process is simple, the process that the conventional yarn-dyed fabric needs dyeing yarn in each batch, warping slashing and then weaving on a machine is changed, different color effects can be achieved on the same batch of grey cloth by using different dyes, the production process is suitable for mass production, the cost of the yarn-dyed fabric is greatly reduced, and the production period is shortened.

Drawings

FIG. 1 is a single weave repeat pattern of the fabric of example 1. Wherein A is a first warp yarn part, the stripe width is 2cm-10cm, a 4-over-1-under satin weave is adopted, B is a second warp yarn part, the stripe width is 0.1cm-0.3cm, a 4-over-1-under twill weave is adopted, C is a third warp yarn part, only 1 warp yarn is used, and a 4-over-1-under weave is adopted.

Detailed Description

The utility model provides a multi-component imitative look weaving strip check surface fabric mainly interweaves after the blending through the component of three kinds of differences and forms, cooperates little jacquard weave compound tissue, forms the look after the dyeing and has obvious difference in the aspect of colour, texture, style look yarn-dyed stripe or check effect.

The specific technical scheme is as follows:

a multi-component yarn-imitated strip-grid fabric is formed by interweaving three different components after blending, wherein warp yarns adopt three different yarns, and weft yarns can adopt a single yarn or two to three different yarns.

The first warp is formed by blending acrylic fibers, regenerated cellulose fibers and cotton, wherein the acrylic fibers are fine denier anti-pilling acrylic fibers, the blending proportion is 10-20%, and the regenerated cellulose fibers are viscose, modal or tencel fibers. The spinning mode of the first warp yarn is combing compact spinning.

The second warp is formed by blending acrylic fibers and regenerated cellulose fibers, wherein the blending proportion of the fine denier anti-pilling acrylic fibers is 50%. The spinning mode is combing compact siro spinning, in the spinning process, acrylic fibers and regenerated cellulose fibers are respectively carded and drawn to form rough yarns, the two rough yarns are combined and drawn to form spun yarns, and the spun yarns are twisted to form single-color double-component AB yarns similar to the plied yarn style.

The third warp is 100% acrylic fiber, and the spinning mode is combing compact spinning.

The weft yarns can be the same as the first warp yarns to form a stripe fabric, and also can be two to three types of yarns which are the same as the warp yarns to form a lattice fabric.

The fabric adopts a small jacquard composite weave, the part of the first warp is a satin weave with the upper part and the lower part of 4, the second warp adopts a twill weave with the upper part and the lower part of 4, and the third warp adopts a weave with the upper part and the lower part of 4.

The ratio of yarns in a single circulation is: the width of the stripe formed by the first warp yarn is 2cm-10cm, the width of the stripe formed by the second warp yarn is 0.1cm-0.3cm, and only 1 warp yarn is used for the third warp yarn.

After the formed fabric is subjected to processes of singeing, cold batch desizing, sanding (whether sanding is determined according to needs), cationic dyeing, washing, tentering and setting and the like, the dyed colors have obvious difference due to different proportions of acrylic fibers in three warp yarns or weft yarns, and the effect of yarn-dyed stripes or lattices with strong stereoscopic impression is formed.

The technical solution of the present invention will be further explained with reference to the following embodiments.

Example 1

The first warp is blended by acrylic fibers, viscose and cotton, wherein the acrylic fibers adopt fine denier anti-pilling acrylic fibers, the blending proportion is viscose/cotton/acrylic fibers 50/40/10, the yarn count is 32s, and the spinning mode is combing compact spinning.

The second warp is formed by blending acrylic fibers and viscose glue, the blending proportion is fine denier anti-pilling acrylic fibers/viscose glue 50/50AB yarn, the yarn count is 32s, and the spinning mode is combing compact siro spinning.

The third warp is 100% acrylic fiber, the yarn count is 32s, and the spinning mode is combing compact spinning.

The weft yarns were spun using the same viscose/cotton/nitrile 50/40/10 combed compact spun 32s as the first warp yarns.

The fabric adopts a small jacquard composite weave, the part of the first warp is a satin weave with the upper part and the lower part of 4, the second warp adopts a twill weave with the upper part and the lower part of 4, and the third warp adopts a weave with the upper part and the lower part of 4. The grey fabric density was 133 x 76.

The ratio of yarns in a single circulation is: the width of the stripe formed by the first warp yarn is 2cm, the width of the stripe formed by the second warp yarn is 0.1cm, and only 1 warp yarn is used for the third warp yarn.

The formed fabric is subjected to processes of singeing, cold-batch desizing, cationic dyeing, washing, tentering and shaping and the like to form colored woven texture and suture style yarn-dyed fine stripe effects. The finished fabric has 3-4 grades of fuzzing and pilling, the warp-direction strength 418N, the weft-direction strength 322N, the warp-direction shrinkage rate of-3.3 percent and the weft-direction shrinkage rate of-2.6 percent, and meets the requirements of bedding fabrics.

Example 2

The difference from the embodiment 1 is that the blending ratio, the yarn count density and the after-finishing process are different, and the final effect is that the style and the hand feeling of the formed fabric are different.

The first warp yarn adopts 21s modal/cotton/fine denier anti-pilling acrylic fibers 40/40/20, the spinning mode is combed compact spinning, the second warp yarn adopts 21s fine denier anti-pilling acrylic fibers/modal 50/50 combed compact spinning siro AB yarn, the third warp yarn is 21s acrylic fibers, and the spinning mode is combed compact spinning. The grey fabric density was 78 x 62. The ratio of yarns in a single circulation is: the width of the stripe formed by the first warp yarn was 10cm, the width of the stripe formed by the second warp yarn was 0.3cm, and only 1 warp yarn was used for the third warp yarn.

The weft yarns adopt three yarns with the same components, and the proportion in a single circulation is the same. The first weft adopts 21s modal/cotton/fine denier anti-pilling acrylic fibers 40/40/20, the spinning mode is combed compact spinning, the second weft adopts 21s fine denier anti-pilling acrylic fibers/modal 50/50 combed compact spinning siro AB yarns, the third weft is 21s acrylic fibers, and the spinning mode is combed compact spinning.

The yarn-dyed plaid style fabric with plump velvet feeling, thickness and warmth retention is formed after sanding and dyeing processes.

Comparative example 1

The difference from example 1 is that the weave structure of the fabric is different, and the final effect is that the style of the formed fabric is obviously different.

The first warp yarn adopts 32s viscose/cotton/fine denier anti-pilling acrylic fibers 50/40/10, the spinning mode is combed compact spinning, the second warp yarn adopts 32s viscose/cotton/fine denier anti-pilling acrylic fibers 50/40/10 combed compact spinning siro AB yarn, the third warp yarn is 32s acrylic fibers, and the spinning mode is combed compact spinning. The weft yarn was 32s viscose/cotton/fine denier anti-pilling acrylic 50/40/10. The grey fabric density was 133 x 76. The weave was 4/1 satin.

The finally formed fabric has stripes in the warp direction, but does not have distinct yarn-dyed effect.

Comparative example 2

The difference from example 1 is that only one yarn is used, and the final effect is that the style of the formed fabric is obviously different.

The warp and weft all adopt 32s viscose/cotton/fine denier anti-pilling acrylic fibers 50/40/10, the spinning mode is combing compact spinning, and the density of grey cloth is 133 × 76. The jacquard weaving method is characterized in that a small jacquard composite weave is adopted, the part of a first warp is a satin weave with an upper portion and a lower portion of 4, the second warp is a twill weave with an upper portion and a lower portion of 4, and the third warp is a twill weave with an upper portion and a lower portion of 4. The ratio of yarns in a single circulation is: the width of the stripe formed by the first warp yarn is 2cm, the width of the stripe formed by the second warp yarn is 0.1cm, and only 1 warp yarn is used for the third warp yarn.

The finally formed fabric is dyed to have colored woven shading without layering, and has no obvious yarn-dyed stripe or lattice effect.

According to the upper table, the utility model discloses a surface fabric through adopt three kinds of different compositions, warp and woof that different spinning modes obtained, weaves the dyeing again after interweaving according to certain proportion, and the stripe that three kinds of warp formed has obvious difference in the aspect of colour, texture, style, and the level is clear and there is the third dimension. When the weft direction adopts single yarn, the fabric is in a color woven stripe style, and when the weft direction adopts two to three kinds of yarns which are the same as those in the warp yarns, the fabric is in a color woven lattice style.

Claims

1. The multi-component yarn-dyed strip-lattice-like fabric is formed by interweaving warp yarns and weft yarns, and is characterized in that:

the warp yarns adopt three yarns, wherein:

the weft yarn is one or more of three warp yarns;

the fabric adopts a small jacquard composite weave, the first warp and weft adopt a satin weave with the number of 4 from top to bottom, the second warp and weft adopt a twill weave with the number of 4 from top to bottom, and the third warp and weft adopt a weave with the number of 4 from top to bottom;

the yarn proportion in a single circulation of the fabric is as follows: the width of the stripe formed by the first warp yarn is 2cm-10cm, the width of the stripe formed by the second warp yarn is 0.1cm-0.3cm, and 1 warp yarn is used as the third warp yarn.