CN211547064U - Steel wire cord for semisteel meridian - Google Patents
Steel wire cord for semisteel meridian Download PDFInfo
- Publication number
- CN211547064U CN211547064U CN201920878522.XU CN201920878522U CN211547064U CN 211547064 U CN211547064 U CN 211547064U CN 201920878522 U CN201920878522 U CN 201920878522U CN 211547064 U CN211547064 U CN 211547064U
- Authority
- CN
- China
- Prior art keywords
- steel cord
- cord
- steel
- tire
- reduce
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The utility model provides a steel cord for semisteel meridian, the carbon content of the single wire of the steel cord is 0.91-0.93%, the chromium content is 0.15% -0.30%, the lay length of the single wire is 13-15mm, and the diameter of the single wire is 0.24-0.25 mm. Steel cord, can reduce curtain cloth thickness when satisfying operation requirement, alleviate the interior steel wire weight of curtain cloth, reduce the interior rubber use amount of curtain cloth, reduce curtain cloth total weight. Steel cord can improve the fatigue resistance ability of tire, increase and renovate the number of times, realize the tire lightweight, reduce rolling resistance, improve tire comprehensive properties to can reduce producer and user use cost, accord with the new requirement of the energy-concerving and environment-protective of tire.
Description
Technical Field
The utility model belongs to the technical field of the steel cord is made, concretely relates to steel cord for semisteel meridian.
Background
Steel cords are widely used in rubber products such as automobile tires, conveyor belts, high-pressure hoses, etc., and are required to have good strength, toughness, fatigue resistance, rubber permeability, adhesion, etc., as reinforcing materials for rubber products. The steel cord is mainly used as a reinforcing material of automobile tires, and can be made into steel cord fabric for use or directly used for a tire body. The steel cord used for semi-steel meridian generally has structures of n x 1, m + n, etc., and they generally consist of two or more steel wires, however, the more steel cords and rubber are needed to achieve a certain strength by twisting the two or more steel wires together, and the production cost is large.
SUMMERY OF THE UTILITY MODEL
The utility model discloses a solve the big problem of high strength semisteel meridian steel cord and rubber quantity, developed a semisteel meridian steel cord, steel cord can improve the fatigue resistance ability of tire, increase and renovate the number of times, realize the tire lightweight, reduce rolling resistance, improve tire comprehensive properties to can reduce producer and user use cost, accord with the new requirement of tire energy-concerving and environment-protective.
The utility model adopts the technical scheme that: a steel cord for semi-steel meridian, the linear density of the steel cord is 3.0-4.0g/m, the carbon content of the monofilament is 0.91-0.93%, and the chromium content is 0.15% -0.30%.
The further monofilament lay length is 13-15 mm.
The further filaments have a diameter of 0.24-0.25 mm.
Further steel cord breaking force 330-.
The steel cord monofilament of the utility model contains a certain amount of carbon element and chromium element, and the quenching strength can be further improved. Steel cord be arranged in radial tire matrix or belted layer, can improve the fatigue resistance ability of tire by a wide margin, can reduce the use of steel cord and sizing material, realize the tire lightweight, reduce rolling resistance, improve tire comprehensive properties to can reduce use cost, accord with the new requirement of tire energy-concerving and environment-protective.
Drawings
Fig. 1 is a cross-sectional view of the steel cord of the present invention.
Detailed Description
In order to facilitate understanding of the present invention, the present invention will be described more fully hereinafter with reference to the accompanying drawings. The preferred embodiments of the present invention are shown in the drawings. The invention may, however, be embodied in many different forms and should not be construed as limited to the embodiments set forth herein. Rather, these embodiments are provided so that this disclosure will be thorough and complete.
The invention is further described with reference to the accompanying drawings and specific embodiments.
Example 1
A steel cord for a semisteel meridian, the linear density of the steel cord is 3.0g/m, the carbon content of a monofilament is 0.91%, the chromium content is 0.15%, the lay length of the monofilament is 13mm, the diameter of the monofilament is 0.24mm, and the breaking force of the steel cord is 330N. The cord fabric data produced with this steel cord is as follows:
item | Numerical value |
Lay length of steel cord | 13mm |
Number of cord threads | 1 root of Chinese thorowax |
Breaking force | 330N |
Linear density of | 3.73g/m |
Breaking force of cord fabric | 4200N/dm |
Thickness of cord fabric | 1.3mm |
Weight of steel wire in each cord | 448g |
Volume of steel wire in each block of cord fabric | 57cm3 |
Volume of rubber in each block of cord fabric | 1243cm3 |
Weight of rubber in each cord fabric | 1429g |
Total weight of cord fabric | 1877g |
Example 2
A steel cord for semi-steel meridian with a linear density of 3.5g/mThe carbon content of the filament is 0.92 percent, the chromium content is 0.2 percent, the further filament lay length is 14mm, the filament diameter is 0.245mm, and the breaking force of the steel cord is 350N. The cord fabric data produced with this steel cord is as follows:
item | Numerical value |
Lay length of steel cord | 14mm |
Number of cord threads | 1 root of Chinese thorowax |
Breaking force | 350N |
Linear density of | 3.73g/m |
Breaking force of cord fabric | 4200N/dm |
Thickness of cord fabric | 1.5mm |
Weight of steel wire in each cord | 400g |
Volume of steel wire in each block of cord fabric | 56cm3 |
Volume of rubber in each block of cord fabric | 1200cm3 |
Weight of rubber in each cord fabric | 1430g |
Total weight of cord fabric | 1830g |
Example 3
A steel cord for a semisteel meridian, the linear density of the steel cord is 4.0g/m, the carbon content of a monofilament is 0.93%, the chromium content is 0.30%, the further monofilament lay length is 15mm, the monofilament diameter is 0.25mm, and the breaking force of the steel cord is 400N. The cord fabric data produced with this steel cord is as follows:
item | Numerical value |
Lay length of steel cord | 15mm |
Number of cord threads | 1 root of Chinese thorowax |
Breaking force | 400N |
Linear density of | 3.75g/m |
Breaking force of cord fabric | 4200N/dm |
Thickness of cord fabric | 1.3mm |
Weight of steel wire in each cord | 458g |
Volume of steel wire in each block of cord fabric | 50cm3 |
Volume of rubber in each block of cord fabric | 1230cm3 |
Weight of rubber in each cord fabric | 1439g |
Total weight of cord fabric | 1907g |
In the description herein, references to the description of "one embodiment," "an example," or "some examples," etc., mean that a particular feature, structure, material, or characteristic described in connection with the embodiment or example is included in at least one embodiment or example of the invention. In this specification, the schematic representations of the terms used above do not necessarily refer to the same embodiment or example. Furthermore, the particular features, structures, materials, or characteristics described may be combined in any suitable manner in any one or more embodiments or examples.
While embodiments of the present invention have been shown and described, it will be understood by those of ordinary skill in the art that: various changes, modifications, substitutions and alterations can be made to the embodiments without departing from the principles and spirit of the invention, the scope of which is defined by the claims and their equivalents.
Claims (1)
1. A steel cord for semi-steel meridian is characterized in that the steel cord is composed of two monofilaments, the monofilament lay length is 13-15mm, the monofilament diameter is 0.24-0.25mm, the linear density of the steel cord is 3.0-4.0g/m, and the breaking force of the steel cord is 330-.