CN211007386U

CN211007386U - Quartz seamless wall cloth

Info

Publication number: CN211007386U
Application number: CN201921792954.5U
Authority: CN
Inventors: 梁根通
Original assignee: Ningbo Liangshifu New Material Technology Co ltd
Current assignee: Ningbo Liangshifu New Material Technology Co ltd
Priority date: 2019-10-23
Filing date: 2019-10-23
Publication date: 2020-07-14
Anticipated expiration: 2029-10-23

Abstract

The application discloses quartz seamless wall cloth which comprises a bonding layer a, a Kelon cloth bottom layer, a bonding layer b and a common cloth surface layer, wherein the common cloth surface layer is bonded on the Kelon cloth bottom layer through the bonding layer b, the Kelon cloth bottom layer is bonded on the surface of a wall body through the bonding layer a, the thickness of the bonding layer a is m1, the thickness of the Kelon cloth bottom layer is m2, the thickness of the bonding layer b is m3, the thickness of the common cloth surface layer is m4, and the value of 0 & lt m3 & lt m4 & lt m1 & lt m2 & lt 200 mu m. The utility model also discloses a preparation method of above-mentioned quartzy seamless wallhanging. The utility model discloses the seamless wallhanging of quartz that the preparation obtained is not only pleasing to the eye, and has excellent fire prevention and mould proof performance, and surface feel is good.

Description

Quartz seamless wall cloth

Technical Field

The utility model relates to a ornamental material's technical field especially relates to a quartzy seamless wallhanging.

Background

The quartz wall cloth is a decorative wall cloth made of glass fiber through special processing and weaving, the main component of the quartz wall cloth is silicon oxide, and the quartz wall cloth belongs to a novel inorganic decorative material.

The quartz wall cloth has high strength, and can play a role in reinforcing the wall surface and preventing cracking when being used for indoor decoration; especially, the base layer is the wall surface of the plywood, the gap between the plywood and the board needs special reinforcement treatment to prevent cracking, and the quartz wall cloth does not need special treatment and never cracks.

The quartz wallcovering has wide and narrow range and can be matched at will during construction. Because the decorative cloth has clear weave, beautiful patterns, rich texture, distinct layers, strong third dimension and good air permeability, the decorative cloth has good sound absorption and sound insulation effects and soft visual effect, is high-grade and elegant, and is particularly suitable for office and residential decoration

The quartz wall cloth is firm and durable, does not deform, does not mildew or rot, is resistant to cleaning, can be freely changed in outer coating, and has long service life.

The Chinese patent application document "an inner wall decoration structure (application publication No. CN 202990305U) combining quartz fiber wall cloth and paint" discloses an inner wall decoration structure combining quartz fiber wall cloth and paint, which is characterized in that: the inner surface of the wall body is sequentially provided with a bonding layer, a quartz fiber wall cloth layer and a coating layer. The coating layer adopts semi-gloss building coating. The advantages are that the quartz fiber wall cloth is adopted as the substrate, so that the texture, the pattern, the crack resistance, the impact resistance and the like can be provided. The semi-gloss architectural coating is adopted for decorating the surface, the color is rich, and the texture and the patterns of the quartz fiber wall cloth can be displayed. If one color needs to be changed, only one coating needs to be recoated, which is very convenient. The inner wall decoration structure combining the quartz fiber wall cloth and the coating not only has various texture, patterns and colors required by decoration, but also has good crack resistance, impact resistance and durability. But the adhesion performance between the coating and the wall body can not meet the requirements of actual use, the adhesion performance is poor, the coating is easy to mildew and fall off in a humid area, the fireproof performance can not meet the requirements of actual use, furthermore, the coating is adopted, the formaldehyde content can exceed the standard inevitably, and the requirement of environmental protection can not be met.

Most of the quartz wallcoverings on the market at present are rough in surface and poor in attractiveness, and the bottom surfaces of the quartz wallcoverings are made of paper and seamless cloth, so that the quartz wallcoverings are poor in adhesion with a wall body when in use, and the fireproof performance, the air permeability and the mildew-proof effect cannot meet the requirements of actual use.

SUMMERY OF THE UTILITY MODEL

The technical problem to be solved in the utility model is to overcome the not enough of prior art and provide a quartzy seamless wallhanging that has excellent cohesiveness, aesthetic property, gas permeability and fire proofness.

Solve the technical problem, the utility model discloses take following technical scheme:

a quartz seamless wall cloth comprises a bonding layer a, a Dacron cloth bottom layer, a bonding layer b and a common cloth surface layer, wherein the common cloth surface layer is bonded on the Dacron cloth bottom layer through the bonding layer b, the Dacron cloth bottom layer is bonded on the surface of a wall body through the bonding layer a, the thickness of the bonding layer a is m1, the thickness of the Dacron cloth bottom layer is m2, the thickness of the bonding layer b is m3, the thickness of the common cloth surface layer is m4, the thickness of the common cloth surface layer is more than 0 and more than m3 and more than m4 and more than m1 and more than m2 and less than.

In the embodiment of the utility model, m2 is not less than 150 μm and not more than 200 μm.

In the embodiment of the present invention, m3 ═ 20 μm, m4 ═ 30 μm, m1 ═ 150 μm, and m2 ═ 175 μm.

In the embodiment of the present invention, the bottom layer of the terylene cloth is provided with a plurality of elastic rubber particles.

In the embodiment of the utility model, the diameter of the elastic rubber particles is m5, and 0 < m5 < 50 μm.

In the embodiment of the present invention, the elastic rubber strips in the terylene cloth base layer are distributed along the length direction of the terylene cloth base layer at equal intervals, and the terylene cloth base layer with the elastic rubber strips is connected with the threading rubber strips.

In the embodiment of the utility model provides an in, elasticity adhesive tape is the S-shaped cylinder adhesive tape that the external diameter is 10 mu m, and the threading adhesive tape is the cylinder adhesive tape that the external diameter is 6 mu m, and the threading adhesive tape runs through the elasticity adhesive tape setting.

The utility model has the advantages that: the structure of the quartz seamless wall cloth of the utility model adopts the terylene cloth bottom layer, the adhesive layer b and the common cloth surface layer which are sequentially the adhesive layer a, the terylene cloth bottom layer and the adhesive layer b from the bottom layer to the surface, one side close to the wall body is adhered on the wall body through the adhesive layer a, the terylene cloth bottom layer is mainly composed of quartz, the quartz is inorganic matter, the main component of the wall body is also inorganic matter, the adhesion strength is greatly improved by the adhesive layer a, the falling of the quartz seamless wall cloth can be effectively prevented, in addition, the quartz realizes better fireproof and air permeability of the quartz seamless wall cloth when the main component of the terylene cloth bottom layer is adopted, and the surface of the quartz seamless wall cloth of the utility model adopts the common cloth surface layer, which not only has good fireproof performance, but also has good texture and texture, and improves the high-grade feeling of the quartz seamless wall cloth, in addition, the thickness through the dacron bottom of guaranteeing is last one deck, can effectively guarantee the utility model discloses a fire resistance of quartzy seamless wallhanging has also kept the better ventilative and mould proof effect of quartzy seamless wallhanging in addition.

Other features and advantages of the present invention will be disclosed in more detail in the following detailed description and the accompanying drawings.

Drawings

FIG. 1 is a schematic structural diagram of a quartz seamless wall cloth of example 1 of the present invention;

FIG. 2 is an enlarged partial schematic view at A of FIG. 1;

FIG. 3 is a schematic structural view of the quartz seamless wallcovering of example 2 of the invention;

FIG. 4 is an enlarged partial schematic view at B of FIG. 3;

FIG. 5 is a schematic structural diagram of the quartz seamless wallcovering of example 3 of the invention;

fig. 6 is a partially enlarged schematic view at C in fig. 5.

The figures are numbered:

1. an adhesive layer a; 2. the bottom layer of the terylene cloth; 3. an adhesive layer b; 4. the surface layer of the terylene cloth; 5. a wall body; 6. elastic rubber particles; 7. an elastic rubber strip; 8. threading adhesive tape.

Detailed Description

The technical solutions of the embodiments of the present invention are explained and explained below with reference to the drawings of the embodiments of the present invention, but the embodiments described below are only preferred embodiments of the present invention, and not all embodiments. Based on the embodiments in the embodiment, other embodiments obtained by those skilled in the art without any creative work belong to the protection scope of the present invention.

In the following description, the appearances of the indicating orientation or positional relationship, such as the terms "inner", "outer", "upper", "lower", "left", "right", etc., are only for convenience in describing the embodiments and for simplicity of description, and do not indicate or imply that the device or element being referred to must have a particular orientation, be constructed and operated in a particular orientation, and are not to be construed as limiting the invention.

Example 1:

a quartz seamless wall cloth comprises a bonding layer a1, a Dacron cloth bottom layer 2, a bonding layer b3 and a common cloth surface layer 4, wherein the common cloth surface layer 4 is bonded on the Dacron cloth bottom layer 2 through a bonding layer b3, the Dacron cloth bottom layer 2 is bonded on the surface of a wall body 5 through a bonding layer a1, the thickness of the bonding layer a1 is m1, the thickness of the Dacron cloth bottom layer 2 is m2, the thickness of the bonding layer b3 is m3, the thickness of the common cloth surface layer 4 is m4, the thickness of the common cloth surface layer 4 is more than 0 and more than m3 and more than m4 and more than m1 and more than m2 and less. Specifically, in the present embodiment, 150 μm. ltoreq. m 2. ltoreq.200. mu.m.

More specifically, m3 ═ 20 μm, m4 ═ 30 μm, m1 ═ 150 μm, and m2 ═ 175 μm.

In the embodiment of the utility model, the ordinary cloth surface layer is formed by weaving cotton cloth and silk.

The preparation method of the quartz seamless wall cloth comprises the following steps: adhering the common cloth surface layer 4 to one side of the terylene cloth bottom layer 2 through an adhesive layer b3, drying and shaping, and finally brushing an adhesive layer a1 on the other side of the terylene cloth bottom layer 2 to adhere to one side of the wall body 5, wherein the adhesive layer a1 and the adhesive layer b3 both adopt BY-101 emulsion. The terylene cloth bottom layer 2 is prepared by the following process: melting 100 parts of quartz by weight, adding 50 parts of glass fiber yarn, 11.5 parts of nano aluminum powder, 6.5 parts of nano aluminum powder, 3.5 parts of nano carbon fiber, 9 parts of bamboo residue powder and 5.5 parts of diethylene glycol monoacrylic acid, uniformly mixing, heating to 130 ℃, preserving heat for 30min, weaving after bulking deformation and warping, and finally dip-coating and curing to obtain the composite material.

Example 2:

referring to fig. 3 to 4, the present embodiment is different from embodiment 1 in that a plurality of elastic rubber particles 6 are provided in the nylon fabric base layer 2. So set up, the better elasticity of dacron bottom 2 that can guarantee can let whole quartzy seamless wallhanging bond to the wall body after, and the surface compliance is better, and the feel and the sense of touch of product are better.

In the embodiment of the utility model, the ordinary cloth top layer is woven by cotton cloth and burlap.

In this example, the diameter of the elastic rubber particles 6 was m5, 0 < m5 < 50 μm.

It is understood that the elastic rubber particle 6 is an elastic rubber particle made of polylactic acid.

Example 3:

referring to fig. 5 and 6, the present embodiment is different from embodiment 1 in that elastic tapes 7 are disposed in the nylon fabric base layer 2, the elastic tapes 7 are disposed at equal intervals along the length direction of the nylon fabric base layer 2, and a threading tape 8 is connected to the elastic tape 7 and the nylon fabric base layer 2. The elastic rubber strip 7 is an S-shaped cylindrical rubber strip with the outer diameter of 10 micrometers, the threading rubber strip 8 is a cylindrical rubber strip with the outer diameter of 6 micrometers, and the threading rubber strip 8 penetrates through the elastic rubber strip 7. According to the arrangement, the elastic rubber strips 7 are fixed in the Dacron fabric bottom layer 2 through the threading rubber strips 8, and the elastic rubber strips 7 are distributed along the Dacron fabric bottom layer 2 at equal intervals in the length direction, so that the elasticity and the strength of the Dacron fabric bottom layer 2 in use can be effectively improved, the whole quartz seamless wall cloth can be bonded to a wall body, the surface flexibility is better, and the texture and the touch feeling of a product are better.

In the embodiment of the utility model, the ordinary cloth top layer is formed by silk and wool fabric weaving.

It will be appreciated that the elastic strip 7 and the threading strip 8 are both made of polylactic acid. The polylactic acid has good biocompatibility, excellent fireproof, mildewproof and antibacterial effects, excellent mechanical strength and can meet the requirements of quartz seamless wallcoverings in use.

Example 4

The difference between this example and example 1 is that the nylon fabric bottom layer 2 is prepared according to the following process: melting 80 parts of quartz by weight, adding 60 parts of glass fiber yarn, 8 parts of nano aluminum powder, 9 parts of nano aluminum powder, 2 parts of nano carbon fiber, 12 parts of bamboo residue powder and 3 parts of diethylene glycol monoacrylic acid, uniformly mixing, heating to 140 ℃, preserving heat for 20min, then weaving after bulking deformation and warping, finally dip-coating and curing to obtain the composite material.

Example 5

The difference between this example and example 1 is that the nylon fabric bottom layer 2 is prepared according to the following process: melting 120 parts of quartz by weight, adding 40 parts of glass fiber yarn, 15 parts of nano aluminum powder, 4 parts of nano aluminum powder, 5 parts of nano carbon fiber, 6 parts of bamboo slag powder and 8 parts of diethylene glycol monoacrylic acid, uniformly mixing, heating to 120 ℃, preserving heat for 40min, then weaving after bulking deformation and warping, finally dip-coating and curing to obtain the product.

Comparative example

The quartz seamless wall cloth of the embodiment in the Chinese patent application document 'an inner wall decoration structure (application publication number: CN 202990305U) combining quartz fiber wall cloth and paint'.

The performance tests of the quartz seamless wall coverings of examples 1-5 and comparative example were carried out, and the data obtained were as follows:

note: the method for testing the anti-dropping performance comprises the following steps: after the quartz seamless wall cloth is pasted on a wall, the quartz seamless wall cloth is naturally dried for 2 weeks, and the situation of whether the edge is warped is observed after 6 months.

Principle analysis: the structure of the quartz seamless wall cloth of the utility model adopts the terylene cloth bottom layer, the adhesive layer b and the common cloth surface layer which are sequentially the adhesive layer a, the terylene cloth bottom layer and the adhesive layer b from the bottom layer to the surface, one side close to the wall body is adhered on the wall body through the adhesive layer a, the terylene cloth bottom layer is mainly composed of quartz, the quartz is inorganic matter, the main component of the wall body is also inorganic matter, the adhesion strength is greatly improved by the adhesive layer a, the falling of the quartz seamless wall cloth can be effectively prevented, in addition, the quartz realizes better fireproof and air permeability of the quartz seamless wall cloth when the main component of the terylene cloth bottom layer is adopted, and the surface of the quartz seamless wall cloth of the utility model adopts the common cloth surface layer, which not only has good fireproof performance, but also has good texture and texture, and improves the high-grade feeling of the quartz seamless wall cloth, in addition, the thickness through the dacron bottom of guaranteeing is last one deck, can effectively guarantee the utility model discloses a fire resistance of quartzy seamless wallhanging has also kept the better ventilative and mould proof effect of quartzy seamless wallhanging in addition.

In addition, the bottom layer of the terylene cloth adopts quartz as a raw material, the quartz is melted and then added with glass fiber yarn, nano aluminum powder, nano carbon fiber, bamboo slag powder and diethylene glycol monoacrylate, wherein the diethylene glycol monoacrylate is grafted to the surface of the quartz, so that the dispersion stability of the diethylene glycol monoacrylate in the quartz can be improved, the added nano aluminum powder has the same amount as that of the diethylene glycol monoacrylate, the diethylene glycol monoacrylate needs to be grafted with the surface of the quartz material in the preparation process, in the grafting process, the nano aluminum powder has the same amount as that of the diethylene glycol monoacrylate, and the hydroxyl of the diethylene glycol monoacrylate losing the hydroxyl needs to be supplemented by the nano aluminum powder, so that the contact area among the nano aluminum powder, the nano carbon fiber and the bamboo slag powder is increased, and the nano aluminum powder, the nano carbon fiber and the bamboo slag powder form a heat, the thermal conductivity of the material is greatly improved, the added nano carbon fiber and bamboo slag powder further compensate the hydroxyl content of the system so as to realize the grafting modification of the diethylene glycol monoacrylate on the surface of the quartz material, and due to the heat conduction performance of the quartz material, the heat generated in the quartz material under the conditions of light and the like can be effectively transferred, so that the thermal stability of the quartz material is improved; the prepared diethylene glycol monoacrylate modified quartz has the function of improving the thermal stability of quartz, so that the fireproof performance of the quartz material can be improved.

The above only is the preferred embodiment of the present invention, not therefore the limit the patent protection scope of the present invention, all applications the equivalent structure transformation made by the contents of the specification and the drawings of the present invention is directly or indirectly applied to other related technical fields, and all the same principles are included in the protection scope of the present invention.

Claims

1. The quartz seamless wall cloth is characterized by comprising a Kelon cloth bottom layer, a bonding layer b and a common cloth surface layer, wherein the common cloth surface layer is bonded on the Kelon cloth bottom layer through the bonding layer b, the Kelon cloth bottom layer is bonded on the wall surface through the bonding layer a, the thickness of the bonding layer a is m1, the thickness of the Kelon cloth bottom layer is m2, the thickness of the bonding layer b is m3, the thickness of the common cloth surface layer is m4, and the value of 0 & lt m3 & lt m4 & lt m1 & lt m2 & lt 200 mu m.

2. The quartz seamless wall cloth according to claim 1, wherein 150 μm2 m 200 μm.

3. The quartz seamless wall cloth according to claim 2, wherein m 3-20 μm, m 4-30 μm, m 1-150 μm, and m 2-175 μm.

4. The quartz seamless wall cloth of claim 1, wherein the nylon fabric base layer has a plurality of elastomeric rubber particles disposed therein.

5. The quartz seamless wall cloth according to claim 4, wherein the elastic rubber grains have a diameter of m5, 0 < m5 < 50 μm.

6. The quartz seamless wall cloth according to claim 1, wherein the elastic tapes are arranged in the nylon fabric bottom layer at equal intervals along the length direction of the nylon fabric bottom layer, and the elastic tapes are connected with the nylon fabric bottom layer by threading tapes.

7. The quartz seamless wall cloth according to claim 6, wherein the elastic rubber strip is an S-shaped cylindrical rubber strip with an outer diameter of 10 μm, the threading rubber strip is a cylindrical rubber strip with an outer diameter of 6 μm, and the threading rubber strip is arranged through the elastic rubber strip.