CN209538597U - A kind of floor structure containing basalt fibre coating - Google Patents
A kind of floor structure containing basalt fibre coating Download PDFInfo
- Publication number
- CN209538597U CN209538597U CN201920013625.XU CN201920013625U CN209538597U CN 209538597 U CN209538597 U CN 209538597U CN 201920013625 U CN201920013625 U CN 201920013625U CN 209538597 U CN209538597 U CN 209538597U
- Authority
- CN
- China
- Prior art keywords
- water
- base
- layer
- epoxy
- base epoxy
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The utility model discloses a kind of floor structures containing basalt fibre coating, belong to floor field, a kind of floor structure containing basalt fibre coating disclosed by the utility model, including terrace base, water-base epoxy plane paint layer；Water-base epoxy plane paint layer lower surface is Nian Jie with terrace base upper surface, several anti-crack fibers are provided in water-base epoxy plane paint layer, anti-crack fiber is random to be interspersed in water-base epoxy plane paint layer, and part anti-crack fiber exposes water-base epoxy plane paint layer lower surface and terrace base adhesive.By adding anti-crack fiber in water-base epoxy plane paint layer, increase the intensity between water-base epoxy plane paint layer, reinforce the tensile strength between water-base epoxy plane paint layer and terrace base simultaneously, so that water-base epoxy plane paint is not easy to crack, improves quality and service life.
Description
Technical field
The utility model relates to floor field more particularly to a kind of floor structures containing basalt fibre coating.
Background technique
Basalt fibre is the glass fibre drawn with natural basalt.It is that basalt building stones are molten at 1450 DEG C ~ 1500 DEG C
After melting, pass through continuous fiber made of platinum-rhodium alloy bushing high speed pulling.The color of pure natural basalt fibre is generally
Brown, some are like golden.Basalt fibre is a kind of novel inorganic environment-friendly and green high performance fibre material, it is by titanium dioxide
The oxides such as silicon, aluminium oxide, calcium oxide, magnesia, iron oxide and titanium dioxide composition basalt building stones after high-temperature fusion,
By made of bushing Defect.Not only intensity is high for basalt continuous fiber, but also has and be electrically insulated, is corrosion-resistant, resistance to height
A variety of excellent properties such as temperature.In addition, the production technology of basalt fibre determines that the waste of generation is few, environmental pollution is small,
And can directly degrade in the environment after product abandonment, it without any harm, thus is the qualified green of one kind, environment-friendly materials.
A kind of basalt fiber cloth reinforced epoxy terrace disclosed in Chinese patent literature publication number CN203669295U.The ring
Oxygen terrace is at least fitted with one group of enhancement layer in base layer side, and the other side of enhancement layer is fitted with coating, and enhancement layer includes
Adjacent epoxy coating and basalt fibre layer of cloth, and epoxy coating is positioned close to base layer side.Basalt
Scrim cloth by being made up of basalt fiber cloth made of basalt fibre weaving yarns, the basalt fiber cloth through Xiang Midu
For 40~50/10cm, latitudinal density is 50~60/10cm.
Existing terrace be easy to cause terrace to crack since base course crack or paint layer from surface are there are rift defect etc., from
And terrace damage is caused to influence to use.
Summary of the invention
In order to overcome the drawbacks of the prior art, a kind of containing profound the technical problem to be solved by the utility model is to propose
The floor structure of military rock fiber coating, by adding anti-crack fiber in water-base epoxy plane paint layer, so that water-base epoxy plane
Paint not easy to crack, raising quality and service life.
For this purpose, the utility model uses following technical scheme:
A kind of floor structure containing basalt fibre coating provided by the utility model, including terrace base, aqueous ring
Oxygen plane paint layer；Water-base epoxy plane paint layer lower surface is Nian Jie with terrace base upper surface, setting in water-base epoxy plane paint layer
There are several anti-crack fibers, anti-crack fiber is random to be interspersed in water-base epoxy plane paint layer, and part anti-crack fiber exposes
Water-base epoxy plane paint layer lower surface and terrace base adhesive.
The utility model preferably technical solution is that anti-crack fiber is times of basalt fibre or polypropylene anti-crack fiber
It is a kind of.
The utility model preferably technical solution is that anti-crack fiber length is 0.5cm-3cm.
The utility model preferably technical solution is that anti-crack fiber diameter is 0.1mm-2mm.
The utility model preferably technical solution is that terrace base includes cement basic layer, water-base epoxy infiltration priming paint, ring
Oxygen screed, putty layer；The upper surface of cement basic layer and water-base epoxy permeate priming paint lower surface bonds, and water-base epoxy permeates priming paint
Upper surface and epoxy resin mortar layer lower surface bonds, epoxy resin mortar layer upper surface and putty layer lower surface bonds, putty layer upper surface
It is Nian Jie with water-base epoxy plane paint layer.
The utility model preferably technical solution is that cement basic layer upper surface is rough frosted structure.
The utility model has the following beneficial effects: a kind of terrace knot containing basalt fibre coating provided by the utility model
Structure, including terrace base, water-base epoxy plane paint layer；Water-base epoxy plane paint layer lower surface is Nian Jie with terrace base upper surface,
Several anti-crack fibers are provided in water-base epoxy plane paint layer, anti-crack fiber is random to be interspersed in water-base epoxy plane paint layer
In, and part anti-crack fiber exposes water-base epoxy plane paint layer lower surface and terrace base adhesive.By in water-base epoxy plane
Add anti-crack fiber in paint layer, increase the intensity between water-base epoxy plane paint layer, at the same reinforce water-base epoxy plane paint layer with
Tensile strength between terrace base improves quality and service life so that water-base epoxy plane paint is not easy to crack.
Detailed description of the invention
Fig. 1 is the floor structure signal containing basalt fibre coating provided in specific embodiment of the present invention
Figure；In figure: 1, water-base epoxy plane paint layer；11, anti-crack fiber；2, terrace base；21, water-base epoxy permeates priming paint；22, epoxy
Screed；23, putty layer；24, cement basic layer.
Specific embodiment
Further illustrate the technical solution of the utility model below with reference to the accompanying drawings and specific embodiments.
As shown in Figure 1, a kind of floor structure containing basalt fibre coating provided in the present embodiment, including terrace base
Layer 2, water-base epoxy plane paint layer 1；1 lower surface of water-base epoxy plane paint layer is Nian Jie with 2 upper surface of terrace base, and water-base epoxy is flat
Several anti-crack fibers 11 are provided in top coat layer 1, anti-crack fiber 11 is random to be interspersed in water-base epoxy plane paint layer 1,
And the exposing of part anti-crack fiber 11 1 lower surface of water-base epoxy plane paint layer is Nian Jie with terrace base 2.By the way that anti-crack fiber 11 is mixed
Enter in 1 raw material of water-base epoxy plane paint layer, allows anti-crack fiber 11 to give the power that raw material is mutually pullled, so that water-base epoxy
Plane paint layer 1 is not easy to crack, while when water-base epoxy plane paint layer 1 is Nian Jie with terrace base 2, water-base epoxy plane paint layer 1
The anti-crack fiber 11 of lower surface and 2 adhesion of terrace base, so that adhesive force between layers is improved, so that terrace quality is more
It is good.
Preferably, anti-crack fiber 11 is basalt fibre, and basalt fibre length is 1cm or so, diameter is the left side 0.5mm
The right side utilizes the stronger pull resistance of basalt fibre by the way that basalt fibre to be uniformly blended into 1 raw material of water-base epoxy plane paint layer
Can, so that water-base epoxy plane paint layer 1 is not easy to crack, improve terrace quality.
Preferably, terrace base 2 includes cement basic layer 24, water-base epoxy infiltration priming paint 21, epoxy resin mortar layer 22, putty layer
23；The upper surface of cement basic layer 24 and water-base epoxy permeate 21 lower surface bonds of priming paint, 24 upper surface of cement basic layer be it is concave-convex not
Flat frosted structure.Water-base epoxy permeates 21 upper surface of priming paint and 22 lower surface bonds of epoxy resin mortar layer, on epoxy resin mortar layer 22
Surface and 23 lower surface bonds of putty layer, 23 upper surface of putty layer are Nian Jie with water-base epoxy plane paint layer 1.Pass through the terrace of multilayer
Base 2 is arranged, so that terrace base 2 is not easy to crack, water-base epoxy permeates 24 adhesion of cement basic layer of priming paint 21 and frosted, adhesion
Securely, while water-base epoxy infiltration priming paint 21 can preferably permeate steam.The setting of epoxy resin mortar layer 22, so that between molecule
There are gaps, under the action of stress, do not have to one and cracking phenomena occurs, so that terrace is not easy to crack, quality is preferable.
The utility model is described with reference to the preferred embodiments, and those skilled in the art know, is not departing from this reality
In the case where with novel spirit and scope, various changes or equivalence replacement can be carried out to these features and embodiment.This reality
It is not limited to the particular embodiment disclosed with novel, other embodiments fallen into claims hereof all belong to
In the range of the utility model protection.
Claims (6)
1. a kind of floor structure containing basalt fibre coating, it is characterised in that: flat including terrace base (2), water-base epoxy
Top coat layer (1)；The water-base epoxy plane paint layer (1) lower surface is Nian Jie with terrace base (2) upper surface, the aqueous ring
It is provided with several anti-crack fibers (11) in oxygen plane paint layer (1), the anti-crack fiber (11) is random to be interspersed in the water
Property epoxy plane paint layer (1) in, and the part anti-crack fiber (11) expose the water-base epoxy plane paint layer (1) lower surface with
Terrace base (2) bonding.
2. the floor structure according to claim 1 containing basalt fibre coating, it is characterised in that: the anti-crack fiber
It (11) is any of basalt fibre or polypropylene anti-crack fiber (11).
3. the floor structure according to claim 1 or 2 containing basalt fibre coating, it is characterised in that: the cracking resistance
Fiber (11) length is 0.5cm-3cm.
4. the floor structure according to claim 3 containing basalt fibre coating, it is characterised in that: the anti-crack fiber
(11) diameter is 0.1mm-2mm.
5. the floor structure according to claim 1 containing basalt fibre coating, it is characterised in that: the terrace base
It (2) include cement basic layer (24), water-base epoxy infiltration priming paint (21), epoxy resin mortar layer (22), putty layer (23)；The cement base
The upper surface of layer (24) and the water-base epoxy permeate priming paint (21) lower surface bonds, and the water-base epoxy permeates on priming paint (21)
Surface and epoxy resin mortar layer (22) lower surface bonds, under epoxy resin mortar layer (22) upper surface and the putty layer (23)
Surface bonding, putty layer (23) upper surface are Nian Jie with water-base epoxy plane paint layer (1).
6. the floor structure according to claim 5 containing basalt fibre coating, it is characterised in that: the cement basic layer
(24) upper surface is rough frosted structure.