CN209293323U - A kind of composite construction with the anti-paste function of flexible wear - Google Patents
A kind of composite construction with the anti-paste function of flexible wear Download PDFInfo
- Publication number
- CN209293323U CN209293323U CN201821674905.7U CN201821674905U CN209293323U CN 209293323 U CN209293323 U CN 209293323U CN 201821674905 U CN201821674905 U CN 201821674905U CN 209293323 U CN209293323 U CN 209293323U
- Authority
- CN
- China
- Prior art keywords
- flexible wear
- paste
- coating
- composite
- layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The utility model discloses a kind of composite constructions with the anti-paste function of flexible wear, belong to anti-paste technical field of composite materials, solve existing anti-stick coating after scraping the technical issues of anti-sticking function reduction.The composite construction includes the composite coating for applying body and its surface, and the hardness of the composite coating is Shore A 20~30, with a thickness of 81~103 μm；The composite coating includes interface processing oxidant layer and the anti-sticking paste layer of flexible wear, and the interface processing oxidant layer and the anti-sticking paste layer of flexible wear successively overlay on the surface for applying body, and the anti-sticking paste layer of flexible wear is organic silicon coating.Body structure surface tool has good wearability and anti-paste performance, can reduce the surface adhesion force of small advertisement paster.
Description
Technical field
The utility model relates to anti-paste technical field of composite materials, more particularly to one kind to have the anti-paste function of flexible wear
The composite construction of energy.
Background technique
With China's rapid development of economy, various industries are also increasing to the demand of information, so various
Information disclosure model also generate therewith." small advertisement " namely small-sized paster advertisement, since its stickup is easier, so almost
Each corner in city it is basic it can be seen that, such as electric pole surface, tile surface, security door surface, glass surface
Region.This small advertisement spread scope is wide, is difficult effectively to supervise.The cleaning difficulty of cleaner is increased, while some people accidentally believe
Content in " small advertisement " there may come a time when that health can be caused certain harm.
In the prior art, one entitled " a kind of Antisticking coating and its application method " (Publication No. CN103409051A)
A kind of water-soluble release coating is disclosed, this coating has the advantages that the drying and forming-film time is short, and in the formula of coating
Pumice granules are added to, the roughness of coating surface is increased, reduces contact area, there are preferable anti-adhesion effects；One
Entitled " a kind of anti-paste coating with rough surface " (Publication No. CN206646752U) discloses a kind of with coarse table
The anti-paste coating in face, is to the effect that distributed with clear coat, and in clear coat on the surface of coarse structure
Hydrophobic stratum granulosum is distributed with above, has the characteristics that rough surface.But when the people's use for pasting " small advertisement " is harder
Tools such as metal product (such as steel wire lump, metallic brush) when being scraped repeatedly to coating surface, the surface after scraping still may be used
To paste upper " small advertisement ".
Therefore, a kind of surface with lasting wear-resisting anti-sticking function is prepared to be of great practical significance.
Utility model content
The utility model in view of the above technical problems, provides a kind of structure with the anti-paste function of flexible wear.
To achieve the goals above, the utility model provides the following technical solutions:
A kind of composite construction with the anti-paste function of flexible wear, the composite coating including applying body and its surface, institute
The hardness for stating composite coating is Shore A 20~30, with a thickness of 81~103 μm；
The composite coating includes interface processing oxidant layer and the anti-sticking paste layer of flexible wear, the interface processing oxidant layer and flexibility
Wear-resisting anti-sticking paste layer successively overlays on the surface for applying body, and the anti-sticking paste layer of flexible wear is organic silicon coating.
Preferably, the interface processing oxidant layer with a thickness of 1~3 μm.
Preferably, the silicone layer with a thickness of 80~100 μm.
Preferably, the silicone layer with a thickness of 85~95 μm.
Preferably, the hardness of the composite coating is Shore A 22~26.
Preferably, the surfacing of the application body is metallic aluminium, stainless steel or concrete.
Compared with prior art, the utility model has the following beneficial effects:
A kind of composite construction with the anti-paste function of flexible wear provided by the utility model, the hardness of composite coating are
Shore A 20~30, since organic silicon coating has certain thickness, hardness is lower, has certain pliability, significantly
Improve the wearability of coating；Due to having used interface treating agent, composite coating can be improved and having applied the adhesive force in body surface face.
Anti-adhesive silicone, which pastes surface, has lower plane breakaway force, can reduce the surface adhesion force of small advertisement paster.
To sum up, a kind of composite construction with the anti-paste function of flexible wear provided by the utility model has wearability
Advantage good, paster surface adhesion force is low.
Detailed description of the invention
It, below will be to institute in embodiment in ord to more clearly illustrate embodiments of the present application with technical solution in the prior art
Attached drawing to be used is needed to be briefly described, it should be apparent that, the accompanying drawings in the following description is only to record in the utility model
Some embodiments be also possible to obtain other drawings based on these drawings for those of ordinary skill in the art.
Fig. 1 is the composite construction schematic diagram provided by the utility model with the anti-paste function of flexible wear.
Description of symbols:
1, organic silicon coating；2, interface processing oxidant layer；3, apply body.
Specific embodiment
In order to make those skilled in the art more fully understand the technical solution of the utility model, below in conjunction with attached drawing pair
The utility model is further detailed.
It is shown in Figure 1, a kind of composite construction with the anti-paste function of flexible wear of the utility model, including apply
Body 3 (such as security door surface, electric pole surface, exterior walls of buildings surface) successively covers from inside to outside on the surface for applying body 3
Have an interface processing oxidant layer 2 and organic silicon coating 1, the interface processing oxidant layer with a thickness of 1~3 μm；The thickness of the silicone layer
Degree is 80~100 μm；The interface processing oxidant layer and silicone layer form composite coating, and the hardness of the composite coating is
Shore A 20~30.
As in preferred embodiment, the silicone layer with a thickness of 85~95 μm.
As in preferred embodiment, the hardness of the composite coating is Shore A 22~26.
As in preferred embodiment, the surfacing for applying body is concrete.
Wherein, interface treating agent and organosilicon coating are all made of material in the prior art.
In order to make those skilled in the art more fully understand the technical solution of the utility model, below in conjunction with embodiment
The utility model is further detailed.
Table 1 is main material used in embodiment
Material therefor in 1 embodiment of table
| Title material | Brand/model | Manufacturer |
| Interface treating agent | K770-5 | Shenzhen Kang Libang organosilicon material Co., Ltd |
| Organosilicon coating | CBP02 | Weihai Newera Chemical Co., Ltd. |
| Commercially available Antisticking coating | 1031-FZ | Jing Lianhua Science and Technology Ltd., Shenzhen |
Embodiment 1
Cleaning treatment is carried out to security door surface first, then interface treating agent, table are brushed in the surface after cleaning is dry
After dry with a thickness of 1 μm.Finally interface processing layer surface after surface drying sprays silicone layer, with a thickness of 80 μm, solidification temperature
It is 85 DEG C, 30 minutes.Finally obtain a kind of structure with the anti-paste function of flexible wear that hardness is Shore A 20.
Embodiment 2
Cleaning treatment is carried out to security door surface first, then interface treating agent, table are brushed in the surface after cleaning is dry
After dry with a thickness of 2 μm.Finally interface processing layer surface after surface drying sprays silicone layer, with a thickness of 90 μm, solidification temperature
It is 90 DEG C, 25 minutes.Finally obtain a kind of structure with the anti-paste function of flexible wear that hardness is Shore A 22.
Embodiment 3
Cleaning treatment is carried out to security door surface first, then interface treating agent, table are brushed in the surface after cleaning is dry
After dry with a thickness of 2 μm.Finally interface processing layer surface after surface drying sprays silicone layer, with a thickness of 95 μm, solidification temperature
It is 100 DEG C, 20 minutes.Finally obtain a kind of structure with the anti-paste function of flexible wear that hardness is Shore A 24.
Embodiment 4
Cleaning treatment is carried out to electric pole surface first, then interface treating agent, table are brushed in the surface after cleaning is dry
After dry with a thickness of 2 μm.Finally interface processing layer surface after surface drying sprays silicone layer, with a thickness of 100 μm, solidification temperature
It is 80 DEG C, 35 minutes.Finally obtain a kind of structure with the anti-paste function of flexible wear that hardness is Shore A 26.
Embodiment 5
Cleaning treatment is carried out to electric pole surface first, then interface treating agent, table are brushed in the surface after cleaning is dry
After dry with a thickness of 3 μm.Finally interface processing layer surface after surface drying sprays silicone layer, with a thickness of 100 μm, solidification temperature
It is 100 DEG C, 25 minutes.Finally obtain a kind of structure with the anti-paste function of flexible wear that hardness is Shore A 30.
Comparative example
Cleaning treatment is carried out to security door surface first, then commercially available anti-paste painting is brushed on the surface after cleaning is dry
Material, with a thickness of 2 μm, solidification temperature is 23 DEG C, 300 minutes.Finally obtain a kind of surface with anti-paste function.
Performance test
Steel wire lump is fixed on pressure gauge compression bar bottom end, then in the anti-paste body structure surface of Examples 1 to 5 and comparative example
Then the normal force for applying 5N is evaluated the state on surface back and forth at mantle friction 5 times.Evaluation equivalence be divided into have scratch,
No marking applies exposed three ranks of body；Anti-paste property is carried out to the application body surface face after friction testing with adhesive paper
It can test, opinion rating is divided into easily peelable, difficult removing, bonding substrates three grades.
The embodiment of the present invention 1~5 and commercially available Antisticking coating are formed by coating surface and carry out performance comparison, as a result such as
Shown in table 2.
2 embodiment of the present invention of table and commercially available Antisticking coating performance comparison sheet
It is above that certain exemplary embodiments of the utility model are only described by way of explanation, undoubtedly, for
Those skilled in the art can be with a variety of different without departing from the spirit and scope of the utility model
Mode is modified described embodiment.Therefore, above-mentioned attached drawing and description are regarded as illustrative in nature, and should not be construed as
Limitation to the utility model claims protection scope.
Claims (6)
1. a kind of composite construction with the anti-paste function of flexible wear, which is characterized in that including applying answering for body and its surface
Coating is closed, the hardness of the composite coating is Shore A 20~30, with a thickness of 81~103 μm；
The composite coating includes interface processing oxidant layer and the anti-sticking paste layer of flexible wear, the interface processing oxidant layer and flexible wear
Anti-sticking paste layer successively overlays on the surface for applying body, and the anti-sticking paste layer of flexible wear is organic silicon coating.
2. the composite construction according to claim 1 with the anti-paste function of flexible wear, which is characterized in that the interface
Handle oxidant layer with a thickness of 1~3 μm.
3. the composite construction according to claim 2 with the anti-paste function of flexible wear, which is characterized in that described organic
Silicon layer with a thickness of 80~100 μm.
4. the composite construction according to claim 3 with the anti-paste function of flexible wear, which is characterized in that described organic
Silicon layer with a thickness of 85~95 μm.
5. the composite construction according to claim 1 with the anti-paste function of flexible wear, which is characterized in that described compound
The hardness of coating is Shore A 22~26.
6. described in any item composite constructions with the anti-paste function of flexible wear, feature exist according to claim 1~5
In the surfacing of the application body is metallic aluminium, stainless steel or concrete.