CN208980814U - A kind of coating structure of zinc alloy diecasting - Google Patents
A kind of coating structure of zinc alloy diecasting Download PDFInfo
- Publication number
- CN208980814U CN208980814U CN201821734807.8U CN201821734807U CN208980814U CN 208980814 U CN208980814 U CN 208980814U CN 201821734807 U CN201821734807 U CN 201821734807U CN 208980814 U CN208980814 U CN 208980814U
- Authority
- CN
- China
- Prior art keywords
- coating
- zinc alloy
- powder paint
- microns
- recessed portion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The utility model provides a kind of coating structure of zinc alloy diecasting, composite layer including being plated on kirsite substrate surface, the composite layer includes the cyaniding copper coating, cupric pyrophosphate coating and black chromium plating stacked gradually, and the compound layer surface forms the recessed portion of a plurality of filiform by wire drawing；It further include antimicrobial powder paint layer, the antimicrobial powder paint layer is attached at the compound layer surface with recessed portion.Simplify with structure, reduces the effect of cost and good anti-bacterial effect.
Description
Technical field
The utility model relates to zinc alloy diecasting manufacture fields, and in particular to a kind of coating knot of zinc alloy diecasting
Structure.
Background technique
Door handle generallys use die-casting process production molding, is one of the product of die casting.As shown in Figure 1, being existing door
One of structure of handle 1.Existing door handle material has using kirsite material, in kirsite door handle processing technology
In, it needs to plate composite layer on kirsite substrate, to play corresponding protection and beautiful effect.In the prior art, conventional
Composite layer generally comprise the cyaniding copper coating being stacked, cupric pyrophosphate coating, sulfuric acid copper coating, semi-gloss nickel coating, Quan Guang
Nickel coating and the black coating of dye, it is subsequent that liquid lacquer coat is enclosed by spraying or electrophoretic in compound layer surface again, it is above-mentioned compound
Structure is complicated for layer, and electroplating work procedure is more, and raw material is more, at high cost；Sulfuric acid copper coating, semi-gloss nickel coating and the plating of full light nickel in above structure
Although the stacking of layer is compound to have certain anti-corrosion effects, structure is more, preparation process is excessively complicated；Liquid lacquer coat nonreactive
Bacterium function, product not can avoid spread of germs in use.
Utility model content
For this purpose, the utility model provides, a kind of lamination layer structure is simple, at low cost, and the zinc alloy diecasting of good anti-bacterial effect
The coating structure of part.
To achieve the above object, the technical scheme that the utility model is provided is as follows:
A kind of coating structure of zinc alloy diecasting, the composite layer including being plated on kirsite substrate surface are described compound
Layer includes cyaniding copper coating, cupric pyrophosphate coating and the black chromium plating stacked gradually, and the compound layer surface is formed by wire drawing
The recessed portion of a plurality of filiform, the bottom of the recessed portion expose the cupric pyrophosphate coating；It further include antimicrobial powder paint layer, it is described
Antimicrobial powder paint layer is attached at the compound layer surface with recessed portion.
Further, the cyaniding copper coating of the composite layer/cupric pyrophosphate coating/black chromium plating is with a thickness of 3 microns/10
Micron/0.5 micron.
Further, the depth of the recessed portion is 0.5-1 microns.
Further, the antimicrobial powder paint layer with a thickness of 60 microns -100 microns.
Further, the antimicrobial powder paint layer with a thickness of 80 microns.
By technical solution provided by the utility model, have the following beneficial effects:
Liquid lacquer coat is arranged to antimicrobial powder paint layer, in the antimicrobial powder paint layer of compound layer surface, with antibacterial
With certain erosion-resisting effect；
Black chromium plating is set, and black chromium plating resistance to corrosion is fine, and the combination of black chromium plating and antimicrobial powder paint layer can be replaced
The structure of sulfuric acid copper coating in the prior art, semi-gloss nickel coating and full light nickel coating is changed, structure simplifies, and reduces cost, simultaneously
Black chromium plating replaces the black coating of dye prepared by original dye black powder water, and sewage treatment is convenient, more environmentally-friendly；
The compound layer surface forms the recessed portion of a plurality of filiform by wire drawing, so that composite layer surface roughening, it can
Preferably attachment antimicrobial powder paint layer, structure are more secured.
Antimicrobial powder paint layer is to be formed using powdered paint by spraying method, and the powdered paint rate of recovery is good, compared to existing skill
In art by the way of liquid lacquer, the rate of recovery is high, and cost is lower.
The Zinc alloy electroplating black chromium plating adds spray antimicrobial powder lacquer coat reasonable in design, and production technology is more optimized；Through
Verification experimental verification, product surface resistance to corrosion are reinforced, and the service life of product is extended, and product surface is made to have antibacterial function
Can, consumer is avoided using the spread of germs in product process, relatively sanitary environmental protection.
Detailed description of the invention
Fig. 1 show the appearance diagram of door handle in background technique；
Fig. 2 show the structural schematic diagram one of the composite layer of the coating structure of kirsite door handle in embodiment；
Fig. 3 show the structural schematic diagram two of the composite layer of the coating structure of kirsite door handle in embodiment；
Fig. 4 show the appearance diagram of kirsite door handle in embodiment；
Fig. 5 show the coating structure schematic diagram of kirsite door handle in embodiment.
Specific embodiment
To further illustrate each embodiment, the utility model is provided with attached drawing.These attached drawings are in the utility model discloses
A part of appearance mainly to illustrate embodiment, and can cooperate the associated description of specification former come the running for explaining embodiment
Reason.Cooperation refers to these contents, and those of ordinary skill in the art will be understood that other possible embodiments and sheet are practical new
The advantages of type.Component in figure is not necessarily to scale, and similar component symbol is conventionally used to indicate similar component.
Now in conjunction with the drawings and specific embodiments, the present invention will be further described.
A kind of coating structure of zinc alloy diecasting provided in this embodiment, it is specially a kind of referring to shown in Fig. 2 to Fig. 5
The coating structure of zinc alloy diecasting, the composite layer including being plated on 10 surface of kirsite substrate, the composite layer include successively
Cyaniding copper coating 21, cupric pyrophosphate coating 23 and the black chromium plating 24 of stacking, in this specific embodiment, the cyaniding of the composite layer
The thickness of 21/ cupric pyrophosphate coating of copper coating, 23/ black chromium plating 24 is preferably 3 microns/10 microns/0.5 micron, can reach knot
The best combination degree of structure, in other embodiments, each thickness degree are not limited thereto.
The compound layer surface forms the recessed portion 25 of a plurality of filiform by wire drawing, as shown in Figure 4 on 1 surface of door handle
Compound layer surface forms the recessed portion 25 of a plurality of filiform by wire drawing；It further include antimicrobial powder paint layer 30, the antimicrobial powder paint
Layer 30 is attached at the compound layer surface with recessed portion 25 by spraying, and certain antimicrobial powder paint layer 30 is attached at composite layer table
The technique in face is also not limited to spraying, is also possible to the common process such as printing, electrophoresis.The recessed portion 25 of a plurality of filiform makes compound
Layer surface roughening, can preferably adhere to antimicrobial powder paint layer 30, structure is more secured.
Specifically, the bottom of the recessed portion 25 exposes the cupric pyrophosphate coating 23, in this way, cupric pyrophosphate coating 23 with
Black chromium plating 24 is staggeredly presented, more aesthetically pleasing.Specifically, the depth-first of the recessed portion 25 is set as 0.5-1 microns, it can
Guarantee the roughness of compound layer surface, while the structure for damaging composite layer that will not also be excessive.
Specifically, in the present embodiment, the antimicrobial powder paint layer 30 with a thickness of 80 microns, which can preferably rise
To the effect of protection, and can guarantee to form good combination with compound layer surface.In other embodiments, antimicrobial powder paint layer
30 thickness can preferentially be set as 60 microns -100 microns.
In the present embodiment, each layer structure material of composite layer is existing material, and specific electro-plating method and parameter are
Those skilled in the art grasps already, is no longer described in detail one by one herein.
Specifically, the effect of cyaniding copper coating 21 is transitional bonding layer, it is the bottoming of kirsite substrate surface, has and well plate
Ability and covering power, coating surface is bright, and crystallization is subtle, and porosity is low, while preparing for rear road coating.
The effect of cupric pyrophosphate coating 23 is transitional bonding layer, is prepared for subsequent black coating chrome plating 24.
Liquid lacquer coat is arranged to antimicrobial powder paint layer 30, in the antimicrobial powder paint layer 30 of compound layer surface, is had
Antibacterial and certain erosion-resisting effect；
Black chromium plating 24 is set, and 24 resistance to corrosion of black chromium plating is fine, black chromium plating 24 and antimicrobial powder paint layer 30
In conjunction with the structure of replaceable sulfuric acid copper coating in the prior art, semi-gloss nickel coating and full light nickel coating, structure simplifies, reduce at
This, while black chromium plating 24 replaces the black coating of dye prepared by original dye black powder water, sewage treatment is convenient, more environmentally-friendly；
The compound layer surface forms the recessed portion 25 of a plurality of filiform by wire drawing, so that composite layer surface roughening, energy
Enough preferably attachment antimicrobial powder paint layers 30, structure is more secured.
Antimicrobial powder paint layer is to be formed using powdered paint by spraying method, and the powdered paint rate of recovery is good, compared to existing skill
In art by the way of liquid lacquer, the rate of recovery is high, and cost is lower.
The Zinc alloy electroplating black chromium plating adds spray antimicrobial powder lacquer coat reasonable in design, and production technology is more optimized；Through
Verification experimental verification, product surface resistance to corrosion are reinforced, and the service life of product is extended, and product surface is made to have antibacterial function
Can, consumer is avoided using the spread of germs in product process, relatively sanitary environmental protection.
Die casting carries out expansion explanation by taking door handle as an example in the present embodiment, and in other embodiments, die casting can also be with
It is other types of product, such as the panel frame of panel light.
Although specifically showing and describing the utility model in conjunction with preferred embodiment, those skilled in the art is answered
This is understood, in the spirit and scope for not departing from the utility model defined by the appended claims, in form and details
On the utility model can be made a variety of changes, be the protection scope of the utility model.
Claims (6)
1. a kind of coating structure of zinc alloy diecasting, the composite layer including being plated on kirsite substrate surface, it is characterised in that:
The composite layer includes the cyaniding copper coating, cupric pyrophosphate coating and black chromium plating stacked gradually, and the compound layer surface passes through
Wire drawing forms the recessed portion of a plurality of filiform；It further include antimicrobial powder paint layer, the antimicrobial powder paint layer is attached at recessed portion
Compound layer surface.
2. the coating structure of zinc alloy diecasting according to claim 1, it is characterised in that: the bottom of the recessed portion is naked
Expose the cupric pyrophosphate coating.
3. the coating structure of zinc alloy diecasting according to claim 2, it is characterised in that: the copper cyanider of the composite layer
Coating/cupric pyrophosphate coating/black chromium plating is with a thickness of 3 microns/10 microns/0.5 micron.
4. the coating structure of zinc alloy diecasting according to claim 3, it is characterised in that: the depth of the recessed portion is
0.5-1 microns.
5. the coating structure of zinc alloy diecasting according to claim 1, it is characterised in that: the antimicrobial powder paint layer
With a thickness of 60 microns -100 microns.
6. the coating structure of zinc alloy diecasting according to claim 5, it is characterised in that: the antimicrobial powder paint layer
With a thickness of 80 microns.