CN208826680U - A kind of high welding quality strip paper cutting blade - Google Patents
A kind of high welding quality strip paper cutting blade Download PDFInfo
- Publication number
- CN208826680U CN208826680U CN201820822390.4U CN201820822390U CN208826680U CN 208826680 U CN208826680 U CN 208826680U CN 201820822390 U CN201820822390 U CN 201820822390U CN 208826680 U CN208826680 U CN 208826680U
- Authority
- CN
- China
- Prior art keywords
- silver soldering
- lamella
- blade
- silver
- copper mesh
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The utility model discloses a kind of high welding quality strip paper cutting blades, belong to alloy blade technical field.The first silver soldering lamella, copper mesh, the second silver soldering lamella are provided between the blade base and alloy blade of the utility model, copper mesh is set between the first silver soldering lamella and the second silver soldering lamella, the first layer of solder paste is set between alloy blade and the first silver soldering lamella, second layer of solder paste is set between blade base and the second silver soldering lamella, and copper mesh uses 50 mesh red copper nets.Copper mesh is set between two layers of silver soldering piece by the utility model, copper mesh there are between very good solution alloy blade, silver soldering piece and blade base three, during heating, internal gas cannot be smoothly discharged, the problem of causing rosin joint, simultaneously, also it solves between alloy blade, silver soldering piece and blade base three during heating, because three kinds of density of material are different, the shrinkage rates that reaction generates of expanding with heat and contract with cold are different, the problem of causing alloy fracture, and copper mesh can also play good buffer function.
Description
Technical field
The utility model relates to alloy blade technical fields, more specifically to a kind of high welding quality strip cut paper
Blade.
Background technique
Paper cutting blade is paper cutter one of the ost important components, is used in automatic paper cutting machine, numerical control slitter, program-controlled cut paper
The dedicated paper cut paper cutting blade of all kinds of high-grade paper cutters such as machine, can be to offers high-precision paper such as press, packing businesses
It cuts, the sharpness and service life of paper cutting blade largely affect the working efficiency of paper cutter.Paper cutting blade is by closing
Golden blade and blade base high temperature welding-on form, and the combination of alloy blade and blade base determines the service life of blade, and
Paper cutting quality.
For strip paper cutting blade, be primarily present in production: alloy blade in the welding process, often occur rosin joint,
Solder skip, fracture;It in grinding process, often bursts, crack phenomenon, very big puzzlement and economic loss is caused to enterprise.
To find out its cause, the strip paper cutting blade processing technology of most original, is that alloy blade and blade base are welded as one using welding rod
Body can make cutter hub uneven heating even, often in the process welded since hand papercutter length is longer using the mode of welding rod
In, before welded place be just broken.Improvement technique starts to use adds one between blade base and alloy blade
The mode of layer silver soldering piece realizes connection, but is although made moderate progress using silver soldering piece, and it is even that there are still uneven heatings, and cutter hub is caused to be broken
The problem of, and the cutter hub processed can also find that there are many stomatas inside it through carrying out flaw detection, this can all seriously affect and cut
The yield rate and service life of paper blade.
Through retrieving, China Patent No. ZL201621191062.6, authorized announcement date is on September 12nd, 2017, innovation and creation
Title are as follows: a kind of reinforced welded shield alloy scraper cutter, this application include scraper body, knife beam, are located at scraper body
The carbide chip of end is equipped with metal mesh and silver-bearing copper weld tabs, is being brazed between the scraper body and carbide chip
It in the process, can be equal after melting silver-bearing copper weld tabs by increasing by one layer of metal mesh between alloy cutter hub and carbide chip
Even is distributed between alloy cutter hub and carbide chip, improves soldering strength, and weld seam has slag inclusion to split after avoiding soldering
Line.But what this application first related to is scraper cutter, and paper cutting blade can not be suitable for by improving it, secondly, this application
One layer of metal mesh and silver-bearing copper weld tabs are only set between scraper body and carbide chip, in alloy cutter hub and carbide cutter tool
Reliably there are hidden danger for welding aspect between piece.
Utility model content
1. utility model technical problems to be solved
The purpose of the utility model is to overcome the defect of the above-mentioned prior art, provides a kind of high welding quality strip and cut
Paper blade;Easily there is fracture, crackle, cracking in the utility model very good solution strip cut paper alloy blade, rosin joint phenomenon
Problem improves the quality and service life of strip cut paper alloy blade product.
2. technical solution
In order to achieve the above objectives, technical solution provided by the utility model are as follows:
A kind of high welding quality strip paper cutting blade of the utility model, including blade base and alloy blade, it is described
Blade base includes the component of following mass percent: C 0.35-0.52%;Si 0.21-0.35%;Mn 0.55-0.86%;
S≤0.02%;P≤0.025%;Cr 0.12-0.23%;Ni≤0.25%;Cu≤0.30%, surplus is for Fe and unavoidably
Impurity;The first silver soldering lamella, copper mesh, the second silver soldering lamella are provided between blade base and alloy blade, copper mesh is set to
Between first silver soldering lamella and the second silver soldering lamella, the first layer of solder paste, blade are set between alloy blade and the first silver soldering lamella
The second layer of solder paste is set between matrix and the second silver soldering lamella.
It is further improved as the utility model, the copper mesh uses purple with a thickness of 50 mesh of 0.25mm-0.3mm
Copper mesh.
It is further improved as the utility model, the first silver soldering lamella and the second silver soldering lamella use thickness
For the silver soldering piece of 0.2-0.25mm.
It further being improved as the utility model, the first silver soldering lamella uses the silver soldering piece of argentiferous 53%,
The second silver soldering lamella uses the silver soldering piece of argentiferous 50%.
It is further improved as the utility model, the copper mesh and the first silver soldering lamella, the second silver soldering lamella phase
The face of contact is also coated with soldering paste.
It is further improved as the utility model, first layer of solder paste, the second layer of solder paste and copper mesh and
The soldering paste that the face that one silver soldering lamella, the second silver soldering lamella are in contact is smeared uses FB125P sliver soldering paste.
3. beneficial effect
Using technical solution provided by the utility model, compared with existing well-known technique, there is following remarkable result:
(1) a kind of high welding quality strip paper cutting blade of the utility model, between blade base and alloy blade
Two layers of silver soldering piece and one layer of copper mesh are set, and copper mesh is set between two layers of silver soldering piece, copper mesh there are very good solutions
Between alloy blade, silver soldering piece and blade base three, during heating, internal gas cannot be smoothly discharged, and cause rosin joint
The problem of, meanwhile, it also solves between alloy blade, silver soldering piece and blade base three during heating, because of three kinds of materials
The problem of density is different, and the shrinkage rates that reaction generates of expanding with heat and contract with cold are different, causes alloy fracture, and copper mesh can also play
Good buffer function;
(2) a kind of high welding quality strip paper cutting blade of the utility model, copper mesh uses 50 mesh red copper nets, purple first
The fusing point of copper mesh is 1083 DEG C, will not be melted in the welding process, secondly the red copper net under the size, will not be too big because of eyelet,
Cause silver soldering piece to be all fused to inside eyelet, be less useful for gas discharge, 50 mesh red copper nets can just make copper mesh two sides silver soldering piece
It is impermeable mutually, be conducive to gas discharge;
(3) a kind of high welding quality strip paper cutting blade of the utility model, the first silver soldering lamella and the second silver soldering lamella
, will not be too high using the silver soldering piece one side cost of the thickness using the silver soldering piece with a thickness of 0.2-0.25mm, on the other hand
It can guarantee and cover silver brazing material on blade base and alloy blade comprehensively, guarantee that blade base and alloy blade reliably weld;
(4) a kind of high welding quality strip paper cutting blade of the utility model, using general between copper mesh and blade base
The silver soldering piece of logical argentiferous 50% has been taken into account cost while guaranteeing welding quality, has been used between copper mesh and alloy blade
The silver soldering piece of argentiferous 53%, the silver soldering piece of the silver content 700 DEG C~750 DEG C at a temperature of can melt very well, effectively avoid producing
It gives birth to weld crack, stomata and is mingled with, so that it is guaranteed that blade base and alloy blade reliably weld, weldquality is high.
Detailed description of the invention
Fig. 1 is a kind of structural schematic diagram of high welding quality strip paper cutting blade of the utility model;
Fig. 2 is the structural schematic diagram of alloy blade fixture in the utility model.
Label declaration in schematic diagram:
1, blade base;2, alloy blade;31, the first layer of solder paste;32, the first silver soldering lamella;33, copper mesh;34, the second silver medal
Weld tabs layer;35, the second layer of solder paste;41, bracket;42, protect-ing frame structure;43, supporting plate;44, bottom plate;45, support plate;46, clamp;
47, nut;51, induction heating equipment;52, it switchs;53, heating coil;54, water pump.
Specific embodiment
For the content for further appreciating that the utility model, the utility model is described in detail in conjunction with the accompanying drawings and embodiments.
Embodiment 1
In conjunction with Fig. 1, a kind of high welding quality strip paper cutting blade of the present embodiment, including blade base 1 and alloy blade
2, blade base 1 includes the component of following mass percent: C 0.35%;Si 0.35%;Mn 0.55%;S 0.02%;P
0.025%;Cr 0.12%;Ni 0.25%;Cu 0.30%, surplus are Fe and inevitable impurity.The blade base
The first silver soldering lamella 32, copper mesh 33, the second silver soldering lamella 34 are provided between 1 and alloy blade 2, copper mesh 33 is set to the first silver medal
Between weld tabs layer 32 and the second silver soldering lamella 34.Wherein copper mesh 33 is using the 50 mesh red copper nets with a thickness of 0.25mm.First silver soldering
Lamella 32 and the second silver soldering lamella 34 using the silver soldering piece with a thickness of 0.2mm, using the thickness silver soldering piece one side cost not
Can be too high, it on the other hand also can guarantee and cover silver brazing material on blade base 1 and alloy blade 2 comprehensively, guarantee 1 He of blade base
Alloy blade 2 reliably welds.And first silver soldering lamella 32 using argentiferous 53% silver soldering piece, the second silver soldering lamella 34 use argentiferous
50% silver soldering piece.
It is worth noting that the silver soldering piece of argentiferous 50% is common silver soldering piece on sale on the market, in copper mesh 33 and blade
The silver soldering piece that common argentiferous 50% is used between matrix 1, has taken into account cost while guaranteeing welding quality.But copper mesh 33
Very crucial with the welding effect of alloy blade 2, welding procedure, which is held, bad can have low intensity, crackle, stomata, be mingled with and oxygen
A series of problems, such as change, blade manufacturer seldom will recognize that be more than using argentiferous 40% welding rod, trace it to its cause mainly because
Content for silver is higher, and the price of welding rod is higher.And the present embodiment is in order to guarantee that institute can be obtained between copper mesh 33 and alloy blade 2
The welding effect needed has used the silver soldering piece with argentiferous 53%, the silver soldering piece of the silver content between copper mesh 33 and alloy blade 2
It can melt, effectively avoid generating weld crack, stomata and be mingled with very well under 700 DEG C~750 DEG C of welding temperature, so that it is guaranteed that
Blade base and alloy blade reliably weld, and weldquality is high.
First layer of solder paste 31, blade base 1 and the second silver soldering lamella are set between alloy blade 2 and the first silver soldering lamella 32
Second layer of solder paste 35 is set between 34.Two layers of silver soldering piece and one layer of copper is arranged in the present embodiment between blade base and alloy blade
Net, and copper mesh is set between two layers of silver soldering piece, copper mesh there are very good solution alloy blade, silver soldering piece and blade bases
Between body three, during heating, the problem of internal gas cannot be smoothly discharged, cause rosin joint, meanwhile, also solve alloy
Between blade, silver soldering piece and blade base three during heating, because three kinds of density of material are different, reaction of expanding with heat and contract with cold is produced
The problem of raw shrinkage rates are different, cause alloy fracture, and copper mesh can also play good buffer function.Copper mesh uses 50
Mesh red copper net, the first fusing point of red copper net are 1083 DEG C, will not be melted in the welding process, secondly the red copper net under the size,
Will not be too big because of eyelet, cause silver soldering piece to be all fused to inside eyelet, be less useful for gas discharge, 50 mesh red copper nets can just make
Copper mesh two sides silver soldering piece is impermeable mutually, is conducive to gas discharge.
Embodiment 2
A kind of high welding quality strip paper cutting blade of the present embodiment, substantially with embodiment 1, the difference is that: this
Blade base 1 includes the component of following mass percent: C 0.52% in embodiment;Si 0.21%;Mn 0.86%;S
0.02%;P 0.025%;Cr 0.23%;Ni 0.25%;Cu 0.30%, surplus are Fe and inevitable impurity.Copper mesh
33 using the 50 mesh red copper nets with a thickness of 0.3mm.First silver soldering lamella 32 and the second silver soldering lamella 34 are using with a thickness of 0.25mm
Silver soldering piece.
Embodiment 3
A kind of high welding quality strip paper cutting blade of the present embodiment, substantially with embodiment 1, the difference is that: this
Blade base 1 includes the component of following mass percent: C 0.46% in embodiment;Si 0.27%;Mn 0.65%;S
0.02%;P 0.025%;Cr 0.18%;Ni 0.25%;Cu 0.30%, surplus are Fe and inevitable impurity.Copper mesh
33 using the 50 mesh red copper nets with a thickness of 0.28mm.First silver soldering lamella 32 and the second silver soldering lamella 34 are using with a thickness of 0.22mm
Silver soldering piece.And the present embodiment also smears weldering in the face that copper mesh 33 is in contact with the first silver soldering lamella 32, the second silver soldering lamella 34
Cream.But very thin one layer is only smeared herein, thickness is far below the first layer of solder paste 31 and the second layer of solder paste 35.In copper mesh 33 and
Soldering paste is also smeared in the face that one silver soldering lamella 32, the second silver soldering lamella 34 are in contact, and is more conducive to blade base, silver soldering piece, copper
Net and alloy blade are reliably bonded as one.First layer of solder paste 31 described in the present embodiment, the second layer of solder paste 35 with
And the soldering paste that the face that is in contact with the first silver soldering lamella 32, the second silver soldering lamella 34 of copper mesh 33 is smeared is using FB125P silver brazing
Cream.
Embodiment 4
A kind of processing method of high welding quality strip paper cutting blade of the present embodiment, the steps include:
Step 1: the good blade base 1 of straightening, blade base 1 includes the component of following mass percent: C 0.35%;Si
0.35%;Mn 0.55%;S 0.02%;P 0.025%;Cr 0.12%;Ni 0.25%;Cu 0.30%, surplus be Fe and
Inevitable impurity.Get out 50 mesh red copper nets of 0.25mm thickness, the silver soldering piece of the argentiferous 53% of 0.2mm thickness, 0.2mm is thick
The silver soldering piece and alloy blade 2 of argentiferous 50%;
Step 2: the material 3min described in sulfuric acid water acid pickling step one of the mass percent concentration for 20%, then use quality
The soda water that percent concentration is 50% cleans repeatedly, is finally rinsed with tap water, washes the residue of pickling and soda water
Matter;
Step 3: soldering paste is uniformly smeared on 1 surface of blade base, argentiferous 50% is then sequentially placed on blade base 1
Silver soldering piece, the silver soldering piece of red copper net and argentiferous 53%, then uniformly smear soldering paste on the silver soldering piece surface of argentiferous 53%, and will close
Golden blade 2 is placed in the silver soldering piece of the argentiferous 53%, is tightened with iron wire.
Step 4: cutter hub obtained by step 3 is placed in holding furnace, 1h is kept the temperature at a temperature of 400 DEG C;
Step 5: heating welding surface to stopping after 750 DEG C after taking out cutter hub clamp pressing using induction heating equipment and adding
Heat, the rate of heat addition are as follows:
V=(T-T0) (Crwt+Cwt)*1000
In above formula, V is heating rate, and unit is DEG C/min;The value of T be 750 DEG C, unit be DEG C, T0 is initial temperature,
Unit be DEG C, CrwtFor the mass percent value of Cr in rough forging, CwtFor the mass percent value of C in rough forging.Again certainly
500 DEG C so are cooled to, cutter hub is placed in holding furnace again, heat preservation is taken out after 48 hours.
Referring to fig. 2, the fixture includes bracket 41, protect-ing frame structure to the clamp structure used in the present embodiment step 5
42, bottom plate 44, clamp 46 and induction heating equipment 51, the essence of bracket 41 are an operating platforms, driving up procedure face, bracket 41
Upper surface is provided with two supporting plates 43 for being spaced a distance setting, and bottom plate 44 is set on supporting plate 43, and the presence of supporting plate 43 makes
There are certain intervals for bottom plate 44 and 41 upper surface of bracket, are conducive to heat conduction, are also unlikely to damage 41 upper surface of bracket.From guarantor
The 400 DEG C of cutter hubs taken out in warm furnace can be placed on bottom plate 44, and the side of bottom plate 44 is provided with support plate 45,45 edge of support plate
The length direction interval of bottom plate 44 is arranged 2, fixes a clamp 46 in each support plate 45, the head of clamp 46 is provided with tune
Nut 47 is saved, after clamp 46 is put down, head bolt just compresses 2 position of alloy blade of cutter hub, can be with by adjusting nut 47
Adjust the degree of bolt presses alloy blade 2.The protect-ing frame structure 42 is set to the side of bracket 41, induction heating equipment 51
It is set in protect-ing frame structure 42, which plays fixed, protection induction heating equipment 51, induction heating equipment 51
Heating coil 53 be set to the top of alloy blade 2, the heating coil 53 is strip, along the length of alloy blade 2
Direction setting, the switch 52 and water pump 54 of induction heating equipment 51 are set to ground, and switch 52 is set to ground and is highly convenient for grasping
It is controlled as personnel.
In the present embodiment in cutter hub heating process, the mass percent value of Mn and C in rate and blade base will heat up
Associated, heating process cooperates blade base component, can make that the tissue of blade base is easy to control and stability is good, is welding
In the process reduce blade base generate weld crack a possibility that, while also can further ensure that alloy blade straightness and
Verticality.By from the bottom plate that the cutter hub taken out in holding furnace is placed in fixture mount upper surface, operation clamp compresses cutter hub
Alloy blade can start induction heating equipment, be added using the heating coil being arranged in above alloy blade to welding surface
Heat, clamp structure setting is simple, easy to operate.
Embodiment 5
A kind of processing method of high welding quality strip paper cutting blade of the present embodiment, the steps include:
Step 1: the good blade base 1 of straightening, blade base 1 includes the component of following mass percent: C 0.52%;Si
0.21%;Mn 0.86%;S 0.02%;P 0.025%;Cr 0.23%;Ni 0.25%;Cu 0.30%, surplus be Fe and
Inevitable impurity.Get out 50 mesh red copper nets of 0.3mm thickness, the silver soldering piece of the argentiferous 53% of 0.25mm thickness, 0.25mm thickness
Argentiferous 50% silver soldering piece and alloy blade 2;
Step 2: the material 5min described in sulfuric acid water acid pickling step one of the mass percent concentration for 20%, then use quality
The soda water that percent concentration is 50% cleans repeatedly, is finally rinsed with tap water, washes the residue of pickling and soda water
Matter;
Step 3: soldering paste is uniformly smeared on 1 surface of blade base, argentiferous 50% is then sequentially placed on blade base 1
Silver soldering piece, the silver soldering piece of red copper net and argentiferous 53%, then uniformly smear soldering paste on the silver soldering piece surface of argentiferous 53%, and will close
Golden blade 2 is placed in the silver soldering piece of the argentiferous 53%, is tightened with iron wire.
Step 4: cutter hub obtained by step 3 is placed in holding furnace, 1.5h is kept the temperature at a temperature of 450 DEG C;
Step 5: heating welding surface to stopping after 700 DEG C after taking out cutter hub clamp pressing using induction heating equipment and adding
Heat, the rate of heat addition are as follows:
V=(T-T0) (Crwt+Cwt)*1000
In above formula, V is heating rate, and unit is DEG C/min;The value of T be 700 DEG C, unit be DEG C, T0 is initial temperature,
Unit be DEG C, CrwtFor the mass percent value of Cr in rough forging, CwtFor the mass percent value of C in rough forging.Again certainly
520 DEG C so are cooled to, cutter hub is placed in holding furnace again, heat preservation is taken out after 48 hours.
The present embodiment clamp substantially with embodiment 4, the difference is that: length direction of the clamp along alloy blade
4 are arranged at equal intervals.
Embodiment 6
A kind of processing method of high welding quality strip paper cutting blade of the present embodiment, the steps include:
Step 1: the good blade base 1 of straightening, blade base 1 includes the component of following mass percent: C 0.46%;Si
0.27%;Mn 0.65%;S 0.02%;P 0.025%;Cr 0.18%;Ni 0.25%;Cu 0.30%, surplus be Fe and
Inevitable impurity.Get out 50 mesh red copper nets of 0.28mm thickness, the silver soldering piece of the argentiferous 53% of 0.22mm thickness, 0.22mm thickness
Argentiferous 50% silver soldering piece and alloy blade 2;
Step 2: the material 4min described in sulfuric acid water acid pickling step one of the mass percent concentration for 20%, then use quality
The soda water that percent concentration is 50% cleans repeatedly, is finally rinsed with tap water, washes the residue of pickling and soda water
Matter;
Step 3: soldering paste is uniformly smeared on 1 surface of blade base, argentiferous 50% is then sequentially placed on blade base 1
Silver soldering piece, the silver soldering piece of red copper net and argentiferous 53%, then uniformly smear soldering paste on the silver soldering piece surface of argentiferous 53%, and will close
Golden blade 2 is placed in the silver soldering piece of the argentiferous 53%, is tightened with iron wire.
Step 4: cutter hub obtained by step 3 is placed in holding furnace, 1.2h is kept the temperature at a temperature of 430 DEG C;
Step 5: heating welding surface to stopping after 740 DEG C after taking out cutter hub clamp pressing using induction heating equipment and adding
Heat, the rate of heat addition are as follows:
V=(T-T0) (Crwt+Cwt)*1000
In above formula, V is heating rate, and unit is DEG C/min;The value of T be 740 DEG C, unit be DEG C, T0 is initial temperature,
Unit be DEG C, CrwtFor the mass percent value of Cr in rough forging, CwtFor the mass percent value of C in rough forging.Again certainly
480 DEG C so are cooled to, cutter hub is placed in holding furnace again, heat preservation is taken out after 48 hours.
The present embodiment clamp substantially with embodiment 4, the difference is that: length direction of the clamp along alloy blade
3 are arranged at equal intervals.
Schematically the utility model and embodiments thereof are described above, description is not limiting, attached drawing
Shown in be also one of the embodiments of the present invention, actual structure is not limited to this.So if this field
Those of ordinary skill enlightened by it, without deviating from the purpose of the present invention, not inventively design
Frame mode similar with the technical solution and embodiment, all should belong to the protection range of the utility model.
Claims (5)
1. a kind of high welding quality strip paper cutting blade, including blade base (1) and alloy blade (2), it is characterised in that: described
Blade base (1) and alloy blade (2) between be provided with the first silver soldering lamella (32), copper mesh (33), the second silver soldering lamella
(34), copper mesh (33) is set between the first silver soldering lamella (32) and the second silver soldering lamella (34), alloy blade (2) and the first silver medal
It is arranged between weld tabs layer (32) the first layer of solder paste (31), the second weldering is set between blade base (1) and the second silver soldering lamella (34)
Layer of paste (35);The copper mesh (33) is with a thickness of 0.25mm-0.3mm;The copper mesh (33) uses 50 mesh red copper nets.
2. a kind of high welding quality strip paper cutting blade according to claim 1, it is characterised in that: first silver soldering
Lamella (32) and the second silver soldering lamella (34) are using the silver soldering piece with a thickness of 0.2-0.25mm.
3. a kind of high welding quality strip paper cutting blade according to claim 2, it is characterised in that: first silver soldering
Lamella (32) uses the silver soldering piece of argentiferous 53%, and the second silver soldering lamella (34) uses the silver soldering piece of argentiferous 50%.
4. a kind of high welding quality strip paper cutting blade according to claim 3, it is characterised in that: the copper mesh (33)
The face being in contact with the first silver soldering lamella (32), the second silver soldering lamella (34) is also coated with soldering paste.
5. a kind of high welding quality strip paper cutting blade according to claim 4, it is characterised in that: first soldering paste
Layer (31), the second layer of solder paste (35) and copper mesh (33) are in contact with the first silver soldering lamella (32), the second silver soldering lamella (34)
The soldering paste that face is smeared uses FB125P sliver soldering paste.