A kind of mosquito repellent ornament materials
Technical field
The utility model relates to decorative materials technologies, and in particular to a kind of mosquito repellent ornament materials.
Background technique
Ornament materials has in fields such as household, Office Space, automobile, high-speed rails and is widely applied at present, wherein wood-based plate
Secondary processing product pattern is more, and kind is complete, can satisfy demand for various purposes.Wood-based plate secondary processing product is included in various
Artificial board substrate sticks on surface various ornament materials, as natural veneer, Recombinant Wood, printed decoration paper or synthetic resin impregnate
Paper.Three-aldehyde glue is mostly used in existing decoration panel production technology, free formaldehyde is easily released, directly affects people's health,
And the quality of production of panel is influenced by production technologies such as adhesive qualities;Meanwhile these decoration materials have a single function, usually
Do not have mosquito-proof, fire-retardant and other effects.Therefore, it needs to design a kind of new technical solution, be existed in the prior art with comprehensive solution
The problem of.
Utility model content
The purpose of the utility model is to provide a kind of mosquito repellent ornament materials, and wherein mosquito repellent ornament materials structure is simple, cost
Cheap, preparation method simple process is easy to make, can effectively release free formaldehyde existing in the prior art endanger people be good for
Health, panel quality difference and original plate have a single function problem.
In order to solve the above technical problems, the utility model uses following technical scheme:
A kind of mosquito repellent ornament materials, including mosquito repellent grass layer, woody debris' layer and adhesive layer, woody debris' layer setting exist
Between the mosquito repellent grass layer, the mosquito repellent grass layer is at least provided with 6 layers, and woody debris layer is at least provided with 2 layers, the drive
Adhesive layer is provided between mosquito grass layer or the upper and lower surface of woody debris' layer.
Further scheme is that the mosquito repellent grass layer is symmetricly set on the two sides of woody debris' layer.
Further scheme is, the adhesive layer is polyvinyl chloride film, and adhesive layer with a thickness of 0.01~
0.08mm。
The mosquito repellent ornament materials provided in above-mentioned technical proposal, using the combined use of Mozzie buster and woody debris, with biography
System wood-based plate is compared, and the utility model mosquito repellent ornament materials uses polyvinyl chloride film for adhesive, formaldehydeless pollution, and polychlorostyrene
Ethylene has flame retardant efficiency;Meanwhile part woody debris layer is replaced using mosquito repellent grass layer, mosquito repellent ornament materials can not only be mitigated
Own wt, moreover it is possible to reach repelling effect;And preparation method, simple process, device requirement amount is small, and preparation time is short, behaviour
Make safe ready, the release of free formaldehyde can be effectively reduced, provided safeguard for health of people.
Detailed description of the invention
Fig. 1 is the structural schematic diagram of the utility model mosquito repellent ornament materials.
In figure: 1, adhesive layer;2, woody debris' layer;3, mosquito repellent grass layer.
Specific embodiment
In order to which the purpose of this utility model and advantage is more clearly understood, with reference to embodiments to the utility model into
Row illustrates.It should be appreciated that following text is only used to one or more of specific embodiments of description the utility model,
Considered critical is not carried out to the protection scope that the utility model is specifically requested.
Embodiment 1
Technical solution that the present embodiment is taken is as shown in Figure 1, with board dimension for 40*40*0.5cm, density 0.6g/
cm3For, a kind of mosquito repellent ornament materials, including mosquito repellent grass layer 3, woody debris' layer 2 and adhesive layer 1, woody debris' layer 2 are set
It sets between the mosquito repellent grass layer 3, the mosquito repellent grass layer 3 is provided with 6 layers, and woody debris' layer 2 is provided with 2 layers, the drive
Adhesive layer 1 is provided between mosquito grass layer 3 or the upper and lower surface of woody debris' layer 2.
As shown in Figure 1, mosquito repellent grass layer 3 is symmetricly set on the two sides of woody debris' layer 2, i.e. two layers of woody debris' layer is set side by side
It sets together, the two sides of woody debris' layer are respectively arranged with three layers of mosquito repellent grass layer, and wherein the dosage of Mozzie buster is 360g, wooden broken
The dosage of material is 120g.
The adhesive layer 1 be polyvinyl chloride film, and adhesive layer 1 with a thickness of 0.08mm.
The production method of above-mentioned mosquito repellent ornament materials the following steps are included:
Step S1, Mozzie buster pre-processes, and the Mozzie buster that cleaning is dried is placed in microwave 1min in micro-wave oven, is pulverized later,
For use;
Step S2, adhesive layer is laid, it is successively uniform spreading step S1 is obtained on adhesive layer later Mozzie buster, wooden
Particle and Mozzie buster, formed mosquito repellent grass layer, woody debris layer and mosquito repellent grass layer interlayer structure, wherein mosquito repellent grass layer with
And the upper and lower surface of woody debris' layer is provided with adhesive layer;
Step S3, the material for paving step S2 carries out heat pressing process, obtains plate;Wherein hot pressing temperature is 90 DEG C,
Hot pressing time is 0.2minmm-1, hot pressing pressure 0.5MPa.
Step S4, the good plate of step S3 hot pressing is transferred in cold press and carries out shaping processing, obtain mosquito repellent ornament materials.
The moisture content of above-mentioned woody debris is 1%, and the moisture content of the Mozzie buster is 1%.
Wherein temperature of colding pressing is 25 DEG C, cold pressing pressure 1MPa, and the processing time is 1~10min.
Embodiment 2
The present embodiment is 40*40*0.9cm, density 0.5g/cm with board dimension3For, a kind of mosquito repellent ornament materials,
Including mosquito repellent grass layer 3, woody debris' layer 2 and adhesive layer 1, woody debris' layer 2 is arranged between the mosquito repellent grass layer 3, institute
State mosquito repellent grass layer 3 and be provided with 8 layers, woody debris' layer 2 is provided with 4 layers, the mosquito repellent grass layer 3 or woody debris' layer 2 it is upper
Adhesive layer 1 is provided between lower surface.
Mosquito repellent grass layer 3 is symmetricly set on the two sides of woody debris' layer 2, i.e. three layers of woody debris' layer are arranged side by side together,
The two sides of four layers of woody debris' layer are respectively arranged with four layers of mosquito repellent grass layer, and wherein the dosage of Mozzie buster is 480g, woody debris
Dosage is 240g.
The adhesive layer 1 be polyvinyl chloride film, and adhesive layer 1 with a thickness of 0.01mm.
The production method of above-mentioned mosquito repellent ornament materials the following steps are included:
Step S1, Mozzie buster pre-processes, and the Mozzie buster that cleaning is dried is placed in microwave 10min in micro-wave oven, is pulverized later,
For use;
Step S2, adhesive layer is laid, it is successively uniform spreading step S1 is obtained on adhesive layer later Mozzie buster, wooden
Particle and Mozzie buster, formed mosquito repellent grass layer, woody debris layer and mosquito repellent grass layer interlayer structure, wherein mosquito repellent grass layer with
And the upper and lower surface of woody debris' layer is provided with adhesive layer;
Step S3, the material for paving step S2 carries out heat pressing process, obtains plate;Wherein hot pressing temperature is 150 DEG C,
Hot pressing time is 0.6minmm-1, hot pressing pressure 5MPa.
Step S4, the good plate of step S3 hot pressing is transferred in cold press and carries out shaping processing, obtain mosquito repellent ornament materials.
The moisture content of above-mentioned woody debris is 15%, and the moisture content of the Mozzie buster is 15%.
Wherein temperature of colding pressing is 40 DEG C, cold pressing pressure 1MPa, and the processing time is 10min.
Embodiment 3
The present embodiment is 40*40*0.9cm, density 0.4g/cm with board dimension3For, a kind of mosquito repellent ornament materials,
Including mosquito repellent grass layer 3, woody debris' layer 2 and adhesive layer 1, woody debris' layer 2 is arranged between the mosquito repellent grass layer 3, institute
State mosquito repellent grass layer 3 and be provided with 6 layers, woody debris' layer 2 is provided with 4 layers, the mosquito repellent grass layer 3 or woody debris' layer 2 it is upper
Adhesive layer 1 is provided between lower surface.
Mosquito repellent grass layer 3 is symmetricly set on the two sides of woody debris' layer 2, i.e. two layers of woody debris' layer is arranged side by side together,
The two sides of four layers of woody debris' layer are respectively arranged with three layers of mosquito repellent grass layer, and wherein the dosage of Mozzie buster is 345.6g, woody debris
Dosage be 230.4g.
The adhesive layer 1 be polyvinyl chloride film, and adhesive layer 1 with a thickness of 0.04mm.
The production method of above-mentioned mosquito repellent ornament materials the following steps are included:
Step S1, Mozzie buster pre-processes, and the Mozzie buster that cleaning is dried is placed in microwave 5min in micro-wave oven, is pulverized later,
For use;
Step S2, adhesive layer is laid, it is successively uniform spreading step S1 is obtained on adhesive layer later Mozzie buster, wooden
Particle and Mozzie buster, formed mosquito repellent grass layer, woody debris layer and mosquito repellent grass layer interlayer structure, wherein mosquito repellent grass layer with
And the upper and lower surface of woody debris' layer is provided with adhesive layer;
Step S3, the material for paving step S2 carries out heat pressing process, obtains plate;Wherein hot pressing temperature is 120 DEG C,
Hot pressing time is 1minmm-1, hot pressing pressure 3MPa.
Step S4, the good plate of step S3 hot pressing is transferred in cold press and carries out shaping processing, obtain mosquito repellent ornament materials.
The moisture content of above-mentioned woody debris is 7%, and the moisture content of the Mozzie buster is 7%.
Wherein temperature of colding pressing is 30 DEG C, cold pressing pressure 1MPa, and the processing time is 5min.
In short, mosquito repellent ornament materials provided by the utility model, mosquito repellent ornament materials structure is simple, low in cost, no
It is only able to solve Form aldehyde release existing in the prior art, the problem of panel quality is influenced by adhesive, also has mosquito repellent fire-retardant
Function;In addition its production method simple process, Production Time is short, required equipment is few, safe operation is quick, and mosquito repellent can quickly be made
Ornament materials.
The embodiments of the present invention is explained in detail above in conjunction with embodiment, but the utility model and unlimited
In above embodiment, for those skilled in the art, in knowing the utility model after contents,
Without departing from the principle of this utility model, several same transformation and substitution can also be made to it, these same transformation
It also should be regarded as belonging to the protection scope of the utility model with substitution.