CN208308976U - A kind of platinum plating titanium plate for Waste Acid From Hua Cheng Foil manufacture - Google Patents
A kind of platinum plating titanium plate for Waste Acid From Hua Cheng Foil manufacture Download PDFInfo
- Publication number
- CN208308976U CN208308976U CN201820878386.XU CN201820878386U CN208308976U CN 208308976 U CN208308976 U CN 208308976U CN 201820878386 U CN201820878386 U CN 201820878386U CN 208308976 U CN208308976 U CN 208308976U
- Authority
- CN
- China
- Prior art keywords
- titanium plate
- platinum plating
- waste acid
- plating titanium
- hua cheng
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The utility model discloses a kind of platinum plating titanium plate for Waste Acid From Hua Cheng Foil manufacture, wherein the platinized titanium plate is polygon, side length number is n；Platinum plating titanium plate edge edge is equipped with shielding strip, and shielding rule number is m, and meets n >=3, m > 1, and n >=m.It the advantage is that, voltage drop can be effectively reduced, and can effectively slow down foil edge part capacity difference of energizing, to extend the service life of platinum plating titanium plate and reduce production cost.
Description
Technical field
The utility model belongs to electrochemical material field, and in particular to for a kind of platinum plating titanium plate for Waste Acid From Hua Cheng Foil manufacture.
Background technique
Currently, anode foil for aluminum electrolytic capacitor is by special high-purity aluminum foil by electrochemistry or chemical attack expansion table
Area, using product of the electrochemical action after surface forms layer oxide film (aluminum oxide).Forming oxidation film
In the process, by being anode with aluminium foil, titanium plate is the electric field of cathode composition, electrochemistry chemical conversion is carried out to corrosive aluminum foil, to make
Produce with certain capacity and can bear the Waste Acid From Hua Cheng Foil of certain voltage.
In actual production, be powered in liquid by titanium plate, have the voltage drop of 10-15V.The titanium plate is by multiple
Coating contains iridic compound, and by high-temperature calcination, forms yttrium oxide on titanium plate surface, the service life of the platinum plating titanium plate is only
1 year.In addition, in production process, the current distribution of titanium plate Analysis of End Electric Field corrosive aluminum foil edge ratio relative to being distributed in corrosion
Aluminium foil inside is more, in this way, the edge oxidation film of corrosive aluminum foil is caused to be destroyed, edge capacity and inside capacity volume variance are big, and
And the probability that disconnected foil occurs increases.Therefore, design it is a kind of for Waste Acid From Hua Cheng Foil and the titanium plate that overcomes drawbacks described above, be to need to solve
Certainly the problem of.
Summary of the invention
The utility model provides a kind of platinum plating titanium plate for Waste Acid From Hua Cheng Foil manufacture, and voltage drop can be effectively reduced and effectively subtract
Slow foil edge part capacity difference of energizing reduces to effectively extend the service life of platinum plating titanium plate and replaces platinum plating titanium plate number in production process,
Achieve the purpose that reduce operating cost.
The utility model patent is achieved by the following means.
A kind of platinum plating titanium plate for Waste Acid From Hua Cheng Foil manufacture, the platinized titanium plate surface are coated with metal platinum, wherein platinum plating titanium plate
For axial symmetry or centrosymmetric polygon, side length number is n；Platinum plating titanium plate edge edge is equipped with shielding strip, and shielding rule number is m, and
And meet n >=3, m > 1, and n >=m.
Further, a kind of platinum plating titanium plate for Waste Acid From Hua Cheng Foil manufacture, wherein the platinized titanium plate can for axial symmetry or
The centrosymmetric concave polygon of person or convex polygon.
Further, a kind of platinum plating titanium plate for Waste Acid From Hua Cheng Foil manufacture, wherein the material of the shielding strip is HT-PVC,
The one or more of PVC, UPVC.
Preferably, a kind of platinum plating titanium plate for Waste Acid From Hua Cheng Foil manufacture, wherein the metal platinum of platinized titanium plate surface plating
With a thickness of 0.01-0.1 mm.
Preferably, a kind of platinum plating titanium plate for Waste Acid From Hua Cheng Foil manufacture, wherein the width of the shielding strip is 5-40 mm.
Preferably, it is a kind of for Waste Acid From Hua Cheng Foil manufacture platinum plating titanium plate, wherein the shielding strip with a thickness of 2-20 mm.
Platinum plating titanium plate described in the utility model for Waste Acid From Hua Cheng Foil manufacture, passes through the superior electrical conductivity energy of platinum, voltage drop
Only 3-8V effectively reduces generation electricity consumption, reduces production cost.And the setting of shielding strip, it is effectively improved point of electric field
Cloth, the consistency enhanced product performance improve the quality of product.Therefore, the plating energized for corrosive aluminum foil of the utility model
Platinum titanium plate, it is simple and reasonable, it is easily manufactured, and product quality of edges can be improved, there is more market popularization value.
Detailed description of the invention
Fig. 1 is a kind of hardened composition of platinized titanium of Waste Acid From Hua Cheng Foil manufacture described in embodiment 1 (wherein dash area is shielding strip).
Fig. 2 is a kind of hardened composition of platinized titanium of Waste Acid From Hua Cheng Foil manufacture described in embodiment 2 (wherein dash area is shielding strip).
Fig. 3 is a kind of hardened composition of platinized titanium of Waste Acid From Hua Cheng Foil manufacture described in embodiment 3 (wherein dash area is shielding strip).
Fig. 4 is a kind of hardened composition of platinized titanium of Waste Acid From Hua Cheng Foil manufacture described in embodiment 4 (wherein dash area is shielding strip).
Specific embodiment
Further illustrate the present invention below in conjunction with specific embodiment, but embodiment the present invention is not done it is any type of
It limits.
Embodiment 1 adds m, n value
A kind of platinum plating titanium plate for Waste Acid From Hua Cheng Foil manufacture, the platinized titanium plate surface are coated with the metal platinum of 0.01 mm thickness, plate
The wide L of platinum titanium plate edges cover is 5 mm, and thickness is the shielding strip of 2 mm, and shielding strip material is HT-PVC.
Embodiment 2
A kind of platinum plating titanium plate for Waste Acid From Hua Cheng Foil manufacture, the platinized titanium plate surface are coated with the metal platinum of 0.05 mm thickness, plate
The wide L of platinum titanium plate edges cover is 10 mm, and thickness is the shielding strip of 5 mm, and shielding strip material is PVC.
Embodiment 3
A kind of platinum plating titanium plate for Waste Acid From Hua Cheng Foil manufacture, the platinized titanium plate surface are coated with the metal platinum of 0.08 mm thickness, plate
Platinum titanium plate edges cover width is 20 mm, and thickness is the shielding strip of 10 mm, and shielding strip material is UPVC.
Embodiment 4
A kind of platinum plating titanium plate for Waste Acid From Hua Cheng Foil manufacture, the platinized titanium plate surface are coated with the metal platinum of 0.1 mm thickness, plate
Platinum titanium plate edges cover width is 40 mm, and thickness is the shielding strip of 20 mm, and shielding strip material is HT-PVC.
Embodiment 5
Platinum plating titanium plate in above-described embodiment is subjected to industrial experiment, and comparative experiments is set.Comparative example 1-4
In, platinized titanium plate shape is identical as embodiment 1-4 difference, only difference is that platinized titanium plate surface in comparative example 1-4
Non- platinum plating and shielding strip.
The step of industrial experiment, is as described below:
The non-platinum plating titanium plate of S1, comparative example is mounted on production line, is produced, and production process is respectively electrolysed using instrument measurement
The voltage of slot, the paillon produced carry out specific volume and reach the performance tests such as voltage.
S2, embodiment titanium plate installation in the production line, titanium plate shape is identical as the non-platinum plating titanium plate of comparative experiments, carry out
Production, production process utilize the voltage of each electrolytic cell of instrument measurement, and the paillon produced carries out specific volume and reaches the property such as voltage
It can test.
When carrying out embodiment and comparative example experiment every time, the product of same size is produced, is produced using the same board same period
Specific volume similar in etched foil, comparative experiments use identical technique.
Test obtained Data induction such as the following table 1, table 2.
Table 1
Table 2
Can be clearly visible by the above correlation data: using after novel platinum plating titanium plate, the voltage of each electrolytic cell be different
The decline of degree, can reduction production cost to a certain extent；And held using the edge that paillon is made in novel platinum plating titanium plate
It still has, but still is can control within 6% partially, and edge situation integrally meets the effect that production needs.
Commerical test is carried out by platinum plating titanium plate to the present embodiment, the service life can achieve 3-5, hence it is evident that better than not plating
The titanium plate of platinum and shielding strip.
In process of production, using the titanium plate of non-platinum plating and shielding strip, after 10 months, voltage reduces 20V or more.
And the platinum plating titanium plate of experiment is used, after two-and-a-half years, voltage, which reduces, only declines 5V than new titanium plate.
The above only expresses the embodiments of the present invention, practical not departing from for those skilled in the art
Under the premise of novel design, the change of other modes can also be made, the protection scope of the utility model is belonged to.
Claims (5)
1. a kind of platinum plating titanium plate for Waste Acid From Hua Cheng Foil manufacture, which is characterized in that the platinum plating titanium plate is axial symmetry or central symmetry
Polygon, side length number are n；Platinum plating titanium plate edge edge is equipped with shielding strip, and shielding rule number is m, and meets n >=3, m > 1, and n >=
m。
2. a kind of platinum plating titanium plate for Waste Acid From Hua Cheng Foil manufacture according to claim 1, which is characterized in that the platinum plating titanium plate can
Think axial symmetry or centrosymmetric concave polygon or convex polygon.
3. a kind of platinum plating titanium plate for Waste Acid From Hua Cheng Foil manufacture according to claim 1, which is characterized in that the shielding strip
Material is HT-PVC, the one or more of PVC, UPVC.
4. a kind of platinum plating titanium plate for Waste Acid From Hua Cheng Foil manufacture according to claim 1, which is characterized in that the width of the shielding strip
For 5-40 mm.
5. a kind of platinum plating titanium plate for Waste Acid From Hua Cheng Foil manufacture according to claim 1, which is characterized in that the wherein shielding strip
With a thickness of 2-20 mm.