CN208308931U - A kind of aluminium silicon carbide material stand-by equipment - Google Patents
A kind of aluminium silicon carbide material stand-by equipment Download PDFInfo
- Publication number
- CN208308931U CN208308931U CN201820582200.6U CN201820582200U CN208308931U CN 208308931 U CN208308931 U CN 208308931U CN 201820582200 U CN201820582200 U CN 201820582200U CN 208308931 U CN208308931 U CN 208308931U
- Authority
- CN
- China
- Prior art keywords
- graphite
- prefabricated
- pipe
- member mould
- silicon carbide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The utility model discloses a kind of aluminium silicon carbide material stand-by equipments, including graphite crucible, prefabricated-member mould, seaming chuck and push-down head, prefabricated-member mould is arranged in the graphite-pipe in graphite crucible, the top of prefabricated-member mould is arranged in seaming chuck, aluminium ingot is provided between seaming chuck and prefabricated-member mould, prefabricated-member mould lower part is provided with graphite bolster plate, and the lower section of graphite bolster plate is arranged in push-down head.The utility model structure is simple, easy to operate, and preparation process is succinct, and casting accuracy is high.
Description
Technical field
The utility model belongs to metallic composite technical field, and in particular to a kind of preparation of aluminium silicon carbide material is with setting
It is standby.
Background technique
Al-base ceramic (such as Al/SiC, Al/Si3N4、Al/Al2O3Deng) composite material is because of its brilliant mechanical property and physics
Performance and be widely used aerospace and microelectronic field, to realize that product closely forms that shape degree is high, and simple process is easy
Operation, existing for the purpose of manufactured properties of product are superior, material preparation process is to produce Al-base ceramic composite material
For starting point, the product produced, size is poor, and later period machine adds task heavy and machine adds size also can be with the increasing of processing times
Add and deviate, since above problem is inevitable, makes increased production cost to be not easy to pushing away for Al-base ceramic composite material
Wide and most of preparation process is complex, brings heavy burden for production.
Utility model content
The technical problem to be solved by the utility model is in view of the deficiency of the prior art, provide a kind of aluminium carbon
Silicon nitride material stand-by equipment is combined by prefabricated component with mold, and prefabricated component is completed to infiltrate in a mold, obtained product
Superior performance, size closely form.
The utility model uses following technical scheme:
A kind of aluminium silicon carbide material stand-by equipment, including graphite crucible, prefabricated-member mould, seaming chuck and push-down head, in advance
Part forming die is arranged in the graphite-pipe in graphite crucible, and seaming chuck is arranged in the top of prefabricated-member mould, seaming chuck and prefabricated
Aluminium ingot is provided between part mold, prefabricated-member mould lower part is provided with graphite bolster plate, and the lower section of graphite bolster plate is arranged in push-down head.
Specifically, being provided with multiple SiC prefabricated components in prefabricated-member mould, the length of SiC prefabricated component is 1~500mm, width
It is highly 10~1000mm for 1~500mm.
Further, SiC prefabricated component includes at least 2.
Specifically, being provided with graphite exocoel between graphite-pipe and graphite crucible.
Specifically, graphite bolster plate is inverted T-type structure, vertical section setting is fitted and connected in graphite-pipe with prefabricated-member mould,
Horizontal segment setting is fitted and connected with graphite-pipe and graphite exocoel respectively outside graphite-pipe.
Specifically, aluminium ingot is arranged in graphite-pipe, it is highly 10~1000mm that the diameter of aluminium ingot, which is 1~800mm,.
Compared with prior art, the utility model at least has the advantages that
Prefabricated-member mould, is arranged in the stone in graphite crucible by a kind of aluminium silicon carbide material stand-by equipment of the utility model
In black pipe, the top of prefabricated-member mould is arranged in seaming chuck, and aluminium ingot, prefabricated-member mould are arranged between seaming chuck and prefabricated-member mould
Graphite bolster plate is arranged in lower part, and the lower section of graphite bolster plate is arranged in push-down head, and structure is simple, and easy to operate, preparation process is succinct, casting
Part precision is high.
Further, it is provided with multiple SiC prefabricated components, the length of SiC prefabricated component is 1~500mm, width is 1~
500mm is highly 10~1000mm, and the transformable size of SiC prefabricated component is wide, raw suitable for the size product in size range
It produces.
Further, with setting graphite exocoel in graphite-pipe in graphite crucible, seaming chuck applies under molten aluminum molten condition
Pressure, molten aluminum can apply pressure to graphite-pipe, and graphite-pipe is unlikely to split under the protection of graphite chamber.
Further, inverted T shaped graphite bolster plate and graphite inside pipe wall, graphite bottom of the tube, prefabricated-member mould and graphite exocoel are tight
The purpose of closely connected conjunction is to guarantee the air-tightness of preparation, and when seaming chuck applies pressure, molten aluminum liquid is impregnated into prefabricated under stress
Part.
Further, aluminium ingot diameter is 1~800mm, is highly 10~1000mm, the size of aluminium ingot can be according to prefabricated component
Size has a greater change range, guarantees that the molten aluminum in infiltration process is sufficient.
Below by drawings and examples, the technical solution of the utility model is described in further detail.
Detailed description of the invention
Fig. 1 is the utility model aluminium silicon carbide material die for preparation structural schematic diagram.
Wherein: 1. seaming chucks;2. graphite-pipe;3. aluminium ingot;4. graphite exocoel;5. prefabricated-member mould;6.SiC prefabricated component;7.
Graphite bolster plate;8. push-down head.
Specific embodiment
Referring to Fig. 1, the utility model discloses a kind of aluminium silicon carbide material stand-by equipment, including graphite crucible, stone
Black pipe 2, aluminium ingot 3, prefabricated-member mould 5, graphite bolster plate 7, seaming chuck 1 and push-down head 8, graphite-pipe 2 are arranged in graphite crucible, stone
Graphite exocoel 4 is set between black pipe 2 and graphite crucible, and aluminium ingot 3 and prefabricated-member mould 5 are arranged in graphite-pipe 2, prefabricated-member mould
SiC prefabricated component 6 is provided in 5, the top of prefabricated-member mould 5 is arranged in aluminium ingot 3, and prefabricated-member mould 5 is arranged in graphite bolster plate 7
The top of lower section, aluminium ingot 3 is contacted with seaming chuck 1, and push-down head 8 is located at the lower section of graphite bolster plate 7.
The length of SiC prefabricated component 6 is 1~500mm, and it is highly 10~1000mm that width, which is 1~500mm,.
3 diameter of aluminium ingot is 1~800mm, is highly 10~1000mm.
Preparation process is as follows:
Referring to Fig. 1, outside is cylindrical graphite crucible, graphite bolster plate 7 is first put into graphite crucible bottom, then by SiC
Prefabricated component 6 is put into prefabricated-member mould 5, is placed on the boss of graphite bolster plate 7 together with prefabricated-member mould 5, in graphite-pipe
Side is coated 2 sets of graphite-pipe after boron carbide on prefabricated-member mould 5, press and under fit closely graphite-pipe 2 with backing plate 7, so
4 sets of graphite exocoel are later put into aluminium ingot 3 in graphite-pipe on graphite-pipe 2 afterwards, seaming chuck 1 is pressed in top and the stone of aluminium ingot 3
Black pipe 2 fits closely, and push-down head 8 is located at the lower section of backing plate 7.
It opens roughing valve to be vacuumized, guarantees it under vacuum conditions, oxidation reaction will not occur, generate harmful miscellaneous
Matter.
Under vacuum conditions, start to warm up it is in a molten state to its molten aluminum, seaming chuck start apply pressure, due to start
It is vacuumized, so being negative pressure in porous ceramics, under the effect of the pressure, molten aluminum starts to be impregnated into porous ceramics heat preservation guarantor
Infiltration is completed after pressing a period of time.
To avoid ceramics are cooling in air from generating harmful substance or ceramics cracking after heat preservation, using cold with furnace, to
Temperature takes out product when being down to room temperature.
The above content is only to illustrate the technical idea of the utility model, and the protection model of the utility model cannot be limited with this
Enclose, it is all according to the utility model proposes technical idea, any changes made on the basis of the technical scheme each falls within this reality
Within protection scope with novel claims.
Claims (6)
1. a kind of aluminium silicon carbide material stand-by equipment, which is characterized in that including graphite crucible, prefabricated-member mould (5), seaming chuck
(1) it is arranged in the graphite-pipe (2) in graphite crucible Nei with push-down head (8), prefabricated-member mould (5), seaming chuck (1) is arranged prefabricated
The top of part mold (5) is provided with aluminium ingot (3) between seaming chuck (1) and prefabricated-member mould (5), and prefabricated-member mould (5) lower part is set
It is equipped with graphite bolster plate (7), push-down head (8) is arranged in the lower section of graphite bolster plate (7).
2. a kind of aluminium silicon carbide material stand-by equipment according to claim 1, which is characterized in that prefabricated-member mould (5)
Multiple SiC prefabricated components (6) are inside provided with, the length of SiC prefabricated component (6) is 1~500mm, and it is highly 10 that width, which is 1~500mm,
~1000mm.
3. a kind of aluminium silicon carbide material stand-by equipment according to claim 2, which is characterized in that SiC prefabricated component (6) is extremely
It less include 2.
4. a kind of aluminium silicon carbide material stand-by equipment according to claim 1, which is characterized in that graphite-pipe (2) and stone
Graphite exocoel (4) are provided between black crucible.
5. a kind of aluminium silicon carbide material stand-by equipment according to claim 1, which is characterized in that graphite bolster plate (7) is
Inverted T-type structure, vertical section setting are fitted and connected in graphite-pipe (2) with prefabricated-member mould (5), and horizontal segment is arranged in graphite-pipe
(2) it is fitted and connected respectively with graphite-pipe (2) and graphite exocoel (4) outside.
6. a kind of aluminium silicon carbide material stand-by equipment according to claim 1, which is characterized in that aluminium ingot (3) setting exists
In graphite-pipe (2), it is highly 10~1000mm that the diameter of aluminium ingot (3), which is 1~800mm,.