CN208208438U - A kind of laminated toughened glass insulator - Google Patents
A kind of laminated toughened glass insulator Download PDFInfo
- Publication number
- CN208208438U CN208208438U CN201820454943.5U CN201820454943U CN208208438U CN 208208438 U CN208208438 U CN 208208438U CN 201820454943 U CN201820454943 U CN 201820454943U CN 208208438 U CN208208438 U CN 208208438U
- Authority
- CN
- China
- Prior art keywords
- vitreum
- chapeau
- fer
- insulator
- glass
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The utility model discloses a kind of laminated toughened glass insulator, this insulator includes vitreum, chapeau de fer, cement glue.Vitreum is centered on DC toughened glass, outer package aluminosilicate glass or low Pyrex.Titanium dioxide coating film layer on glass external surface;It is bonded between chapeau de fer and the lug boss of vitreum and by one layer of cement glue between the inner hole at the full skirt center of steel feet and vitreum.Phenomena such as the utility model laminated toughened glass insulator has high mechanical strength, and the uniformity of tempering is fine, resistance to external force collision, does not easily cause unfilled corner, rupture, does not generate cracking;The resistance to temperature difference can avoid glass insulator and reveal phenomenon, and the hard careful no pore in surface is easily self-cleaning, and intensity is high, and anti-pollution sudden strain of a muscle ability is strong and suitable for direct current, is of great significance to the normal operation for guaranteeing electric system.
Description
Technical field
The utility model relates to technical field of electricity, specifically a kind of laminated toughened glass insulator.
Background technique
Glass insulator is due to good with resistance to electric arc and anti-vibration performance, the features such as non-aging and self-cleaning is good, extensively
It is general to be applied in transmission line of electricity.With the continuous development of science and technology, there is super-pressure, large capacity, the remote and small spy of line loss
The direct current transportation of point has become the trend of electric power industry development.In high pressure, ultrahigh-voltage alternating-current transmission of electricity, the dish type of existing production is outstanding
Hanging tempered glass steel insulator has been widely used, but this dish type suspension type tempered glass steel insulator cannot be straight
It scoops out and is used in super high voltage direct current electricity transmission, this is because dish type suspension type tempered glass steel insulator is defeated applied to superhigh voltage DC
There is also have following point in electricity: first is that DC line electric current is different from AC line current, it is defeated in direct current under DC electric field
One Direction Transfer and the local ion aggregation that ion can occur during electricity operation inside toughened glass insulator, to cause tempering
The aging of glass insulator;Second is that being effectively improved under heavy pollution to reduce a possibility that toughened glass insulator is by air breakdown
The flashover voltage and breakdown voltage of toughened glass insulator, DC circuit move the volume resistance and ion of toughened glass insulator
Shifting rate requires high than volume resistance and ionic mobility of the alternating current circuit to toughened glass insulator;It is tempering in DC circuit again
The steel feet of glass insulator cement interface than steel feet in alternating current circuit cement interface be easier corrode, make steel feet and
The mechanical strength of toughened glass insulator reduces.And the insulator of on-line operation, in the natural environment by sulfur dioxide, nitrogen
The influence of the atmospheric environments such as oxide and graininess dust gradually deposited one layer of dunghill on its surface.In dry weather
In the case where, these surfaces can be worked normally with the insulator of dunghill, but when encountering the wet weathers such as mist, dew, rain,
Pollution severity of insulators object absorbs moisture, makes electrolyte dissolution in pollution layer, ionization, eventually leads to flashover.
Because the invention one kind can with direct current and seem with the laminated toughened glass insulator of fine antifouling work ability
It is particularly important.
Summary of the invention
The purpose of this utility model is to provide a kind of with available direct current and folded with fine antifouling work ability
Layer toughened glass insulator.
Technical scheme of realizing the purpose of the utility model is that
A kind of laminated toughened glass insulator, including vitreum, chapeau de fer and steel feet, the vitreum are insulator body,
Its top center is lug boss, and lower end is full skirt;The vitreum is centered on DC toughened glass, outer package aluminosilicate glass
Or low Pyrex layer;The chapeau de fer is set on the lug boss on vitreum top, and the steel feet is arranged in vitreum full skirt
In the inner hole of heart bottom;Between chapeau de fer and the lug boss of vitreum and between the inner hole at the full skirt center of steel feet and vitreum
It is bonded by one layer of cement glue, chapeau de fer and steel feet is firmly combined together with vitreum.
The middle layer DC toughened glass thickness 6-7mm.
The outer casing aluminosilicate glass or low Pyrex thickness degree 0.6-0.8mm.
Titanium dioxide coating layer on the glass external surface.
Zinc oxide coating is coated in the outer surface of chapeau de fer.
Zinc oxide coating is coated in the outer surface of steel feet.
Locking pin is equipped in the centre bore of chapeau de fer.
The utility model the utility model has the advantages that
(1) vitreum central core is different from surrounding layer material in the utility model insulator, and the coefficient of expansion is also different, cold
When but, surrounding layer is first shunk, and will form pressure to central core naturally, it is made to generate prestressing force, thus achieve the purpose that tempering,
Its effect is better than common air hardening steel effect, and the uniformity of tempering is fine, can avoid glass insulator and reveals phenomenon.General steel
Change glass insulator compression in 100~140MPa, the compression of the utility model glass insulator up to 250~350MPa,
More resistant to external force collision, phenomena such as not easily causing unfilled corner, rupture, cracking is not generated;The resistance to temperature difference is greater than 150 DEG C, permanent open air use
It still becomes clear as new, the hard careful no pore in surface is easily self-cleaning, and intensity is high, has to the normal operation for guaranteeing electric system
Significance.
(2) vitreum has included boron oxide and aluminium oxide, titanium dioxide coating on outer surface in the utility model insulator
Layer makes the utility model insulator with very high mechanical strength and there is good anti-pollution to dodge ability.
(3) in the utility model insulator in vitreum titanium dioxide layer sterilizing ability cooperation lithia inhibit sodium from
The One Direction Transfer and localized clusters that son, potassium oxide and sodium oxide molybdena occur under DC electric field long term improve volume resistivity,
Delay the aging of vitreum and fails and can be used in direct current.
(4) the utility model insulator cap and the coating of steel feet outer surface are coated with the Zinc oxide coating of high temperature process, mention
High chapeau de fer and steel feet anti-electrocorrosion, extend the service life of chapeau de fer and steel feet.
Detailed description of the invention
Fig. 1 is the utility model laminated toughened glass insulator overall structure diagram,
Fig. 2 is the structural schematic diagram of the vitreum of laminated toughened glass insulator.
Marked in the figure: 1, vitreum, 1.1, DC toughened glass, 1.2, aluminosilicate glass or low Pyrex layer, 2, iron
Cap, 3, steel feet, 4, locking pin, 5, cement glue, 6, titanium dioxide layer, 7, Zinc oxide coating.
Specific embodiment
The utility model is further elaborated below in conjunction with Fig. 1-embodiment shown in Fig. 2.
A kind of laminated toughened glass insulator, including vitreum 1, chapeau de fer 2 and steel feet 3, the vitreum 1 are insulator master
Body, top center are lug boss, and lower end is full skirt.The vitreum 1 is centered on DC toughened glass 1.1, outer package
Aluminosilicate glass or low Pyrex layer 1.2.1.1 thickness 6-7mm of middle layer DC toughened glass, coefficient of expansion 72-78;Outsourcing
1.2 thickness 0.6-0.8mm of covering layer aluminosilicate glass or low Pyrex layer, coefficient of expansion 42-48.On 1 outer surface of vitreum
Titanium dioxide coating layer 6.The chapeau de fer 2 is set on the lug boss on 1 top of vitreum, and the steel feet 3 is arranged in vitreum 1
In the inner hole of full skirt centre bottom.Between chapeau de fer 2 and the lug boss of the vitreum 1 and full skirt center of steel feet 3 and vitreum 1
Inner hole between bonded by one layer of cement glue 5, chapeau de fer 2 and steel feet 3 are firmly combined together with vitreum 1.?
It is equipped with locking pin 4 in the centre bore of chapeau de fer 2, is used for and the steel feet 3 of a upper insulator is connected and fixed.In chapeau de fer 2 and steel feet 3
Outer surface is coated with the Zinc oxide coating 7 of high temperature process.
Embodiment
A kind of laminated toughened glass insulator, DC toughened glass component by weight include following raw material: quartz
65 parts, 2 parts of aluminium oxide, 0.1 part of iron oxide, 10 parts of calcium oxide, 1 part of magnesia, 1 part of potassium oxide, 1 part of sodium oxide molybdena, lithia
0.1 part, 0.1 part of boron oxide, 0.3 part of titanium dioxide layer.
The vitreum the preparation method comprises the following steps:
(1) glass raw material is put into the double-deck melting furnace, DC toughened glass liquid, fusion temperature are melted in melting furnace upper layer
1200 DEG C, 1150 DEG C of material path temperature;Melting furnace lower layer fusing aluminosilicate glass glass metal, 1400 DEG C of fusion temperature, material path temperature
1000℃;
(2) the DC toughened glass liquid for having melted step (1) and one of aluminosilicate glass or low borosilicate glass metal
By the outlet of servo feeding machine, through scissor cut, the center that formed is DC toughened glass liquid, outer package aluminosilicate glass or low
The glass material blank of Pyrex liquid.1000 DEG C of glass material blank temperature, be lamination green body.
(3) glass material blank that step (2) obtains is placed in shaping mechanism into lamination glass insulator, 500 DEG C of forming temperature.
(4) the laminated glass insulator that step (3) obtains is sent into liquid cooling bath through conveyer and is annealed to 45 DEG C automatically,
Room temperature laminated toughened glass insulator is formed through equipment cold wind again.
A kind of method preparing the laminated toughened glass insulator is further comprising the steps of: (1) leading to chapeau de fer and steel feet
It crosses cement glue to be bonded and fixed on vitreum, vitreum is set to another glass insulation by the inner hole sleeve of chapeau de fer by (2)
Son steel feet and by the locking pin locked, obtain laminated toughened glass insulator.
The cement glue the preparation method comprises the following steps: (1) in parts by weight by 60 parts of sulphate aluminium cement, lignin sulfonic acid
1 part of salt, 1 part of fire resisting swelling agent, 2 parts of defoaming agent, 2 parts of retarder, 17 parts of water mixing obtain mixture;(2) by step (1)
Obtained mixture is stirred, and is stirred 30 minutes, and temperature is controlled at 20 DEG C, then carries out water curing 3d, and it is 30 DEG C that water, which supports temperature,
Obtain cement glue.
Above embodiments only illustrate the embodiments of the present invention, and there is no have in any form the utility model
Limitation;It is any to be engaged in professional and technical personnel, it all has the ability to make some changes or modification using the technology contents disclosed, at
The utility model is simply modified, is equally become according to the utility model technical spirit for the equivalent embodiment of equivalent variations
Change and modify, is all within the scope of the technical scheme of the utility model.
Claims (7)
1. a kind of laminated toughened glass insulator, including vitreum (1), chapeau de fer (2) and steel feet (3), the vitreum (1) is exhausted
Edge main body, top center are lug boss, and lower end is full skirt;It is characterized by: the vitreum (1) is with once-through type tempering glass
Centered on glass (1.1), outer package aluminosilicate glass or low Pyrex layer (1.2);The chapeau de fer (2) is set in vitreum (1) top
On the lug boss at end, the steel feet (3) is arranged in the inner hole of vitreum (1) full skirt centre bottom;Chapeau de fer (2) and vitreum
(1) by one layer of cement glue between lug boss and between the inner hole at the full skirt center of steel feet (3) and vitreum (1)
(5) it bonds, chapeau de fer (2) and steel feet (3) is firmly combined together with vitreum (1).
2. insulator according to claim 1, it is characterised in that: DC toughened glass (1.1) the thickness 6-7mm.
3. insulator according to claim 1, it is characterised in that: the aluminosilicate glass or low Pyrex layer (1.2) are thick
Spend 0.6-0.8mm.
4. insulator according to claim 1, it is characterised in that: titanium dioxide coating on vitreum (1) outer surface
Layer (6).
5. insulator according to claim 1, it is characterised in that: be coated with Zinc oxide coating in the outer surface of chapeau de fer (2)
(7)。
6. insulator according to claim 1, it is characterised in that: coat Zinc oxide coating in the outer surface of steel feet (3)
(7)。
7. insulator according to claim 1, it is characterised in that: be equipped with locking pin (4) in the centre bore of chapeau de fer (2).