CN207916228U - A kind of removable adhering film to glass - Google Patents
A kind of removable adhering film to glass Download PDFInfo
- Publication number
- CN207916228U CN207916228U CN201721865451.7U CN201721865451U CN207916228U CN 207916228 U CN207916228 U CN 207916228U CN 201721865451 U CN201721865451 U CN 201721865451U CN 207916228 U CN207916228 U CN 207916228U
- Authority
- CN
- China
- Prior art keywords
- film
- layer
- base membrane
- glass
- repeatedly
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The utility model is related to a kind of removable adhering film to glass, it is by wearing layer（1）, first base membrane layer（2）, function glue-line（3）, second base membrane layer（4）, pressure-sensitive adhesive layer can be positioned repeatedly（5）With release protection film layer（6）It constitutes, and sequentially compoiste adhering is integrated each layer, wherein pressure-sensitive adhesive layer can be positioned repeatedly（5）Mixed material formed by pressure-sensitive adhesive, solvent, crosslinking agent can be positioned repeatedly, and it can be pressure-sensitive acrylate viscose glue that can position pressure-sensitive adhesive repeatedly, can also be polyurethanes pressure-sensitive adhesive.The utility model is related to a kind of removable adhering film to glass product can paste positioning repeatedly, and will not damage adherend surface during tearing patch repeatedly, adhesion strength will not be reduced because tearing patch repeatedly, and glue-line will not be transferred to adherend surface.
Description
Technical field
The utility model is related to a kind of removable adhering film to glass, are suitable for protection and the decoration of all kinds of glass surfaces.
Background technology
Adhering film to glass product, in order to reach stronger cohesive force, mostly uses the higher pressure-sensitive adhesive of peel strength in production
Agent enables film, by pressure-sensitive adhesive firm connection, to enhance safety, but product is after installation is complete in the presence of primary fixed with glass
Type, the case where patch cannot be torn repeatedly and replace position.In addition to glass door and window, interior still have more furniture glass, partition glass or
Minute surface etc. needs installation adhering film to glass to be protected or decorated, and can be pacified to pad pasting position according to actual conditions when in order to use
Dress or adjustment position, design a kind of removable adhering film to glass, make it can basis when glass or other smooth panels are installed
It needs to adjust position repeatedly.Removable adhering film to glass installation operation is simple and convenient and system can be designed according to environmental demand
It is standby, make it that can carry out designed, designed and repacking in smooth flat, is suitble at home and office space glass safety protects or decoration is answered
With.
Invention content
The purpose of this utility model is：There is provided it is a kind of have can the removable adhering film to glass of locating effect repeatedly technical side
The technical issues of case solves existing product and there is one-step building after installation is complete, cannot tear patch repeatedly and replace position.
To realize that the utility model aim, spy adopt the following technical scheme that：
A kind of preparation method of removable adhering film to glass, by 1, first base membrane layer 2 of wearing layer, function glue-line 3, second
Base membrane layer 4 can position pressure-sensitive adhesive layer 5 and the composition of release film 6 repeatedly, and sequentially compoiste adhering is integrated each layer；
In the above-mentioned technical solutions, first base membrane layer 2 and second base membrane layer 4 may each be polyester film, poly- carbon
Any type of acid esters, polychloroethylene film, polyurethane film, fluorinated ethylene propylene film；
Preferably, first base membrane layer 2 and second base membrane layer 4 can be transparent polyester film, printed polyester film, original
Any one of color polyester film, aluminized polyester film, magnetron sputtering polyester film.
The release film 6 can be polyester release film, fluorinated ethylene propylene film release film, makrolon release film, gather
Any type of ethylene release film or polyvinyl chloride release film.
In the above-mentioned technical solutions, on a surface of first base film layer 2, coating forms the mixture of wearing layer 1
After material, dry and photocuring obtains wearing layer 1, the mixing of coating functions glue-line on another surface of first base membrane layer 2
After material, dry and heat cure obtains function glue-line 3, second base membrane layer 4 a surface recombination in the outer of function glue-line 3
Surface, it is dry after coating forms the mixed material that can tear patch pressure-sensitive adhesive layer repeatedly on another surface of second base membrane layer 4
And heat cure obtains that patch pressure-sensitive adhesive layer 5 can be torn repeatedly, then release film 6 is compounded in tear repeatedly and pastes 5 outer surface of pressure-sensitive adhesive layer, from
And obtain a kind of removable adhering film to glass that each layer is complex as a whole.
In the above-mentioned technical solutions, a kind of thickness of removable adhering film to glass is 53~556 μm.
The utility model has the technical effect that：A kind of removable adhering film to glass has composite construction, it is by wearing layer 1, the
3, second one base membrane layer 2, function glue-line base membrane layers 4 can position pressure-sensitive adhesive layer 5 and the composition of release film 6 repeatedly, and each layer is pressed
Sequence compoiste adhering is integrated, and each layer has mutually synergistic effect.The low stripping force characteristic that pressure-sensitive adhesive layer 5 can be positioned repeatedly makes institute
The installation function for tearing patch and movement repeatedly can be realized by stating a kind of removable adhering film to glass, and product has good Electrostatic Absorption concurrently
Energy and venting quality are bonded effect with excellent with glass surface, install and use simple and fast.As long as being cut according to specific size
Afterwards, will a kind of outermost release film 6 of removable adhering film to glass remove after be pasted onto glass surface, by repeatedly paste with
It remains to keep good bonding patch performance, and the excellent characteristics with zero residue glue after stripping.
Description of the drawings
Fig. 1 is a kind of structural schematic diagram of removable adhering film to glass described in the utility model.
Specific implementation mode
The utility model is further described in detail below in conjunction with drawings and examples, but not limited.
Embodiment is raw materials used, is commercially available industrial goods unless otherwise stated, commercially available by commercial channel.
As shown in Figure 1, a kind of removable adhering film to glass, it is by 1, first base membrane layer 2 of wearing layer, function glue-line 3,
Two base membrane layers 4 can tear patch pressure-sensitive adhesive layer 5 and the composition of release film 6 repeatedly, and sequentially compoiste adhering is integrated each layer.
In the above-mentioned technical solutions, first base membrane layer 2 and second base membrane layer 4 may each be polyester film, poly- carbon
Any type of acid esters, polychloroethylene film, polyurethane film, fluorinated ethylene propylene film；
Preferably, it can be transparent polyester film, printed polyester film, primary colors to state first base membrane layer 2 and second base membrane layer 4
Any one of polyester film, aluminized polyester film, magnetron sputtering polyester film.
In the above-mentioned technical solutions, the release film 6 can be polyester release film, fluorinated ethylene propylene release film, gather
Any type of ethylene release film, polyvinyl chloride release film.
In the above-mentioned technical solutions, on a surface of first base membrane layer 2, coating forms the mixture of wearing layer 1
After material, dry and photocuring obtains wearing layer 1, the mixing of coating functions glue-line on another surface of first base membrane layer 2
After material, dry and heat cure obtains function glue-line 3, second base membrane layer 4 a surface recombination in the outer of function glue-line 3
Surface, it is dry after coating forms the mixed material that can tear patch pressure-sensitive adhesive layer repeatedly on another surface of second base membrane layer 4
And heat cure obtains that patch pressure-sensitive adhesive layer 5 can be torn repeatedly, then release film 6 is compounded in tear repeatedly and pastes 5 outer surface of pressure-sensitive adhesive layer, from
And obtain a kind of removable adhering film to glass that each layer is complex as a whole.
Optionally, first base membrane layer 2 and second base membrane layer 4 may be selected identical or different materials and be made；Optionally,
The base membrane layer for example can be but be not limited by mass coloration, magnetron sputtering, vacuum evaporation or cure process mode and add
Work；Optionally, the thickness of first base membrane layer 2 and second base membrane layer 4 can be the same or different；It is appreciated that
, when adhering film to glass includes more than two layers of base membrane layer, the material that each base membrane layer uses can be the same or different.
In the above-mentioned technical solutions, a kind of thickness of removable adhering film to glass is 53~556 μm.
It should be noted that although above-mentioned steps are to describe the operation of present embodiment with particular order, this is simultaneously
Undesired or hint must execute these operations according to the particular order.Function glue-line 3 in present embodiment and repeatedly
It tears in the raw material of patch pressure-sensitive adhesive layer 5 and contains adhesive, therefore, function glue-line 3 can be used as bonding agent and connect first base membrane layer 2
With second base membrane layer 4, patch pressure-sensitive adhesive layer 5 is torn repeatedly and can be used as bonding agent second base membrane layer 4 of connection and release film 6, this reality
Apply composite sequence when mode does not limit each functional layer and the preparation of base membrane layer.By the way that the compound glass that obtains of each functional layer is pasted
Film, simple process is flexible, for example, can be but be not limited to the adhering film to glass functional layer quantity, can pass through and increase and decrease each function
The quantity of layer meets the performance that sequence adjusts adhering film to glass.
It is as follows that embodiment prepares a kind of removable adhering film to glass concrete operations：
(A) prepare raw material
1. preparing base membrane layer and release film
Prepare the transparent polyester film that first base membrane layer 2 is 23 μm of thickness；It is 75 μm of thickness to prepare second base membrane layer 4
Printed polyester film with frosted finish effect；Prepare the polyester release film 6 that thickness is 36 μm；
2. wearing layer material prepares
It is 1.0 in mass ratio:The polyurethane acrylate paint that refractive index is 1.65 by 1.0 ratios；Ethyl acetate mixes
It stirs evenly, the mixed material for forming wearing layer is made, it is spare；
3. function glue-line material prepares
The mixed material for forming the function glue-line 3 is made of adhesive, solvent, ultraviolet absorber, crosslinking agent, specifically
Formula is shown in Table 1.
1 composite layer formula rate of table
| Component | Adhesive | Solvent | Ultraviolet absorber | Crosslinking agent |
| Ratio (wt%) | 64.00 | 34.00 | 1.20 | 0.80 |
Both each component is weighed by 1 formula ratio of table, by ultraviolet absorber and solvent toluene mixing 5-10 minutes, then
It is mixed 10-30 minutes, polyacrylate adhesives is added, after stirring 25 minutes, diisocyanates crosslinking agent is added again
Stirring 10-20 minutes, it is 80-110 centipoises to measure viscosity with Cai's grace cup, obtained to form the function glue for having ultraviolet-resistant function
The mixed material of layer, saves backup；
4. patch pressure-sensitive adhesive layer material can be torn repeatedly to prepare
The mixed material that pressure-sensitive adhesive layer 5 can be positioned repeatedly can be by weight including the following raw material：Polyacrylic acid
30-50 parts of ester pressure-sensitive adhesive, 20-40 parts of solvent, 0-5.0 parts of ultraviolet absorber, 5-50 parts of diisocyanates crosslinking agent),
Can also be includes following raw material by weight：20-40 parts of polyurethanes pressure-sensitive adhesive, 30-50 parts of solvent, ultraviolet absorber
0-5.0 parts, 5-50 parts of diisocyanates crosslinking agent.Wherein diisocyanates crosslinking agent can be two isocyanide of diphenyl methane
Acid esters, 1,6- hexamethylene diisocyanates, isophorone diisocyanate, diisocyanate trimer or polyisocyanates.
(B) a kind of removable adhering film to glass is prepared
On a surface of first base membrane layer 2, after coating forms the mixed material of wearing layer 1, dry and photocuring
Wearing layer 1 is obtained, on another surface of first base membrane layer 2 after the mixed material of coating functions glue-line, dry and thermosetting
Change obtains function glue-line 3, has the function of a surface recombination of second base membrane layer 4 of frosted finish effect in the outer surface of glue-line 3,
After coating forms the mixed material that can tear patch pressure-sensitive adhesive layer repeatedly on another surface of first base membrane layer 4, dry and heat
Solidification obtains that patch pressure-sensitive adhesive layer 5 can be torn repeatedly, then release film 6 is compounded in tear repeatedly and pastes 5 outer surface of pressure-sensitive adhesive layer, to
A kind of removable adhering film to glass (as shown in Fig. 1) being complex as a whole to each layer.
(C) a kind of removable adhering film to glass performance is detected
A kind of performance of removable adhering film to glass of above-mentioned preparation is detected, the results are shown in Table 2.
A kind of removable adhering film to glass performance test table of table 2
Note：In table 2, each item data is that removable glass a kind of to the utility model made from embodiment pastes as follows
Film is detected acquisition.
A kind of removable adhering film to glass provided by the utility model is can be seen that from 2 testing result of table, is had good
Low stripping force and have the effect of tear-off repeatedly, while there are wear-resisting and decoration functions again, can be installed on office partitions or
Glass surface, the design of frosted finish effect is needed so that privacy can be decorated and covered while not influencing daylighting at home.
Claims (5)
1. a kind of removable adhering film to glass, which is characterized in that it is by wearing layer (1), first base membrane layer (2), function glue-line
(3), second base membrane layer (4), pressure-sensitive adhesive layer (5) and release film (6) can be positioned repeatedly constitute, and sequentially compoiste adhering is each layer
One.
2. a kind of removable adhering film to glass according to claim 1, which is characterized in that first base membrane layer (2) and
Second base membrane layer (4) is appointing in polyester film, polycarbonate membrane, polychloroethylene film, polyurethane film, fluorinated ethylene propylene film
What is a kind of.
3. a kind of removable adhering film to glass according to claim 1, which is characterized in that the release film (6) be polyester from
Appointing in type film, fluorinated ethylene propylene film release film, makrolon release film, polyethylene release film, polyvinyl chloride release film
What is a kind of.
4. a kind of removable adhering film to glass according to claim 1, which is characterized in that first base membrane layer (2) and second
A base membrane layer (4) thickness is 12~188 μm, and the thickness of two base membrane layers is identical, or different.
5. a kind of removable adhering film to glass according to claim 1, which is characterized in that a kind of removable adhering film to glass
Thickness be 53~556 μm.