CN207692155U - A kind of anti-excessive glue, the reinforcement harden structure of high temperature tablet pressing - Google Patents
A kind of anti-excessive glue, the reinforcement harden structure of high temperature tablet pressing Download PDFInfo
- Publication number
- CN207692155U CN207692155U CN201820108993.8U CN201820108993U CN207692155U CN 207692155 U CN207692155 U CN 207692155U CN 201820108993 U CN201820108993 U CN 201820108993U CN 207692155 U CN207692155 U CN 207692155U
- Authority
- CN
- China
- Prior art keywords
- glue
- polyester
- line
- excessive glue
- excessive
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The utility model discloses the reinforcement harden structures that a kind of anti-excessive glue, high temperature tablet press, including biaxially oriented polyester film, polyester oil layer of ink, anti-excessive glue polyester hot melting glue-line, polyester glue-line and matt film, the polyester oil layer of ink is arranged in the lower surface of the biaxially oriented polyester film, the anti-excessive glue polyester hot melting glue-line is arranged in the lower surface of the polyester oil layer of ink, the polyester glue-line is arranged in the lower surface of the anti-excessive glue polyester hot melting glue-line, and the matt film is arranged in the lower surface of the polyester glue-line.Peel strength test (glue-line and the pressing of 160 DEG C of glued membrane face, are vertically pullled, and machine speed is 100 ㎜/min) is carried out to the reinforcement harden structure of the anti-excessive glue, the pressing of high temperature tablet, measures peeling force >=1kg/cm；Using purl machine at a temperature of 210 DEG C, the anti-excessive glue, the reinforcement harden structure not excessive glue of high temperature tablet pressing after pressing 3 seconds.
Description
Technical field
The utility model is related to stiffening plate field more particularly to the reinforcement harden structures of a kind of anti-excessive glue, the pressing of high temperature tablet.
Background technology
Stiffening plate is called reinforcing plate, reinforcing plate, and support plate protects strong plate, reinforcing rib.Stiffening plate is used primarily in building, oil
Pipeline, machine construction equipment, electronic product etc..It is widely used in FPC flexible circuit boards in electronic product, stiffening plate mainly solves
The suppleness of flexible PCB improves the intensity of plugging position, facilitates the overall package of product.For stiffening plate and copper wire
Pressing production, hot pressing reinforcement are to be melted the thermmohardening glue of reinforced rubber sheet using high temperature, and make reinforcement glue using appropriate pressure
Piece is fitted tightly on product, and pressing mode includes roller pressing and tablet pressing.Wherein, the pressing-in temp highest of tablet pressing
Up to 210 DEG C, it is susceptible to glue-line excessive glue, influences the function of finished product, causes to generate a large amount of substandard products, increases being manufactured into for product
This.
Utility model content
The purpose of this utility model is that the reinforcement harden structure of a kind of anti-excessive glue of proposition, the pressing of high temperature tablet, is provided with anti-
Excessive glue polyester hot melting glue-line greatly improves the anti-excessive glue ability of stiffening plate, is pressed 3 seconds at a temperature of 210 DEG C using purl machine
Not excessive glue afterwards.
For this purpose, the utility model uses following technical scheme：
A kind of anti-excessive glue, the reinforcement harden structure of high temperature tablet pressing, including biaxially oriented polyester film, polyester oil layer of ink,
The polyester is arranged in the lower surface of anti-excessive glue polyester hot melting glue-line, polyester glue-line and matt film, the biaxially oriented polyester film
The anti-excessive glue polyester hot melting glue-line, the anti-excessive glue polyester hot-melt adhesive is arranged in the lower surface of ink layer, the polyester oil layer of ink
The polyester glue-line is arranged in the lower surface of layer, and the matt film is arranged in the lower surface of the polyester glue-line.
Preferably, the thickness of the biaxially oriented polyester film is 50 μm~250 μm, and the thickness of the polyester oil layer of ink is
1 μm~6 μm, the thickness of the anti-excessive glue polyester hot melting glue-line is 10 μm~42 μm, and the thickness of the polyester glue-line is 1 μm~8 μ
The thickness of m, the matt film are 20 μm~35 μm.
Preferably, the polyester oil layer of ink printing is covered in the biaxially oriented polyester film.
Preferably, the anti-excessive glue polyester hot melting glue-line coating is covered in the polyester oil layer of ink.
Preferably, the polyester glue-line coating is covered in the anti-excessive glue polyester hot melting glue-line.
Preferably, the matt film is covered in the polyester glue-line by combination process.
The anti-excessive glue polyester hot melting glue-line is the polyester hot-melt adhesive containing aerosil, greatly improves the reinforcement
The anti-excessive glue ability of plate；Polyester glue-line can effectively increase the bonding force of glue-line and metal wire；Matt film can increase micropore, in turn
Enhance the viscous metal power of glue and metal wire.Peel strength is carried out to the reinforcement harden structure of the anti-excessive glue, the pressing of high temperature tablet
Test (glue-line and the pressing of 160 DEG C of glued membrane face, vertically pull, machine speed is 100 ㎜/min), measures peeling force >=1kg/cm；It uses
Purl machine is at a temperature of 210 DEG C, the anti-excessive glue, the reinforcement harden structure not excessive glue of high temperature tablet pressing after pressing 3 seconds.
Description of the drawings
Attached drawing is described further the utility model, but the content in attached drawing does not constitute any limit to the utility model
System.
Fig. 1 is the reinforcement plate structure schematic diagram of the one of embodiment of the utility model.
Wherein：Biaxially oriented polyester film 1；Polyester oil layer of ink 2；Anti- excessive glue polyester hot melting glue-line 3；Polyester glue-line 4；Delustring
Film 5.
Specific implementation mode
Further illustrate the technical solution of the utility model below with reference to the accompanying drawings and specific embodiments.
The anti-excessive glue of the present embodiment, the reinforcement harden structure of high temperature tablet pressing, as shown in Figure 1, including biaxial stretching polyester
Film 1, polyester oil layer of ink 2, anti-excessive glue polyester hot melting glue-line 3, polyester glue-line 4 and matt film 5, the biaxially oriented polyester film
The polyester oil layer of ink 2 is arranged in 1 lower surface, and the anti-excessive glue polyester hot-melt adhesive is arranged in the lower surface of the polyester oil layer of ink 2
The polyester glue-line 4 is arranged in the lower surface of layer 3, the anti-excessive glue polyester hot melting glue-line 3, and the lower surface of the polyester glue-line 4 is set
Set the matt film 5.
The anti-excessive glue polyester hot melting glue-line 3 is the polyester hot-melt adhesive containing aerosil, greatly improves the benefit
The anti-excessive glue ability of strong plate；Polyester glue-line 4 can effectively increase the bonding force of glue-line and metal wire；Matt film 5 can increase micropore,
And then enhance the viscous metal power of glue and metal wire.The reinforcement harden structure of the anti-excessive glue, the pressing of high temperature tablet is removed
Strength test (glue-line and the pressing of 160 DEG C of glued membrane face, vertically pull, machine speed is 100 ㎜/min), measures peeling force >=1kg/cm；
Using purl machine at a temperature of 210 DEG C, the anti-excessive glue, the reinforcement harden structure not excessive glue of high temperature tablet pressing after pressing 3 seconds；Energy
It is widely used on the connection wires of products such as printer, scanner, duplicator, sound equipment, projecting apparatus and various small household appliances.
Preferably, the thickness of the biaxially oriented polyester film 1 is 50 μm~250 μm, the thickness of the polyester oil layer of ink 2
It it is 1 μm~6 μm, the thickness of the anti-excessive glue polyester hot melting glue-line 3 is 10 μm~42 μm, and the thickness of the polyester glue-line 4 is 1 μm
~8 μm, the thickness of the matt film 5 is 20 μm~35 μm.Such as the thickness of the biaxially oriented polyester film 1 is set as 50
μm, the thickness of the polyester oil layer of ink 2 is 1 μm, and the thickness of the anti-excessive glue polyester hot melting glue-line 3 is 10 μm, the polyester adhesive
The thickness of layer 4 is 1 μm, and the thickness of the matt film 5 is 20 μm；Or it sets the thickness of the biaxially oriented polyester film 1 to
200 μm, the thickness of the polyester oil layer of ink 2 is 3 μm, and the thickness of the anti-excessive glue polyester hot melting glue-line 3 is 30 μm, the polyester
The thickness of glue-line 4 is 4 μm, and the thickness of the matt film 5 is 25 μm；Or the thickness of the biaxially oriented polyester film 1 is arranged
It it is 250 μm, the thickness of the polyester oil layer of ink 2 is 6 μm, and the thickness of the anti-excessive glue polyester hot melting glue-line 3 is 42 μm, described poly-
The thickness of ester gum layer 4 is 8 μm, and the thickness of the matt film 5 is 35 μm.
Preferably, the printing of polyester oil layer of ink 2 is covered in the biaxially oriented polyester film 1.
Preferably, the anti-coating of excessive glue polyester hot melting glue-line 3 is covered in the polyester oil layer of ink 2.
Preferably, the coating of polyester glue-line 4 is covered in the anti-excessive glue polyester hot melting glue-line 3.
Preferably, the matt film 5 is covered in the polyester glue-line 4 by combination process.
On biaxially oriented polyester film 1, polyester oil layer of ink 2 is coated using printing technology, then use coating process according to
It is secondary to coat anti-excessive glue polyester hot melting glue-line 3 and polyester glue-line 4, last compound one layer of matt film 5.
The technical principle of the utility model is described above in association with specific embodiment.These descriptions are intended merely to explain this reality
With novel principle, and it cannot be construed to the limitation to scope of protection of the utility model in any way.Based on the explanation herein,
Those skilled in the art would not require any inventive effort the other specific implementation modes that can associate the utility model,
These modes are fallen within the scope of protection of the utility model.
Claims (6)
1. the reinforcement harden structure of a kind of anti-excessive glue, high temperature tablet pressing, it is characterised in that：Including biaxially oriented polyester film, gather
Ester oil layer of ink, anti-excessive glue polyester hot melting glue-line, polyester glue-line and matt film, the lower surface setting of the biaxially oriented polyester film
The anti-excessive glue polyester hot melting glue-line is arranged in the lower surface of the polyester oil layer of ink, the polyester oil layer of ink, and the anti-excessive glue is poly-
The polyester glue-line is arranged in the lower surface of ester hot melt adhesive layer, and the matt film is arranged in the lower surface of the polyester glue-line.
2. the reinforcement harden structure of anti-excessive glue according to claim 1, high temperature tablet pressing, it is characterised in that：It is described two-way
The thickness of oriented polyester film is 50 μm~250 μm, and the thickness of the polyester oil layer of ink is 1 μm~6 μm, the anti-excessive glue polyester
The thickness of hot melt adhesive layer is 10 μm~42 μm, and the thickness of the polyester glue-line is 1 μm~8 μm, and the thickness of the matt film is 20 μ
M~35 μm.
3. the reinforcement harden structure of anti-excessive glue according to claim 1, high temperature tablet pressing, it is characterised in that：The polyester
Ink layer printing is covered in the biaxially oriented polyester film.
4. the reinforcement harden structure of anti-excessive glue according to claim 1, high temperature tablet pressing, it is characterised in that：It is described anti-excessive
The coating of glue polyester hot melting glue-line is covered in the polyester oil layer of ink.
5. the reinforcement harden structure of anti-excessive glue according to claim 1, high temperature tablet pressing, it is characterised in that：The polyester
Glue-line coating is covered in the anti-excessive glue polyester hot melting glue-line.
6. the reinforcement harden structure of anti-excessive glue according to claim 1, high temperature tablet pressing, it is characterised in that：The delustring
Film is covered in the polyester glue-line by combination process.