CN207391934U - Exempt to plate metal paperboard - Google Patents
Exempt to plate metal paperboard Download PDFInfo
- Publication number
- CN207391934U CN207391934U CN201721386456.1U CN201721386456U CN207391934U CN 207391934 U CN207391934 U CN 207391934U CN 201721386456 U CN201721386456 U CN 201721386456U CN 207391934 U CN207391934 U CN 207391934U
- Authority
- CN
- China
- Prior art keywords
- layer
- paperboard
- ink layer
- peeling
- exempt
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
Exempt to plate metal paperboard the utility model is related to one kind, including paperboard body；The paperboard body includes the paperboard layer, aqueous glue-line, ink layer and the peeling layer that are complex as a whole successively from bottom to top；The metallic particles that grain size is 20~100 μm is evenly distributed in the ink layer, the coating number of plies of ink layer is at least one layer, and every layer of ink layer is that dry-coated amount is 0.7~1.8g/m2Ink layer.The metal card paper structure of the utility model is simple, and not peeling-off layer infiltration is diffused in paperboard layer, the good leveling property of peeling layer, and surface is very smooth, brightness is high；In addition, the metal card of the utility model standby dosage using release coating and metallic particles made of paper is small, product is more environmentally friendly, and production cost is reduced.
Description
Technical field
The utility model is related to a kind of metal paperboards, particularly relate to one kind and exempt to plate metal paperboard.
Background technology
The latex that the making of current metal paperboard is mainly blended with metallic particles of the grain size less than 50 μm directly applies
Cloth makes to be formed on paperboard surface.The surface of the paperboards used due to the overwhelming majority is more coarse, and when latex coating is extremely difficult to
Good levelling effect causes metal paperboard uneven color obtained, and latex infiltration capacity is big or even pornographic condition thoroughly occurs,
Its dosage of latex is big, and production cost is high.
The content of the invention
The utility model provides one kind and exempts to plate metal paperboard, to overcome uneven color existing for existing metal paperboard,
Dosage of latex is big, it is of high cost the problem of.
The utility model adopts the following technical solution：
Exempt to plate metal paperboard, including paperboard body；The paperboard body includes the paperboard being complex as a whole successively from bottom to top
Layer, aqueous glue-line, ink layer and peeling layer.The metallic particles that grain size is 20~100 μm is evenly distributed in the ink layer, it is golden
The preferred copper particle of metallic particles, the preferred alumina particles of argentine particle, metallic particles by weight percentage for 10~20% ratios with
Release coating dispersion mixing uses reticulate pattern depth to be coated with for 45~100 μm of roller.The coating number of plies of ink layer is at least one
Layer, preferably the coating number of plies of ink layer are 1 layer either 2 or 3 layers.The coating weight of every layer of ink layer is：Wet coating amount 5~
12g/m2, dry-coated amount is in 0.7~1.8g/m2.Peeling layer is coated directly onto in PET film layer or BOPP light film layers, peeling layer
Coating weight be：Wet coating amount is in 5~10g/m2, dry-coated amount is in 0.7~1.5g/m2.Ink layer is to be coated directly onto peeling layer
On, be compounded with peeling layer, the PET film layer of ink layer or BOPP light film layer directly by aqueous glue-line and paperboard layer it is compound, dry
It is dry can obtain product, it is necessary to when can remove PET film layer or BOPP light film layers.
From the above-mentioned description to the utility model structure, compared to the prior art, the utility model has following excellent
Point：The metal card paper structure of the utility model is simple, and not peeling-off layer infiltration is diffused in paperboard layer, the levelling of peeling layer
Property is good, and surface is very smooth, brightness is high；In addition, the metal card of the utility model standby use release coating and metallic particles made of paper
Dosage it is small, product is more environmentally friendly, and production cost is reduced.
Description of the drawings
Fig. 1 is the schematic cross-sectional view of the metal paperboard of the utility model.
Fig. 2 is the schematic cross-sectional view for the metal paperboard for being compounded with PET or BOPP film layer.
Specific embodiment
Illustrate specific embodiment of the present utility model with reference to the accompanying drawings.
With reference to Fig. 1, exempt to plate metal paperboard, including paperboard body 1；The paperboard body 1 includes being complex as successively from bottom to top
Paperboard layer 11, aqueous glue-line 12, ink layer 13 and the peeling layer 14 of one.Be evenly distributed in the ink layer 13 grain size for 20~
100 μm of metallic particles, the preferred copper particle of golden metallic particle, the preferred alumina particles of argentine particle.Metallic particles is by weight
Percentage is 10~20% ratios and release coating dispersion mixing, and reticulate pattern depth is used to be coated with for 45~100 μm of roller.Ink
The coating number of plies of layer 13 is preferably 1 layer either 2 or 3 layers, is coated with 1 layer of ink layer 13 in the metal paperboard in Fig. 1, in Fig. 2
Metal paperboard in coating have three layers ink layer 13.The coating weight of every layer of ink layer 13 is：Wet coating amount is in 5~12g/m2, it is dry-coated
Cloth amount is in 0.7~1.8g/m2.Peeling layer 14 is coated directly onto in PET film layer or BOPP light film layer 15, the painting of peeling layer 14
Cloth amount is：Wet coating amount is in 5~10g/m2, dry-coated amount is in 0.7~1.5g/m2.Ink layer 13 is to be coated directly onto peeling layer 14
On, peeling layer 14, the PET film layer of ink layer 13 or BOPP light film layer 15 are compounded with directly by aqueous glue-line 12 and paperboard layer
11 is compound, drying can obtain product；Unstripped PET film layer as shown in Figure 2 or BOPP light film layer 15 can be to peeling layers
14 and the ink layer 13 containing metallic particles good protective effect is provided, can effectively reduce metal paperboard abrasive damage metal
Coating.PET film layer or BOPP light film layer 15 can be removed when needing, obtains metal paperboard shown in FIG. 1.The utility model
Metal card paper structure is simple, and not peeling-off layer 1413 is permeated, diffused in paperboard layer 11, the good leveling property of peeling layer 1413,
Surface is very smooth, brightness is high；In addition, the metal card of the utility model standby dosage using release coating and metallic particles made of paper
Small, product is more environmentally friendly, and production cost is reduced.
The above is only the specific embodiments of the present invention, but the design concept of the present invention is not limited thereto,
All non-essential modifications to the present invention made by this concept should all belong to the row for invading scope of protection of the utility model
For.
Claims (4)
1. exempt to plate metal paperboard, including paperboard body；It is characterized in that：The paperboard body includes being complex as successively from bottom to top
Paperboard layer, aqueous glue-line, ink layer and the peeling layer of one；The gold that grain size is 20~100 μm is evenly distributed in the ink layer
Metal particles, the coating number of plies of ink layer is at least one layer, and every layer of ink layer is that dry-coated amount is 0.7~1.8g/m2Ink layer.
2. as described in claim 1 exempt to plate metal paperboard, it is characterised in that：The coating number of plies of the ink layer is 2 or 3
Layer.
3. as described in claim 1 exempt to plate metal paperboard, it is characterised in that：The peeling layer be dry-coated amount be 0.7~
1.5g/m2Peeling layer.
4. as described in claim 1 exempt to plate metal paperboard, it is characterised in that：PET film layer is compounded with above the peeling layer
Or BOPP light film layers.