CN207310119U - A kind of container plate - Google Patents
A kind of container plate Download PDFInfo
- Publication number
- CN207310119U CN207310119U CN201721315169.1U CN201721315169U CN207310119U CN 207310119 U CN207310119 U CN 207310119U CN 201721315169 U CN201721315169 U CN 201721315169U CN 207310119 U CN207310119 U CN 207310119U
- Authority
- CN
- China
- Prior art keywords
- bamboo
- chip layer
- placed longitudinally
- full
- flattening
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The utility model discloses a kind of container plate, it includes the full bamboo flattening bamboo chip layer on placed longitudinally surface（1）, the full bamboo flattening bamboo chip layer at placed longitudinally middle part（2）Bamboo chip layer is flattened with the full bamboo of placed longitudinally bottom surface（3）, the full bamboo flattening bamboo chip layer on the placed longitudinally surface（1）Bamboo chip layer is flattened with the full bamboo at the placed longitudinally middle part（2）Between be equipped with the first laterally disposed wood chip layer（4）, the full bamboo flattening bamboo chip layer at the placed longitudinally middle part（2）Bamboo chip layer is flattened with the full bamboo of the placed longitudinally bottom surface（3）Between be equipped with the second laterally disposed wood chip layer（5）, it is every to bond hot pressing into an entirety between wood chip layer and bamboo chip layer between adjacent bamboo chip layer and wood chip layer, between wood chip layer and wood chip layer.This container plate has full bamboo utilization rate high, the advantages of simplifying production technology, save activity time and reduce production cost.
Description
Technical field
It the utility model is related to a kind of container plate.
Background technology
China is the native place of mao bamboon, on the south the Changjiang river, grows in the world 90% mao bamboon.It is distributed widely in 300~1000
The mountain forest area of rice.
China mao bamboon is wide in variety, aboundresources, and the speed of growth of mao bamboon is fast, power of regeneration is strong, with short production cycle, yield
Height, preferably protecting ecology and environmental protection, and mao bamboon has good intensity and toughness, and wood substituted by bamboo production container plate is gradual
As mainstream.
But in the production method of existing container plate, the full bamboo utilization rate also there is mao bamboon is not high, and structure owes to close
Reason, complex production process, production process is more, and intensity is general, and the easy aliquation in surface, anti-pressure ability is general, and production cost is high, during use
Between it is not long the deficiencies of and defect.
Utility model content
The technical problems to be solved in the utility model is:It is high to provide a kind of full bamboo utilization rate, production technology can be simplified, saved
Activity time and the container plate for reducing production cost.This container plate has intensity height, toughness is strong, anti-pressure ability is strong, uses
The advantages of time is long and has a wide range of application.
To solve the technical problem, the technical solution adopted in the utility model is：A kind of container plate, it includes longitudinal direction and puts
The full bamboo flattening bamboo chip layer on the surface put, the full bamboo flattening bamboo chip layer at placed longitudinally middle part and the full bamboo of placed longitudinally bottom surface
Bamboo chip layer is flattened, is flattened in the full bamboo flattening bamboo chip layer on the placed longitudinally surface and the full bamboo at the placed longitudinally middle part
The first laterally disposed wood chip layer is equipped between bamboo chip layer, the placed longitudinally middle part full bamboo flattening bamboo chip layer with it is described
The second laterally disposed wood chip layer is equipped between the full bamboo flattening bamboo chip layer of placed longitudinally bottom surface, it is per adjacent bamboo chip layer and wooden
Hot pressing is bonded into an entirety between wood chip layer and bamboo chip layer between lamella, between wood chip layer and wood chip layer.
The full bamboo flattening bamboo chip layer on the placed longitudinally surface, the full bamboo at placed longitudinally middle part flatten bamboo chip layer and indulge
Thickness to the full bamboo flattening bamboo chip layer of the bottom surface of placement is 5-7mm, length 2000mm-2500mm, width 1000mm-
1250mm。
The full bamboo flattening bamboo chip layer on the placed longitudinally surface, the full bamboo at placed longitudinally middle part flatten bamboo chip layer and indulge
Thickness to the full bamboo flattening bamboo chip layer of the bottom surface of placement is 6mm, length 2400mm, width 1160mm.
The first wood chip layer is 3-4 layers of wooden stamen plate.
The wooden stamen plate uses Eucalyptus or poplar.
The thickness of the wooden stamen flaggy for using Eucalyptus or poplar is 1-2mm, length 2000mm-2500mm, width
For 1000mm-1250mm.
The second wood chip layer is 3-4 layers of wooden stamen plate.
The wooden stamen plate uses Eucalyptus or poplar.
The thickness of the wooden stamen flaggy for using Eucalyptus or poplar is 1-2mm, length 2000mm-2500mm, width
For 1000mm-1250mm.
The second wood chip layer is 4 layers of the wooden stamen flaggy of Eucalyptus, and the thickness of the wooden stamen flaggy of every layer of Eucalyptus is 1.5mm,
Length is 2400mm, width 116mm.
The beneficial effects of the utility model are：
1st, full bamboo utilization rate is high.Available after as long as a full bamboo removes bluish yellow, the utilization rate of a full bamboo is up to
More than 92%.
2nd, intensity is high, toughness is strong, anti-pressure ability is strong.Substantially the original thickness of raw bamboo is maintained, that is, maintains original
The original intensity of bamboo and toughness, anti-pressure ability are strong.More than 6 times considerably beyond bamboo curtain splint intensity of its intensity.
3rd, simplify technique, save activity time, speed of production is fast.Container plate originally is up to more than 15 layers, and some is up to
21 layers, as long as and 7-9 layer now, not only reduced the dosage of material, but also reduce activity time, and can effectively improve work and give birth to
Yield, greatly reduces production cost.
4th, usage time is grown.Usage time is more than 5 times of bamboo curtain splint.
5th, have a wide range of application.Based on application container, it is each to also can be widely used to car floor and vessel bottom plate etc.
Aspect.
6th, there is good wearability and impact resistance.
7th, production cost is reduced.3000 yuan or so of every cubic metre of bamboo plate, and every cubic metre of Eucalyptus or poplar are 1200 yuan,
The dosage of part mao bamboon is substituted with Eucalyptus or poplar, can reach using required intensity and toughness and effectively reduce
Production cost.
8th, with material aspect：By the volume ratio with material, the volume of the full bamboo flattening bamboo of one piece of container plate accounts for a monoblock container
The volume of the 55-65% of plate bulk, Eucalyptus or poplar accounts for the 35-45% of a monoblock container plate volume.By the weight ratio with material, one
The weight of the full bamboo flattening bamboo of block container plate and the weight ratio of Eucalyptus or poplar are about 1:1.
Brief description of the drawings
Fig. 1 is that the structure of the utility model container plate shows that embodiment 1 is intended to.
Fig. 2 is that the structure of the utility model container plate shows that embodiment 2 is intended to.
Embodiment
The utility model will be further described below with reference to the accompanying drawings.
Referring to attached drawing 1-2：Embodiment 1：Sequentially consist of, first layer：Placed longitudinally bottom surface flattens bamboo chip layer 3, the
Two to five layers：Laterally disposed wooden stamen flaggy 54,53,52,51, layer 6：Placed longitudinally middle part flattening bamboo chip layer 2, the 7th
To ten layers：Laterally disposed wooden stamen flaggy 44,43,42,41, the placed longitudinally surface flattening bamboo chip layer 1 of eleventh floor.
Embodiment 2：Sequentially consist of, first layer：Placed longitudinally bottom surface flattening bamboo chip layer 3, the second to four layer：Laterally
The wooden stamen flaggy 53,52,51 placed, layer 5：Placed longitudinally middle part flattening bamboo chip layer 2, the six to eight layer：Laterally disposed
Wooden stamen flaggy 43,42,41, the 9th layer of placed longitudinally surface flattening bamboo chip layer 1.
The step of manufacture method of 1 bamboo and wood container plate of above-described embodiment is：
First by mao bamboon per segment saw into 2.0-2.5m, preferably every section 2.4m or 2.3m, then split into 2 half.
The bamboo splitted is softened into 6-8 in 160 DEG C -180 DEG C of high-temperature steam boiler
Minute；Preferably softening 7 minutes in 170 DEG C of high-temperature steam boiler.
The bamboo of softening in 15 minutes by bamboo chip flattening machine flattening-out into flattening bamboo chip；Thickness of the bamboo after bamboo chip flattening machine
For 5-7mm, length 2000-2500mm, width 100-200mm.Using thickness as 6mm, length 2400mm, width is
150mm is preferably.
Flattening bamboo chip planer after flattening-out is removed into bluish yellow.
The flattening bamboo chip both sides cut-off of bluish yellow will be removed.
Flattening bamboo chip after cut-off is Tumblied Dry, its temperature control is at 50 DEG C -60 DEG C, the 5-6 days time, with 55
DEG C, 5 days time or 6 days are preferably.
By the flattening bamboo chip of drying, wooden stamen plate gluing on gluing machine；
Flattening bamboo chip after gluing, wooden stamen plate are alternately placed into assembly in length and breadth by the Product Process requirement number of plies, under
It is supreme to be followed successively by placed longitudinally bottom flattening bamboo chip, laterally disposed 4 layers of wooden stamen plate, flattening bamboo chip, the horizontal stroke at placed longitudinally middle part
To 4 layers of wooden stamen plate of placement, the flattening bamboo chip on placed longitudinally surface.
The good blanket of assembly is transferred to hot pressing in hot press, 120 DEG C -130 DEG C of the temperature of hot pressing, compressive load per unit area is
10mPa-12mPa, time 28-32 minute；, 120 DEG C, compressive load per unit area 12mPa of the temperature of hot pressing, 30 minutes time was
It is good.
Container plate after release is down to room temperature ejecting plate naturally.
Wooden stamen plate uses Eucalyptus or poplar.It uses the thickness of the wooden stamen flaggy of Eucalyptus or poplar as 1-2mm, length
For 2000mm-2500mm, width 1000mm-1250mm.
The Eucalyptus of 4 layers of the first wood chip layer 4 use or the wooden stamen flaggy of poplar of embodiment 1, its every layer thickness are
1.5mm, length are 2400mm, and width is 1160mm.Second wood chip layer 5 is using 4 layers of Eucalyptus or the wooden stamen plate of poplar
Layer, its every layer thickness is 1.5mm, and length is 2400mm, and width is 1160mm.
The thickness of wooden every layer of stamen flaggy is 1-2 mm, using 1.5mm, 1.6mm, 1.7mm, 1.8mm, 1.9mm and 2.0mm as
It is good.If the thickness of wooden every layer of stamen flaggy can have an impact bonding strength more than 2.0mm.
By the volume ratio with material, the volume of the full bamboo flattening bamboo of one piece of container plate accounts for the 55- of a monoblock container plate volume
65%, the volume of Eucalyptus or poplar accounts for the 35-45% of a monoblock container plate volume；By the weight ratio with material, one piece of container plate
The weight and the weight ratio of Eucalyptus or poplar of full bamboo flattening bamboo are about 1:1.
The manufacture method of the bamboo and wood container plate of embodiment 2 is same as above.
The Eucalyptus of 3 layers of the first wood chip layer 4 use or the wooden stamen flaggy of poplar of embodiment 2, its every layer thickness are
2mm, length are 2400mm, and width is 1160mm.Second wood chip layer 5 uses 3 layers of Eucalyptus or the wooden stamen flaggy of poplar,
Its every layer thickness is 2mm, and length is 2400mm, and width is 1160mm.
Claims (10)
1. a kind of container plate, it is characterized in that, it includes the full bamboo flattening bamboo chip layer on placed longitudinally surface（1）, it is placed longitudinally
Middle part full bamboo flattening bamboo chip layer（2）Bamboo chip layer is flattened with the full bamboo of placed longitudinally bottom surface（3）, described placed longitudinally
The full bamboo flattening bamboo chip layer on surface（1）Bamboo chip layer is flattened with the full bamboo at the placed longitudinally middle part（2）Between be equipped with laterally put
The the first wood chip layer put（4）, the full bamboo flattening bamboo chip layer at the placed longitudinally middle part（2）With the placed longitudinally bottom surface
Full bamboo flattening bamboo chip layer（3）Between be equipped with the second laterally disposed wood chip layer（5）, per adjacent bamboo chip layer and wood chip layer it
Between, that hot pressing is bonded between wood chip layer and bamboo chip layer between wood chip layer and wood chip layer is overall into one.
2. a kind of container plate according to claim 1, it is characterized in that：The full bamboo flattening bamboo on the placed longitudinally surface
Lamella（1）, placed longitudinally middle part full bamboo flattening bamboo chip layer（2）Bamboo chip layer is flattened with the full bamboo of placed longitudinally bottom surface（3）
Thickness be 5-7mm, length 2000mm-2500mm, width 1000mm-1250mm.
3. a kind of container plate according to claim 2, it is characterized in that：The full bamboo flattening bamboo on the placed longitudinally surface
Lamella（1）, placed longitudinally middle part full bamboo flattening bamboo chip layer（2）Bamboo chip layer is flattened with the full bamboo of placed longitudinally bottom surface（3）
Thickness be 6mm, length 2400mm, width 1160mm.
4. a kind of container plate according to claim 1, it is characterized in that：The first wood chip layer（4）It is wooden for 3-4 layers
Stamen plate.
5. a kind of container plate according to claim 4, it is characterized in that：The wooden stamen plate uses Eucalyptus or poplar.
6. a kind of container plate according to claim 5, it is characterized in that：It is described using Eucalyptus or the wooden stamen flaggy of poplar
Thickness be 1-2mm, length 2000mm-2500mm, width 1000mm-1250mm.
7. a kind of container plate according to claim 1, it is characterized in that：The second wood chip layer（5）It is wooden for 3-4 layers
Stamen plate.
8. a kind of container plate according to claim 7, it is characterized in that：The wooden stamen plate uses Eucalyptus or poplar.
9. a kind of container plate according to claim 8, it is characterized in that：It is described using Eucalyptus or the wooden stamen flaggy of poplar
Thickness be 1-2mm, length 2000mm-2500mm, width 1000mm-1250mm.
10. a kind of container plate according to claim 7, it is characterized in that：The second wood chip layer（5）For 4 layers of Eucalyptus
Wooden stamen flaggy, the thickness of the wooden stamen flaggy of every layer of Eucalyptus is 1.5mm, length 2400mm, width 116mm.