CN206692722U - A kind of coating material - Google Patents
A kind of coating material Download PDFInfo
- Publication number
- CN206692722U CN206692722U CN201720259881.8U CN201720259881U CN206692722U CN 206692722 U CN206692722 U CN 206692722U CN 201720259881 U CN201720259881 U CN 201720259881U CN 206692722 U CN206692722 U CN 206692722U
- Authority
- CN
- China
- Prior art keywords
- layer
- thickness
- titanium
- coating material
- oxide layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The utility model discloses a kind of coating material, the coating material includes metal base substrate (0), and the metal base substrate (0) is followed successively by metal foil layer (1), indium tin oxide layer (2), titanium nitride layer (3), the first silicon oxide layer (4), titanium dioxide layer (5), zirconium nitride titanium layer (6), the second silicon oxide layer (7) and silicone polymer layer (8) from inside to outside.The utility model has very strong hydro-oleophobicity, does not glue effect, and fluid erosion prevention performance is good, increases the service life, and equipment service efficiency is high, dense uniform, and color is soft.
Description
Technical field
It the utility model is related to base material manufacturing technology field, and in particular to a kind of coating material.
Background technology
Since 18th century of Christian era, Treatment of Metal Surface become either research and develop or application it is upper, pole paid attention to and
Widely used technology, its main contents are the technologies such as plating and anodic corrosion protection, and through researching and developing improvement all the year round, such treatment technology is
Quite ripe, its finished product function tends to meet customer requirement and quality is good, but the limitation of seriously polluted and base material is it all the time
Maximum bottleneck.
The method for preparing CoPt thin magnetic films the most frequently used at present is magnetron sputtering method.Argon ion is accelerated and bombarded by negative electrode
Cathode target surface, target material surface atom sputtering is out deposited and forms film on the surface of the substrate.By changing unlike material
The target sputtering time different with control, can be to obtain the film of unlike material and different-thickness.Magnetron sputtering method has plated film
Layer and the advantages that adhesion of base material is strong, film plating layer is fine and close, uniform.With metal, alloy, low-valent metal compound or semiconductor material
Material is used as target cathode, thin with gas particle reaction generation compound in sputter procedure or in substrate surface deposits film forming procedure
Film, here it is reaction magnetocontrol sputtering.Reaction magnetocontrol sputtering is widely used in the production in enormous quantities of compound film.
At present, a kind of good coating material of hydrophobic oleophobic effect is lacked.
Utility model content
The purpose of this utility model is in view of the above-mentioned problems, providing a kind of hydrophobic oleophobic effect good coating material.
To reach above-mentioned purpose, the utility model employs following technical proposal:A kind of coating material of the present utility model,
The coating material includes metal base substrate, and the metal base substrate is followed successively by metal foil layer, tin indium oxide from inside to outside
Layer, titanium nitride layer, the first silicon oxide layer, titanium dioxide layer, zirconium nitride titanium layer, the second silicon oxide layer and silicone polymer layer.
Further, the thickness of the metal foil layer is 12~30nm, and the thickness of the indium tin oxide layer is 6~15nm,
The thickness of the titanium nitride layer is 8~12nm, and the thickness of first silicon oxide layer is 10~20nm.
Further, the thickness of the titanium dioxide layer is 10~16nm, the thickness of the zirconium nitride titanium layer for 10~
20nm, the thickness of second silicon oxide layer is 6~12nm, and the thickness of the silicone polymer layer is 12~16nm.
Further, the material of the metal base substrate is iron, copper or stainless steel.
Beneficial effect:The utility model has very strong hydro-oleophobicity, does not glue effect, and fluid erosion prevention performance is good, and extension makes
With the life-span, equipment service efficiency is high, dense uniform, and color is soft.
Compared with prior art, the utility model has the following advantages that:
(1) the utility model membrane system is formed using metal foil layer and metal nitride, and metal foil layer is used for transition and improved
Membranous layer binding force, metal nitride possess higher hardness, rub resistance and decay resistance.
(2) the utility model is that primary raw material carries out disperse combination processing to coating using silicon polymer resin, is formed and closed
Gold-polymer composite coating.Alloy particle and crosslinked polymer are firm in coating, and coating surface can be low, have very strong dredge
Water, oleophobic, do not glue effect.
(3) the utility model film layer outermost layer is zirconium nitride film, can improve fluid erosion prevention performance, the rub resistance of overall film layer
While performance, possesses low coefficient of friction, film layer coefficient of friction is less than 0.36, improves fluid erosion prevention energy of the present utility model
Power.
Brief description of the drawings
Fig. 1 is the schematic diagram of coating material of the present utility model;
Wherein, 0 metal base substrate, 1 metal foil layer, 2 indium tin oxide layers, 3 titanium nitride layers, 4 first silicon oxide layers, 5 two
Titanium oxide layer, 6 zirconium nitride titanium layers, 7 second silicon oxide layers, 8 silicone polymer layers.
Embodiment
It is new to this practicality below with reference to accompanying drawing to make the purpose of this utility model, technical scheme and advantage clearer
The embodiment of type is described in further detail.
Embodiment 1
A kind of coating material of the present utility model, the coating material include metal base substrate 0, the metal base base
Bottom 0 is followed successively by metal foil layer 1, indium tin oxide layer 2, titanium nitride layer 3, the first silicon oxide layer 4, titanium dioxide layer 5, nitrogen from inside to outside
Change zirconium titanium layer 6, the second silicon oxide layer 7 and silicone polymer layer 8.
The thickness of the metal foil layer 1 is 12nm, and the thickness of the indium tin oxide layer 2 is 15nm, the titanium nitride layer 3
Thickness is 10nm, and the thickness of first silicon oxide layer 4 is 10nm.
The thickness of the titanium dioxide layer 5 is 14nm, and the thickness of the zirconium nitride titanium layer 6 is 10nm, second oxidation
The thickness of silicon layer 7 is 6nm, and the thickness of the silicone polymer layer 8 is 16nm.
The material of the metal base substrate 0 is stainless steel.
Embodiment 2
The difference of embodiment 2 and embodiment 1 is:A kind of coating material of the present utility model, the thickness of the metal foil layer 1
Spend for 20nm, the thickness of the indium tin oxide layer 2 is 6nm, and the thickness of the titanium nitride layer 3 is 8nm, first silicon oxide layer
4 thickness is 16nm.
The thickness of the titanium dioxide layer 5 is 10nm, and the thickness of the zirconium nitride titanium layer 6 is 20nm, second oxidation
The thickness of silicon layer 7 is 10nm, and the thickness of the silicone polymer layer 8 is 12nm.
The material of the metal base substrate 0 is iron.
Embodiment 3
The difference of embodiment 3 and embodiment 1 is:A kind of coating material of the present utility model, the thickness of the metal foil layer 1
Spend for 30nm, the thickness of the indium tin oxide layer 2 is 13nm, and the thickness of the titanium nitride layer 3 is 12nm, first silica
The thickness of layer 4 is 20nm.
The thickness of the titanium dioxide layer 5 is 16nm, and the thickness of the zirconium nitride titanium layer 6 is 15nm, second oxidation
The thickness of silicon layer 7 is 12nm, and the thickness of the silicone polymer layer 8 is 14nm.
The material of the metal base substrate 0 is copper.
Although metal base substrate 0, metal foil layer 1, indium tin oxide layer 2, titanium nitride layer 3, have more been used herein
The terms such as one silica layer 4, titanium dioxide layer 5, zirconium nitride titanium layer 6, the second silicon oxide layer 7 and silicone polymer layer 8, but simultaneously
It is not excluded for the possibility using other terms.It is used for the purpose of more easily describing and explaining the utility model using these terms
Essence;Any additional limitation is construed as all to disagree with the utility model spirit.
Specific embodiment described herein is only to the utility model spirit explanation for example.The utility model institute
Category those skilled in the art can make various modifications or supplement to described specific embodiment or using similar
Mode substitute, but without departing from spirit of the present utility model or surmount scope defined in appended claims.
Claims (4)
- A kind of 1. coating material, it is characterised in that:The coating material includes metal base substrate (0), the metal base base Bottom (0) is followed successively by metal foil layer (1), indium tin oxide layer (2), titanium nitride layer (3), the first silicon oxide layer (4), dioxy from inside to outside Change titanium layer (5), zirconium nitride titanium layer (6), the second silicon oxide layer (7) and silicone polymer layer (8).
- 2. coating material according to claim 1, it is characterised in that:The thickness of the metal foil layer (1) is 12~30nm, The thickness of the indium tin oxide layer (2) is 6~15nm, and the thickness of the titanium nitride layer (3) is 8~12nm, first oxidation The thickness of silicon layer (4) is 10~20nm.
- 3. coating material according to claim 2, it is characterised in that:The thickness of the titanium dioxide layer (5) be 10~ 16nm, the thickness of the zirconium nitride titanium layer (6) is 10~20nm, and the thickness of second silicon oxide layer (7) is 6~12nm, institute The thickness for stating silicone polymer layer (8) is 12~16nm.
- 4. coating material according to claim 3, it is characterised in that:The material of the metal base substrate (0) is iron, copper Or stainless steel.