CN206535993U - Continuous casting flow control molding casting siphon spout device - Google Patents
Continuous casting flow control molding casting siphon spout device Download PDFInfo
- Publication number
- CN206535993U CN206535993U CN201720261150.7U CN201720261150U CN206535993U CN 206535993 U CN206535993 U CN 206535993U CN 201720261150 U CN201720261150 U CN 201720261150U CN 206535993 U CN206535993 U CN 206535993U
- Authority
- CN
- China
- Prior art keywords
- flow control
- comer
- molten steel
- siphon
- crystallizer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
A kind of continuous casting flow control molding casting siphon spout device, the tedge at the siphon mouth of a river, horizontal inclined tube and down-comer are welded across middle containment wall, tedge insertion tundish, down-comer insertion crystallizer successively；Flow control slide plate is arranged on position on the upper side in the middle part of down-comer, and molten steel caching Bao Yitou is connected with down-comer top, and connection aspiration pump in other end is with its method poured into a mould：Tedge inserts tundish, and down-comer insertion crystallizer adjusts and fixes siphon mouth of a river position, flow control slide plate is remained turned-off, and after tundish molten steel rises and reaches and open and pour liquid level, opens aspirator valve, in gas in suction channel, molten steel injection crystallizer, completion, which is opened, pours；Adjust flow control slide plate opening degree and carry out flow control operation, flow control slide plate is closed when stopping pouring.The utility model can the mouth of a river of on-line control siphon at any time insert the depth of crystallizer, improve Mold flow field, adjust slag line attack sites.The horizontally disposed pattern of " left, center, right ", improves continuous casting system.
Description
Technical field
The utility model belongs to steel industry continuous casting flow control molding casting application field, more particularly to a kind of simply high
The continuous casting flow control molding casting siphon spout device of effect.
Background technology
Continuous casting is the technical process for molten steel being cast into solid strand, and molten steel flows into middle from the long nozzle of ladle bottom
Bag, then the submersed nozzle from tundish downstream is continuously injected into water mold, is cooled into definite shape and thickness
Green shell, from crystallizer outlet pull straight, form strand after being solidified through water-spraying control.In the 1950s, being used as steel work
The steel Development of Continuous Casting Technique of industry revolution mark gets up, compared with conventional molding techniques, and there is continuous casting metal recovery rate height, energy to disappear
The low advantage of consumption, the realization of sequence casting more simplifies steel making working procedure, and production efficiency is improved.
In casting process, flowing of the molten steel in tundish and crystallizer is a kind of multiphase flow and non-stationary flow, while companion
With a large amount of fine motions being mingled with and the heat transfer of molten steel, tundish and crystallizer be then by submersed nozzle and stopper or
Sliding plate flow-control system connectivity is with blocking.Traditional submersed nozzle is arranged on tundish bottom, and molten steel leans on molten steel in tundish
Static pressure flows into tundish bottom outlet, through submersed nozzle molding casting, injects in crystallizer.The research of current people is main
The research concentrated in terms of material, shape, structure, additional device and the function of submersed nozzle, but be all confined to be arranged on
The mode of tundish bottom, i.e. tundish, submersed nozzle, crystallizer are the vertical arrangement arrangements of upper, middle and lower.To existing company
The case study for casting system equipment arrangement finds that the arrangement podium level of upper, middle and lower is big, and molten steel impact can be strong, system energy
Consumption is high.
During traditional continuous casting flow control molding casting, there is whirlpool to conflux at middle water containing opening, molten steel stream in submersed nozzle
Fast high, impact is big, makes Mold flow field complicated.
Utility model content
In order to solve prior art presence go out many defects, the purpose of this utility model is to provide a kind of casting process molten steel
The siphon spout device of molding casting, the device improves traditional continuous casting system, and continuous casting is carried out using the device
The continuous casting platform total height in workshop can be reduced, it is adaptable to the technological improvement of existing steel plant's continuous casting process.
Realize that above-mentioned purpose uses following technical scheme：
A kind of siphon spout device, the siphon mouth of a river is arranged between molten steel crystallizer and tundish, including siphon piping, is taken out
Inhale device, flow control slide plate, it is characterised in that described siphon piping is divided into tedge, horizontal inclined tube and down-comer, tedge,
Horizontal inclined tube and down-comer are closely connected in middle containment wall, tedge bottom insertion tundish successively, the water of horizontal inclined tube
Flat angle is 30 ~ 45 degree, the bottom insertion crystallizer of down-comer；Flow control slide plate is arranged on position on the upper side in the middle part of down-comer, is located at
Between aspirator and crystallizer molten steel liquid level；Aspirator is that molten steel caches bag, and molten steel caching bag sets up two tube heads, one separately
It is connected with down-comer top, connection aspiration pump in other end is provided with control valve between molten steel caching bag and down-comer；Described
Tundish, the siphon mouth of a river, crystallizer are arranged according to the horizontal pattern of left, center, right.
Further, described tedge, horizontal inclined tube are identical with down-comer specification, and material is identical.
Further, rise tube inlet close to tundish bottom and plane of inlet is higher than crystallizer molten steel liquid when stabilization is poured into a mould
Face.
Further, flow control slide plate is the sliding panel with open and close function.
Compared with prior art, the utility model uses tundish, submersed nozzle, the horizontal cloth of crystallizer " left, center, right "
Pattern is put, continuous casting system is improved, compared to traditional continuous casting, it is possible to decrease the continuous casting platform total height in workshop.The utility model
The siphon mouth of a river of setting breaches conventional thought, and during its flow control molding casting, tundish confluxes without whirlpool, and in the mouth of a river
Molten steel flow velocity is low.Siphon mouth of a river down-comer and crystallizer convenience, accurate centering, can on-line control alignment degree, and without moving at any time
Dynamic tundish；Can the mouth of a river of on-line control siphon at any time insert the depth of crystallizer, improve Mold flow field, adjust slag line
Attack sites.
Brief description of the drawings
Fig. 1 is continuous casting siphon mouth of a river flow control molding casting artwork.
Marked in figure：Aspiration pump 1, molten steel caching bag 2, valve 3, tundish molten steel 4, tundish 5, tedge 6, level is oblique
Pipe 7, down-comer 8, flow control slide plate 9, crystallizer 10, crystallizer molten steel 11, covering slag 12.
Embodiment
Following examples are used to illustrate the utility model, but can not be used for limiting protection domain of the present utility model.Implement
Condition in example can be adjusted according to actual conditions is further, and unaccounted condition is normal condition.
See Fig. 1, a kind of siphon spout device, the siphon spout device is arranged between molten steel crystallizer and tundish, rainbow
Water sucking mouth device is made up of siphon piping, aspirator, flow control slide plate etc..Siphon piping is divided into tedge 6, the and of horizontal inclined tube 7
Down-comer 8, tedge 6, horizontal inclined tube 7 and down-comer 8 are welded as a whole successively, across in the containment wall of tundish 5, tedge 6
In the tundish molten steel 4 of bottom insertion tundish, the entrance of tedge 6 is close to the bottom of tundish 4 and plane of inlet is higher than stable pour
The liquid level of crystallizer molten steel 11 during note.Horizontal inclined tube 7 is located between tedge 6 and down-comer 8, the horizontal sextant angle of horizontal inclined tube 7
For 30 ~ 45 degree, the bottom of down-comer 8 is rushed across in the crystallizer molten steel 11 of the insertion crystallizer 10 of covering slag 12；Tedge 6, level
It is identical that specification is made using refractory material with down-comer 8 in inclined tube 7.Flow control slide plate 9 is the sliding panel with open and close function.Peace
Mounted in the middle part of down-comer 8 position on the upper side, between aspirator and crystallizer molten steel liquid level；Aspirator is that molten steel caches bag
2, molten steel caching bag 2 sets up two tube heads separately, and one is connected with the top of down-comer 9, other end connection aspiration pump 1, molten steel caching bag 2
Control valve 3 is installed between down-comer 9.
Siphon piping, molten steel caching bag are respectively that refractory material is made.Tundish 5, the siphon mouth of a river, crystallizer 10 according to
The horizontal pattern arrangement of left, center, right.
With the method for siphon mouth of a river continuous casting flow control molding casting, it is characterised in that methods described includes：
A. by siphon mouth of a river pipeline across middle containment wall, tedge 6 inserts tundish, and the entrance of tedge 6 is close to tundish 4
The liquid level of crystallizer molten steel 11 when bottom and plane of inlet are higher than stable cast.
Down-comer 7 inserts crystallizer 10, adjusts and fixes siphon mouth of a river position, flow control slide plate 9 is remained turned-off；
B. after tundish molten steel 4 rises and reaches and open and pour liquid level, the gas in aspirator valve 3, suction channel is opened,
Tundish molten steel 4 opens flow control slide plate 9 from after tedge 6 flows into down-comer 8 through horizontal inclined tube 7, closes aspirator valve 3,
In molten steel injection crystallizer 10, completion, which is opened, pours；
C. according to the liquid level of crystallizer molten steel 11 and the liquid level situation of tundish molten steel 4 during molding casting, adjustment flow control is slided
The opening degree of plate 9 carries out flow control operation；
When d. stopping pouring, close flow control slide plate 9 and stop cast.
During molding casting, if the siphon mouth of a river blocks the mouth of a river because of field trash dross, a new siphon water is inserted side by side
Mouthful, the old siphon mouth of a river under quick replacement.
Specific embodiment is as follows：
Embodiment 1
By tedge 6, horizontal inclined tube 7, the down-comer 8 of the siphon mouth of a river pipeline being made of refractory material, connect successively,
The entrance of tedge 6 is close to the bottom of tundish 5 and plane of inlet is higher than the liquid level of crystallizer molten steel 11, horizontal inclined tube 7 when stabilization is poured into a mould
Horizontal sextant angle be 30 degree；The molten steel caching bag 2 being made of refractory material, sets up separately on two tube heads, a connection down-comer 8
Portion, a connection aspiration pump 1；Flow control slide plate 9 is arranged on the upper side in the middle part of down-comer 8, positioned at aspirator and crystallizer molten steel 11
Between liquid level.
The method of siphon mouth of a river flow control molding casting is：By siphon mouth of a river pipeline across the wall of tundish 5, tedge 6 is inserted
60t tundish 5, down-comer 8 inserts 150 × 150mm billet moulds 10, adjusts and fixes siphon mouth of a river position, flow control
Slide plate 9 is remained turned-off；After tundish molten steel 5 is risen to away from bag bottom 800mm, open in aspirator valve 3, suction channel
Gas, tundish molten steel 4 is from after tedge 6 flows into down-comer 8 through horizontal inclined tube 7, and it is 100% to open the opening degree of flow control slide plate 9,
Close in aspirator valve 3, molten steel injection crystallizer 10, completion, which is opened, pours.According to crystallizer molten steel 11 during molding casting
Liquid level and the liquid level situation of tundish molten steel 4, the opening degree of adjustment flow control slide plate 9 carry out flow control operation 65 ~ 80%；Molding casting mistake
Cheng Zhong, if the siphon mouth of a river blocks the mouth of a river because of field trash dross, can insert old under a new siphon mouth of a river, quick replacement side by side
The siphon mouth of a river；When stopping pouring, close flow control slide plate 9 and stop cast.
Embodiment 2
By tedge 6, horizontal inclined tube 7, the down-comer 8 of the siphon mouth of a river pipeline being made of refractory material, connect successively,
The entrance of tedge 6 is close to the bottom of tundish 5 and plane of inlet is higher than the liquid level of crystallizer molten steel 11, horizontal inclined tube 7 when stabilization is poured into a mould
Horizontal sextant angle be 35 degree；The molten steel caching bag 2 for the aspirator that refractory material is made, sets up two tube heads separately, under a connection
The top of pipe 8, a connection aspiration pump 1 drop；Flow control slide plate 9 is arranged on the upper side in the middle part of down-comer 8, positioned at aspirator and crystallizer
Between the liquid level of molten steel 11.
Method with siphon mouth of a river flow control molding casting is：By siphon mouth of a river pipeline across the wall of tundish 5, tedge 6 is inserted
Enter 60t tundish 5, down-comer 8 inserts 200 × 350mm rectangular-blank crystallizers 10, adjusts and fix siphon mouth of a river position, controls
Fluent plate 9 is remained turned-off；After tundish molten steel 5 is risen to away from bag bottom 700mm, open in aspirator valve 3, suction channel
Gas, tundish molten steel 4 is from after tedge 6 flows into down-comer 8 through horizontal inclined tube 7, and opening the opening degree of flow control slide plate 9 is
100%, close in aspirator valve 3, molten steel injection crystallizer 10, completion, which is opened, pours；According to crystallizer steel during molding casting
The liquid level of liquid 11 and the liquid level situation of tundish molten steel 4, the opening degree of adjustment flow control slide plate 9 carry out flow control operation 70 ~ 85%；Protection is poured
During note, if the siphon mouth of a river blocks the mouth of a river because of field trash dross, it can insert side by side under a new siphon mouth of a river, quick replacement
The old siphon mouth of a river；When stopping pouring, close flow control slide plate 9 and stop cast.
Embodiment 3
By tedge 6, horizontal inclined tube 7, the down-comer 8 of the siphon mouth of a river pipeline being made of refractory material, connect successively,
The entrance of tedge 6 is close to the bottom of tundish 5 and plane of inlet is higher than the liquid level of crystallizer molten steel 11, horizontal inclined tube 7 when stabilization is poured into a mould
Horizontal sextant angle be 45 degree；The molten steel caching bag 2 for the aspirator being made of refractory material, sets up two tube heads, a connection separately
The top of down-comer 8, a connection aspiration pump 1；Flow control slide plate 9 is arranged on the upper side in the middle part of down-comer 8, positioned at aspirator and crystallization
Between the liquid level of device molten steel 11.
Method with siphon mouth of a river flow control molding casting is：By siphon mouth of a river pipeline across the wall of tundish 5, tedge 6 is inserted
Enter 80t tundish 5, down-comer 8 inserts 200 × 1600mm rectangular-blank crystallizers 10, adjusts and fix siphon mouth of a river position, controls
Fluent plate 9 is remained turned-off；After tundish molten steel 5 is risen to away from bag bottom 850mm, open in aspirator valve 3, suction channel
Gas, tundish molten steel 4 is from after tedge 6 flows into down-comer 8 through horizontal inclined tube 7, and opening the opening degree of flow control slide plate 9 is
100%, close in aspirator valve 3, molten steel injection crystallizer 10, completion, which is opened, pours；According to crystallizer steel during molding casting
The liquid level of liquid 11 and the liquid level situation of tundish molten steel 4, the opening degree of adjustment flow control slide plate 9 carry out flow control operation 80 ~ 95%；Protection is poured
During note, if the siphon mouth of a river blocks the mouth of a river because of field trash dross, it can insert side by side under a new siphon mouth of a river, quick replacement
The old siphon mouth of a river；When stopping pouring, close flow control slide plate 9 and stop cast.
Claims (4)
1. a kind of continuous casting flow control molding casting siphon spout device, the device is arranged between molten steel crystallizer and tundish,
Including siphon piping, aspirator and flow control slide plate, it is characterised in that described siphon piping is divided into tedge, horizontal inclined tube
And down-comer, tedge, horizontal inclined tube and down-comer are closely connected across middle containment wall, tedge bottom insertion tundish successively
Interior, the horizontal sextant angle of horizontal inclined tube is 30 ~ 45 degree, the bottom insertion crystallizer of down-comer；Flow control slide plate is arranged in down-comer
Portion position on the upper side, between aspirator and crystallizer molten steel liquid level；Aspirator is that molten steel caches bag, molten steel caching bag point
If two tube heads, one is connected with down-comer top, other end connection aspiration pump, is provided between molten steel caching bag and down-comer
Control valve；Described tundish, the siphon mouth of a river, crystallizer are arranged according to the horizontal pattern of left, center, right.
2. continuous casting flow control molding casting siphon spout device according to claim 1, it is characterised in that described rising
Pipe, horizontal inclined tube are identical with down-comer specification, and material is identical.
3. continuous casting flow control molding casting siphon spout device according to claim 1 or 2, it is characterised in that tedge
Entrance is close to tundish bottom and plane of inlet is higher than crystallizer molten steel liquid level when stabilization is poured into a mould.
4. continuous casting flow control molding casting siphon spout device according to claim 1, it is characterised in that flow control slide plate is
Sliding panel with open and close function.