CN206416612U - A kind of in-molded silica gel flat surface or cambered surface trade mark label - Google Patents
A kind of in-molded silica gel flat surface or cambered surface trade mark label Download PDFInfo
- Publication number
- CN206416612U CN206416612U CN201621388339.4U CN201621388339U CN206416612U CN 206416612 U CN206416612 U CN 206416612U CN 201621388339 U CN201621388339 U CN 201621388339U CN 206416612 U CN206416612 U CN 206416612U
- Authority
- CN
- China
- Prior art keywords
- silica
- thickness
- coating
- layer
- gel
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
Utility model provides a kind of in-molded silica gel flat surface or cambered surface trade mark label, layer of silica gel including bottom, the bottom of bottom layer of silica gel is provided with hot melt adhesive layer, tack coat has been sequentially arranged above in described layer of silica gel, color printing layer, silica-gel coating, environment-friendly coating, PET sheet layer and environmental protection treatment agent coating, the tack coat includes the first tack coat and the second tack coat, the thickness of first tack coat is 2~5 μm, the thickness of second tack coat is 3~5 μm, the silica-gel coating includes the first silica-gel coating and the second silica-gel coating, the thickness of first silica-gel coating is 3~6 μm, the thickness of second silica-gel coating is 2~4 μm, the thickness of the environment-friendly coating is 1~3 μm, the thickness of the environmental protection treatment agent coating is 1~3 μm, the hot melt adhesive layer includes the first hot melt adhesive layer and the second hot melt adhesive layer, this product has been printed rear difficult for drop-off.
Description
Technical field
The utility model is related to a kind of in-molded silica gel flat surface or cambered surface trade mark and cloth blanching adhering technique, specifically relates to
And a kind of in-molded silica gel flat surface or cambered surface trade mark label.
Background technology
The bonding of current existing silica gel and cloth the first be after first silica gel product is formed out, then on cloth sewed
Go, this efficiency low cost is high, and outward appearance is unsightly.Second is that cloth is put into mould to form out together with silica gel, this
The product adhesive property made is poor, and easy to fall off, bad height is easily damaged cloth, causes cost superelevation.
Utility model content
In view of this, main purpose of the present utility model is to provide a kind of in-molded silica gel flat surface or cambered surface trade mark mark
Board.
The technical solution adopted in the utility model is:
A kind of in-molded silica gel flat surface or cambered surface trade mark label, includes the layer of silica gel of bottom, the bottom of bottom layer of silica gel
Portion is provided with hot melt adhesive layer, and tack coat, color printing layer, silica-gel coating, environmental protection painting have been sequentially arranged above in described layer of silica gel
Layer, PET sheet layer and environmental protection treatment agent coating, the tack coat include the first tack coat and the second tack coat, described first
The thickness of tack coat is 2~5 μm, and the thickness of second tack coat is 3~5 μm, and the silica-gel coating includes the first silica gel
Coating and the second silica-gel coating, the thickness of first silica-gel coating is 3~6 μm, and the thickness of second silica-gel coating is 2
~4 μm, the thickness of the environment-friendly coating is 1~3 μm, and the thickness of the environmental protection treatment agent coating is 1~3 μm, the hot melt
Glue-line includes the first hot melt adhesive layer and the second hot melt adhesive layer, described, and the thickness of first hot melt adhesive layer is 1~2 μm, described
The thickness of second hot melt adhesive layer is 0.5~1 μm.
It is preferred that, the PET sheet layer uses poly terephthalic acid class plastics.
The utility model beneficial effect is:The technical program is laminated using multi-layered bonded layer, silica gel and PUR,
Laminate product is difficult for drop-off.
Brief description of the drawings
Fig. 1 is structural representation of the present utility model;
Fig. 2 is the utility model process chart.
Embodiment
Describe the utility model in detail below in conjunction with accompanying drawing and specific embodiment, herein signal of the present utility model
Property embodiment and explanation be used for explaining the utility model, but be not intended as limiting of the present utility model.
Reference picture 1, the utility model discloses a kind of in-molded silica gel flat surface or cambered surface trade mark label, including bottom
Layer of silica gel 3, the bottom of bottom layer of silica gel 3 is provided with hot melt adhesive layer, bonding has been sequentially arranged above in described layer of silica gel 3
Layer, color printing layer 6, silica-gel coating, environment-friendly coating 9, PET sheet layer 10 and environmental protection treatment agent coating 11, the tack coat includes
First tack coat 4 and the second tack coat 5, the thickness of first tack coat 4 is 2~5 μm, the thickness of second tack coat 5
For 3~5 μm, the silica-gel coating includes the first silica-gel coating 7 and the second silica-gel coating 8, the thickness of first silica-gel coating 7
Spend for 3~6 μm, the thickness of second silica-gel coating 8 is 2~4 μm, the thickness of the environment-friendly coating is 1~3 μm, described
The thickness of environmental protection treatment agent coating 11 is 1~3 μm, and the hot melt adhesive layer includes the first hot melt adhesive layer 1 and the second hot melt adhesive layer 2,
The thickness of first hot melt adhesive layer 1 is 1~2 μm, and the thickness of second hot melt adhesive layer 2 is 0.5~1 μm.The PET sheet
Material layer 10 uses poly terephthalic acid class plastics.
First tack coat 4 uses Environment-friendlyglue glue B, and the components of Environment-friendlyglue glue B by mass percentage are:Coupling agent
2.1 ~ 2.8%, delayed-action activator 0.9 ~ 1.3%, curing agent 3 ~ 3.2%, surplus is methyl ethylene.
Second tack coat 5 uses Environment-friendlyglue glue A, and the components of Environment-friendlyglue glue A by mass percentage are:Coupling agent
2.2%, delayed-action activator 18 ~ 25%, curing agent 3 ~ 3.9%, flatting silica 19 ~ 21%, surplus is methyl ethylene.
First silica-gel coating 7 uses environmental protection treatment agent B, and the components of environmental protection treatment agent B by mass percentage are:It is even
Connection agent 5 ~ 5.3%, delayed-action activator 8 ~ 8.7%, curing agent 7 ~ 7.9%, surplus is methyl ethylene.
Second silica-gel coating 8 is using the component of environmental protection treatment agent A, the environmental protection treatment agent A by mass percentage:
Coupling agent 3 ~ 3.8%, electrostatic agent 5 ~ 5.9%, curing agent 2 ~ 2.5%, surplus is methyl ethylene.
The environmental protection treatment agent coating 9 is using the component of Environment-friendlyglue glue E, the Environment-friendlyglue glue E by mass percentage:It is even
Connection agent 3 ~ 3.8%, electrostatic agent 5 ~ 6.2%, curing agent 2 ~ 2.9%, surplus is methyl ethylene.
Reference picture 2, the utility model is made using following technique, the PET back sides is applied using environmental protection treatment agent A, PET
The coating layer thickness that the back side is applied is 2 μm, and the components of the environmental protection treatment agent A by mass percentage are about:Coupling agent 3%, electrostatic agent
5%, curing agent 2%, surplus is methyl ethylene;Coating baking, the speed being coated with during baking is 50m/min, is coated with baking temperature
115 DEG C~125 DEG C/15min;PET fronts are applied using environmental protection treatment agent B, the coating layer thickness that PET fronts are applied is 2 μm, the ring
Protecting the components of inorganic agent B by mass percentage is:Coupling agent 5%, delayed-action activator 8%, curing agent 7%, surplus is methyl ethylene;Apply
Cloth is toasted, and the speed being coated with during baking is 50m/min, is coated with 115 DEG C of baking temperature~125 DEG C/15min;Using environmental protection treatment
Agent B is applied to PET fronts, utilizes the continuous 2 processing coatings of environmental protection treatment agent B, it is ensured that the wearability of pattern, 4 μm of coating layer thickness, institute
Stating the components of environmental protection treatment agent B by mass percentage is:Coupling agent 5%, delayed-action activator 8%, curing agent 7%, surplus is ethylene methacrylic
Base;Coating baking, the speed being coated with during baking is 30m/min, is coated with 115 DEG C of baking temperature~125 DEG C/15min;Printing environment-friendly
Glue A, and toasted, baking condition is 115 DEG C~125 DEG C/20min, the components of the Environment-friendlyglue glue A by mass percentage
For:Coupling agent 2.2%, delayed-action activator 18 ~ 25%, curing agent 3 ~ 3.9%, flatting silica 19 ~ 21%, surplus is methyl ethylene;Utilize print
Brush machine carries out 3D printings, printed patterns, and carries UV baking machines using printing machine and toasted;Printing environment-friendly glue B, and carry out
Baking, baking condition is 115 DEG C~125 DEG C/20min, and the components of the Environment-friendlyglue glue B by mass percentage are:Coupling agent 2.1
~ 2.8%, delayed-action activator 0.9 ~ 1.3%, curing agent 3 ~ 3.2%;Machinery beats positioning hole;Using special laminating machine by silica gel double exposure to PET
On sheet material;Silica gel oil pressure is molded, and its method is routinely to produce dumping and expect on mould, and the contraposition of ready-made PET film is put into silicon
In sealing rubber die positioning;Matched moulds vulcanizes, conditions of vulcanization, 175 DEG C~205 DEG C degree/30min ~ 60min of temperature, and pressure is 8~12kg;
The print component of Environment-friendlyglue glue E, the Environment-friendlyglue glue E by mass percentage on PET sheet, silica gel is torn after having vulcanized is:Coupling
Agent 2%, curing agent 1%, surplus is methyl ethylene;PUR is printed, 75 DEG C of parameters of temperature~85 DEG C/30min is printed, pressure is
1.5~2.5kg, is toasted after being completed for printing, and is discharged, and laser cutting finally carries out quality testing, again by this silicon after the completion of detection
The blanching of glue trade mark is to cloth(Clothes)On.
The technical scheme disclosed in the utility model embodiment is described in detail above, it is used herein specifically
Embodiment is set forth to the principle and embodiment of the utility model embodiment, and the explanation of above example is only applicable to
Help understands the principle of the utility model embodiment;It is real according to the utility model simultaneously for those of ordinary skill in the art
Example is applied, be will change in embodiment and application, in summary, this specification content should not be understood
For to limitation of the present utility model.
Claims (2)
1. a kind of in-molded silica gel flat surface or cambered surface trade mark label, it is characterised in that the layer of silica gel including bottom, bottom silicon
The bottom of glue-line is provided with hot melt adhesive layer, is applied in be sequentially arranged above tack coat, color printing layer, the silica gel of described layer of silica gel
Layer, environment-friendly coating, PET sheet layer and environmental protection treatment agent coating, the tack coat include the first tack coat and the second tack coat,
The thickness of first tack coat is 2~5 μm, and the thickness of second tack coat is 3~5 μm, and the silica-gel coating includes
First silica-gel coating and the second silica-gel coating, the thickness of first silica-gel coating is 3~6 μm, second silica-gel coating
Thickness is 2~4 μm, and the thickness of the environment-friendly coating is 1~3 μm, and the thickness of the environmental protection treatment agent coating is 1~3 μm,
The hot melt adhesive layer includes the first hot melt adhesive layer and the second hot melt adhesive layer, and the thickness of first hot melt adhesive layer is 1~2 μm, institute
The thickness for stating the second hot melt adhesive layer is 0.5~1 μm.
2. in-molded silica gel flat surface according to claim 1 or cambered surface trade mark label, it is characterised in that the PET
Sheet layer uses poly terephthalic acid class plastics.