CN206232610U - It is a kind of it is new prevent condense frosting glass - Google Patents
It is a kind of it is new prevent condense frosting glass Download PDFInfo
- Publication number
- CN206232610U CN206232610U CN201621281540.2U CN201621281540U CN206232610U CN 206232610 U CN206232610 U CN 206232610U CN 201621281540 U CN201621281540 U CN 201621281540U CN 206232610 U CN206232610 U CN 206232610U
- Authority
- CN
- China
- Prior art keywords
- glass substrate
- glass
- mixed coating
- intermediate layer
- frosting
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The utility model discloses a kind of glass of the new frosting that prevents from condensing, including left glass substrate, right glass substrate, intermediate layer, mixed coating；Left glass substrate is arranged on the left side in intermediate layer, right glass substrate is arranged on the right side in intermediate layer, intermediate layer is the glass sandwich of sealing, it is arranged on the position in the middle of left glass substrate and right glass substrate, being rushed in intermediate layer completely has argon gas, and intermediate layer is with left glass substrate and right glass substrate by being sealedly and fixedly connected.It is this it is new prevent condense frosting glass, can solve the problem that the problem of the currently used method high cost for preventing condensation frosting, the problem for preventing the persistence of condensation frosting not strong is also solved simultaneously, the cost for preventing condensing spent by fogging is greatly reduced, the persistence for preventing condensation frosting is extended.
Description
Technical field
The utility model belongs to the deep process technology field of glass, and in particular to it is a kind of it is new prevent condense frosting glass
Glass.
Background technology
With the continuous progressive of glassmaking technology and develop, the manufacture and deep processing of glass towards difference in functionality,
The direction of sectionalization is developed；In the life of our reality, the table of glass is whether frequently encountered in the winter time or in summer
Face produces the phenomenon of fumulus and condensation（For example, the glass used in the windshield and building doors and windows of automobile）, condensation
Or frosting is the phenomenon that condensed water just occurs when the surface temperature of glass is less than the temperature with the dew point of surrounding.
The method for preventing glass condensation frosting in the prior art is a lot, and being broadly divided into coating prevents condensation frosting, structural type
Fogging frosting is prevented, chemical liquid is sprayed in glass surface；Prevent from fogging frosting to be mainly using coating to be plated in glass surface
Layer of metal layer（Such as titanium dioxide, silver）Sandwich establishment between preventing fogging frosting from mainly using in glass Deng, structural type, puts
Enter the methods such as drier；Although the effect of good demisting dew removing can be played in the method for glass surface spraying chemical liquid,
But persistence is not strong；It is currently used prevent condense frosting method, or be demisting dew removing effect it is good, but persistence
It is not strong；Be prevent condense frosting needed for it is relatively costly；Inventor have developed a kind of new based on defect of the prior art
Type prevents the glass of condensation frosting, can solve the problem that the problems of the prior art.
Utility model content
The utility model is in order to solve the above-mentioned technical problem, there is provided it is a kind of it is new prevent condense frosting glass, its design
Simple structure, scientific and reasonable, the effect of the frosting that prevents from condensing is good；Can solve the problem that the currently used method for preventing condensation frosting
The problem of high cost, while also solving the problem for preventing the persistence of condensation frosting not strong, greatly reducing prevents condensation
Cost spent by fogging, extends the persistence for preventing condensation frosting.
The technical scheme that the utility model is used is：A kind of glass of the new frosting that prevents from condensing, including left glass base
Plate, right glass substrate, intermediate layer, mixed coating；Left glass substrate is arranged on the left side in intermediate layer, during right glass substrate is arranged on
The right side of interbed, intermediate layer is the glass sandwich of sealing, is arranged on the position in the middle of left glass substrate and right glass substrate, middle
Being rushed in layer completely has argon gas, and intermediate layer is with left glass substrate and right glass substrate by being sealedly and fixedly connected；Mixed coating sets respectively
The both sides of left glass substrate and right glass substrate are put, mixed coating is made up of left mixed coating and right mixed coating, in left glass
One layer of left mixed coating is scribbled on the left of substrate, one layer of right mixed coating, left mixed coating are scribbled on the right side of right glass substrate
It is PEG-4000 with right mixed coating.
PEG-4000 in the left mixed coating and right mixed coating is mixed for oxirane and water polycondensation
Compound.
The left mixed coating and right mixed coating are 8~12 μm.
The thickness of the glass sandwich of the intermediate layer sealing is 40~50 μm.
The left mixed coating and right mixed coating fill the surface of whole glass substrate and right glass substrate.
It is this it is new prevent condense frosting glass prevent condensation Frost formation process be：First with lifting degree embrane method to having added
The good glass with intermediate layer of work, carries out lifting plated film, PEG-4000 is plated to the surface of glass, whether in the summer
Season still in the winter time, according to weather condition, in summer, when there is heavy rain or thunderstorm weather or winter extraneous temperature and glass table
It is this with argon gas when the temperature of glass surface is less than the dew-point temperature of surrounding when face temperature difference is larger
Interbed, is prevented from glass and is exchanged with the cold and hot of surrounding dew-point temperature, the temperature of glass surface is become with the dew-point temperature of surrounding
In balance, so as to prevent the phenomenon of glass surface condensation frosting；While mixed coating is on the one hand, using PEG-4000
Be integrated with water the property with notable heat release, improves the temperature of glass surface, in making the surface temperature of glass and surrounding air
Dew-point temperature it is close, so as to prevent the condensation frost of interior surfaces of glass from root；On the other hand, polyethylene glycol-
6000 molecular structures that can change water, make the structure of hydrone further diminish, so as to prevent the condensation of interior surfaces of glass
Frost；Above procedure is the new glass for preventing condensation frosting and prevents condensation Frost formation process.
The intermediate layer is the glass sandwich of sealing, is arranged on the position in the middle of left glass substrate and right glass substrate, in
Being rushed in interbed completely has argon gas, and intermediate layer passes through to be sealedly and fixedly connected with left glass substrate and right glass substrate, the thickness in intermediate layer
It is 40~50 μm；The main purpose for so setting is to prevent the heat exchange between extraneous cooler air and glass, preventing glass
Glass surface reduces the temperature of glass surface because of exchange of cold air, because argon gas belongs to inert gas, molecular structure stabilized is not allowed
Chemical reaction easily is produced with extraneous any material, due to this special property of argon gas, cool ambient air and glass can be prevented
Cold and hot transmission between glass.
The mixed coating is respectively provided with the both sides of left glass substrate and right glass substrate, and mixed coating has left mixed coating
With right mixed coating composition, one layer of left mixed coating is scribbled on the left of left glass substrate, scribbled on the right side of right glass substrate
One layer of right mixed coating, left mixed coating and right mixed coating are PEG-4000；So set main purpose be for
, PEG-4000 is merged with the dew point that will be formed, so as to prevent glass surface to form the phenomenon of condensation frosting；
Because PEG-4000 chemical stability in itself is good, there is very strong water solubility, surface-active is big, has when being integrated with water
Significant exothermic phenomenon；On the one hand the molecular structure of water can be changed, the structure of hydrone is further diminished, so as to prevent
The condensation frost of interior surfaces of glass；On the other hand, it is integrated with water the property with notable heat release using PEG-4000
Matter, improves the temperature of glass surface, makes the surface temperature of glass close with the dew-point temperature in surrounding air, so as to from root
On prevent the condensation frost of interior surfaces of glass.
The left mixed coating and right mixed coating are 8~12 μm；So set main purpose be, it is ensured that it is left mixing apply
Layer and right mixed coating have the thickness of optimal coating, to extend the service life of mixed coating because when polyethylene glycol-
6000 when be integrated with water, and the volume of PEG-4000 has slight contraction, in order to ensure the use longevity of mixed coating
Life, left mixed coating and right mixed coating are 8~12 μm the most suitable.
This PEG-4000 be it is a kind of be readily available, stable performance, cheap material, with very
Good prevents the effect of glass condensation frosting, and works well.
The beneficial effects of the utility model：The technical program provide it is a kind of it is new prevent condense frosting glass, its design
Simple structure, scientific and reasonable, the effect of the frosting that prevents from condensing is good；Can solve the problem that the currently used method for preventing condensation frosting
The problem of high cost, while also solving the problem for preventing the persistence of condensation frosting not strong, greatly reducing prevents condensation
Cost spent by fogging, extends the persistence for preventing condensation frosting.
Brief description of the drawings
Fig. 1 is structural representation of the present utility model；
Marked in figure：1st, left glass substrate, 2, right glass substrate, 3, intermediate layer, 4, mixed coating, 5 left mixed coatings, 6,
Right mixed coating.
Specific embodiment
Specific embodiment of the present utility model is described in further detail below in conjunction with accompanying drawing.
It is as illustrated, a kind of glass of the new frosting that prevents from condensing including left glass substrate 1, right glass substrate 2, middle
Layer 3, mixed coating 4；Left glass substrate 1 is arranged on the left side in intermediate layer 3, and right glass substrate 2 is arranged on the right side in intermediate layer 3,
Intermediate layer 3 is the glass sandwich of sealing, is arranged on the position in the middle of left glass substrate 1 and right glass substrate 2, is rushed in intermediate layer 3
Completely there is argon gas, intermediate layer 3 is with left glass substrate 1 and right glass substrate 2 by being sealedly and fixedly connected；Mixed coating 4 is respectively provided with
The both sides of left glass substrate 1 and right glass substrate 2, mixed coating 4 is made up of left mixed coating 5 and right mixed coating 6, in left glass
The left side of glass substrate 1 scribbles one layer of left mixed coating 5, and one layer of right mixed coating 6 is scribbled on the right side of right glass substrate 2, and a left side is mixed
It is PEG-4000 to close coating 5 and right mixed coating 6.
PEG-4000 in the left mixed coating 5 and right mixed coating 6 is oxirane and water polycondensation
Mixture.
The left mixed coating 5 and right mixed coating 6 are 8~12 μm.
The thickness of the glass sandwich of the sealing of the intermediate layer 3 is 40~50 μm.
The left mixed coating 5 and right mixed coating 6 fill the surface of whole glass substrate 1 and right glass substrate 2.
It is this it is new prevent condense frosting glass prevent condensation Frost formation process be：First with lifting degree embrane method to having added
The good glass with intermediate layer 3 of work, carries out lifting plated film, PEG-4000 is plated to the surface of glass, whether in the summer
Season still in the winter time, according to weather condition, in summer, when there is heavy rain or thunderstorm weather or winter extraneous temperature and glass table
It is this with argon gas when the temperature of glass surface is less than the dew-point temperature of surrounding when face temperature difference is larger
Interbed, is prevented from glass and is exchanged with the cold and hot of surrounding dew-point temperature, the temperature of glass surface is become with the dew-point temperature of surrounding
In balance, so as to prevent the phenomenon of glass surface condensation frosting；While mixed coating 4 is on the one hand, using PEG-4000
Be integrated with water the property with notable heat release, improves the temperature of glass surface, in making the surface temperature of glass and surrounding air
Dew-point temperature it is close, so as to prevent the condensation frost of interior surfaces of glass from root；On the other hand, polyethylene glycol-
6000 molecular structures that can change water, make the structure of hydrone further diminish, and the globule is formed one layer of water in glass surface
Film, so as to prevent the condensation frost of interior surfaces of glass；Above procedure is the new glass for preventing condensation frosting and prevents
Condensation Frost formation process.
Embodiment one：
Left glass substrate 1 is arranged on the left side in intermediate layer 3, and right glass substrate 2 is arranged on the right side in intermediate layer 3, intermediate layer 3
It is the glass sandwich of sealing, is arranged on the position in the middle of left glass substrate 1 and right glass substrate 2, being rushed in intermediate layer 3 completely has argon
Gas, the thickness of intermediate layer 3 is 40 μm, and intermediate layer 3 is with left glass substrate 1 and right glass substrate 2 by being sealedly and fixedly connected；Mixing is applied
Layer 4 is respectively provided with the both sides of left glass substrate 1 and right glass substrate 2, and mixed coating 4 has left mixed coating 5 and right mixed coating 6
Composition, one layer of left mixed coating 5 is scribbled in the left side of left glass substrate 1, and one layer of right mixing is scribbled on the right side of right glass substrate 2
Coating 6, left mixed coating 5 and right mixed coating 6 are PEG-4000, and left mixed coating 5 and right mixed coating 6 are 8 μm.
Embodiment two：
Left glass substrate 1 is arranged on the left side in intermediate layer 3, and right glass substrate 2 is arranged on the right side in intermediate layer 3, intermediate layer 3
It is the glass sandwich of sealing, is arranged on the position in the middle of left glass substrate 1 and right glass substrate 2, being rushed in intermediate layer 3 completely has argon
Gas, the thickness of intermediate layer 3 is 45 μm, and intermediate layer 3 is with left glass substrate 1 and right glass substrate 2 by being sealedly and fixedly connected；Mixing is applied
Layer 4 is respectively provided with the both sides of left glass substrate 1 and right glass substrate 2, and mixed coating 4 has left mixed coating 5 and right mixed coating 6
Composition, one layer of left mixed coating 5 is scribbled in the left side of left glass substrate 1, and one layer of right mixing is scribbled on the right side of right glass substrate 2
Coating 6, left mixed coating 5 and right mixed coating 6 are PEG-4000, and left mixed coating 5 and right mixed coating 6 are 10 μm.
Embodiment three：
Left glass substrate 1 is arranged on the left side in intermediate layer 3, and right glass substrate 2 is arranged on the right side in intermediate layer 3, intermediate layer 3
It is the glass sandwich of sealing, is arranged on the position in the middle of left glass substrate 1 and right glass substrate 2, being rushed in intermediate layer 3 completely has argon
Gas, the thickness of intermediate layer 3 is 50 μm, and intermediate layer 3 is with left glass substrate 1 and right glass substrate 2 by being sealedly and fixedly connected；Mixing is applied
Layer 4 is respectively provided with the both sides of left glass substrate 1 and right glass substrate 2, and mixed coating 4 has left mixed coating 5 and right mixed coating 6
Composition, one layer of left mixed coating 5 is scribbled in the left side of left glass substrate 1, and one layer of right mixing is scribbled on the right side of right glass substrate 2
Coating 6, left mixed coating 5 and right mixed coating 6 are PEG-4000, and left mixed coating 5 and right mixed coating 6 are 12 μm.
Claims (4)
1. a kind of glass of the new frosting that prevents from condensing, including left glass substrate, right glass substrate, intermediate layer, mixed coating；Its
It is characterised by：Left glass substrate is arranged on the left side in intermediate layer, and right glass substrate is arranged on the right side in intermediate layer, and intermediate layer is close
The glass sandwich of envelope, is arranged on the position in the middle of left glass substrate and right glass substrate, and being rushed in intermediate layer completely has argon gas, intermediate layer
With left glass substrate and right glass substrate by being sealedly and fixedly connected；Mixed coating is respectively provided with left glass substrate and right glass base
The both sides of plate, mixed coating is made up of left mixed coating and right mixed coating, one layer of left side is scribbled on the left of left glass substrate and is mixed
Coating is closed, one layer of right mixed coating is scribbled on the right side of right glass substrate, left mixed coating and right mixed coating are polyethylene glycol
PEG-6000。
2. it is according to claim 1 it is a kind of it is new prevent condense frosting glass, it is characterised in that：Left mixed coating and the right side
Mixed coating is 8~12 μm.
3. it is according to claim 1 it is a kind of it is new prevent condense frosting glass, it is characterised in that：The glass of intermediate layer sealing
The thickness of glass interlayer is 40~50 μm.
4. it is according to claim 3 it is a kind of it is new prevent condense frosting glass, it is characterised in that：Left mixed coating and the right side
Mixed coating fills the surface of whole glass substrate and right glass substrate.