CN206085840U - 一种高性能编织物 - Google Patents
一种高性能编织物 Download PDFInfo
- Publication number
- CN206085840U CN206085840U CN201621030531.6U CN201621030531U CN206085840U CN 206085840 U CN206085840 U CN 206085840U CN 201621030531 U CN201621030531 U CN 201621030531U CN 206085840 U CN206085840 U CN 206085840U
- Authority
- CN
- China
- Prior art keywords
- performance
- layer
- fabric
- fiber
- warp
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本实用新型涉及一种高性能编织物。现有的高性能编织物的力学和工艺性能指标均有所欠缺。本实用新型其特征在于经向方向铺入主体结构的高性能纤维层，在织物的背面一层铺入30‑60度方向的纬向纤维层，在织物的背面二层铺入负30‑60度方向的纬向纤维层，再由涤纶丝通过经编捆绑编织上述的纤维层构成一个整体结构，最后利用热加工粘合将纬向双层与经向层热粘合成一个固定稳定的结构。本实用新型是一种突出织物高性能的织物结构，通过使用双层交叉的两层纬向层，与经向纤维层构成热粘合结构，提高了织物的结构稳定性和力学均匀性能，从而整体上提升织物的力学性能和工艺性能，织物的结构具备了轻量化的特点，符合高性能复合材料增强体的技术要求。
Description
技术领域
本实用新型属于新型材料技术领域，涉及一种工业用纺织品，特别涉及一种高性能编织物。
背景技术
随着我国新型树脂基复合材料应用领域越来越广泛，高性能的复合材料基材也不断被开发出来，适应航天航空、风力发电、轨道交通等高性能应用，特别是风力发电机组从小叶型开始整体过渡到大叶型，领域从陆地风场，开始大力发展海上风电，对复合材料的力学工艺性能提出更高要求，高性能纤维及复合材料开始普及发展，高性能的纤维材料目前主要有高强高模玻璃纤维、碳纤维、芳伦等，同时各类高性能纤维混编的工艺也作为一种低成本高性能的复合材料被使用，但现有的高性能编织物的力学和工艺性能指标均有所欠缺。
实用新型内容
本实用新型的目的是为了解决现有技术存在的问题，从而提供一种高性能编织物，具有优良的力学性能和工艺性能。
本实用新型采用的技术方案是：一种高性能编织物，其特征在于经向方向铺入主体结构的高性能纤维层，在织物的背面一层铺入30-60度方向的纬向纤维层，在织物的背面二层铺入负30-60度方向的纬向纤维层，再由涤纶丝通过经编捆绑编织上述的纤维层构成一个整体结构，最后利用热加工粘合将纬向双层与经向层热粘合成一个固定稳定的结构。
所述的高性能纤维层的纤维为高强高模玻璃纤维、碳纤维、芳纶等高性能纤维。
所述的纬向纤维层使用玻璃纤维热熔线，规格为75TEX。
所述高性能纤维层的纤维规格为1500TEX-3300TEX。
所述的高性能纤维层的密度为4.5-10根/英寸，纤维单位重量600克。
本实用新型是一种突出织物高性能的织物结构，通过使用双层交叉的两层纬向层，与经向纤维层构成热粘合结构，提高了织物的结构稳定性和力学均匀性能，从而整体上提升织物的力学性能和工艺性能，织物的结构具备了轻量化的特点，符合高性能复合材料增强体的技术要求。本实用新型也可以根据对织物的纱线、轴向密度、结构的调整进行多种设计，适应不同的应用需求。
附图说明
图1是本实用新型的结构示意图。
具体实施方式
下面结合附图，对本实用新型一种一种高性能编织物进行说细描述：
如图1所示：本实用新型以50K碳纤维，通过合理的纱架分布将该纱线均匀分布、张力一致的衬入到多轴向编织设备的编织区，形成经向纤维层1，密度不小于4.5根/英寸，纤维单位重量600克；背面层2、背面层3分别为玻璃纤维热熔线75tex，两层热熔线成+/-60度角度平行交叉，通过全副衬纬装置平行铺设在两侧同步的纬向链带挂纱针上，并根据要求与编织机同步衬入编织区，形成纬向(+/-60度)双层加强层；所有纤维层在编织区通过涤纶纱捆绑成一个整体，再经过热熔装置将三层纱线粘合成一个固定稳定的多层织物结构。
以上列举的仅是本实用新型的具体实施例子，本实用新型不限于以上实施例子，还可以有许多变形。本领域的普通技术人员能从本实用新型公开的内容直接导出或联想到的所有变形，均应认为是本实用新型的保护范围。
Claims (5)
1.一种高性能编织物，其特征在于经向方向铺入主体结构的高性能纤维层，在织物的背面一层铺入30-60度方向的纬向纤维层，在织物的背面二层铺入负30-60度方向的纬向纤维层，再由涤纶丝通过经编捆绑编织上述的纤维层构成一个整体结构，最后利用热加工粘合将纬向双层与经向层热粘合成一个固定稳定的结构。
2.根据权利要求1所述的高性能编织物，其特征在于所述的高性能纤维层的纤维为高强高模玻璃纤维、碳纤维或芳纶。
3.根据权利要求2所述的高性能编织物，其特征在于所述的纬向纤维层使用玻璃纤维热熔线，规格为75TEX。
4.根据权利要求3所述的高性能编织物，其特征在于所述高性能纤维层的纤维规格为1500TEX-3300TEX。
5.根据权利要求4所述的高性能编织物，其特征在于所述的高性能纤维层的密度为4.5-10根/英寸，纤维单位重量600克。