CN205851817U - A kind of noble metal metallurgy cooling water-cooled shaping mould - Google Patents
A kind of noble metal metallurgy cooling water-cooled shaping mould Download PDFInfo
- Publication number
- CN205851817U CN205851817U CN201620868416.XU CN201620868416U CN205851817U CN 205851817 U CN205851817 U CN 205851817U CN 201620868416 U CN201620868416 U CN 201620868416U CN 205851817 U CN205851817 U CN 205851817U
- Authority
- CN
- China
- Prior art keywords
- water
- shaping mould
- cooled shaping
- cooled
- cavity
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
This utility model provides a kind of noble metal metallurgy cooling water-cooled shaping mould, including water-cooled shaping mould A, water-cooled shaping mould B, cast chamber, water-cooled shaping mould A short cavity connect with water-cooled shaping mould A long chamber root and in set water-cooled shaping mould A circulating water cavity, water-cooled shaping mould A circulating water cavity two ends connect water-cooled shaping mould A water inlet interface and water-cooled shaping mould A water outlet mouthpiece respectively；Water-cooled shaping mould B short cavity connect with end, water-cooled shaping mould B long chamber and in set water-cooled shaping mould B circulating water cavity, water-cooled shaping mould B circulating water cavity two ends connect water-cooled shaping mould B water inlet interface and water-cooled shaping mould B water outlet mouthpiece respectively, and end, water-cooled shaping mould A long chamber connects water-cooled shaping mould B short cavity end and water-cooled shaping mould A short cavity end and connects the long chamber of water-cooled shaping mould B and form cast chamber.This utility model device solves the problem of casting moulds Reusability, increases equipment cast capacity, can adjust ingot casting volume and weight on request, improves production capacity and energy Reusability.
Description
Technical field
This utility model relates to the technical field of Metal Melting, especially a kind of noble metal metallurgy cooling water-cooled shaping mould.
Background technology
In platinum-rhodium alloy fusion process, prior art is cast based on graphite crucible or Single-use crucible, platinum rhodium material
In the molten state, its pouring temperature, for reaching 1860 DEG C ~ 1960 DEG C, typically uses resistant to elevated temperatures zirconium oxide or alumina crucible
Carry out melting, after being smelted into ingot, destroy crucible after cooling, take out ingot, use graphite crucible surface to be made to process.
It is all disposable owing to crucible uses, it is impossible to reusing, cost is the highest, and crucible is typically not more than
200mL, therefore melting the most not can exceed that 2kg, inadequate by its resistant to elevated temperatures degree of metal pattern, it is impossible to pours into a mould for noble metal,
In order to solve to reduce cost in existing production, meet specified weight and specification demands.
Utility model content
The purpose of this utility model is the problems referred to above existed for existing technology, it is provided that a kind of noble metal metallurgy is cold
But water-cooled shaping mould, the problem that this utility model device solves casting moulds Reusability, it is ensured that equipment is high temperature resistant, increase equipment
Cast capacity, can adjust ingot casting volume and weight on request, improves production capacity and energy Reusability.
To this end, the technical solution that this utility model is taked is:
A kind of noble metal metallurgy cooling water-cooled shaping mould, including water-cooled shaping mould A, water-cooled shaping mould B, cast chamber, water-cooled
Shaping mould A is provided with water-cooled shaping mould A short cavity, the long chamber of water-cooled shaping mould A, water-cooled shaping mould A circulating water cavity, water-cooled shaping mould A enter
Water interface, water-cooled shaping mould A water outlet mouthpiece, water-cooled shaping mould A short cavity connect with water-cooled shaping mould A long chamber root and in set water-cooled
Shaping mould A circulating water cavity, water-cooled shaping mould A circulating water cavity two ends connect water-cooled shaping mould A water inlet interface and water-cooled molding respectively
Mould A water outlet mouthpiece；Water-cooled shaping mould B is provided with water-cooled shaping mould B short cavity, the long chamber of water-cooled shaping mould B, water-cooled shaping mould B recirculated water
Chamber, water-cooled shaping mould B are intake interface, water-cooled shaping mould B water outlet mouthpiece, water-cooled shaping mould B short cavity and water-cooled shaping mould B long chamber end
Setting water-cooled shaping mould B circulating water cavity in portion's connection also, water-cooled shaping mould B circulating water cavity two ends connect water-cooled shaping mould B respectively and enter
Water interface and water-cooled shaping mould B water outlet mouthpiece, end, water-cooled shaping mould A long chamber connects water-cooled shaping mould B short cavity end and water-cooled
Shaping mould A short cavity end connects the long chamber of water-cooled shaping mould B and forms cast chamber.
As further preferably, described water-cooled shaping mould A circulating water cavity and described water-cooled shaping mould B circulating water cavity are a diameter of
6cm~12cm。
As further preferably, described water-cooled shaping mould A and described water-cooled shaping mould B material are red copper.
As further preferably, described cast cavity volume is 50mL ~ 1000mL.
Having the beneficial effects that of technique scheme:
This utility model device water-cooled shaping mould A and water-cooled shaping mould B can form required cast chamber with relative displacement,
Can ensure that equipment is high temperature resistant, increase equipment cast capacity, the volume in cast chamber can be adjusted according to demand, i.e. adjust ingot casting
Volume and weight, improves production capacity, also saves the consumption of crucible simultaneously, this device energy Reusability, reduces and consumes, and also
Meeting the demand of ingot casting specification, cast forms the cuboid of different size, easy following process, and can pour into a mould continuously, uses
Life-span is long.
Accompanying drawing explanation
Fig. 1 is the structural representation of the side-looking in noble metal metallurgy of the present utility model cooling water-cooled shaping mould A face.
Fig. 2 is the cross-sectional view in noble metal metallurgy of the present utility model cooling water-cooled shaping mould A face.
Fig. 3 is the structural representation of the side-looking in noble metal metallurgy of the present utility model cooling water-cooled shaping mould B face.
Fig. 4 is the cross-sectional view in noble metal metallurgy of the present utility model cooling water-cooled shaping mould B face.
Fig. 5 is maximum cast cavity configuration schematic diagram of the present utility model.
Fig. 6 is adjustable cast cavity configuration schematic diagram of the present utility model.
In figure: 1, water-cooled shaping mould A；2, water-cooled shaping mould B；3, cast chamber；101, water-cooled shaping mould A short cavity；102, water
The long chamber of cold forming mould A；103, water-cooled shaping mould A circulating water cavity；104, water-cooled shaping mould A water inlet interface；105, water-cooled shaping mould A
Water outlet mouthpiece；201, water-cooled shaping mould B short cavity；202, the long chamber of water-cooled shaping mould B；203, water-cooled shaping mould B circulating water cavity；204、
Water-cooled shaping mould B is intake interface；205, water-cooled shaping mould B water outlet mouthpiece.
Detailed description of the invention
For making feature of the present utility model and advantage clearer, it is described below in conjunction with specific embodiment.
As shown in Fig. 1 ~ 6, a kind of noble metal metallurgy cooling water-cooled shaping mould, including water-cooled shaping mould A1, water-cooled shaping mould
B2, cast chamber 3, water-cooled shaping mould A1 is provided with water-cooled shaping mould A short cavity 101, the long chamber of water-cooled shaping mould A 102, water-cooled shaping mould A
Circulating water cavity 103, water-cooled shaping mould A are intake interface 104, water-cooled shaping mould A water outlet mouthpiece 105, water-cooled shaping mould A short cavity 101
Connect with water-cooled shaping mould A long chamber 102 root and in set water-cooled shaping mould A circulating water cavity 103, water-cooled shaping mould A circulating water cavity
103 two ends connect water-cooled shaping mould A water inlet interface 104 and water-cooled shaping mould A water outlet mouthpiece 105 respectively；Water-cooled shaping mould B2 sets
Water-cooled shaping mould B short cavity 201, the long chamber of water-cooled shaping mould B 202, water-cooled shaping mould B circulating water cavity 203, water-cooled shaping mould B is had to enter
Water interface 204, water-cooled shaping mould B water outlet mouthpiece 205, water-cooled shaping mould B short cavity 201 is with end, water-cooled shaping mould B long chamber 202 even
Logical and in set water-cooled shaping mould B circulating water cavity 203, water-cooled shaping mould B circulating water cavity 203 two ends connect water-cooled shaping mould B respectively
Water inlet interface 204 and water-cooled shaping mould B water outlet mouthpiece 205, end, water-cooled shaping mould A long chamber 102 connects water-cooled shaping mould B short cavity
201 ends and water-cooled shaping mould A short cavity 101 end connect water-cooled shaping mould B long chamber 202 and form cast chamber 3.
In the present embodiment, described water-cooled shaping mould A circulating water cavity 103 and described water-cooled shaping mould B circulating water cavity 203 diameter
For 6cm ~ 12cm, for meeting cooling effect, water-cooled shaping mould A circulating water cavity 103 and water-cooled shaping mould B circulating water cavity 203 need
Enough heat exchange areas, diameter needs to meet certain requirements.
In the present embodiment, described water-cooled shaping mould A1 and described water-cooled shaping mould B2 material are red copper, by water-cooled molding
Mould A circulating water cavity 103 and water-cooled shaping mould B circulating water cavity 203 dispel the heat rapidly, make in platinum-rhodium alloy casting process, red copper
Surface temperature be less than red copper solution temperature, contact surface with cast platinum rhodium material formed cold shut from, do not affect the purity of platinum rhodium material.
In the present embodiment, described cast chamber 3 volume is 50mL ~ 1000mL, can make water-cooled shaping mould according to cast requirement
A1 and water-cooled shaping mould B2 relative movement, adjust ingot casting volume, and platinum rhodium material, through high-frequency melting furnace, is cast in cast chamber 3,
Before cast, opening water-cooled shaping mould A1 and the recirculated water of water-cooled shaping mould B2, platinum rhodium liquid material can quickly cool down, and then opens water
Cold forming mould A1 and water-cooled shaping mould B2, takes out platinum rhodium ingot.
During use, according to platinum rhodium ingot volume needs, the body in the cast chamber 3 of regulation water-cooled shaping mould A1 and water-cooled shaping mould B2
Long-pending, then by platinum rhodium material through high-frequency melting furnace, it is cast in cast chamber 3, forms the platinum rhodium ingot of demand.
In addition to the implementation, this utility model can also have other embodiments.All employing equivalents or equivalence become
Change the technical scheme of formation, all fall within protection domain of the present utility model.
Claims (4)
1. a noble metal metallurgy cooling water-cooled shaping mould, it is characterised in that: include water-cooled shaping mould A, water-cooled shaping mould B, water
Note chamber, water-cooled shaping mould A is provided with water-cooled shaping mould A short cavity, the long chamber of water-cooled shaping mould A, water-cooled shaping mould A circulating water cavity, water-cooled
Shaping mould A is intake interface, water-cooled shaping mould A water outlet mouthpiece, and water-cooled shaping mould A short cavity connects with water-cooled shaping mould A long chamber root
Setting water-cooled shaping mould A circulating water cavity in and, water-cooled shaping mould A circulating water cavity two ends connect water-cooled shaping mould A water inlet interface respectively
With water-cooled shaping mould A water outlet mouthpiece；Water-cooled shaping mould B is provided with water-cooled shaping mould B short cavity, the long chamber of water-cooled shaping mould B, water-cooled molding
Mould B circulating water cavity, water-cooled shaping mould B are intake interface, water-cooled shaping mould B water outlet mouthpiece, water-cooled shaping mould B short cavity and water-cooled molding
Setting water-cooled shaping mould B circulating water cavity in the connection also of end, mould B long chamber, water-cooled shaping mould B circulating water cavity two ends connect water-cooled respectively
Shaping mould B water inlet interface and water-cooled shaping mould B water outlet mouthpiece, end, water-cooled shaping mould A long chamber connects water-cooled shaping mould B short cavity end
Portion and water-cooled shaping mould A short cavity end connect the long chamber of water-cooled shaping mould B and form cast chamber.
Noble metal metallurgy the most according to claim 1 cooling water-cooled shaping mould, it is characterised in that: described water-cooled shaping mould A
Circulating water cavity and the described water-cooled shaping mould a diameter of 6cm ~ 12cm of B circulating water cavity.
Noble metal metallurgy the most according to claim 1 cooling water-cooled shaping mould, it is characterised in that: described water-cooled shaping mould A
It is red copper with described water-cooled shaping mould B material.
Noble metal metallurgy the most according to claim 1 cooling water-cooled shaping mould, it is characterised in that: described cast cavity volume is
50mL~1000mL。