CN205777082U - A kind of safe cladding glass for libraries of the universities - Google Patents
A kind of safe cladding glass for libraries of the universities Download PDFInfo
- Publication number
- CN205777082U CN205777082U CN201620731793.9U CN201620731793U CN205777082U CN 205777082 U CN205777082 U CN 205777082U CN 201620731793 U CN201620731793 U CN 201620731793U CN 205777082 U CN205777082 U CN 205777082U
- Authority
- CN
- China
- Prior art keywords
- film
- protection face
- universities
- libraries
- face coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
This utility model provides a kind of safe cladding glass for libraries of the universities, including organic glass substrate, lucite substrate be arranged above with priming coat, Low emissivity thermal insulation layer, protection face coating;Lucite substrate protection face coating is provided below;Lucite substrate material is Merlon, and priming coat is polyurethane film, and Low emissivity thermal insulation layer is indium zinc oxide (IZO) thin layer, and protection face coating includes polyurethane film, the organosilicon film arranged from the inside to the outside.Described safe cladding glass have lightweight, do not reveal and the feature of Low emissivity.
Description
Technical field
This utility model relates to a kind of safe cladding glass for libraries of the universities.
Background technology
College and university library undertakes college and the important task of scientific research service, meets colleges and universities teachers and students and society
Reader's demand to various information such as economic information, scientific research information, business informations.In Modern University Library Buildings, pursue
The Glass Design of large area daylighting becomes trend.Glass lighting is preferable, and good visual effect has shown that Modern College Libraries is built
The individual character built.Low radiation coated glass (Low-E glass) can significantly reduce while not significantly reducing visible light transmissivity
The indoor and outdoor heat exchange produced due to heat radiation.Low radiation coated glass receives state with the energy-saving and environmental protection performance of its excellence
Inside and outside common concern, is used widely in China university library building engineering.Although but glass curtain wall shows
The individual character of modern architecture, also brings along all secret worries.Particularly the when of summer, indoor/outdoor temperature-difference is big, and glass is particularly easy to certainly
Quick-fried.Winter, season in summer two are taking place frequently season of cladding glass explosion, and main cause is that central air-conditioning temperature is long in many library buildings
The phase too high or too low hidden danger brought.Library generation glass self-explosion happens occasionally, hard to guard against.Libraries of the universities' flow of the people
Greatly, glass self-explosion uphangs skyborne " bomb " just as one, makes each passerby on tenterhooks.The glass of fragmentation after glass explosion
Fragment splashes and drops, and brings potential safety hazard and maintenance cost to libraries of the universities.How on the premise of ensureing light transmittance,
Stopping glass self-explosion is current urgent problem.
Utility model content
For solving the problem of above-mentioned existence, the purpose of this utility model is to provide a kind of safety for libraries of the universities
Cladding glass, reduces the self-destruction rate of glass, the heat insulation and heat-insulating property of reinforcing glass, improves glass weatherability.
For reaching above-mentioned purpose, the technical solution of the utility model is:
A kind of safe cladding glass for libraries of the universities, including organic glass substrate, above lucite substrate
Priming coat, Low emissivity thermal insulation layer, protection face coating are set;Lucite substrate protection face coating is provided below;Lucite
Substrate material is Merlon, and priming coat is polyurethane film, and Low emissivity thermal insulation layer is indium zinc oxide (IZO) thin layer, protection
Finishing coat includes polyurethane film, the organosilicon film arranged from the inside to the outside.
Described each film plating layer thickness is: in priming coat polyurethane film be 0.5-1 μm, IZO thin film be 100-500nm, anti-
During in mask coating, polyurethane film is 0.5-1 μm, protection face coating, organosilicon film is 2-5 μm.In described IZO thin film
The weight/mass percentage composition of In2O3 is 10-13%, and surplus is ZnO.
The beneficial effects of the utility model are as follows:
Simple glass is frangible, toughness is low, and main component is silicon dioxide.Lucite substrate material of the present utility model
Selecting Merlon, Merlon has the feature such as high transparent, lightweight, high tenacity, and more traditional glass material has more
High impact resistance, overcomes the defect of glass self-explosion.Use amorphous state IZO thin film as Low emissivity thermal insulation layer, plating can be made
Film lucite has higher visible light transmissivity and the isolation thermal-radiating ability of infrared band.Inorganic conductive thin film is with organic
There is thermal coefficient of expansion and stress state difference between glass substrate, in use Low emissivity thermal insulation layer is easy to crack and film
Layer adhesion failure, increases polyurethane film between Low emissivity thermal insulation layer and lucite and solves this technical barrier.Organic
In silicon coating, Si-O-Si cross-links in rigidity network structure, and protection face coating has good hardness and wearability, improves poly-carbon
The wearability of acid esters substrate and dependability.Safe cladding glass of the present utility model has lightweight, visible light transmissivity
High and low radiance is good, weatherability strong, overcomes " self-destruction " defect of traditional glass, so that safety curtain of the present utility model
Wall glass has the highest practicality in people intensive buildings such as libraries of the universities.
Accompanying drawing explanation
Fig. 1 is a kind of safe curtain wall glass structure schematic diagram for libraries of the universities described in the utility model.In figure:
1, lucite substrate;2, priming coat;3, Low emissivity thermal insulation layer;4, protection face coating;41, polyurethane film;42, organosilicon membrane
Layer.
Detailed description of the invention
As it is shown in figure 1, a kind of safe cladding glass for libraries of the universities described in the utility model, including: organic
Glass substrate 1, lucite substrate 1 be arranged above with priming coat 2, Low emissivity thermal insulation layer 3, protection face coating 4, lucite base
Sheet 1 protection face coating 4 is provided below;Described protection face coating 4 includes the polyurethane film 41 that arranges from the inside to the outside and organic
Silicon film 42;Merlon material selected by described lucite substrate 1;Described priming coat 2 is polyurethane film;Described Low emissivity
Thermal insulation layer 3 is indium zinc oxide (IZO) thin layer.
The design parameter of each layer of above-mentioned film plating layer is: in priming coat polyurethane film be 0.5-1 μm, IZO thin film be 100-
During in 500nm, protection face coating, polyurethane film is 0.5-1 μm, protection face coating, organosilicon film is 2-5 μm.Described IZO is thin
In film, the weight/mass percentage composition of In2O3 is 10-13%, and surplus is ZnO.
This utility model is further illustrated below by way of specific embodiment:
Embodiment 1: polycarbonate substrate selected by lucite substrate 1, the thickness of polycarbonate substrate is 5mm, poly-carbonic acid
The above of ester group sheet is followed successively by: polyurethane film 2, indium zinc oxide (IZO) thin layer 3, polyurethane film 41, organosilicon film
42;Polycarbonate substrate polyurethane film 41 and organosilicon film 42 are provided below;The design parameter of each layer of above-mentioned film plating layer
For: polyurethane film be 0.7 μm, IZO thin film be 250nm, organosilicon film be 4 μm.The quality of In2O3 and ZnO in IZO thin film
Percentage ratio is 10.7:89.3 wt%.
In the present embodiment, as follows for the preparation technology of the safe cladding glass of libraries of the universities:
The first step, use ultrasonic waves for cleaning polycarbonate substrate, be then placed in drying oven and dry;
Second step, by adding the viscosity of appropriate diluent regulation polyurethane solutions, again through super after stirring with agitator
Sonication makes polyurethane solutions in 10 minutes;
Polyurethane-coated above polycarbonate substrate, is toasted 12 with baking oven at 50 DEG C by the 3rd step, employing knife coating
Hour, the film-forming that is completely dried to be coated, thicknesses of layers 0.7 μm;
4th step, by coating polyurethane film polycarbonate substrate put in magnetic control sputtering device, at polyurethane film
Sputtering IZO thin film above, target In2O3 and ZnO powder mixed sintering target, mass percent is 10.7:89.3 wt%, Ar
Throughput 40 sccm, O2 throughput 0.8 sccm, d.c. sputtering power 40W, sputtering pressure 0.5Pa, underlayer temperature room temperature, spatter
Penetrate the time 30 minutes, film thickness 250nm;
Polyurethane-coated in IZO film surface, is toasted 12 hours at 50 DEG C with baking oven, is treated by the 5th step, employing knife coating
Coating is completely dried film-forming, thicknesses of layers 0.7 μm;
Polyurethane-coated below polycarbonate substrate, is toasted 12 with baking oven at 50 DEG C little by the 6th step, employing knife coating
Time, the film-forming that is completely dried to be coated, thicknesses of layers 0.7 μm;
7th step, employing showering method, by organic silicon wear resistance coating material showering on band film polycarbonate substrate two sides,
It is placed in prebake 10 minutes in 40-50 DEG C of baking oven, is then put in 60 DEG C of baking ovens solidification 2 hours, obtains the wear-resisting of thickness about 4 μm
Coating.
It should be noted that above example is only in order to illustrate the technical solution of the utility model and unrestricted.Based on this
The description at place, those skilled in the art need not to pay performing creative labour can associate that of the present utility model other is concrete
Embodiment, within these modes fall within protection domain of the present utility model.
Claims (3)
1., for a safe cladding glass for libraries of the universities, including organic glass substrate, the above of lucite substrate sets
Bottom set coating, Low emissivity thermal insulation layer, protection face coating, lucite substrate protection face coating is provided below;
Described lucite substrate material is Merlon, and priming coat is polyurethane film, and Low emissivity thermal insulation layer is indium zinc oxide
(IZO) thin layer, protection face coating includes polyurethane film, the organosilicon film arranged from the inside to the outside.
A kind of safe cladding glass for libraries of the universities the most according to claim 1, it is characterised in that described each plating
Thicknesses of layers is: in priming coat polyurethane film be 0.5-1 μm, IZO thin film be 100-500nm, polyurethane in protection face coating
Film layer is that in 0.5-1 μm, protection face coating, organosilicon film is 2-5 μm.
A kind of safe cladding glass for libraries of the universities the most according to claim 1, it is characterised in that described IZO is thin
In in film2O3Weight/mass percentage composition be 10-13%, surplus is ZnO.