CN205688627U - A kind of ceramet plate realizing transferring artistic effect - Google Patents
A kind of ceramet plate realizing transferring artistic effect Download PDFInfo
- Publication number
- CN205688627U CN205688627U CN201620498255.XU CN201620498255U CN205688627U CN 205688627 U CN205688627 U CN 205688627U CN 201620498255 U CN201620498255 U CN 201620498255U CN 205688627 U CN205688627 U CN 205688627U
- Authority
- CN
- China
- Prior art keywords
- ceramet
- artistic effect
- transfer
- plate
- film
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The utility model discloses a kind of ceramet plate realizing transferring artistic effect, it is characterised in that including: a metal plate substrate；One pottery film, is sprayed on described metal plate substrate；One transfer pattern layer, is arranged on described pottery film.The ceramet plate dicoration of transfer artistic effect of the present utility model is higher, and transfer pattern layer has been dissolved in ceramic film very well, remains high rigidity characteristic and the ceramic texture of uniqueness of pottery film.
Description
Technical field
This utility model relates to metal curtain wall and track traffic furnishing fields, is specifically related to a kind of realization and transfers artistic effect
Ceramet plate.
Background technology
The fire protecting performance that ceramic coating is remarkable, good weatherability, resistance to marring, and the ring that aqueous inorganic paint has
Guarantor property so that ceramet plate is mainly used in high-end public domain in curtain wall market, station base curtain wall and rail such as subway are handed over
Large-scale people's stream aggregation, fire prevention and the safety requirements such as automobile interior and hospital, museum, market, gymnasium, school, tunnel are relatively
High field.But existing process color is single, can not meet people's diversified decoration demand.
Utility model content
This utility model provides a kind of ceramet plate realizing transferring artistic effect.There is blue-and-white porcelain, marble, wood
The ceramet plate of the artistic effects such as stricture of vagina.Transfer is simple, clear patterns is natural.Transfer pattern can pass through digital printing, and can root
Customizing according to customer demand, artistic effect is varied.
In order to realize foregoing invention purpose, this utility model provides a kind of ceramet realizing transferring artistic effect
Plate, it is characterised in that including a: metal plate substrate；One pottery film, is sprayed on described metal plate substrate；One transfer figure
Pattern layer, is arranged on described pottery film.
Reasonable, that this utility model the provides ceramet plate realizing transfer artistic effect, it is characterised in that institute
State metal plate substrate and include aluminum, steel, copper, ferrum and alloy material thereof.
Reasonable, that this utility model the provides ceramet plate realizing transfer artistic effect, it is characterised in that
Described pottery coating thickness is 25～60um.
Reasonable, that this utility model the provides ceramet plate realizing transfer artistic effect, it is characterised in that institute
State transfer pattern layer to be made up of the ink with heat sublimation animal migration.
Reasonable, that this utility model the provides ceramet plate realizing transfer artistic effect, it is characterised in that institute
State transfer pattern layer to be made up of diversified decoration layer, including blue-and-white porcelain, marble, wood grain.
The ceramet plate dicoration that this utility model achieves transfer artistic effect is higher, and transfer pattern layer melts very well
Enter in ceramic film, remain high rigidity characteristic and the ceramic texture of uniqueness of pottery film.
Accompanying drawing explanation
Below, referring to the drawings, for those skilled in the art, to detailed description of the present utility model
In, above and other objects, features and advantages of the present utility model will be apparent to.
Fig. 1 is structural representation of the present utility model.
Reference
1---sheet metal
2---pottery film
3---transfer pattern layer
10---ceramet plate
Detailed description of the invention
Describe with detailed reference to accompanying drawing now and embodiment of the disclosure.Being preferable to carry out with detailed reference to the disclosure now
Example, its example is shown in the drawings.In the case of any possible, identical labelling will be used to represent phase in all of the figs
Same or similar part.Although additionally, the term used in the disclosure is to select from public term, but
Some terms mentioned in present disclosure specification are probably what applicant was selected by his or her judgement, and its detailed meanings exists
Explanation in the relevant portion of description herein.Additionally, require not only by the actual terms used, and it is also to by often
The meaning that individual term is contained is to understand the disclosure.
As it is shown in figure 1, ceramet plate 10 of the present utility model is with sheet metal 1 as base material, coated ceramic film 2
After, then transfer pattern layer 3.
Specifically, the processing steps of ceramet plate 10 of the present utility model includes:
Step one a, it is provided that base material, it is common that the sheet metal including the base material etc. of aluminum, steel, copper, ferrum and alloy thereof
1, need to carry out sandblasting or passivation pre-treatment；
Step 2, uses ceramic coating to spray this sheet metal 1, forms pottery film 2, and this film is inorganic oxygen
The film that compound colloidal sol and water-disintegrable alkoxide are formed through chemical reaction, thickness 25～60um, this ceramic coating have prevent fires do not fire,
High rigidity, scratch resistant distinguishing feature；
Step 3, to spraying after sheet metal 1 carry out precuring, solidification temperature is 80～90 DEG C, the time 10～
20min；
Step 4, transfers on pottery film 2, specifically transfer pattern layer 3 moistening is pasted ceramic coating 2
Surface, this transfer pattern layer 3 is made up of the ink with heat sublimation animal migration, and transfer pattern layer 3 includes blue-and-white porcelain, Dali
The diversified decoration layer such as stone, wood grain；
Step 5, carries out hot setting to the ceramet plate 10 after transfer, and solidification temperature is 180～190 DEG C, the time 15
～20min, on the one hand this hot setting makes pottery film 2 itself reach bond strength, on the other hand makes transfer pattern layer 3 migrate
To the inside of pottery film 2, and be combined well with pottery film 2；
Step 6 is cleaned, and by clean for the surface clean of pottery film 2, i.e. obtains the ceramet with specific artistic effect
Plate.
By the solidification intensity of three, 4 two stage control pottery films 2 of above-mentioned steps, the low-temperature setting section of step 3 is real
The precuring of existing pottery film 2, pottery film 2 is after precuring, and surface pastes transfer pattern layer 3, then the high temperature through step 4
Solidification, during hot setting, on the one hand pottery film 2 itself reaches bond strength, and on the other hand transfer pattern layer 3 can move to
Pottery film 2 is internal, and is combined very well with pottery film 2.
The caloric transfer printing technology that this utility model is used is by low temperature precuring section and two stages of hot setting section
Control the combination between solidification intensity and transfer pattern layer and the pottery film of pottery film self.
The ceramet plate realizing transfer artistic effect of the present utility model, compared with traditional ceramet plate, it is achieved
The ceramet plate dicoration of transfer artistic effect is higher, and transfer pattern layer 3 has been dissolved in ceramic film 2 very well, retains
The high rigidity characteristic of ceramic film 2 and the ceramic texture of uniqueness.
In above-mentioned making technology, in pottery film 2 transfer printing process, low-temperature setting temperature and time needs according to base material
Depending on kind and thickness.
The description to preferred embodiment provided above, so that any technical staff in this area can use or utilize this
Invention.Various amendments to these embodiments are evident for personnel skilled in the art, can be described here total
Principle be applied to other embodiments and do not use creativeness.Thus, the present invention is not limited to embodiment depicted herein, and answers
According to the widest range meeting teachings disclosed herein and new feature.
Claims (5)
1. the ceramet plate realizing transferring artistic effect, it is characterised in that including:
One metal plate substrate；
One pottery film, is sprayed on described metal plate substrate；
One transfer pattern layer, is arranged on described pottery film.
The ceramet plate realizing transfer artistic effect the most according to claim 1, it is characterised in that
Described metal plate substrate includes aluminum, steel, copper, ferrum and alloy material thereof.
3. the ceramet plate realizing transfer artistic effect as claimed in claim 1 or 2, it is characterised in that
Described pottery coating thickness is 25～60um.
4. the ceramet plate realizing transfer artistic effect as claimed in claim 3, it is characterised in that
Described transfer pattern layer is made up of the ink with heat sublimation animal migration.
5. the ceramet plate realizing transfer artistic effect as claimed in claim 4, it is characterised in that
Described transfer pattern layer is made up of diversified decoration layer, including blue-and-white porcelain, marble, wood grain.