CN205528437U - Glass panel is decorated to glass granule - Google Patents
Glass panel is decorated to glass granule Download PDFInfo
- Publication number
- CN205528437U CN205528437U CN201620117686.7U CN201620117686U CN205528437U CN 205528437 U CN205528437 U CN 205528437U CN 201620117686 U CN201620117686 U CN 201620117686U CN 205528437 U CN205528437 U CN 205528437U
- Authority
- CN
- China
- Prior art keywords
- glass
- glass particle
- utility
- model
- granule
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The utility model relates to a glass panel is decorated to glass granule is aimed at providing in architectural decoration building materials field. This product includes as architectural glass (1) of basement, has still adhered to one deck glass particle coating (2) on architectural glass's (1) surface, this glass particle coating (2) comprise glass granule and bonding agent, and its surface has irregularly distributed's concaveconvex shape. The utility model discloses an in the concavo -convex special structure of glass surface formation, the vision was pleasing to the eye, unique, provides a new architectural decoration material after glass granule decorative board can adopt all size and shape glass granule through mixture with the bonding agent and thermofixation. And simultaneously, the utility model provides a glass carries out the an effective way to that utilizes to the abandonment.
Description
Technical field
The invention belongs to building decoration building materials field, especially a kind of glass particle ambetti sheet material.
Background technology
Along with expanding economy, people are increasing for the demand of novel appearance decorative building material attractive in appearance.Glass particle has
The effect having scattering light can produce again concavo-convex third dimension simultaneously thus is laid in plate surface and can produce uniqueness
Visual effect.On the other hand, glass material uses more and more under construction, and consequent category of glass construction waste is also
More and more, the recycling for discarded building glass is also a problem demanding prompt solution, and by discarded building glass
Being processed into glass particle recycling is a good approach.This utility model is by mixing glass particle by bonding agent
After be bonded in surface of plate glass and obtain a kind of glass plate with decoration functions.
Utility model content
The technical problems to be solved in the utility model is, overcomes deficiency of the prior art, it is provided that a kind of glass particle decoration
Glass board material.
For solving technical problem, solution of the present utility model is:
There is provided a kind of glass particle ambetti sheet material, including the building glass (1) as substrate, in building glass (1)
Surface be also attached to one layer of glass particle coating (2);This glass particle coating (2) is by glass particle and bonding agent
Composition, its surface has the concaveconvex shape being randomly distributed.
Improving as one, the thickness of described glass particle coating (2) is 1~5mm.
Improving as one, described building glass (1) is plate glass.
Improving as one, the average diameter of described glass particle is 1~5mm.
Improve as one, the shape of described glass particle be following any one or a few: spherical, tear drop shape, pros
Body, cuboid, cone or irregular three-dimensional shape.
Compared with prior art, of the present utility model have the technical effect that
Glass particle decorative panel of the present utility model can use mixed by with bonding agent of all size and shape glass particle
Close and form concavo-convex special structure, visual appearance, uniqueness at glass surface after heat cure, it is provided that a kind of new building
Ornament materials.Meanwhile, the technical solution of the utility model is the effective way utilizing scrap glass.
Accompanying drawing explanation
Fig. 1 is this utility model structural representation.
Detailed description of the invention
Illustrated embodiment below in conjunction with the accompanying drawings, the utility model is described in further detail.
As it is shown in figure 1, glass particle ambetti sheet material includes the building glass 1 as substrate, at building glass 1
Surface is also attached to one layer of glass particle coating 2;This glass particle coating 2 is made up of with bonding agent glass particle,
Its surface has the concaveconvex shape being randomly distributed.The thickness of glass particle coating 2 is 1~5mm.
Building glass 1 can carry out type selecting, the most optional common plate glass according to actual needs, or has song
The special type glass of face radian.Glass particle coating 2 in this utility model is mixed with bonding agent by glass particle.
Glass particle dalle in this utility model can be prepared by following method: by glass particle coating with roller
The mode being coated with or watering pouring is attached on building glass 1, forms the glass particle not yet solidified on the surface of building glass 1 and is coated with
Layer 2;Semi-finished product after cured 5min, are put into solidification 20min, glass particle in the drying tunnel of 180 DEG C at 80 DEG C
Coating 2 is solidified, and i.e. can get the final products of glass particle ambetti sheet material.Wherein, glass particle coating 2
Thickness be 1~5mm.Owing to glass particle shape is uncertain, and the distribution in bonding agent is random, therefore originally
The surface of utility model product has the concaveconvex shape being randomly distributed.
Glass particle coating can be prepared by following method: under the rotary speed of 100~200r/min, by 30~50
The glass particle of mass parts and the organo-mineral complexing bonding agent of 50 mass parts mix 30min in rolling oil machine, obtain glass
Glass particulate coating material.
Organo-mineral complexing bonding agent used in this utility model preparation process can be prepared by following method:
(1) under the mixing speed of 300r/min, by the positive esters of silicon acis of 10~20 mass parts, 20~30 bands of mass parts
The silane coupler of long-chain joins mix homogeneously in the mixed solution of 20 mass parts ethanol and 20 mass parts isopropanols, uses
Concentrated hydrochloric acid regulation solution ph is between 1~2;
(2) under 200~300r/min mixing speeds, the deionized water of 5~10 mass parts is joined step (1) institute
Obtaining in mixture, at 40~60 DEG C, reaction obtains organo-mineral complexing bonding agent in 6~8 hours.
Or, it is also possible to select commercially available organic/inorganic composite caking agent, the EC-1386 one-component ring of such as 3M company
Epoxy resins heat cure glue or Henkel PUR Q3218.As long as color or property will not be able to occur under the conditions of being heating and curing
The bonding agent of qualitative change, may be used to the preparation of this utility model product.
Finally it should be noted that listed above is only specific embodiment of the utility model.Obviously, the present invention is not
It is limited to above example, it is also possible to have many variations.Those of ordinary skill in the art can be from present disclosure
The all deformation directly derived or associate, are all considered as protection domain of the present utility model.
Claims (5)
1. a glass particle ambetti sheet material, including the building glass (1) as substrate, it is characterised in that be also attached to one layer of glass particle coating (2) on the surface of building glass (1);This glass particle coating (2) is made up of with bonding agent glass particle, and its surface has the concaveconvex shape being randomly distributed.
Glass particle ambetti sheet material the most according to claim 1, it is characterised in that the thickness of described glass particle coating (2) is 1~5mm.
Glass particle ambetti sheet material the most according to claim 1, it is characterised in that described building glass (1) is plate glass.
Glass particle ambetti sheet material the most according to claim 1, it is characterised in that the average diameter of described glass particle is 1~5mm.
Glass particle ambetti sheet material the most according to claim 1, it is characterised in that the shape of described glass particle be following any one or a few: spherical, square, cuboid or cone.