CN205344017U - Phenolic foam presss from both sides core flame -retardant composite board - Google Patents
Phenolic foam presss from both sides core flame -retardant composite board Download PDFInfo
- Publication number
- CN205344017U CN205344017U CN201521095785.1U CN201521095785U CN205344017U CN 205344017 U CN205344017 U CN 205344017U CN 201521095785 U CN201521095785 U CN 201521095785U CN 205344017 U CN205344017 U CN 205344017U
- Authority
- CN
- China
- Prior art keywords
- flame
- phenolic foam
- surface course
- flame retardant
- retardant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The utility model discloses a phenolic foam presss from both sides core flame -retardant composite board, including last surface course, lower surface course and sandwich layer, its characterized in that to the flame retardant fiber board is as last surface course, lower surface course, uses stereoplasm phenolic foam as the sandwich layer, contains phenol -formaldehyde resin adhesive or amino resin adhesive layer on the flame retardant fiber board between surface course and the stereoplasm phenolic foam sandwich layer and under the flame retardant fiber board between surface course and the stereoplasm phenolic foam sandwich layer, the thickness of surface course is 1.0 -45.0mm on the flame retardant fiber board, the thickness of surface course is 1.0 -45.0mm under the flame retardant fiber board, the thickness of stereoplasm phenolic foam sandwich layer is 10.0 -450.0mm. Phenol -formaldehyde resin adhesive or amino resin adhesive layer's adhesive spread is 100kg -150kgm2. The utility model discloses when improving its adhesion strength, give fire -retardant combined material light, heat preservation, thermal -insulated and fire behavior again. Phenolic foam presss from both sides core flame -retardant composite board's application range has been enlarged.
Description
Technical field
This utility model belongs to composite board manufacturing technology field, particularly relates to a kind of phenolic foam sandwich flame-retardant composite board and manufacturing technology.
Background technology
Phenolic foam sandwich flame-retardant composite board is as upper and lower plane materiel by flame retardant fibre board, with hard phenol formaldehyde foam for core, by the sandwich composite board that one-shot forming or secondary forming process (hot pressing or mode of colding pressing) are prepared from, also known as light-duty flame retardant fibre board sandwich hard phenolic foam composite plate.General density is less than or equal to 350kg/m3Sandwich composite board.
Interior/exterior decoration finishing material is the key factor determining building trade safety, and the generation of a large amount of fire incidents all shows, mainly uses combustible material to cause.Flame retardant fibre board is a kind of artificial wood-based board, there is the features such as fire-retardant and easy secondary operations use, it is widely used in the furniture of public place, floor and door-plate manufacture and indoor decorating field, but the defect such as self there is matter weight, thickness is little and thermal and insulating performance is poor, use scope is subject to a definite limitation.Wang Zhicai, Bai Peikang scholar points out at " research of phenol formaldehyde foam and composite thereof and application " literary composition, phenol formaldehyde foam is a kind of lightweight, fire-retardant, insulation and heat insulation expanded plastic material, there is fire-retardant, low-smoke low-toxicity and the heat stability of excellence, but have that intensity is low, surface quality is poor, easy dry linting and the defect such as fragility is big.
Currently, along with the development of material manufacturing technology, sandwich sandwich is increasingly used widely.Hong Lu, Wang Meilan etc. " prediction of phenolic foam material industry development " the article pointed out, phenolic foam board is many with phenolic foam for central layer, and surface pastes aluminium sheet, color steel or non-woven fabrics.And at present flame retardant fibre board pastes phenolic foam products and still belongs to lab scale conceptual phase in market, industrialization is had not yet been formed.How to overcome flame retardant fibre board and the self-defect of phenolic foam board own, the advantage playing each material, solve that flame-retarded light composite production efficiency is low or difficulty realizes the drawback of automated production, thus widening fire-retardant composite wood in applications such as industry and civil buildings warming plate, internal partition wall, roofing, ceilings, meet market place differentiation demand, to promoting the development of wood-based plate transition and upgrade, eliminate disaster hidden-trouble, ensure safety, significant.For solving above-mentioned technical bottleneck, research utility model phenolic foam sandwich flame-retardant composite board and industrialization produce significant.
Utility model content
The purpose of this utility model is in that for the deficiencies in the prior art, it is provided that a kind of phenolic foam sandwich flame-retardant composite board, widens it as field ranges of application such as non-structural building decoration, warming plate, partition wall, roofing, variolas, eliminates disaster hidden-trouble, it is ensured that safety.
The purpose of this utility model is achieved through the following technical solutions.
A kind of phenolic foam sandwich flame-retardant composite board, including upper layer, cutting optimal and sandwich layer, it is characterized in that, using flame retardant fibre board as upper layer, cutting optimal, with hard phenol formaldehyde foam for sandwich layer, between flame retardant fibre board upper layer and hard phenol formaldehyde foam sandwich layer and between flame retardant fibre board cutting optimal and hard phenol formaldehyde foam sandwich layer, contain phenolic resin glue or amino resin adhesive layer；The thickness of described flame retardant fibre board upper layer is 1.0-45.0mm, and the thickness of described flame retardant fibre board cutting optimal is 1.0-45.0mm, and the thickness of described hard phenol formaldehyde foam sandwich layer is 10.0-450.0mm.
The glue-spread of described phenolic resin glue or amino resin adhesive layer is 100kg-150kg/m2。
The breadth of described composite plate be shaped as arbitrary shape.
Being shaped as of the breadth of described composite plate is square.
The breadth of described composite plate is arbitrary dimension.
The book size of described composite plate is 4 × 8 chis or 4 × 16 chis.
Relative to prior art, the method have the advantages that in phenolic foam sandwich flame-retardant composite board of the present utility model containing phenolic resin glue or amino resin adhesive layer.While improving its adhesion strength, give again composite material light, insulation, heat insulation and fire protecting performance.Expand the use scope of phenolic foam sandwich flame-retardant composite board, solve and be difficult to the common technology bottleneck problem such as industrialization or automated production.Contribute to promoting the further development of forest product industry, there is good Social benefit and economic benefit.
Accompanying drawing explanation
Fig. 1 is the structural representation of a kind of embodiment of the present utility model
Fig. 2 is the structural representation of another kind of embodiment of the present utility model
In figure, 1-fire resistance fibre flaggy, 2-adhesive layer, 3-phenol formaldehyde foam layer
Detailed description of the invention
Below in conjunction with accompanying drawing, detailed description of the invention of the present utility model is described further.
Fig. 1 is a kind of example structure schematic diagram of the present utility model, and this phenolic foam sandwich flame-retardant composite board 1 is square.
It is adopt artificial or glue spreader to carry out uniform gluing and metering on flame retardant fibre board or phenolic foam board face that enhancement mode adhesive described in this practicality applies using method.
Fig. 2 is another kind of example structure schematic diagram of the present utility model, and thickness is 10.0-450.0mm, and phenolic resin glue described in the utility model or amino resin adhesive layer glue-spread are 100.0kg-150.0kg/m2。
This utility model is by detecting the 10.0-450.0mm phenolic foam sandwich flame-retardant composite board produced, its adhesion strength >=0.08MPa, heat conductivity≤0.045W/ (m k), burst size of methanal specifies E1 level (≤1.5mg/L) far below GB18580-2001, and fire-retardant (fire prevention) performance reaches the GB/T8624-2012 B1 grade standard specified.
Phenolic foam sandwich flame-retardant composite board manufacturing process flow of the present utility model is:
1) flame retardant fibre board is placed into by fork truck and pushes away buttress position；
2) flame retardant fibre board is by charging transplanting mechanism suction and conveying to press dolly；
3) carrying out phenol formaldehyde foam group embryo (after gluing) on press dolly, the suction of charging transplanting mechanism is covered second flame retardant fibre board and is transported on slab in cover alignment (completing composite plate group embryo)；
4) the composite plate group embryo organized is transported on platen platform by press dolly；
5) on 100-200 DEG C of hot press, after hot pressing 0.5-10.0min, release ejecting plate and positions to (ejecting plate) roller line；
6) discharging transplanting mechanism (suction) presss from both sides the composite plate of firm hot pressing ejecting plate and moves stacking to specifying position；
7) last fork truck is transported finished product composite plate and is namely completed automated production manufacture process through room temperature placement health preserving.
Experimental data proves, phenolic foam sandwich flame-retardant composite board of the present utility model, not only has higher adhesion strength, has again the lightweight of composite, insulation, heat insulation and fire-retardant fireproof performance.
Claims (6)
1. a phenolic foam sandwich flame-retardant composite board, including upper layer, cutting optimal and sandwich layer, it is characterized in that, using flame retardant fibre board as upper layer, cutting optimal, with hard phenol formaldehyde foam for sandwich layer, between flame retardant fibre board upper layer and hard phenol formaldehyde foam sandwich layer and between flame retardant fibre board cutting optimal and hard phenol formaldehyde foam sandwich layer, contain phenolic resin glue or amino resin adhesive layer；The thickness of described flame retardant fibre board upper layer is 1.0-45.0mm, and the thickness of described flame retardant fibre board cutting optimal is 1.0-45.0mm, and the thickness of described hard phenol formaldehyde foam sandwich layer is 10.0-450.0mm.
2. a kind of phenolic foam sandwich flame-retardant composite board according to claim 1, the glue-spread of described phenolic resin glue or amino resin adhesive layer is 100kg-150kg/m2。
3. a kind of phenolic foam sandwich flame-retardant composite board according to claim 1, it is characterised in that the web-shaped of described composite plate is arbitrary shape.
4. a kind of phenolic foam sandwich flame-retardant composite board according to claim 3, it is characterised in that the web-shaped of described composite plate is square.
5. a kind of phenolic foam sandwich flame-retardant composite board according to claim 4, it is characterised in that the book size of described composite plate is arbitrary dimension.
6. a kind of phenolic foam sandwich flame-retardant composite board according to claim 4, it is characterised in that the book size of described composite plate is 4 × 8 chis or 4 × 16 chis.