CN205280479U - A aluminum sheet base plate for coating shear strength is experimental and sample is used in test thereof - Google Patents
A aluminum sheet base plate for coating shear strength is experimental and sample is used in test thereof Download PDFInfo
- Publication number
- CN205280479U CN205280479U CN201521061826.5U CN201521061826U CN205280479U CN 205280479 U CN205280479 U CN 205280479U CN 201521061826 U CN201521061826 U CN 201521061826U CN 205280479 U CN205280479 U CN 205280479U
- Authority
- CN
- China
- Prior art keywords
- caulking groove
- aluminium flake
- aluminum sheet
- porcelain plate
- sheet base
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The utility model belongs to the technical field of coating shear strength is experimental, especially, relate to an aluminum sheet base plate for coating shear strength is experimental and sample is used in test thereof, the aluminum sheet base plate includes: the setting is at the caulking groove that is arranged in mosaic glass board or porcelain plate of one side of aluminum sheet base plate and the one or more activity buckle that is used for after glass board or porcelain plate are placed to the caulking groove this glass board of chucking or porcelain plate, but the activity buckle including fix the pivot pivoted activity chucking piece of caulking groove one side with fix the fixed knot at the caulking groove opposite side. The test comprises two superimposed aluminum sheet base plates of part with the sample, and two aluminum sheet base plates are inlayed and are had glass board or porcelain plate with the mode setting that the caulking groove is relative, the caulking groove separately of two aluminum sheet base plates, has between inlaid glass board or the porcelain plate in the caulking groove of two aluminum sheet base plates glass board or the porcelain plate part bonding coating that awaits measuring together. The utility model discloses having reduced the test moment of torsion, having makeed the base plate be difficult to more warp simultaneously, while convenient to detach, but repetitious usage need not to bond.
Description
Technical field
This utility model belongs to coating shear strength test technical field, particularly relates to a kind of aluminium flake substrate for coating shear strength test and test sample thereof.
Background technology
Shear strength test is applicable to the coating of preparation under rated condition and the shearing sample that two parallel plates (or porcelain plate) are bonding. Coating is next bonding by vulcanizing with glass plate (or porcelain plate). Sample is the bridging arrangement that coating is clipped between two parallel plates (or porcelain plate). The bonding plane of sample applies tensile shear power, measures the maximum tension shearing force of sample. Maximum tension shearing force on sample unit bonding plane is coating tensile shear strength bonding with glass plate (or porcelain plate).
In prepared by existing shear strength sample, as it is shown in figure 1, constituted a shearing sheet by a glass sheets 2 is bonding with a piece of aluminium sheet 1, with coating 3 to be measured, the glass-board surface of the two of said structure shearing sheets is bonded together one sample of composition. Preparing sample and should use fixture, to ensure that sample is correctly bonding, the dislocation of bonding plane is not more than 0.2mm. When test, regulating the temperature of experimental enviroment to 23 �� 2 DEG C, humidity, to 40-70%, by the length and width of gage measuring sample bonding plane, is accurate to 0.05mm, is fixed on the upper and lower holder of tensile testing machine by the aluminium sheet of sample end. Start testing machine, make clamper with the speed of (50 �� 5) mm/min, sample be loaded, until coating destroys completely with the bonding of glass plate, record the maximum load of sample destruction and the Failure type of bonding plane.
Above-mentioned prior art has the drawback that when holder aluminium sheet termination stretches, two power effects are not point-blank, there is moment of torsion, adopt original method film-making, moment of torsion is big, and (position of power is calculated with the centrage of aluminium sheet, when sheet thickness is 5mm, about 12mm), in testing, it is easily caused aluminium sheet bending, warpage and aluminium sheet and glass plate bonding plane destruction so that final result invalid (to destroy between two pieces of glass plates be effective), or test data are inaccurate, the situations such as data fluctuations is big.
Utility model content
For above-mentioned prior art defect, the utility model proposes a kind of aluminium flake substrate for coating shear strength test and test sample thereof, including: it is arranged on the caulking groove for mosaic glass plate or porcelain plate of the side of aluminium flake substrate and for placing one or more movable buckles of this glass plate of clamping or porcelain plate after glass plate or porcelain plate in caulking groove, described movable buckle includes being fixed on the pivotable movable clamping sheet of caulking groove side and being fixed on the clip of caulking groove opposite side, and described movable clamping sheet is provided with the clamping slot that can coordinate with clip.
Described aluminium flake substrate is provided with the thickness thickness less than the side being not provided with caulking groove of the side of caulking groove.
Described aluminium flake substrate is provided with the thickness 1.0mm less of the thickness of the side being not provided with caulking groove of the side of caulking groove.
Described test sample is made up of the aluminium flake substrate of two part overlappings, two aluminium flake substrates are arranged in the way of caulking groove is relative, the respective caulking groove of two aluminium flake substrates is inlaid with glass plate or porcelain plate, has the coating to be measured glass plate or porcelain plate part bonded together in the caulking groove of two aluminium flake substrates between incrusted glass plate or porcelain plate.
Described coating to be measured is Prospect on RTV of Solidified Silicon Rubber in Normal Temperature for Insulator.
This utility model by being mounted in aluminium flake substrate by glass plate, (position of power is calculated with the centrage of aluminium sheet to reduce moment of torsion, when sheet thickness is 5mm, about 6mm), the simultaneously increase of the thickness of aluminium flake and the mode inlayed make more to be not easy deformation, simultaneously facilitate dismounting, can repeatedly use, without bonding, not only solve the test inaccurate problem of data, also improve the convenience of test simultaneously.
Additionally this utility model may extend to the test of the shear strength of any other bonding test material, adopts aluminium flake to make substrate and is because glass plate and cannot clamp, and can skid in testing, broken; If running into equally other materials when cannot directly test, it would however also be possible to employ the method, making substrate with aluminium flake and realizing test. Former method must carry out bonding, when testing material with aluminium flake poor attachment, it is impossible to test; In improved method of the present utility model, employing is inlayed, the mode of compression, it is possible to solve very well. Such as thickness 0.5��1.5mm less of the thickness of the side being not provided with caulking groove, it is preferable that 0.8��1.2mm, more preferably from about 1.0mm.
Accompanying drawing explanation
Fig. 1 a and Fig. 1 b is top view and the side view of prior art shear strength sample.
Fig. 2 a and Fig. 2 b is this utility model for the aluminium flake substrate top view of coating shear strength test and side view.
Fig. 3 a and Fig. 3 b is test sample top view of the present utility model and side view.
Detailed description of the invention
Below in conjunction with accompanying drawing, embodiment is elaborated.
As shown in Figure 2 a and 2 b, the caulking groove 11 for mosaic glass plate or porcelain plate that aluminium flake substrate 10 for coating shear strength test of the present utility model includes being arranged on the side of aluminium flake substrate and for placing one or more movable buckles of this glass plate of clamping or porcelain plate after glass plate or porcelain plate in caulking groove, described movable buckle includes the pivotable movable clamping sheet 12 being fixed on caulking groove side and the clip 13 being fixed on caulking groove opposite side, and described movable clamping sheet is provided with the clamping slot that can coordinate with clip. It is in the state of clamping with clip for the clamping slot of movable clamping sheet coordinates shown in figure.
Preferably, aluminium flake substrate is provided with the thickness thickness less than the side being not provided with caulking groove of the side of caulking groove, for instance thickness 0.5��1.5mm less of the thickness of the side being not provided with caulking groove, it is preferable that 0.8��1.2mm, more preferably from about 1.0mm.
Wherein, the thickness of glass plate or porcelain plate is such as 5mm, and width is 20-25mm, and length is about 70mm, and the size of the size of the caulking groove of aluminium flake substrate and glass plate or porcelain plate adapts to so that just can put into glass plate or porcelain plate. The width of aluminium flake substrate can be 30��45mm, it is preferable that about 36mm, and it is 5mm that aluminium flake substrate is provided with the thickness of the side of caulking groove, it does not have the thickness arranging the side of caulking groove is 6mm, and the length of aluminium flake substrate can be 120��200mm, it is preferable that about 150mm.
Test sample of the present utility model, as best shown in figures 3 a and 3b, including: the aluminium flake substrate 10 of two part overlappings, the caulking groove 11 for mosaic glass plate or porcelain plate that each of which aluminium flake substrate includes being arranged on the side of aluminium flake substrate and for placing one or more movable buckles of this glass plate of clamping or porcelain plate after glass plate or porcelain plate in caulking groove, two aluminium flake substrates are arranged in the way of caulking groove is relative, described movable buckle includes the pivotable movable clamping sheet 12 being fixed on caulking groove side and the clip 13 being fixed on caulking groove opposite side, described movable clamping sheet is provided with the clamping slot that can coordinate with clip, the respective caulking groove of two aluminium flake substrates is inlaid with glass plate or porcelain plate 2, the caulking groove of two aluminium flake substrates has between incrusted glass plate or porcelain plate the coating to be measured 3 glass plate or porcelain plate part bonded together.
This utility model by being mounted in aluminium flake substrate by glass plate, (position of power is calculated with the centrage of aluminium sheet to reduce moment of torsion, when sheet thickness is 5mm, about 6mm), the simultaneously increase of the thickness of aluminium flake and the mode inlayed make more to be not easy deformation, simultaneously facilitate dismounting, can repeatedly use, without bonding, not only solve the test inaccurate problem of data, also improve the convenience of test simultaneously.
Additionally this flaking method may extend to the test of the shear strength of any other bonding test material, adopts aluminium flake to make substrate and is because glass plate and cannot clamp, and can skid in testing, broken; If running into equally other materials when cannot directly test, it would however also be possible to employ the method, making substrate with aluminium flake and realizing test. Former method must carry out bonding, when testing material with aluminium flake poor attachment, it is impossible to test; In improved method of the present utility model, employing is inlayed, the mode of compression, it is possible to solve very well.
This embodiment is only this utility model preferably detailed description of the invention; but protection domain of the present utility model is not limited thereto; any those familiar with the art is in the technical scope that this utility model discloses; the change that can readily occur in or replacement, all should be encompassed within protection domain of the present utility model. Therefore, protection domain of the present utility model should be as the criterion with scope of the claims.
Claims (5)
1. the aluminium flake substrate for coating shear strength test, it is characterized in that, including: it is arranged on the caulking groove for mosaic glass plate or porcelain plate of the side of aluminium flake substrate and for placing one or more movable buckles of this glass plate of clamping or porcelain plate after glass plate or porcelain plate in caulking groove, described movable buckle includes being fixed on the pivotable movable clamping sheet of caulking groove side and being fixed on the clip of caulking groove opposite side, and described movable clamping sheet is provided with the clamping slot that can coordinate with clip.
2. aluminium flake substrate according to claim 1, it is characterised in that described aluminium flake substrate is provided with the thickness thickness less than the side being not provided with caulking groove of the side of caulking groove.
3. aluminium flake substrate according to claim 1, it is characterised in that described aluminium flake substrate is provided with the thickness 1.0mm less of the thickness of the side being not provided with caulking groove of the side of caulking groove.
4. the shear strength test sample of the aluminium flake substrate according to any one of claims 1 to 3, it is characterized in that, it is made up of the aluminium flake substrate of two part overlappings, two aluminium flake substrates are arranged in the way of caulking groove is relative, the respective caulking groove of two aluminium flake substrates is inlaid with glass plate or porcelain plate, has the coating to be measured glass plate or porcelain plate part bonded together in the caulking groove of two aluminium flake substrates between incrusted glass plate or porcelain plate.
5. shear strength test sample according to claim 4, it is characterised in that described coating to be measured is Prospect on RTV of Solidified Silicon Rubber in Normal Temperature for Insulator.