CN205134068U - Photocatalyst tiO2 hydrosol concreties in fabric apparatus for producing - Google Patents
Photocatalyst tiO2 hydrosol concreties in fabric apparatus for producing Download PDFInfo
- Publication number
- CN205134068U CN205134068U CN201520937412.8U CN201520937412U CN205134068U CN 205134068 U CN205134068 U CN 205134068U CN 201520937412 U CN201520937412 U CN 201520937412U CN 205134068 U CN205134068 U CN 205134068U
- Authority
- CN
- China
- Prior art keywords
- fabric
- hydrosol
- photocatalyst
- producing
- roller
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The utility model discloses a photocatalyst tiO2 hydrosol concreties in fabric apparatus for producing, pad groove, roll roller, draw and lay including fabric conveying roller, the hydrosol of process in proper order be equipped with, design drying equipment and finished product fabric cloth roller, the hydrosol pads the inslot establishes temperature control equipment. The tiO2 solid content rate on the photocatalyst fabric surface of the final output of this apparatus for producing aim at promotes the stability of photocatalyst fabric product and the final catalysis performance of photocatalyst, and improves production efficiency up to more than 80%.
Description
Technical field
The utility model relates to photocatalyst product production equipment field, is specifically related to photocatalyst TiO
2the hydrosol is consolidated in fabric production apparatus.
Background technology
Light urges matchmaker to be a kind of with nanosized TiO_2 being the general name with the photosemiconductor material of photo-catalysis function of representative, it is the current most ideal material administering indoor environmental pollution in the world, under the effect of light, produce strong catalytic degradation function, as toxic and harmfuls such as formaldehyde in air of effectively degrading; Effectively can kill various bacteria, antibiotic rate is up to 99.99%, and the toxin that bacterium or fungi can be discharged decomposes and harmless treatment; Also possesses the function such as deodorizing, anti-soil simultaneously.
In recent years, due to the appearance of " finishing pollution syndrome ", pollution of indoor environment is frequently existing, becomes the focus that people pay close attention to.According to authority, exceed standard at the house fitting pollution of China more than 70%, and seriously polluted exceeding standard reaches more than 30%.It not only can cause the diseases such as pneumonia, tracheitis, leukaemia, cerebral thrombus, also may cause a series of diseases such as pregnant woman miscarries, newborn teratogenesis.
Arranged by nanosized TiO_2 in fabric face, form photocatalyst product, meet consumer's " demand for security ", market prospects are very wide.It is form shaping after dipped for the common fabric nanosized TiO_2 hydrosol that Photo-Catalyst Fabric arranges, but the process conditions in arranging are most important, nanosized TiO_2 in the hydrosol is bonded to final solid content on fabric and stability, directly affects the final catalytic performance of the stable of Photo-Catalyst Fabric product and photocatalyst.Therefore a set of rationally complete production equipment is very important for the realization arranging required process conditions.
Utility model content
The technical problems to be solved in the utility model is to provide photocatalyst TiO
2the hydrosol is consolidated in fabric production apparatus, is applicable to TiO
2hydrosol finish fabric, can ensure fabric face nanoscale TiO
2solid content is up to more than 80%, and stability is high, and photocatalysis performance is strong.
The utility model is achieved through the following technical solutions:
Photocatalyst TiO
2the hydrosol is consolidated in fabric production apparatus, comprise fabric successively the conveying roller of process, the hydrosol pad groove, roll compacting roller, draw cloth equipment, shaping and drying equipment and finished textile product cloth beam, the described hydrosol pads in groove establishes temperature control device.
The further improvement project of the present invention is, described roll compacting roller is two rollers relatively rotated, and fabric closely passes between its intermediate gap.
The present invention further improvement project is, it is 20 ~ 60 DEG C that the described hydrosol pads temperature control device design temperature in groove.
The present invention further improvement project is, in described shaping and drying equipment, temperature is set as 160 ~ 180 DEG C.
The present invention further improvement project is, the biography speed of described conveying roller is 20 ~ 40 ms/min.
The utility model compared with prior art, has following obvious advantage:
Photo-catalytic nano TiO
2the hydrosol is consolidated in the method for fabric needs to limit the fabric speed of travel, hydrosol temperature keeps, the setting of shaping and drying temperature.The restriction object of process conditions is the TiO on the Photo-Catalyst Fabric surface of final output
2solid content, up to more than 80%, promotes the final catalytic performance of the stable of Photo-Catalyst Fabric product and photocatalyst.Therefore the rational production line of the utility model meets manufacturing technique requirent.
Accompanying drawing explanation
Fig. 1 is the utility model structural representation.
Detailed description of the invention
Photocatalyst TiO
2the hydrosol is consolidated in fabric production apparatus, comprise fabric 21 successively the conveying roller 22 of process, the hydrosol pad groove 23, roll compacting roller 24, draw cloth equipment 25, shaping and drying equipment 26 and finished textile product cloth beam 27, the described hydrosol pads in groove 23 establishes temperature control device 28.Described roll compacting roller 24 is two rollers relatively rotated, and fabric closely passes between its intermediate gap.The biography speed of described conveying roller is 20 ~ 40 ms/min; It is 20 ~ 60 DEG C that the described hydrosol pads temperature control device 28 design temperature in groove 23; In described shaping and drying equipment 26, temperature is set as 160 ~ 180 DEG C.
Photocatalyst TiO
2the hydrosol is consolidated in fabric face production process:
(1) fabric is equipped with photocatalyst TiO through capable being dipped in of conveying roller
2the hydrosol pad groove, hydrosol temperature keep 20 ~ 60 DEG C, the fabric speed of travel is 20 ~ 40 ms/min;
(2) cross roll compacting after fabric goes out to soak turn trough, draw cloth, shaping and drying obtains Photo-Catalyst Fabric, shaping and drying temperature is 160 ~ 180 DEG C.
The TiO on the Photo-Catalyst Fabric surface of final output
2solid content, up to more than 80%, promotes the final catalytic performance of the stable of Photo-Catalyst Fabric product and photocatalyst.
Claims (2)
1. photocatalyst TiO
2the hydrosol is consolidated in fabric production apparatus, it is characterized in that: comprise fabric (21) successively the conveying roller (22) of process, the hydrosol pad groove (23), roll compacting roller (24), draw cloth equipment (25), shaping and drying equipment (26) and finished textile product cloth beam (27), the described hydrosol pads in groove (23) establishes temperature control device (28).
2. photocatalyst TiO according to claim 1
2the hydrosol is consolidated in fabric production apparatus, it is characterized in that: described roll compacting roller (24) is two rollers relatively rotated, and fabric closely passes between its intermediate gap.