CN205036986U - A dash stake hose assembly that is used for self -elevating drilling unit to dash transport high pressure sea water of stake system - Google Patents
A dash stake hose assembly that is used for self -elevating drilling unit to dash transport high pressure sea water of stake system Download PDFInfo
- Publication number
- CN205036986U CN205036986U CN201520637158.XU CN201520637158U CN205036986U CN 205036986 U CN205036986 U CN 205036986U CN 201520637158 U CN201520637158 U CN 201520637158U CN 205036986 U CN205036986 U CN 205036986U
- Authority
- CN
- China
- Prior art keywords
- layer
- wire rope
- mesoglea
- wound around
- hose
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The utility model discloses a dash stake hose assembly that is used for self -elevating drilling unit to dash transport high pressure sea water of stake system, including the hose and with the joint of hose connection, the hose is from interior to being the inlayer film outward in proper order, buffering cloth plaster layer, the first layer mesoglea, first layer wire rope, second floor mesoglea, second floor wire rope, third layer mesoglea, protect cloth plaster layer and outer film outward, first layer wire rope and second floor wire rope's winding angle adopts 50~60, - 50~ - 60 the balanced angle of collocation, through withholding the extrusion of equipment to the contractive pressure overcoat of outside, the wire rope who peels off out to the front end forms the extrusion, the inner core cover and the hose hose lining synusia in close contact with that connect, connect as an organic wholely. The utility model provides a this hose assembly's manufacturing method. The utility model aims at providing a body is light, bending property good, bearing strength is high, the deformation is little, tensile strength is high dashes a hose and preparation method.
Description
Technical field
The utility model relates to rubber product preparation field, and what be specifically related to a kind of conveying high-pressure seawater for self-elevating drilling platform pile punching system rushes a hose assembly.
Background technique
Rush the high-voltage flexible connection that stake flexible pipe is exactly sea water pipe between self-elevating drilling platform Main deck and spud leg, conveying high-pressure seawater.
Rush stake flexible pipe be mainly used in offshore oil probing spontaneous formula drill platform rush in a system, after the operation of spontaneous formula drill platform, need mobile spud leg to extract shoe, the mud around shoe blows loose by the impulse force now will using high pressure sea water generation, makes pile pulling easier.And the existing pipe structure rushing pile pipe is all thick and heavy structure of steel wire on market, structural design is unreasonable, and body weight, bending radius is large.
Model utility content
The purpose of this utility model is to provide that a kind of body is light, good bending property, bearing strength are high, it is little to be out of shape, tensile strength is high rushes a flexible pipe.
In order to achieve the above object, the utility model has following technological scheme:
A kind of conveying high-pressure seawater for self-elevating drilling platform pile punching system of the present utility model rush a hose assembly; the joint comprising flexible pipe and be connected with flexible pipe; this flexible pipe comprises inner film, buffering adhesive layer of cloth, first layer mesoglea, first layer wire rope, second layer mesoglea, second layer wire rope, third layer mesoglea, outer protecting glue layer of cloth and outer film from the inside to the outside successively, and first layer mesoglea, first layer wire rope, second layer mesoglea, second layer wire rope and third layer mesoglea form pressure-bearing skeletal structure jointly.
Wherein, interior film layers is the nitrile butadiene rubber that acrylonitrile content reaches 40%, coordinates oil resistant Weather-resistant and the good interpolation neoprene of ozone resistance, and improves the physical and mechanical properties carbon black of Nitrile Rubber and the elastomer of petroleum resin composition; With thiazole accelerator and thuriam acceserator for vulcanizing accelerator system, with age resister 6PPD, anti-aging agent RD and be full of cracks preventing agent for antiaging system, with dibutyl ester for softening Plasticising system.
First layer mesoglea in pressure-bearing skeletal structure, second layer mesoglea and third layer mesoglea all with bacon rubber, butadiene-styrene rubber for elastic material, the in addition binding system that becomes of silica-hexa-resorcinol system (silica-hexa-resorcinol is resorcinol, formaldehyde donor and and white carbon), new type resin and a small amount of cobalt salt, be reinforcement system again with high wear-resistant carbon black, make it to bond and in the space fully filled up between framework layer, define the enhancement tackiness agent having good adhesive property with wire rope and the reinforcing agent that heat production is little under dynamic action.
Outer glue-line sheet thinks that neoprene is sizing material, take metallic oxide as vulcanizing system, with thiazole accelerator and sulfenamide type accelerators for sulfuration Promotion system, take antiozonant as protection system, increase ozone-resistant and the ultraviolet ray ageing of sizing material, add petroleum resin as auxiliary material, in order to ensure the bond properties of sizing material.
In pressure-bearing skeletal structure, first layer wire rope is S twist composite steel rope, and second layer wire rope is Z twist composite steel rope; The winding direction of first layer wire rope is left-handed 50 ° ~ 60 °, and the winding direction of second layer wire rope is dextrorotation 50 ° ~ 60 °; The steel wire gap of first layer wire rope and second layer wirerope-winding steel wire is less than or equal to 2mm.
The preparation method of this punching stake flexible pipe, comprises the steps to make:
The mandrel surface of stake flexible pipe is rushed in wiping for being wound around, the releasing agent modulated is applied in plug and forms releasing agent; The outer surface of plug is wound around inner film, and being wound around should be smooth non-wrinkled, is wound around seamless; Inner film outside is wound around buffering adhesive layer of cloth, relative to the plug longitudinal axis 45 degree of loopings, and whip stitch 4-6mm; Be wound around first layer mesoglea outward at buffering adhesive layer of cloth, be wound around smooth non-wrinkled, be wound around seamless; Be wound around first layer wire rope outward at first layer mesoglea, use S twist composite steel rope, winding direction is left-handed, and lay winding wire ropes should be closely smooth, and gap is less than or equal to 2mm; Be wound around second layer mesoglea outward at first layer wire rope, be wound around smooth non-wrinkled, be wound around seamless; Glue-line is wound around second layer wire rope outward in the second layer, and use Z twist composite steel rope, winding direction dextrorotation, lay winding wire ropes is closely smooth, and gap is less than or equal to 2mm; Be wound around third layer mesoglea outward at second layer wire rope, be wound around smooth non-wrinkled, be wound around seamless; Be wound around outer protecting glue layer of cloth in third layer mesoglea outside, be wound around looping relative to the plug longitudinal axis 45 degree, whip stitch 4-6mm; Protecting glue layer of cloth is wound around outer film outward outside, is wound around smooth non-wrinkled, is wound around seamless; Use nylon water cloth to be wrapped in outside outer film, be wound around two-layer, water cloth joint clearance should be not less than 1m; In sulfurizing pot, put into sulfuration chassis, close the exhaust steam valve of sulfurizing pot, the steam inlet valve opening sulfurizing pot carries out warm tank, and warm tank condition is 0.16MPa × 10 ~ 20min; After temperature tank terminates, open the outlet valve exhaust steam of sulfurizing pot, without when swashing steam flow in tank, open cover pull-out vulcanized vehicle; Sulfuration chassis cushion is put in order, the flexible pipe having twined water cloth is arranged in bundle jail on vulcanized vehicle, sulfuration chassis is sent into sulfurizing pot, and shuts cover; Open steam inlet valve, in tank, send into steam, when temperature reaches 150 DEG C, start to calculate sulfurizing time, cure time 45 minutes; After sulfuration terminates, unlatching outlet valve exhaust steam, without when swashing steam flow in tank, opens cover, and pull-out vulcanized vehicle also cools the sebific duct being tied with nylon water cloth with cold water; The sebific duct being tied with nylon water cloth is fixed on forming machine, nylon water cloth is led out, leave flexible pipe in ventilation together with plug; Plug is taken out from flexible pipe;
Flexible pipe is balanced straight line and is placed, and carries out length cutting to flexible pipe; The inner film at flexible pipe two ends and outer film peel off by size according to the rules, expose wire rope, remove the included glue of clean wire rope with grafter, to polish the outer attached glue of clean wire rope, and wipe clean clearly with solvent with wire wheel; Inner core cover and the contractive pressure overcoat of hose coupling are installed, by the extruding of crimping equipment to the contractive pressure overcoat of outside, extruding is formed to the wire rope that front end is stripped out, play the effect of the anti-pull-off of joint, glue close contact in the inner core cover of joint and flexible pipe, extruded by the contractive pressure overcoat of outside, internal glue forms seal action.
Owing to taking above technological scheme, the utility model has the advantage of:
The overall product using above method to obtain has that body is light, good bending property, bearing strength are high, it is little to be out of shape, tensile strength is high, the feature of simple to operate, easy to use, stable performance;
The design of the inner glue layer sheet of body, both ensure that the oil resistance of sizing material in turn ensure that anti-weather-aging property and the ozone resistance of sizing material, had improve physical and mechanical properties, and not swelling by medium in Long-Time Service situation and gas permeates again, reaches zero leakage requirement;
The first layer mesoglea of body, first layer wire rope, second layer mesoglea, second layer wire rope and third layer mesoglea form pressure-bearing skeletal structure jointly, play wire rope bonding between layers and buffer function, to ensure density and the integrity of pipe structure, thus the fatigue under scrubbing reduced between body framework layer in a dynamic state and heat-dissipating impact, prevent framework layer from occurring delamination, make bond properties reach the bonding strength of ∮ 3.5 more than Galvanized Steel Wire Rope 1300N/12.5mm; Interlayer laminating firmly, do not occur that wire rope is loose, multilayer wire rope is made to be bonded as one flexibly, improve the bending properties of sebific duct and anti-dynamic deformation torsion capacity, the medium osmosis impact in using can be ensured simultaneously, so namely, require that sizing material has good adhesiveness, have good elasticity, ductility and flexible resistance again;
The design of the outer film of body, makes skin have good tensile strength, tearing toughness and elongation percentage, can play again the effect of ozone-resistant and ultraviolet ray ageing simultaneously.
The winding angle of first layer wire rope layer and the second wire rope layer adopts the balance angle of 54 ° 44 ' ,-54 ° 44 ', this angle is optimal angle, also can change between 50 ° ~ 60 °, one can be found during flexible pipe pressure-bearing to balance angle, flexible pipe is made to have extraordinary sealing and pressure-bearing stability, bear higher pressure, control flexible pipe distortion.
Accompanying drawing explanation
Fig. 1 is that the utility model rushes each construction layer schematic diagram of stake flexible pipe;
Fig. 2 is schematic diagram after the process of the utility model hose end cutting stripping glue;
Fig. 3 is that schematic diagram assembled by flexible pipe and joint;
Fig. 4 is that schematic diagram withheld by joint;
Fig. 5 is the schematic flow sheet of method of the present utility model.
In figure: the outer protecting glue layer of cloth of 1-inner film, 2-buffering adhesive layer of cloth, 3-first layer mesoglea, 4-first layer wire rope, 5-second layer mesoglea, 6-second layer wire rope, 7-third layer mesoglea, 8-, the outer film of 9-, 10-inner core cover, 11-contractive pressure overcoat 12-flexible pipe, 13-ridge are convex, 14-seam
Embodiment
The utility model is described in detail by specific embodiment below in conjunction with accompanying drawing:
Embodiment 1:
As shown in Figure 1, a kind of conveying high-pressure seawater for self-elevating drilling platform pile punching system of the present utility model rush a hose assembly, this flexible pipe is followed successively by inner film 1, buffering adhesive layer of cloth 2, first layer mesoglea 3, first layer wire rope 4, second layer mesoglea 5, second layer wire rope 6, third layer mesoglea 7, outer protecting glue layer of cloth 8 and outer film 9 from the inside to the outside; Wherein, first layer mesoglea 3, first layer wire rope 4, second layer mesoglea 5, second layer wire rope 6 and third layer mesoglea 7 form pressure-bearing skeletal structure jointly.
Inner film is the nitrile butadiene rubber that acrylonitrile content reaches 40%, interpolation neoprene, carbon black and petroleum resin are that the proportioning mixing of 7:3:2:1 is obtained with mass ratio, add thiazole accelerator and thiuram, age resister 6PPD, chap preventing agent, dibutyl ester in the process making this film; Mesoglea in pressure-bearing skeletal structure with bacon rubber, butadiene-styrene rubber for colloidal materials, the in addition binding system that becomes of silica-hexa-resorcinol system (silica-hexa-resorcinol is resorcinol, formaldehyde donor and and white carbon), new type resin and a small amount of cobalt salt, then be reinforcement system with high wear-resistant carbon black; Outer glue-line sheet thinks that neoprene is sizing material, take metallic oxide as vulcanizing system, with thiazole accelerator and sulfenamide type accelerators for sulfuration Promotion system, take antiozonant as protection system, adds the bond properties that petroleum resin ensure sizing material.
As shown in Figure 5, make the step of above-mentioned flexible pipe, first using plug as supporter, use for spiral rubber hose thereon, before preparing sebific duct, by clean for plug clean; Happy auspicious solid 1808 releasing agents of modulation, releasing agent is stirred to the liquid that is creamy white, plug is coated with auspicious solid 1808 releasing agents of pleasure that one deck has been modulated, and the effect of releasing agent is after sebific duct has been prepared and shaped, and can be taken out from sebific duct by plug smoothly; The outer surface of plug is wound around inner film, and being wound around should be smooth non-wrinkled, and be wound around seamless, the thickness of inner film is about 0.5mm, and many plugs can be adopted during preparation to carry out simultaneously; In inner film outer felt around buffering adhesive layer of cloth, buffering adhesive layer of cloth can be high-tenacity fiber cord, buffering adhesive layer of cloth relative to the plug longitudinal axis 45 degree of loopings, whip stitch 4mm; Be wound around first layer mesoglea outward at buffering adhesive layer of cloth, be wound around smooth non-wrinkled, be wound around seamless; Be wound around first layer wire rope outward at first layer mesoglea, use Φ 2.1mmS twist composite steel rope, winding direction is left-handed, and lay winding wire ropes is closely smooth, and gap is less than or equal to 2mm; Be wound around second layer mesoglea outward at first layer wire rope, be wound around smooth non-wrinkled, be wound around seamless; Glue-line is wound around second layer wire rope outward in the second layer, use Φ 2.1mmZ twist composite steel rope, winding direction dextrorotation, lay winding wire ropes is closely smooth, and gap is less than or equal to 2mm, in fact in the present embodiment, first layer wire rope is for have angle 54 ° 44 ' relative to sebific duct longitudinal center axis, second layer wire rope, for have angle-54 ° 44 ' relative to sebific duct longitudinal center axis, wherein left-handedly represents counterclockwise, and dextrorotation represents clockwise direction; Be wound around third layer mesoglea outward at second layer wire rope, be wound around smooth non-wrinkled, be wound around seamless; Be wound around outer protecting glue layer of cloth in third layer mesoglea outside, be wound around looping relative to the plug longitudinal axis 45 degree, whip stitch 5mm, outer protecting glue layer of cloth is high-tenacity fiber cord; Protecting glue layer of cloth is wound around outer film outward outside, is wound around smooth non-wrinkled, is wound around seamless; Use the nylon water cloth that width is 110mm to be wrapped in outside outer film, be wound around two-layer, water cloth joint clearance should be not less than 1m, to carry out pressure treatment.
Carry out vulcanizing treatment to the flexible pipe be wound around afterwards, put into sulfuration chassis in sulfurizing pot, close the exhaust steam valve of sulfurizing pot, the steam inlet valve opening sulfurizing pot carries out warm tank, and warm tank condition is 0.16MPa × 10-20min; After temperature tank terminates, open the outlet valve exhaust steam of sulfurizing pot, without when swashing steam flow in tank, open cover pull-out vulcanized vehicle; Sulfuration chassis cushion is put in order, the flexible pipe having twined water cloth is arranged in bundle jail on vulcanized vehicle, sulfuration chassis is sent into sulfurizing pot, and shuts cover; Open steam inlet valve, in tank, send into steam, when temperature reaches 150 DEG C, start to calculate sulfurizing time, cure time 45 minutes; After sulfuration terminates, open outlet valve exhaust steam, without when swashing steam flow in tank, open cover, pulling out vulcanized vehicle and cooling with cold water the sebific duct being tied with nylon water cloth is fixed on forming machine by the sebific duct being tied with nylon water cloth, is led out by nylon water cloth, leaves flexible pipe in ventilation together with plug; Plug is taken out from flexible pipe; The flexible pipe handled well is balanced straight line to place, length cutting is carried out to flexible pipe; As shown in Figure 2, the inner film at flexible pipe two ends and outer film peel off by size according to the rules, inner film is peeled off and is of a size of 65mm, outer film is respectively peeled off and is of a size of 153mm, inner core cover and the contractive pressure overcoat of hose coupling are installed, by the extruding of crimping equipment to the contractive pressure overcoat of outside, extruding is formed to the wire rope that front end is stripped out, play the effect of the anti-pull-off of joint, glue close contact in the inner core cover of joint and flexible pipe, extruded by the contractive pressure overcoat of outside, internal glue forms seal action.
What the model using the present embodiment method to obtain was CZ2K rushes a flexible pipe, and internal diameter is 51mm, and external diameter is 77mm.
Embodiment 2
The sizing material that each glue-line of flexible pipe uses is identical with embodiment 1.
When making flexible pipe, using plug as supporter, use for spiral rubber hose thereon, before preparing sebific duct, by clean for plug clean; Happy auspicious solid 1808 releasing agents of modulation, releasing agent is stirred to the liquid that is creamy white, plug is coated with auspicious solid 1808 releasing agents of pleasure that one deck has been modulated, and the effect of releasing agent is after sebific duct has been prepared and shaped, and can be taken out from sebific duct by plug smoothly; The outer surface of plug is wound around inner film, and being wound around should be smooth non-wrinkled, is wound around seamless, many plugs can be adopted during preparation simultaneously to carry out; In the first inner film outer felt around buffering adhesive layer of cloth, buffering adhesive layer of cloth can be high-tenacity fiber cord, buffering adhesive layer of cloth relative to the plug longitudinal axis 45 degree of loopings, whip stitch 5mm; Be wound around first layer mesoglea outward at buffering adhesive layer of cloth, be wound around smooth non-wrinkled, be wound around seamless; Be wound around first layer wire rope outward at first layer mesoglea, use Φ 4.0mmS twist composite steel rope, winding direction is left-handed, and lay winding wire ropes is closely smooth, and gap is less than or equal to 2mm; Be wound around second layer mesoglea outward at first layer wire rope, be wound around smooth non-wrinkled, be wound around seamless; Glue-line is wound around second layer wire rope outward in the second layer, use Φ 4.0mmZ twist composite steel rope, winding direction dextrorotation, lay winding wire ropes is closely smooth, and gap is less than or equal to 2mm, in fact in the present embodiment, first layer wire rope is for have angle 54 ° 44 ' relative to sebific duct longitudinal center axis, second layer wire rope, for have angle-54 ° 44 ' relative to sebific duct longitudinal center axis, wherein left-handedly represents counterclockwise, and dextrorotation represents clockwise direction; Be wound around third layer mesoglea outward at second layer wire rope, be wound around smooth non-wrinkled, be wound around seamless; Be wound around outer protecting glue layer of cloth in third layer mesoglea outside, be wound around looping relative to the plug longitudinal axis 45 degree, whip stitch 5mm, outer protecting glue layer of cloth is high-tenacity fiber cord; Protecting glue layer of cloth is wound around outer film outward outside, is wound around smooth non-wrinkled, is wound around seamless; Use the nylon water cloth that width is 110mm to be wrapped in outside outer film, be wound around two-layer, water cloth joint clearance should be not less than 1m, to carry out pressure treatment.Subsequent step is with embodiment 1.
What the model using the present embodiment method to obtain was CZ3K rushes a flexible pipe, and internal diameter is 102mm, and external diameter is 139mm.
Embodiment 3
The sizing material that each glue-line of flexible pipe uses is identical with embodiment 1.
Using plug as supporter when making flexible pipe, use for spiral rubber hose thereon, before preparing sebific duct, by clean for plug clean; Happy auspicious solid 1808 releasing agents of modulation, releasing agent is stirred to the liquid that is creamy white, plug is coated with auspicious solid 1808 releasing agents of pleasure that one deck has been modulated, and the effect of releasing agent is after sebific duct has been prepared and shaped, and can be taken out from sebific duct by plug smoothly; The outer surface of plug is wound around inner film, and being wound around should be smooth non-wrinkled, is wound around seamless, many plugs can be adopted during preparation simultaneously to carry out; In the first inner film outer felt around buffering adhesive layer of cloth, buffering adhesive layer of cloth can be high-tenacity fiber cord, buffering adhesive layer of cloth relative to the plug longitudinal axis 45 degree of loopings, whip stitch 6mm; Be wound around first layer mesoglea outward at buffering adhesive layer of cloth, be wound around smooth non-wrinkled, be wound around seamless; Be wound around first layer wire rope outward at first layer mesoglea, use Φ 3.0mmS twist composite steel rope, winding direction is left-handed, and lay winding wire ropes is closely smooth, and gap is less than or equal to 2mm; Be wound around second layer mesoglea outward at first layer wire rope, be wound around smooth non-wrinkled, be wound around seamless; Glue-line is wound around second layer wire rope outward in the second layer, use Φ 3.0mmZ twist composite steel rope, winding direction dextrorotation, lay winding wire ropes is closely smooth, and gap is less than or equal to 2mm, in fact in the present embodiment, first layer wire rope is for have angle 54 ° 44 ' relative to sebific duct longitudinal center axis, second layer wire rope, for have angle-54 ° 44 ' relative to sebific duct longitudinal center axis, wherein left-handedly represents counterclockwise, and dextrorotation represents clockwise direction; Be wound around third layer mesoglea outward at second layer wire rope, be wound around smooth non-wrinkled, be wound around seamless; Be wound around outer protecting glue layer of cloth in third layer mesoglea outside, be wound around looping relative to the plug longitudinal axis 45 degree, whip stitch 5mm, outer protecting glue layer of cloth is high-tenacity fiber cord; Protecting glue layer of cloth is wound around outer film outward outside, is wound around smooth non-wrinkled, is wound around seamless; Use the nylon water cloth that width is 110mm to be wrapped in outside outer film, be wound around two-layer, water cloth joint clearance should be not less than 1m, to carry out pressure treatment.Subsequent step is with embodiment 1.
What the model using the present embodiment method to obtain was CZ3K rushes a flexible pipe, and internal diameter is 51mm, and external diameter is 86mm.
Embodiment 4
As shown in Figure 3, Figure 4, inner core cover 10 and the contractive pressure overcoat 11 of hose coupling are installed, by the extruding of crimping equipment to the contractive pressure overcoat 11 of outside, extruding are formed to the wire rope that front end is stripped out, inner core cover 10 and flexible pipe inner glue layer sheet 1 close contact of joint, connect as one.
Hose coupling inner core cover and contractive pressure overcoat are assembled, inside hose is inserted under the effect of external force, by the contraction deformation of equipment to contractive pressure overcoat, compressive force is formed to the pressure-bearing skeletal structure that flexible pipe mesoglea and wire rope are formed, the distortion of contractive pressure overcoat forms evenly spaced ridge convex 13 to the pressure-bearing skeletal structure that flexible pipe mesoglea and wire rope are formed, prevent joint pull-off, inner core cover is processed with seam 14, the seam 14 of inner core cover forms gapless with the convex 13 pairs of wire rope pressure-bearing skeletons of the ridge of contractive pressure overcoat and is engaged mutually; And inner glue layer sheet 1 is under the punching press of external force, the seamless close contact of inner core cover 10 with joint, forms some sealed rubber rings.
Testing property
Subjects: embodiment 1, embodiment 2, embodiment 3, control group rush stake flexible pipe.
Control group rushes stake flexible pipe and chooses ordinary steel rope as reinforced layer, inside and outside bonding inner glue layer and outer glue-line respectively.
Index test is as following table:
Obviously, above-described embodiment of the present utility model is only for the utility model example is clearly described, and is not the restriction to mode of execution of the present utility model.For those of ordinary skill in the field, can also make other changes in different forms on the basis of the above description.Here cannot give exhaustive to all mode of executions.Every belong to the technical solution of the utility model the apparent change of extending out or variation be still in the row of protection domain of the present utility model.
Claims (5)
1. the conveying high-pressure seawater for self-elevating drilling platform pile punching system rush a hose assembly; the joint comprising flexible pipe and be connected with flexible pipe; it is characterized in that; this flexible pipe comprises inner film, buffering adhesive layer of cloth, first layer mesoglea, first layer wire rope, second layer mesoglea, second layer wire rope, third layer mesoglea, outer protecting glue layer of cloth and outer film from the inside to the outside successively, and described first layer mesoglea, first layer wire rope, second layer mesoglea, second layer wire rope and third layer mesoglea form pressure-bearing skeletal structure jointly.
2. as claimed in claim 1 a kind of conveying high-pressure seawater for self-elevating drilling platform pile punching system rush a hose assembly, it is characterized in that, described first layer wire rope is S twist composite steel rope, and described second layer wire rope is Z twist composite steel rope.
3. as claimed in claim 1 a kind of conveying high-pressure seawater for self-elevating drilling platform pile punching system rush a hose assembly, it is characterized in that, the winding direction of described first layer wire rope is left-handed 50 ° ~ 60 °, and the winding direction of second layer wire rope is dextrorotation 50 ° ~ 60 °
4. as claimed in claim 3 a kind of conveying high-pressure seawater for self-elevating drilling platform pile punching system rush a hose assembly, it is characterized in that, the steel wire gap of first layer wire rope and second layer wirerope-winding steel wire is less than or equal to 2mm.
5. as claimed in claim 1 a kind of conveying high-pressure seawater for self-elevating drilling platform pile punching system rush a hose assembly, it is characterized in that, described buffering adhesive layer of cloth 45 ° be wound around looping, whip stitch 5mm.